• Journal of Korea Foundry Society
• /
• v.27 no.4
• /
• pp.179-183
• /
• 2007

The TiC layer was formed on Ti and Ti alloys by plasma carburizing method. The main experimental parameters for plasma car boozing were temperature and time. XRD, EDX, hardness test and corrosion test were employed to analyze the evolution and material properties of the layer. The preferred orientation of TiC layers is (220) at treated temperature of $700^{\circ}C\;and\;880^{\circ}C$ However, it is changed to (200) at temperature of $800^{\circ}C$ The thickness of carbide layer increase with increasing carburizing temperature. Highest hardness of hardened layer formed on CP-Ti was obtained at the carburizing condition of processing temperature $880^{\circ}C$ and processing time 1080min. The corrosion potential of carburizing specimen was higher than untreated CP-titanium, and corrosion potential increased as carburizing temperature and time increased. Thus the corrosion resistance of CP-Ti was greatly enhanced after plasma carburizing treatment.

• Journal of Surface Science and Engineering
• /
• v.50 no.4
• /
• pp.272-276
• /
• 2017

The response of AISI 310 type austenitic stainless steel to the novel low temperature plasma carburizing process has been investigated in this work. This grade of stainless steel shows better corrosion resistance and high temperature oxidation resistance due to its high chromium and nickel content. In this experiment, plasma carburizing was performed on AISI 310 stainless steel in a D.C. pulsed plasma ion nitriding system at different temperatures in $H_2-Ar-CH_4$ gas mixtures. The working pressure was 4 Torr (533Pa approx.) and the applied voltage was 600 V during the plasma carburizing treatment. The hardness of the samples was measured by using a Vickers micro hardness tester with the load of 100 g. The phase of carburized layer formed on the surface was confirmed by X-ray diffraction. The resultant carburized layer was found to be precipitation free and resulted in significantly improved hardness and corrosion resistance.

• Journal of Advanced Marine Engineering and Technology
• /
• v.41 no.3
• /
• pp.238-244
• /
• 2017

Plasma ion nitriding has been widely used in various industries to improve the mechanical properties of materials, especially stainless steels by increasing the surface hardness. It has the particular advantages of less distortion compared to that in the case of hardening of steel, gas nitriding, and carburizing; in addition, it allows treatment at low-temperatures, and results in a high surface hardness and improved corrosion resistance. Many researchers have demonstrated that the plasma ion nitriding process should be carried out at temperatures of below $450^{\circ}C$ to improve corrosion resistance via the formation of the expanded austenite phase(S-phase). Most experimentals studied to date have been carried out in chloride solutions like HCl or NaCl. However, the electrochemical characteristics for the chloride solutions and natural seawater differ. Hence, in this work, plasma ion nitriding of 304 stainless steels was performed at various temperatures, and the electrochemical characteristics corresponding to the different process temperatures were analyzed for the samples in natural seawater. Finally the optimum plasma ion nitriding temperature that resulted in the highest corrosion resistance was determined.