• 반도체디스플레이기술학회지
• /
• 제15권1호
• /
• pp.70-75
• /
• 2016

GZO films prepared on ITO glasses were annealed at various temperatures in a vacuum condition to research the relationship between oxygen vacancies and optical properties. GZO films after annealing in a vacuum showed the various optical-chemical properties depending on the annealing temperatures and oxygen gas flow rate during the deposition. The oxygen vacancy of GZO film prepared by oxygen gas flows of 22 sccm increased with increasing the annealing temperatures, because of the extraction of oxygen by the annealing. But the intensity of photoluminance of GZO with 22 sccm decreased in accordance with the annealing temperature, because of the reduction of ionized charge carriers. The oxygen vacancy by the extraction of oxygen enhanced a depletion, so the widen depletion had the strong Schottky barrier and the PL intensity due to the low carrier density decreased.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 추계학술대회 논문집
• /
• pp.594-597
• /
• 1999

The new green and red phosphors for PDP application activated by T $b^{3+}$ and E $u^{3+}$ were synthesized, and their photoluminance properties were investigated. It was found that the brightness of $Al_3$Gd $B_4$ $O_{12}$ :T $b^{3+}$ green phosphor under 147nm VUV irradiation was higher than that of commercial Z $n_2$ $SiO_4$:M $n^{2+}$ phosphor. But the emitting intensity of A1$_3$Gd $B_4$ $O^{12}$ :E $u^{3+}$ red phosphor was inferior to the commercial (Y,Gd)B $O_3$:E $u^{3+}$. $Al_3$Gd $B_4$ $O_{12}$ Phosphor had a strong excitation band at 160nm associated with the host absorption, and also the photoluminance excitation intensity of $Al_3$Gd $B_4$ $O_{12}$ :T $b^{3+}$ was higher than that of Z $n_2$ $SiO_4$:M $n^{2+}$, but the intensity of $Al_3$Gd $B_4$ $O_{12}$ :E $u^{3+}$ phosphor was smaller than (Y,Gd)B $O_3$:E $u^{3+}$ phosphor In the VUV range. C $e^{3+}$ co-doping in A1$_3$Gd $B_4$ $O^{12}$ :E $u^{3+}$ and substitution of $Al^{3+}$ by G $a^{3+}$ A1$_3$Gd $B_4$ $O^{12}$ :E $u^{3+}$ phosphor were tried, but they did not improved the optical property .d the optical property .ty .

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 추계학술대회 논문집
• /
• pp.107-110
• /
• 1999

The ultrasonic spray method was employed to make (Y,Gd)BO$_3$:Eu Phosphor, and its optical properties under 147nm VUV and 254 nm UV excitations were characterized and then compared with that produced by the solid-state reaction. The mixed solution of acetate hydrates of Y, Gd, Eu and boric acid diluted in water or methanol was used as the precursor fur the spray. It was found that (Y,Gd)BO$_3$:Eu phosphor made by this ultrasonic spray had a spherical shape and fine particle size of 1${\mu}{\textrm}{m}$. The crystalline structure for the as-sprayed phosphor was amorphous, but it converted into the same polycrystalline phase of solid state reaction after post heat treatment at 110$0^{\circ}C$ for 2hr. The emitting intensity under VUV and UV excitations for the spray-formed (Y,Gd)BO$_3$:Eu phosphor, however, was inferior to the later one. The excitation spectra were also studied and compared under VUV and UV excitations to explain the change of emitting intensity with Gd substitution in (Y$_{1-x}$ Gd$_{x}$)BO$_3$:Eu Phosphors made by spray and solid state reaction.on.

• 한국재료학회지
• /
• 제10권3호
• /
• pp.204-211
• /
• 2000

초음파 분무법으로 $(Y,Gd)BO_3:Eu$의 PDP 적색 형광체를 제조하여 147nm VUV 여기에 따른 발광 특성을 분석하였다. 초음파 분무에 사용된 전구체 용액은 Y, Gd, Eu의 아세트산염과 $H_3BO_3$를 증류수에 용해하여 1.7MHz의 초음파 분무기로 고온의 반응관내로 분무하였다. 분무된 액적은 반응관내에서 통과시 불충분한 반응으로 C-C와 C-H를 함유한 비정질 상이었으나, $1100^{\circ}C$에서 추가 열처리 한 시편은 고상반응법으로 제조한 형광체와 동일한 결정구조와 성분을 보였다. 고상반응법으로 제조한 형광체의 분말 크기는 $3{\mu\textrm{m}}$으로 조대하고 불균일한 분포를 보인 반면, $500^{\circ}C$에서 분무한 후 $900^{\circ}C$에서 열처리하여 제조한 $(Y_{0.7}Gd_{0.3})_{0.95}BO_3:Eu_{0.05}\;^{3+}$ 형광체의 모양은 비교적 구형이었으며 평균 입자크기는 $0.7{\mu\textrm{m}}$로 미세하고 균일한 분포를 하고 있었다. 147nm VUV 여기시 초음파 분무로 제조한 $(Y_{0.7}Gd_{0.3})_{0.95}BO_3:Eu_{0.05}\;^{3+}$ 형광체의 적색 발광강도는 고상반응법으로 제조한 시편이나 상용품인 $(Y,Gd)BO_3:Eu$ 형광체에 비해 그 휘도가 증가되었다.

• 한국재료학회지
• /
• 제10권1호
• /
• pp.49-54
• /
• 2000

PDP용의 새로운 녹색 $Al_3GdB_4O_{12}:Tb^{3+} 형광체와 Al_3GdB_4O_{12}:Eu_{3+}$ 적색형광체를 제조한 후 광특성을 분석하였다. 또한 이들 형광체의 발광특성을 상용품인 $Zn_2SiO_4:Mn^{2+}$ 녹색 형광체와 $(Y,Gd)BO_3: Eu^{3+}$ 적색의 PDP 형광체와 상호 비교하였다. 형광체는 $1150^{\circ}C$에서 4시간 동안 공상 반응으로 제조하였다. 147nm의 진공자외선 조사시 $Al_3GdB_4O_{12}:Tb^{3+}$(15mol%) 녹색 형광체의 발광휘도는 상용품 $Zn_2SiO_4: Mn^{2+}$ 보다 증가하였으나 색좌표는 상대적으로 저하되었다. 한편 $Al_3GdB_4O_{12}:Eu^{3+}$(15mol%) 적색 형광체의 발광 휘도는 상용품$(Y,Gd)BO_3: Eu^{3+}$ 보다 작았으나 CIE 색좌표는 일부 개선되었다. $Al_3GdB_4O_{12}$ 형광체는 $\lambda=160nm$에서 모체 흡수에 의한 강한 여기밴드가 있으며, 진공자외선 영역에서 $Al_3GdB_4O_{12}:Tb^{3+}$ 녹색형광체의 여기강도는 $Zn_2SiO_4: Mn^{2+}$ 보다 컸으나 $Al_3GdB_4O_{12}:Eu^{3+}$ 적색 형광체의 여기강도는 $(Y,Gd)BO_3: Eu^{3+}$ 보다는 작았다.

• 한국재료학회지
• /
• 제8권6호
• /
• pp.520-525
• /
• 1998

활성제로 $Eu^{+2}$을 사용한 BaO-MgO-$AI_2O_3$에서 화학조성 변화에 따른 청색 형광체의 광학특성을 254nm 자외선 및 147nm의 진공자외선 하에서 측정하였다. 동 형광체는 자외선 및 진공자외선 조사를 받아 주 파장이 445nm 인 가시광선의 청색을 발하는 형광체이다. $BaMgAI_{14}O_{23}$ : Eu 농도에 따라 증가하였으며 진공자외선의 경우에는 5%농도에서 최대가 됨을 알 수 있었다. 자외선 및 진공자외선 모두에서 $BaMgAI_{10}O_{17}$형광체의 청색 발광강도는$BaMgAI_{14}O_{23}$보다 좋았다. 또한 $BaMgAI_{10}O_{17}$에서 Ba대신 Ca이나 Sr을 0.1mole 치환시킨 $Ba_{0.9}Ca_{0.1}MgAI_{10}O_{17}$과 $Ba_{0.9}Sr_{0.1}MgAI_{10}O_{17}$ 형광체로 광특성을 더욱 개선할 수 있었다.