• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제38회 동계학술대회 초록집
• /
• pp.356-356
• /
• 2010

Tribological behaviors of the hard film on soft substrate system were explored using the hard thin film of diamond-like carbon (DLC) coated the soft polymer of polydimethysiloxane (PDMS). A DLC film with the Young's modulus of 100 GPa was coated on PDMS substrate with Young's modulus of 10 MPa using plasma enhanced chemical vapor deposition (PECVD) technique. The deposition time was varied from 10 sec to 10 min, resulting in nanoscale roughness of wrinkle patterns with the thickness of 20 nm to 510 nm, respectively, at a bias voltage of $400\;V_b$, working pressure 10 mTorr. Nanoscale wrinkle patterns with 20-100 nm in width and 10-30 nm height were formed on DLC coating due to the residual stress in compression and difference in Young's modulus. Nanoscale roughness effect on tribological behaviors was observed by performing a tribo-experiment using the ball-on-disk type tribometer with a steel ball of 6 mm in diameter at the sliding speed of 220 rpm, normal load of 1N and 25% humidity at ambient temperature of $25^{\circ}C$. Friction force were measured with respect to thickness change of coated DLC thin film on PDMS. It was found that with increases the thickness of DLC coating on PDMS, the coefficient of friction decreased by comparison to that of the uncoated PDMS. The wear tracks before and after tribo-test were analyzed using SEM and AFM.

• 공업화학
• /
• 제30권1호
• /
• pp.39-42
• /
• 2019

본 연구에서는 PET 상용 소재를 기반으로 제작된 유수분리막을 오일 폐수 처리에 효과적으로 적용하기 위하여 유수분리장치 성능 향상 및 적절한 소재 선정에 대하여 검토하였다. PET 섬유 소재의 방수 능력과 선택성을 유지할 수 있는 최적 조건을 탐색하였으며, 밀도 $60g/m^2$ 이상의 PET 소재를 2겹 이상으로 사용하여야 분리 효율을 유지하면서 본 연구에서 설계한 단위 셀에 적합한 수준의 방수 능력을 보여주었다. 유수분리장치는 회전하는 타공 원통 구조로 설계되고, 외부에 유수분리막이 감싸는 구조로 장착되어 연속적인 흡착제거가 가능하며, 내부에 부유형 방해판을 설치하여 오일 성분을 강제적으로 유수분리막 방향으로 유도하여 제거 효율과 안정성을 극대화하였다.