• 한국세라믹학회지
• /
• 제34권3호
• /
• pp.281-288
• /
• 1997

유전율이 높고 온도안정성이 우수하다고 알려져 있는 40Pb(Mg1/3Nb2/3)O3-30PbTiO3-30Pb(Mg1/2W1/2)O3계 세라믹스에 소결온도를 낮추기 위하여 저온에서 액상을 형성하는 91PbO-9WO3를 과잉첨가하여 소결성, 미세구조 및 유전성의 변화에 대하여 조사하였다. 91PbO-9WO3의 첨가량이 증가함에 따라 소결온도가 저하하였으며 6 mol%첨가시는 875$^{\circ}C$에서 소결이 가능하였다. 유전율은 기본조성에서 16,400이었고, 첨가제가 1 mol% 과잉첨가된 경우 18,500으로 최대값을 나타냈으며 이후 첨가량이 증가함에 따라 감소하였다. 첨가제의 첨가량이 2~4mol%인 시편의 온도에 따른 유전율 변화곡선에서 double peak maxima가 나타났으나, 첨가량이 5 mol% 이상인 시편에서는 입계에 텅스텐을 많이 포함하고 있는 결정상이 생성되었고 double peak maxima는 나타나지 않았다.

• 한국세라믹학회지
• /
• 제30권8호
• /
• pp.671-677
• /
• 1993

Effects of PbTiO3 addition on dielectric properties and extent of PbO loss in Nd-doped Pb(Mg1/3Nb2/3)O3 system were investigated. As the proportion of dopping increased, the phase transition temperature shifted to low region, and the dielectric constant at room temperature decreased rapidly. But as the proportion of PbTiO3 increased, the phase transition temperature shifted to high retion, and the dielectric constant at room temperature increased. The substitution of Nd3+ for Pb2+ decreased the amount of PbO evaporation, therefore the sample sintered well in case of only 1 mole% adding excess PbO.

• 한국세라믹학회지
• /
• 제37권7호
• /
• pp.673-680
• /
• 2000

The effect of excess PbO(0, 1, 2, 4, and 8 mol%) on grain growth and densification of (65)Pb(Mg1/3Nb2/3)O3-(35)PbTiO3 [mol%] ceramics has been investigaetd. With increasing the amount of excess PbO and sintering time, densities of sintered samples decreased gradually. The samples containing less than 1 mol% of PbO showed normal grain growth behavior, however abnormal grain growth was observed to occur in the samples with more than 2 mol% of PbO. In the samples with more than 2 mol% of PbO, the number of abnormal grains decreased and thus the average grain size became smaller with increasing the amount of excess PbO. These results demonstrated that the abnormal grain growth started to occur when a critical amount of excess PbO was added to a (65)Pb(Mg1/3Nb2/3)O3-(35)PbTiO3 sample. Since PMN-PT grains in a liquid matrix were angular, the observed abnormal grain growth was explained to proceed through the two dimensional nucleation process.

• 한국세라믹학회지
• /
• 제22권2호
• /
• pp.17-24
• /
• 1985

In the composition of $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ the effect of particle size on PbO vaporization were measured, . The initial step of discontinuous vaporization of unreated PbO during the calcining process was depended on the particle size. All additives $La_2O_3Nb_2O_5$ and $Al_2O_3$ inhibited the grain growth of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ +2wt% excess PbO. The dielectric and piezoelectric properties of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ were improved by the addition of 2wt% excess PbO and proper additive. The electromechanical planar coupling factor of 0.65 and mechnical quality factor of 390 could be obtained by adding 5wt% $Nb_2O_5$ to the composition 2wt% excess PbO+$Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$.

• The Korean Journal of Ceramics
• /
• 제4권4호
• /
• pp.286-291
• /
• 1998

Dielectric properties of $Pb(Mg_{1/3}Nb_{2/3})O_{3}-PbTiO_{3}$, ceramics prepared by the columbite precursor method have been investigated as a function of the sintering temperature in the range of 1000∼$1250^{\circ}C$. The $Pb(Mg_{1/3}Nb_{2/3})O_{3}-PbTiO_{3}$ ceramics show typical relaxor ferroelectric behavior. As the sintering temperature increased, the dielectric constant increased and the phase transition temperature shifted to lower temperature. The TCK(temperature coefficient of dielectric constant) and VRK (variation rate of dielectric constant) increased with increasing sintering temperature. The $Pb(Mg_{1/3}Nb_{2/3})O_{3}-PbTiO_{3}$ compositions sintered at $1250^{\circ}C$ appear to be suitable for ferroelectric bolometer.

• 한국세라믹학회지
• /
• 제33권5호
• /
• pp.556-562
• /
• 1996

In order to understand the electrostrictive behavior of Pb(Mg1/3Nb2/3)O3-PbTiO3 (PMN-PT) solid solutions the dielectric constants the electric-field-induced strains and the pyroelectric coefficients of (1-x)PMN-xPT (x=0.1-0.4) were investigated in the temperature range -50~20$0^{\circ}C$. For x=0.1~0.35 where the phase transi-tion is diffusive the strain has a maxima at the temperature of maximum pyroelectric coefficient (depolrizing temperature) rather than the temperature of maximum dielectric constant. For x=0.4 where the phase transition is relatively sharp the strain decreases monotonically as the temperature increases. Relationships among the above experimental results are discussed.

• 한국세라믹학회지
• /
• 제30권11호
• /
• pp.925-932
• /
• 1993

The perovskite phase in PZN-PMN-PT (Pb(Zn, Mg)1/3Nb2/3O3-PbTiO3) pseudoternary ceramics was stabilized by the addition of excess constituent divalent oxides (PbO, MgO and ZnO). The excess addition of 5mol% MgO or 7.5mol% PbO fully stabilized the perovskite phase. The enhanced diffuse phase transition (DPT) and the decrease in the electrical resistivity observed in the presence of excess ZnO or MgO were interpreted in terms of the additional formation of negatively charged, short-range ordered 1:1 domains with a concomitant generation of charge carriers, holes.

• 한국세라믹학회지
• /
• 제26권2호
• /
• pp.249-257
• /
• 1989

Dielectric properties and the stability of the perovskite phase in the Pb(Mg1/3Nb2/3)O3 system have been investigated as a function of amount of BaTiO3 and firing temperature. In the specimens fired at 120$0^{\circ}C$, the pyrochlore phase was eliminated by the addition of 10-15m/o BaTiO3 and also the dielectric constant increased. However, the dielectric constant decreased with further addition of BaTiO3 even though no pyrochlore phase was found to be present. The reducing tendency of the pyrochlore phase decreased with lowering the firing temperature in the system of Pb(Mg1/3Nb2/3)O3 with BaTiO3. Dielectric properties in PMN ceramics were affected by the character of the BaTiO3 rather than the pyrochlore phase.

• 한국재료학회지
• /
• 제11권6호
• /
• pp.498-501
• /
• 2001

0.9Pb($Mg_{1/3}Nb_{2/3}$)$O_3$-0.1Pb$TiO_3$계 완화형 강유전체에서 MnO$_2$ 첨가가 압전물성에 미치는 영향을 강유전성이 우세한 온도영역인 -40~3$0^{\circ}C$의 온도범위에 걸쳐 조사하였다. MnO$_2$ 첨가에 의한 효과를 유전특성, 압전특성, 전계유기 변형특성 등의 영역에서 고찰하였다 MnO$_2$ 첨가량이 증가할수록 유전성 및 압전성은 hard piezoelectric의 경향을 나타내었다. 이러한 실험적 고찰로부터 첨가된 Mn은 강유전 도메인 분역을 고정하는 역할을 하는 것으로 제안되었다.

• 한국세라믹학회지
• /
• 제34권1호
• /
• pp.31-36
• /
• 1997

유전율이 높고 온도안정성이우수하다고 알려져 있는 Pb(Mg1/3Nb2/3)O3-PbTiO3-Pb(Mg1/2W1/2)O3 계 세라믹스를 산화물혼합법 및 precursor방법으로 제조함에 있어 과잉 MgO의 첨가에 따른 미세구조와 유전특성의 변화에 대하여 조사하였다. MgO를 5mol%이상 과잉첨가하여 100$0^{\circ}C$에 소결한 시편의 유전율은 5000이상이고, -55$^{\circ}C$에서 1$25^{\circ}C$범위에서 변화율은 +25%에서 -5$0^{\circ}C$ 정도를 나타냈다. XRD 분석결과 perovskite상과 Pb2WO5 결정이 주된상이었으며, 소결온도 및 MgO 첨가량이 증가함에 따라 cubic pyrochlore상인 Pb3Nb4O13와 PbWO4는 감소하였다. SEM에 의한 미세구조의 관찰에서 MgO첨가량이 증가함에 따라 결정성장이 촉진되는 것을 알 수 있었으며 이것이 소결온도 증가에 따른 pyrochlore상의 감소와 함께 유전율을 증가시키는 원인이었다. BSE관찰에서 화학성분 분포의 불균일성이 나타났으며, 각각의 소결온도에서 생성되는 결정상과 함께 유전율의 온도의존성을 완만하게 만드는 원인임을 알 수 있었다.