• The Korean Journal of Ceramics
• /
• 제6권1호
• /
• pp.68-73
• /
• 2000

The effects of oxygen annealing on the carbon content in MgO thin films were investigated, MgO thin films were deposited on Si(100) substrate at different temperatures of 400 to $700^{\circ}C$ and different deposition rates of 3.4 to 11.6$\AA$/min. Using rf magnetron sputtering method. Carbon content change on the surface of MgO thin films with the oxygen annealing at different temperatures was investigated using various method. The carbon content decreased as the annealing temperature increased. $Pb(Zr_{0.53}Ti_{0.47})O_3$(PZT) thin films were deposited on the MgO/Si(100) substrates. The effects of carbon content on the phase formation and the electrical properties of PZT thin films were also investigated.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.144.2-144
• /
• 2000

• 한국재료학회지
• /
• 제8권12호
• /
• pp.1170-1175
• /
• 1998

하부전극 없이 MgO 중간층을 갖는 고농도로 도핑된 Si(100) 기판(MgO/Si)위에 고주파 마그네트론 스퍼터링 방법으로 as-deposited PZT 박막을 증착한후 $650^{\circ}C$ 온도에서 RTA 후속열처리를 실시하였다. 제작된 PZT 박막시료에 대해 MgO 중간층의 두께 및 후속열처리에 따른 결정학적, 전기적특성을 조사하였다. XRD 분석결과 MgO층이 전혀 증착되지 않은 bare Si 기판위에 증착된 PZT 시료는 pyrochlore 결정상만이 나타났으나 50 두께의 M gO층 위에 증착된 PZT/MgO/Si 박막시료는 전형적인 perovskite 결정구조를 나타내었다. SEM 및 AES 분석결과 PZT 박막두게는 약 7000 이었으며 비교적 매끄러운 계면형상을 보여 주었다. PZT 박막내의 각 성분원소가 깊이에 따라 비교적 균일한 분포를 나타내었다. $650^{\circ}C$의 온도로 후속열처리된 PZT/MgO/Si 박막의 1KHz 주파수에서 유전상수 ($\varepsilon_{r}$ )와 잔류분극 (2Pr)은 약 300 및 $14\mu$C/$\textrm{cm}^2$의 값을 각각 나타내었으며 누설전류의 크기는 약 $3.2\mu$A/$\textrm{cm}^2$이었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.734-737
• /
• 2004

The metal-ferroelectric-semiconductor (MFS) structure is widely studied for nondestructive readout (NDRO) memory devices, but conventional MFS structure has a critical problem. It is difficult to obtain ferroelectric films like PZT on Si substrate without interdiffusion of impurities such as Pb, Ti and other elements. In order to solve these problems, the metal-ferroelectric-insulator-semiconductor (MFIS) structure has been proposed with a buffer layer of high dielectric constant such as MgO, $Y_2O_3$, and $CeO_2$. In this study, the etching characteristics (etch rate, selectivity) of MgO thin films were etched using $Cl_2/Ar$ plasma. The maximum etch rate of 85 nm/min for MgO thin films was obtained at $Cl_2$(30%)/Ar(70%) gas mixing ratio. Also, the etch rate was measured by varying the etching parameters such as ICP rf power, dc-bias voltage, and chamber pressure. Plasma diagnostics was performed by Langmuir probe (LP) and optical emission spectroscopy (OES).

• Applied Microscopy
• /
• 제34권2호
• /
• pp.95-102
• /
• 2004

본 실험에서는 tripod polishing 방법을 이용하여 Pd/GaN/Sapphire 박막, PZT/MgO/Si 박막, 304 stainless steel 분말, $Mo_5Si_3/Mo_2B$ diffusion couple의 매우 다양한 물성이 포함된 불균질 재료의 TEM 시편을 제작하고 분석하였다. Tripod polishing을 사용하여 시편을 준비하면 시편의 종류에 관계없이 시편의 선단부에 매우 광범위한 전자빔 투과 영역을 지닌 TEM 시편을 얻을 수 있었으며, Pd/GaN/Sapphire 박막, PZT/MgO/Si 박막과 같이 기판이 경한 반도체 재료의 경우에는 연마 정도가 균일하며 연마과정 동안 오염이 심하지 않기 때문에 ion milling으로 cleaning 없이 TEM 관찰이 가능하다. 한편 304 stainless steel 분말과 같은 금속재료의 경우 짧은 시간의 ion milling 은 시편의 오염 제거에 도움된다. $Mo_5Si_3/Mo_2B$ diffusion couple에 형성된 실리사이드는 큰 취성 때문에 polishing 동안 시편이 깨지는 현상으로 전자가 투과할 수 있을 정도의 연마가 불가능하여 1시간 정도 ion milling 연마가 필요하다. Tripod polishing으로 TEM 시편을 준비하면 분석하고자 하는 지역을 정확하고도 넓게 연마할 수 있다. 또한 비교적 짧은 시간 내에 ion milling 없이 TEM 시편을 제작할 수 있기 때문에 ion milling에서 유발되는 여러 가지 문제점들을 해결할 수 있는 장점이 있었다. 그러나 tripod polishing은 전부 수작업으로 시편을 준비하기 때문에 시편을 제작하는 과정 동안 매우 세심한 주의가 요구되며 제작자의 숙련도와 경험을 필요로 하는 단점이 있다.