[Li0.055(K0.5Na0.5)0.945](Nb1-xTax)O3 (0.05 ≤ x ≤ 0.25) ceramics were prepared by the partial sol-gel (PSG) method to improve the microstructure homogeneity of Ta5+ ion and were compared to those prepared by the conventional mixed oxide (CMO) method. For the PSG method, Ta(OC2H5)5 was directly reacted with calcined [Li0.055(K0.5Na0.5)0.945]NbO3 powders and the specimens sintered at 1100 ℃ for 5 hrs showed a single phase with a perovskite structure. Compared to the specimens prepared by conventional mixed oxide powders, the relative ratio of tetragonal phase to orthorhombic phase of the sintered specimens prepared by Ta(OC2H5)5 was larger than that of the sintered specimens prepared by Ta2O5. The electromechanical coupling factor (kp), piezoelectric constant (d33) and dielectric constant (εr) of the sintered specimens were increased with Ta5+ content. These results could be attributed to the decrease of the orthorhombic-tetragonal polymorphic phase transition temperature (To-t), which could be evaluated by oxygen octahedral distortion. Strain of the sintered specimens prepared by the PSG method was higher than that of specimens prepared by the CMO method due to the increase of relative density. The effects of crystal structure on the strain characteristics of the specimens were also discussed.

• 한국세라믹학회지
• /
• 제41권1호
• /
• pp.30-35
• /
• 2004

스크린 인쇄법 및 PZT sol 처리의 복합공정을 적용하여 $30{\mu}m$ 두께의 PMW-PZT 후막을 Pt/$TiO_2$/$SiN_x$Si 기판위에 제작하였다. 그 결과 PZT sol 처리 횟수가 증가함에 따라 후막의 소결 밀도가 증가하고 전기적, 압전 특성의 증진되는 것을 관찰할 수 있었다. $800^{\circ}C$에서 소결한 10회 sol 처리한 PMW-PZT 후막은 745의 유전상수 및 155 pC/N의 $d_33$ 값을 나타내었다.

• Advances in materials Research
• /
• 제5권2호
• /
• pp.93-105
• /
• 2016

KNN-based ceramics modified with small amounts of $Bi_4Zr_3O_{12}$ (BiZ) has been synthesized using high-throughput experimentation (HTE). The results from X-ray diffraction show that for samples with base composition $(K_{0.5}Na_{0.5})NbO_3$ (KNN), the phase present changes from orthorhombic to pseudo-cubic with more than 0.2 mol% BiZ addition; for samples with base composition $(K_{0.48}Na_{0.48}Li_{0.04})(Nb_{0.9}Ta_{0.1})O_3$ (KNNLT), the phase present changes from a mixture of orthorhombic and tetragonal symmetry to pseudo-cubic with more than 0.4 mol % while for samples with base composition $(K_{0.48}Na_{0.48}Li_{0.04})(Nb_{0.86}Ta_{0.1}Sb_{0.04})O_3$ (KNNLST), the phase present is tetragonal with <0.3 mol% BiZ addition and transforms to pseudo-cubic with more dopant addition. The microstructures of the samples show that addition of BiZ decreases the average grain size and increases the volume of pores at the grain boundaries. The values of dielectric constant for KNN and KNNLT compositions increase slightly with BiZ addition while that for KNNLST decreases gradually with BiZ addition. The dielectric loss values are between 0.02 and 0.04 for KNNLT and KNNLST compositions while they are ~ 0.05 for KNN samples. The resistivity values increases with BiZ addition and values in the range of $10^{10}{\Omega}cm$ and $10^{12}{\Omega}cm$ are obtained. The piezoelectric charge coefficient ($d{^*}_{33}$) is highest for KNNLST samples and decreases gradually from ~400 pm/V to ~100 pm/V with BiZ addition.