• Journal of Sensor Science and Technology
• /
• v.17 no.6
• /
• pp.418-424
• /
• 2008

The PZT based piezoelectric thick films prepared by screen printing method have been mainly used as a functional material for MEMS applications due to their compatibility of MEMS process. However the screen printed thick films generally reveal poor electrical and mechanical properties because of their porous microstructure. To improve microstructure we mixed attrition milled powder with ball milled powder of 0.01Pb$(Mg_{1/2}W_{1/2})O_3$-0.41Pb$(Ni_{1/3}Nb_{2/3})O_3$-$0.35PbTiO_3$-$0.23PbZrO_3$+0.1 wt% ${Y_2}{O_3}$+1.5 wt% ZnO composition. By mixing 25 % of attrition milled powder and 75 % of ball milled powder, the broadest particle size distribution was obtained, leading to a dense thick film with crack-free microstructure and improved dielectric properties. The X-ray diffraction analysis revealed that the film was in wellcrystallized perovskite phase. The remanent polarization was increased from $13.7{\mu}C/cm^2$ to $23.3{\mu}C/cm^2$ at the addition of 25 % attrition milled powder.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.329-330
• /
• 2006

본연구에서는 초음파 모터 등의 고출력 액츄에이터에 응용 가능한 $0.4Pb(Ni_{1/3}Nb_{2/3})O_3$-$0.6Pb(Zr_{0.405}Ti_{0.595})O_3$ + 0.25wt% $Fe_2O_3$ 조성시스템에 $MnO_2$ (0~1 wt.%)첨가하여 압전, 유전특성 및 미세구조에 관해 고찰하였다. 본조성을 $1125{\sim}1175^{\circ}C$ 온도에서 2시간 소결하여 시편을 제조하였으며 이의 결정구조 및 미세조직을 분석하였다. $MnO_2$ 첨가량 증가에 따라 압전 상수와 전기기계결함계수는 감소하였으며, 기계적 품질계수는 0.5 wt% 첨가시까지 증가하였으나 첨가량이 그 이상 증가함에 따라 감소하였다. 압전특성은 $1125^{\circ}C$에서 소결한 $MnO_2$ 0.5wt%조성에서 ${\varepsilon}r$ = 2040, kp = 0.66, $d_{33}$ = 504, Qm=438의 우수한 특성을 나타내었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.8
• /
• pp.676-680
• /
• 2003

In this study, to develop the low temperature sintering ceramics for piezoelectric transformer, PSN-PNN-PZT system ceramics were manufactured as a function of V$_2$O$_{5}$ addition, that is the low melting point oxide. Its dielectric and piezoelectric characteristics were investigated. With increasing the amount of V$_2$O$_{5}$ addition, electromechanical coupling factor(kp) and mechanical quality factor(Qm) were decreased. For piezoelectric transformer application, the 0.1wt% V$_2$O$_{5}$ added specimen sintered at 1,00$0^{\circ}C$ showed the proper value of $\varepsilon$r=1,590, kp=0.51 and Qm=748.m=748.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.1
• /
• pp.35-39
• /
• 2006

In this study, in order to develop the multilayer piezoelectric actuator and ultrasonic resonator, PMN-PNN-PZT ceramics were fabricated by sintering with $Li_2CO_3-Na_2CO_3$ as sintering aids at $950^{\circ}C$ and their piezoelectric and dielectric characteristics were investigated as a function of PNN substitution. With increasing PNN substitution, dielectric constant(${\epsilon}_r$), electromechanical coupling factor(kp), and piezoelectric d constant($d_{33}$) were increased to $12 mol\%$ PNN substitution and then showed a tendency to decrease rapidly With increasing PNN substitution, crystal structure changed from tetragonal to rhombohedral at $12 mol\%$ PNN substitution and then secondary phase was appeared and its intensity was increased. At the $12 mol\%$ PNN substituted PMN-PZT composition ceramic sintered at $950^{\circ}C$, density, kp, $d_{33}$ and Qm showed the optimum value of $7.79 g/cm^3$, 0.599, 419 pC/N, and 894, respectively for multilayer piezoelectric actuator application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.2
• /
• pp.184-189
• /
• 2004

The effects of $Y_2$ $O_3$-substitution on the piezoelectric properties of Pb[(N $i_{1}$3/N $b_{2}$3/)$_{0.15}$(Z $r_{1}$2/ $Ti_{1}$2/)$_{0.85}$] $O_3$ceramics were investigated. It was found that $Y^{3+}$ ions incorporate into Pb-sites of the ceramics, resulting in a increased lattice anisotropy and formation of Pb-vacancies. As a result, an orthorhombic-tetragonal phase transition was induced when $\chi$>0.005. At the morphotropic phase boundary of x=0.005, piezoelectric constants( $k_{p}$, $k_{33}$, and $d_{33}$) showed maximum values of 0.53, 0.58, and 350pC/N, respectively. A 30-layer actuator fabricated with the above material showed a maximum strain of 0.12％ under 100V DC bias.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.317-321
• /
• 2002

Piezoelectric properties of $(Pb_{1-x}Y_x)[(Ni_{1/3}Nb_{2/3})_{0.15}(Zr_{1/2}Ti_{1/2)})_{0.85}]O_{3}$ (x=0~0.05) ceramics were investigated, The stoichiometric PNN-PZT ceramics required the sintering temperature above $1100^{\circ}C$, but the addition of $Y_{2}O_{3}$ in the PNN-PZT ceramic lowered the sintering temperature down to $1000^{\circ}C$. In case of x=0.005, the electro-mechanical coupling $factor(K_p)$, the piezoelectric $constant(d_{33})$, and the maximum strain ratio of PNN-PZT ceramics sintered at $1000^{\circ}C$ were 53.1%, 395pC/N, and $2200{\times}10^{-6}$ respectively, A 30-layer piezoelectric actuator$(10{\times}10{\times}1.7mm)$ fabricated with the above material showed the maximum strain of $2.09{\mu}m$ under 100V DC bias.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.499-503
• /
• 2002

In this study, to develop the high power piezoelectric transformer for adaptor, PSN-PNN-PZT system ceramics were formulated as a function of $MnO_2$ addition and its dielectric and piezoelectric characteristics were investigated. Multi-layer piezoelectric transformer using an excellent composition was also fabricated and its electrical properties evaluated. The composition ceramics added to 0.5wt%$MnO_2$ showed the maximum value of $k_p=0.61$ and $Q_m=1.321$. As the output power of piezoelectric transformer is increased, its temperature rise increased. At the fixed 18W output power, the transformer was stably operated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.434-437
• /
• 2001

In this study piezoelectric and dielectric properties of $Pb(Mn_{1/3}Nb_{2/3})O_{3}-Pb(Zr,Ti)O_{3}$ ceramics were investigated with $Pb(Ni_{1/3}Nb_{2/3})O_{3}$ substitution. As the $Pb(Ni_{1/3}Nb_{2/3})O_{3}$ substitution was increased, dielectric constant and electromechanical coupling factor (kp) were increased while mechanical quality factor decreased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.434-437
• /
• 2001

In this study piezoelectric and dielectric properties of Pb(Mn$\sub$1/3/Nb$\sub$2/3/)O$_3$-Pb(Zr,Ti)O$_3$ ceramics were investigated with Pb(Ni$\sub$1/3/Nb$\sub$2/3/)O$_3$ substitution. As the Pb(Ni$\sub$1/3/Nb$\sub$2/3/)O$_3$) substitution was increased, dielectric constant and electromechanical coupling factor (kp) were increased while mechanical quality factor decreased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.138-141
• /
• 2004

[ $MnO_2$ ]가 첨가된 $0.9Pb(Zr_{0.5}Ti_{0.5})O_3-0.2Pb[(Zn_{0.8}Ni_{0.2})_{1/3}Nb_{2/3}]O_3$(0.8PZT-0.2PZNN) 세라믹스는 그 압전특성과 유전특성이 뛰어나지만 $1000^{\circ}C$ 이하의 낮은 소결 온도에서는 소결되지 않는다. $1000^{\circ}C$이하의 낮은 소결온도에서 소결하기 위해 CuO를 첨가한 결과, 소결온도 $920^{\circ}C$에서 소결성은 우수하였으나 그 압전 특성의 저하가 두드러졌다. 이는 XRD에서 확인한 결과에 따르면 CuO의 첨가가 우수한 MPB 조성으로 판명된 $MnO_2$ 가 첨가된 0.8PZT-0.2PZNN 세라믹스의 결정구조를 Rhombohedral 구조로 바꾸기 때문인 것으로 보였으며 이러한 문제는 PZNN의 비율을 조절하여 0.875PZT-0.125PZNN 세라믹스를 선택함으로 인해 해결할 수 있었다. 그러나 여전히 낮은 $Q_m$값을 높이기 위해서 $Al_2O_3$를 첨가하였고 그 결과 시편의 tetragonality 감소와 $Q_m$값의 증가를 확인할 수 있었으나 그 첨가량이 0.2wt% 이상일 경우에는 밀도의 감소로 인한 압전특성의 저하가 나타났다. 밀도의 향상을 위해 Zn and Ni excess 조성을 선택하였고 그 결과 0.5wt% $MnO_2$와 0.2wt% CuO 그리고 0.3wt% $Al_2O_3$를 첨가한 0.875PZT-0.125PZNN 세라믹스(Zn and Ni excess 조성)를 $920^{\circ}C$에서 소결한 경우 $k_p=0.581,\;Q_m=809,\;d_{33}=345\;pC/N\;and\;{\varepsilon}_{33}/{\varepsilon}_0=1345$의 빼어난 압전 및 유전특성과 $330^{\circ}C$의 높은 $T_c$를 보였고 그 조성의 vibration velocity는 약4.5 m/s로 나타났다.