• Journal of the Korean Ceramic Society
• /
• v.36 no.3
• /
• pp.225-230
• /
• 1999

Ball-on-3-ball 시험에서 이축 강도를 결정하기 위한 방법에 대해 고찰하였다. 알루미나 시편을 이용하여 ball-on-3-ball 시험과 poston-on-3-ball 시험을 하여 이축 강도를 측정하였다. piston-on-3-ball 시험에서의 강도 식과 등가 반지름을 이용하여 계산한 ball-on-3-ball 시험에서의 이축 강도와, piston-on-3-ball 시험에서의 이축 강도를 분산 분석(ANOVA)한 결과, 두 평균이 동일하다고 할 수 있었다. 따라서, ball-on-3-ball 시험에서의 이축 강도는 piston-on-3-ball 시험에서의 강도 식과 등가 반지름을 이용하여 계산할 수 있다. 또한, 유한 요소법을 이용하여 ball-on-3-ball 시험시 시편에 인가되는 응력 분포를 고찰해 보았다.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.4
• /
• pp.269-281
• /
• 2007

Fluoric acid etching is an essential procedure in cementation of reinforced ceramics to tooth surface. But there have been few studies about the changes of surface structure and flexural strength of IPS $Empress^{(R)}$ 2 ceramic according to the etching time. The objectives of this study were to examine the surface structure changes and the difference in biaxial flexural strength of IPS $Empress^{(R)}$ 2 ceramic according to various etching times. Sixty one disk-shaped specimens of IPS $Empress^{(R)}$ 2 ceramic($14mm{\times}1.2mm$) were fabricated for the biaxial flexural strength test and SEM analysis according to the manufacturer's recommendations. Sixty specimens were divided into 6 groups(n=10) according to the time of HF acid etching(0, 20, 180 and 300s)and silane/resin cement application. Each disk was loaded using a piston-on-3 ball biaxial configuration in a universal testing machine. The failure loads(N) were recorded, and the biaxial flexural strength for each disk was calculated. A one-way analysis of variance and independent t-test on transformed fracture strength data were used to determine significant differences between groups. The groups of no cementation showed a trend toward progressive weakening with increasing the etching time. However, this was not statistically significant at p=0.05 level. The groups of resin cementation exhibited no apparent trend in their mean strength values. SEM photomicrographs showed very different results of etching. Within the conditions of this study, alteration of surface topography by acid etching does not have a deleterious effect on the biaxial flexural strength of IPS $Empress^{(R)}$ 2 ceramic.

• Restorative Dentistry and Endodontics
• /
• v.31 no.1
• /
• pp.58-65
• /
• 2006

The possibility of applying a hi-axial flexure strength test on composite resin was examined using three point and hi-axial flexure strength tests to measure the strength of the light-cured resin and to compare the relative reliability using the Weibull modulus. The materials used in this study were light-curing restorative materials, $MICRONEW^{TM},\;RENEW^{(R)}$ (Bisco, Schaumburg, USA). The hi-axial flexure strength measurements used the piston-on-3-ball test according to the regulations of the International Organization for Standardization (ISO) 6872 and were divided into 6 groups, where the radius of the specimens were 12mm (radius connecting the 3-balls: 3.75mm), 16 mm(radius connecting the 3-balls: 5mm), and the thickness were 0.5mm, 1mm, 2mn for each radius. The hi-axial flexure strength of the $MICRONEW^{TM}\;and\;RENEW^{(R)}$ were higher than the three point flexure strength and the Weibull modulus value were also higher in all of the bi-axial flexure strength groups, indicating that the hi-axial strength test is relatively less affected by experimental error. In addition, the 2 mm thick specimens had the highest Weibull modulus values in the hi-axial flexure strength test, and the $MICRONEW^{TM}$ group showed no significant statistical difference (p>0.05). Besides the 2mm $MICRONEW^{TM}$ group, each group showed significant statistical differences (p<0.05) according to the thickness of the specimen and the radius connecting the 3-balls. The results indicate that for the 2mm group, the hi-axial flexure strength test is a more reliable testing method than the three point flexure strength test.