• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.4
• /
• pp.63-68
• /
• 2019

Dielectric and piezoelectric properties of PIN-PMN-PT piezoelectric single crystals with variation of temperature and compressive stress were investigated. The crystal phase of the single crystal was changed from the ferroelectric rhombohedral structure to tetragonal structure in the 110℃ region and from the tetragonal structure to the paraelectric cubic structure in the 190℃ region. The piezoelectric constant and relative dielectric constant were calculated from the rate of change of polarization and displacement with the application of electric field, which was similar to the value measured from the instrument. As the compressive stress applied to the sample increased, the piezoelectric constant d₃₃ and relative dielectric constant values tended to increase. When the compressive stress applied to the sample at 5℃ was 60 MPa, the d₃₃ was calculated as 4,500 pC/N. At 60℃, the relative dielectric constant of 62000 was calculated when the compressive stress applied to the sample was 40 MPa. The increase in piezoelectric constant and relative dielectric constant when the compressive stress increased could be attributed to the phase transition from the rhombohedral structure to orthorhombic.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.32-33
• /
• 2006

In this study, in order to develop multilayer ceramic actuator for ultrasonic nozzle and ultrasonic vibrator, PMN-PNN-PZT ceramics were fabricated using $Li_2CO_3$. $Na_2CO_3$ and ZnO as sintering aids. And then, their piezoelectric and dielectric properties according to the amount of ZnO addition were investigated. The addition of ZnO improved density, dielectric constant, electromechanical coupling factor, mechanical quality factor and piezoelectric d constant of PMN-PNN-PZT ceramics due to the increase of sinterability and accepter doping effect. Electromechanical coupling factor and mechanical quality factor of PMN-PNN-PZT ceramics increased with ZnO amount up to 0.4wt% and then decreased. At the sintering temperature of $900^{\circ}C$ and 0.4wt% ZnO addition, density, dielectric constant, electromechanical coupling factor, mechanical quality factor and piezoelectric d constant showed the optimum value of 7.876g/$cm^2$, 1299, 0.612, 1151 and 369pC/N, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.356-360
• /
• 2002

The piezoelectric properties of $0.05Pb(Al_{0.5}Nb_{0.5})O_3-0.95Pb(Zr_{0.52}Ti_{0.48})O_3+0.7wt%Nb_2O_5+o.5wt%MnO_2$ ceramics with the additive of BaCO$_3$were investigated. As the addition of BaCO$_3$increased from 0 to 0.4 wt%, the dielectric constant ($\epsilon^T _{33}$), piezoelectric constant ($d_33$), electromechanical coupling factor ($k_p$), and mechanical quality factor ($Q_m$) increased, while the dielectric loss ($tan\delta$) decreased. The highest piezoelectric and dielectric properties were observed at $1200^{\circ}C$ of the sintered temperature with 0.4 wt% of $BaCO_3$, and the properties of $d_33$, $k_p$, and $Q_m$ were 339 pC/N, 60% and 1754, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.6
• /
• pp.484-488
• /
• 2009

In this study, in order to develop the lead-free piezoelectric ceramics with high piezoelectric and dielectric properties, $[(K_{0.5}Na_{0.5})_{0.95}Li_{0.05}(Nb_{0.96}Sb_{0.04})]O_3$ ceramics were fabricated using $Ag_2O$ as sintering aid and a conventional mixed oxide process and their piezoelectric and dielectric characteristics were investigated according to the $SrTiO_3$ substitution. $SrTiO_3$ substitution enhanced density, dielectric constant(${\varepsilon}_r$) and electromechanical coupling factor($k_p$). However, mechanical quality factor was deteriorated. And also, Curie temperature ($T_c$), and phase transition temperature($T_p$) were rapidly decreased. At the 0.5 mol% $SrTiO_3$ substitution, density, electromechanical coupling factor($k_p$), dielectric constant(${\varepsilon}_r$) and piezoelectric constant($d_{33}$) of specimen showed the optimum value of $4.437\;g/cm^3$, 0.457, 1294, 265 pC/N, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.10
• /
• pp.966-970
• /
• 2006

We reported on characteristics of the piezoelectric ceramic-polymer composite for the application of the thick-film speaker. The PVDF-PZT composites were fabricated to incorporate the advantages of both ceramic and polymer with various mixing ratios by 3-roll mill mixer. The composite solutions were coated by the conventional screen-printing method on ITO electrode coated PET (Polyethylene terephthalate) polymer film. After depositing the top-electrode of silver-paste, 4 kV/mm of DC field was applied at $120^{\circ}C$ for 30 min to poling the composite films. The value of $d_{33}$ (piezoelectric charge constant) was increased when the PZT weight percent was increased. The maximum value of the $d_{33}$ was 24 pC/N at 70 wt% PZT. But the $g{33}$ (piezoelectric voltage constant) showed the maximum value of $32mV{\cdot}m/N$ at 65 wt% of PZT powder. The SPL (sound pressure level) of the speaker fabricated with the 65:35 composite film was about 68 dB at 1 kHz.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.6
• /
• pp.332-336
• /
• 2016

In this study, in order to develop the composition ceramics for ultrasonic sensor with high $d_{33}*g_{33}$, $Pb_{1-3x/2}Bix(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_{0.09}(Zr_{0.5}Ti_{0.5})_{0.88}O_3$(PMW-PNN-PZT) system ceramics were prepared using CuO as sintering aids. And then, their microstructure, piezoelectric and dielectric characteristics were systemetically investigated with bismuth substitution. The PMW-PNN-PZT ceramic specimens could be sintered at sintering temperature of $940^{\circ}C$ by adding sintering aids. At x=0.015 specimen, the density, electromechanical coupling factor($k_p$), dielectric constant, piezoelectric constant($d_{33}$) and piezoelectric figure of merit($d_{33}*g_{33}$) indicated the optimal properties of $7.90g/cm^3$, 0.67, 2,511, 628 pC/N, and $17.7pm^2/N$, respectively, for duplex ultrasonic sensor application.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.620-623
• /
• 2003

Non-linear behaviors of multilayer piezoelectric ceramic actuator (MCA) were investigated under electrical and mechanical stress. DC 100 V bias was applied to the MCA to obtain displacement. Laser vibrometer, which using Doppler effect, was employed to characterize displacement caused by $d_{33}$ mode of MCA. To understand this non-linear behavior of MCA, displacement was measured and compared under different load states. By increasing load, electric field-induced strain and piezoelectric constant($d_{33}$) of MCA was decreased. We attribute this phenomenon to the domain wall motion and depoling of MCA under heavy load.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.3
• /
• pp.214-219
• /
• 2000

In this paper the structural dielectric and piezoelectric properties of Pb［(M $g_{1}$2// $W_{1}$2/)$_{x}$-(N $i_{1}$3//N $b_{2}$3/)$_{0.15-x-(Zr_{0.5})}$ $Ti_{0.5}$)$_{0.85}$］ $O_3$ (x=0.0~0.10) ceramic were investigated with the substitution of Pb(M $g_{1}$2// $W_{1}$2/) $O_3$. According to the substitution of Pb(M $g_{1}$2//W/1/2/) $O_3$ curie temperatures were slightly decrease due to the decrease of the tetrag-onality of crystal structure and coercive fields were decreased. Up to the substitution of Pb(M $g_{1}$2// $W_{1}$2/) $O_3$ 3mol%,remnant polarization dielectric constant piezoelectric constant were increased. Dielectric constant and electro-mechanical coupling factor( $k_{p}$, $k_{31}$ ) were appeared the highest value of 2230, 0.64, and 0.38 and piezoelectric constant( $d_{33}$ , $d_{31}$ ) was the largest value of 418, 202($\times$10$^{-12}$ /C/N), respectively, when the substitution amount of Pb(M $g_{1}$2// $W_{1}$2/N) respectively, when the substitution amount of Pb(M $g_{1}$2// $W_{1}$2/) $O_3$ was 3mol%.s 3mol%.%.

• Proceedings of the KIEE Conference
• /
• 1991.11a
• /
• pp.293-295
• /
• 1991

In this study, we investigated the possibilty that $Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3-PbZrO_3$ ceramics with strontium substitutions could be used for piezoelectric sounders. Piezoelectric buzzer is one of them. By partially substituting Sr for Ph, dielectric constants had values greater than 2000, the value proper piezoelectric buzzer, piezoelectric constant($d_{31}$) had a maximum value, 298 $[10^{-12}C/N]$, at the Sr 5 mol % substitution. Sound level of piezoelectric buzzer had the highest value of 91 dB at the Sr 5 mol % substitution.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.981-984
• /
• 2001

The piezoelectric properties of 0.05pb(A $l_{0.5}$N $b_{0.5}$) $O_3$-0.95Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_3$+0.7wt%N $b_2$ $O_{5}$ +0.5wt%Mn $O_2$ceramics with the additives of BaC $O_3$were investigated. For the additions of BaC $O_3$, the dielectric constant ($\varepsilon$$^{T}$ $_{33}$ ), the piezoelectric constant ( $d_{33}$ ), the electromechanical coupling factor ( $k_{p}$ ), and . the mechanical quality factor ( $Q_{m}$ ) were increased, but dielectric loss (tan$\delta$) was decreased. The highest piezoelectric properties and dielectric properties were observed at the sintered temperature of 120$0^{\circ}C$ and 0.4 wt% of BaC $O_3$, and the properties of $d_{33}$ , $k_{p}$ , and $Q_{m}$ were 339(x10$^{-12}$ C/N), 59% and 1754, respectively.vely.y.y.