• 열처리공학회지
• /
• 제3권2호
• /
• pp.37-44
• /
• 1990

The effect of the microstructural change on the near threshold fatigue crack growth rate in SM40C steel has been studied using the ${\Delta}K$ decreasing method. Below the total strain amplitude of 0.56%, cyclic softening occured, whereas above this value cyclic hardening occurred in the pearlitic lamellar structure. However, in the spherodized structure the cyclic hardening solely occurred. The crack growth rate in the near-threshold region was decreased with increasing prior austenite grain size and this was due to surface roughness. The crack growth rate of the spherodized structure was lower than that of the pearlite lamellar structure and the ${\Delta}K_{th}$ of the former was higher than that of the latter. It was understood that the crack propagates preferentially through the ferrite phase. The intergranular facets in the near-threshold region appeared in the spherodized structure.

• Applied Microscopy
• /
• 제52권
• /
• pp.10.1-10.15
• /
• 2022

The effect of carbon doping contents on the microstructure, hardness, and corrosion properties of heat-treated AISI steel grades of plain carbon steel was investigated in this study. Various microstructures including coarse ferrite-pearlite, fine ferrite-pearlite, martensite, and bainite were developed by different heat treatments i.e. annealing, normalizing, quenching, and austempering, respectively. The developed microstructures, micro-hardness, and corrosion properties were investigated by a light optical microscope, scanning electron microscope, electromechanical (Vickers Hardness tester), and electrochemical (Gamry Potentiostat) equipment, respectively. The highest corrosion rates were observed in bainitic microstructures (2.68-12.12 mpy), whereas the lowest were found in the fine ferritic-pearlitic microstructures (1.57-6.36 mpy). A direct correlation has been observed between carbon concentration and corrosion rate, i.e. carbon content resulted in an increase in corrosion rate (2.37 mpy for AISI 1020 to 9.67 mpy for AISI 1050 in annealed condition).

• 대한조선학회지
• /
• 제10권2호
• /
• pp.9-18
• /
• 1973

The effects of carburization on the fatigue strength and cracks were studied. The fatigue phenomena of the carburized specimens were compared with noncarburized specimens those were either heat-treated or un-treated. The fatigue strength of these specimens were measured by rotating bending fatigue machine. The obtained results indicated that the fatigue strength of carburized specimens were increased ranging from 24-59 % than those of un-treated, and 22-38% than those of heat-treated. The Vickers hardness of carburized were also increased as much as 138-195% than those of un-treated, and 42-125% than those of heat-treated. The microscopic observation of the carburized specimens mostly composed of minute pearlitic structure at hard case exhibited to have more localized slip than those of non-carburized specimens.

• 대한기계학회논문집
• /
• 제12권3호
• /
• pp.505-512
• /
• 1988

본 연구에서는 상술한 $\boxDr$한계정유길이$\boxUl$를 찾아내는 것을 주요수단으로 하여, 그 전파 하한계응력으로서의 피로한도와의 관계를 정량적으로 검토하고, 미소크랙전파 거동이 미시조직 또는 피로부하이력등에 민감함을 감안하여, 이들 인자가 미소크랙 전 파의 하한계조건에 미치는 영향에 관하여 검토하기로 하였다.