Sulfonated polyetherimide having anionic charge and better hydrophilicity than polyetherimide was prepared by reacting polyetherimide with chlorosulfonic acid. To prepare casting solution, from which the membrane having good performance can produce. Polyvinylpyrrolidone as a pore forming agent and volatile weak solvent such as dichloromethane to foml the dense skin layer were added to the sulfonated polyetherimide / N -methyl-2-pyrrolidone solution. Membrane fabricated sulfonated PEl showed better fouling resistance to the protein than those fabricated PEL because of its hydrophilicity. Solute having negative charge was removed effectively with membrane fabricated from the sulfonated PEl because of its the same electron charge.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2000.04a
• /
• pp.109-112
• /
• 2000

• Proceedings of the Membrane Society of Korea Conference
• /
• 1996.10a
• /
• pp.71-72
• /
• 1996

Polyetherimide(PEI)계의 고분자는 막 성능이 우수하고 내열성과 내유기용매성 등이 우수한 열가소성수지로서 film, sheet, tubular형으로 만들 수 있어 한외여과막이나 역삼투막, 기체분리막 등에 이용되고 있다. 한편 투과속도를 높이고, fouling을 줄이기 위한 친수성 향상은 막 소재의 화학적 개질에 있어서 주된 목표이다. sulfonation은 막 재질의 소수성을 감소시켜 water permeability를 향상시키는데 있어서 매우 유용한 방법으로 이온교환수지, 이온교환막, anion형 하전막의 제조에 이용되어 왔다. 본 실험에서는 polyetherimide계 고분자를 chlorosulfonic acid(CSA)를 이용하여 술폰화시킨 sulfonated polyetherimide(SPEI)를 제조하여 막 성능을 측정하였다.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1998.10a
• /
• pp.93-95
• /
• 1998

1. 서론 : 폴리이미드계 고분자는 기계적 성질과 내열성이 우수한 고분자 소재이다. 일반적으로 기체분리막으로서의 유리상 고분자는 기체의 투과성은 결여되지만, 고분자쇄의 동결속박에 의한 자유부피에 따라 기체의 선택성이 높게 나타난다. 본 연구에서는 고분자로서 polyetherimide(PEI) 를 이용하여 제막조건(고분자 농도, air gap, 용매, 내부응고제 주입량 등)을 달리하는 중공사막을 제조하여, 제막변수에 따른 막의 구조 및 기체투과 특성을 검토하였다.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2000.11a
• /
• pp.47-49
• /
• 2000

No Abstract, See Full Text

• Applied Chemistry for Engineering
• /
• v.10 no.4
• /
• pp.515-522
• /
• 1999

Asymmetric polyetherimide membrane were prepared by phase inversion method, and the effects of NaOH concentration and reaction time on the morphology change of the polyetherimide membranes were studied. The morphology of skin layers varied from dense structure to sphere structure with increasing concentration of modification solution. The thickness of dense layer increased with increasing reaction time. However, when either the concentration of modifying solution was very high or the reaction time was very long, the dense layers of the asymmetric membrane were disappeared. From these results, it was found that the surface morphology of the asymmetric polyetherimide membranes depended strongly on the modification conditions such as concentration of modification solution and reaction time. These results might be explained by the hydrolysis reaction of polyetherimide into polyamic acid by the NaOH solution.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1997.10a
• /
• pp.94-95
• /
• 1997

1. 서론 : Polyetherimide를 이용하여 기체분리용 고분자막을 제조하여 막 구조에 대한 첨가제 효과를 규명하고자 하였다. 막 제조는 상전환법에 기초한 습식방사법을 이용하여 Polyetherimide막을 제조하였다. 상전환법에 의한 막의 제조에 있어 막의 구조 및 투과성능은 사용되는 고분자용액의 농도 및 solvent의 종류 그리고 nonsolvent와 고분자 용액에 사용되는 첨가제와 밀접한 관계를 가지고 있다.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1993.04a
• /
• pp.36-37
• /
• 1993

상전이 공정에 의해 제조된 기체분리용 중공사막은 1차적으로 방사원액의 조성과 내.외부응고제의 조성, 중공사 방사조건 그리고 후처리 과정에 의해서 전체적인 구조가 결정되어진다. 특히 기체 분리에 이용되는 Nonprous Membrane의 경우 Dense Skin의 Thickness와 Pinhole의 유무에 따라 투과성과 선택성에 커다란 영향을 미친다. 따라서 최근에는 Dense Skin의 초박막화와 Pinhole이 없는 비대칭막 제조등 폭넓은 연구가 이루어지고 있다. 본 연구에서는 CO$_2$ Gas 분리용 Polyetherimide 중공사막을 제조하여, 중공사막 제조조건과 후처리 조건에 따른 $CO_2/N_2$ Gas의 분리계수를 측정하였다.

• Membrane Journal
• /
• v.9 no.1
• /
• pp.10-16
• /
• 1999

In this study, polyetherimide with pellet state was sulfonated with a chlorosulfonic acid. The volume ratio of carbon tetrachloride (CCI$_4$/1,2-dichloroethane (DCE) was 5/1. Therefore, sulfonated polyetherimide of anionic charge and more hydrophilicity were produced. The optimum reaction conditions of sulfonation were that PES/CSA mole ratio was I/I, temperature were lO$^{\circ}$ and reaction time were 3hr. SPEls having ion capacity in the range of 0.2-1.2meq/mg were synthesized. Through FT-IR, sulfonic acid peak was shown at 1020cm$^{-1}$ and 1170cm$^{-1}$ Polymer dispersity index was broad and we confirmed that PEl was hydrophilzed in the measure of contact angle.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1998.10a
• /
• pp.91-92
• /
• 1998

1. 서론 : 고분자를 소재로 하는 중공사막의 제막은 일반적으로 상전환법(phase inversion method)에 의하여 제조된다. 이 방법에 의한 비대칭막의 생성은 용매가 고분자용액을 빠져나가는 속도와 응결액이 고분자쪽으로 침투되는 속도의 차이에 의해서 막의 1차구조가 형성된다. 그러므로 이 속도를 첨가제 등을 사용하여 조절하므로서 막의 특성을 변화시킬 수 있다. 본 연구에서는 polyetherimide(PEI) 중공사막의 첨가제로서 dioxane 등 9종류를 사용하여 중공사막의 생성 구조에 미치는 영향을 검토하였다.