• Journal of the Korean Electrochemical Society
• /
• v.24 no.2
• /
• pp.28-33
• /
• 2021

Many researchers have increased the loading level of electrodes to improve the energy density of secondary batteries. In this study, high-loading NCM523 (LiNi_0.5Co_0.2Mn_0.3O₂) positive electrode is manufactured using a polytetrafluoroethylene (PTFE) binder, not the conventional polyvinylidene fluoride (PVdF) binder, which has been commonly used in lithium-ion batteries. Through the kneading process using PTFE suspension, not the conventional slurry process using PVdF solution in N-methyl-2-pyrrolidinone (NMP), thick electrodes with high loading are easily manufactured. When the PTFE and PVdF-based electrodes are prepared at a loading level of 5.0 mAh/cm², respectively, the PTFE-based electrode shows better cycle performance and rate capability than those of PVdF-based electrodes. The electrode manufactured by the kneading process using a PTFE binder has high electrode porosity due to insufficient roll-press, but the porosity can be lowered by high temperature roll-press over 120℃. However, there is no significant difference in cycle performance according to the roll press temperature. In addition, the cycle performance of the high loading electrode is slightly improved by increasing the content of the conductive material. Overall, the PTFE binder can improve the performance of the high loading electrode, but additional solutions will be needed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.10
• /
• pp.1079-1084
• /
• 2004

This work describes the effect of electrode binder on the characteristics of electric double layer capacitor. Among carboxymethylcellulose (CMC), Polyvinylpyrrolidone (PVP), Polyvinyl Alcohol (PVA), and Polyvinylidene Fluoride (PVDF), the unit cell using CMC showed good rate capability at current densities between 2.5 mA/$\textrm{cm}^2$～100 mA/$\textrm{cm}^2$. However, CMC as a binder is incongruent, because the electrode bound with CMC is rigid and easy to crack during a press and winding process for fabrication of capacitor. The unit cell capacitor using the electrode bound with binary binder composed of CMC and Polytetrafluoroethylene (PTFE), especially in composition CMC : PTFE =60 : 40 wt.%, has exhibited the better mechanical properties than those of the unit cell with CMC. On the other hand, the mechanical properties of CMC+PTFE electrode, coated on underlayer composed of CMC and carbon black, were much improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1248-1253
• /
• 2004

This work describes the effect of electrode binder on the characteristics of electric double layer capacitor Among carboxymethylcellulose (CMC), Polyvinylpyrrolidone (PVP), Polyvinyl Alcohol (PVA), and Polyvinylidene Fluoride (PVDF), the unit cell using CMC showed good rate capability between $2.5mA/cm^2{\sim}100mA/cm^2$ current density. However, CMC as a binder is incongruent, because the electrode bound with CMC is rigid and easy to crack during a press and winding process for fabrication of capacitor. The unit cell capacitor using the electrode bound with binary binder composed of CMC and Polytetrafluoroethylene (PTFE), especially in composition CMC : PTFE : 60 : 40 wt.%, has exhibited the better mechanical properties than those of the unit cell with CMC. On the other hand, it was also noted that the mechanical properties of CMC+PTFE electrode, coated on underlayer composed of CMC and carbon black, were much improved the binding force.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.353-354
• /
• 2006

This work describes the effect of binders, such as carboxymethylcellulose (CMC), CMC+Polytetrafluoroethylene (PTFE) and PTFE, on the electrochemical and mechanical properties of activated carbon-electrode for electric double layer capacitor. The cell capacitors using the electrode bound with binary binder composed of CMC and PTFE, especially m composition CMC ; PTFE = 60 : 40 wt %, has exhibited the better rate capability and the lower internal resistance than those of the cell capacitor with CMC. On the other hand, the sheet type electrode kneaded with PTFE was bonded with conductive adhesive on Al foil. This cell capacitor using the electrode with PTFE exhibited the best mechanical properties and rate capability compared to the CMC and CMC+PTFE one These behaviors could be explained by the well-developed network structure of PTFE fibrils during the kneading process.

• Transactions of the Korean hydrogen and new energy society
• /
• v.5 no.1
• /
• pp.51-57
• /
• 1994

Compaction techniques of hydrogen storage alloy 'powders, to solve the problems due to disintegration during the cyclic hydriding and dehydriding, by using polytetrafluoroethylene (PTFE) and silicon sealant as a polymer binder were studied. Optimum conditions of compaction were as follows. Binder content, 10 % for PTFE and 5 % for silicon sealant ; particle size of alloy powders, $-25{\mu}m$ ; compacting pressure, $4ton/cm^2$. Compacts obtained were easily activated and had a good strength even after 30 cycles of hydriding and dehydriding. PTFE added compacts showed very good rate capability, however, in the silicon added compacts hydrogen absorption rate was somewhat slow because of higher elasticity and adhesiveness of the binder.

• Transactions of the Korean hydrogen and new energy society
• /
• v.31 no.3
• /
• pp.276-283
• /
• 2020

Alcohol-based solvents including ethanol (EtOH) and tert-butyl alcohol (TBA) are investigated instead of isopropanol (IPA), which is a common solvent for polytetrafluoroethylene (PTFE), as an alternative solvent for preparing the catalyst slurry with PTFE binder. As a result, the performance at 0.2 A/㎠ from the single cells from using catalyst slurries based on EtOH and TBA showed very similar value to that from the slurry using IPA, which implies the EtOH and TBA can be used as a solvent for the catalyst slurry. It is also confirmed by the very close values of the total resistance of the membrane electrode assemblies from the slurries using different solvents. In the energy dispersive spectrometry (EDS) image, the shape of crack and dispersion of PTFE are changed according to the vapor pressure of the solvent.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.12
• /
• pp.1167-1171
• /
• 2006

This work describes the effect of binders, such as carboxymethylcellulose (CMC), CMC+ Polytetrafluoroethylene (PTFE) and PTFE, on the electrochemical and mechanical properties of activated carbon-electrode for electric double layer capacitor. The cell capacitors using the electrode bound with binary binder composed of CMC and PTFE, especially in composition CMC PTFE = 60 : 40 wt.%, has better rate capability and the lower internal resistance than those of the cell capacitor with CMC. On the other hand, the sheet type electrode kneaded with PTFE was bonded with conductive adhesive on Al foil. This cell capacitor using the electrode with PTFE exhibited the best mechanical properties and rate capability compared to the CMC and CMC+PTFE one. These behaviors could be explained by the well-developed network structure of PTFE fibrils doting the kneading process.

• Journal of Energy Engineering
• /
• v.2 no.2
• /
• pp.187-193
• /
• 1993

Porous matrices to contain and support phosphoric acid were prepared with PTFE as binder and SiC whisker or SiC powders of various particle size for phosphoric acid fuel cell(PAFC). Among the matrix characteristics the most important factors in stack performances were thought to be the bubble pressure and electrolyte wettability And then matrix was constructed to have pore size smaller than that of electrode. The bubble pressures and wettabilities of matrices manufactured with various size of SiC and different PTFE contents were investigated and related with the porosities measured by porosimeter, and then the optimum manufacturing condition of matrix for PAFC was determined.

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.102-107
• /
• 2017

Porous polytetrafluoroethylene (PTFE) thin films are fabricated by spin-coating using a dispersion solution containing PTFE powders, and their crystalline properties are investigated after thermal annealing at various temperatures ranging from 300 to $500^{\circ}C$. Before thermal annealing, the film is densely packed and consists of many granular particles 200-300 nm in diameter. However, after thermal annealing, the film contains many voids and fibrous grains on the surface. In addition, the film thickness decreases after thermal annealing owing to evaporation of the surfactant, binder, and solvent composing the PTFE dispersion solution. The film thickness is systematically controlled from 2 to $6.5{\mu}m$ by decreasing the spin speed from 1,500 to 500 rpm. A triboelectric nanogenerator is fabricated by spin-coating PTFE thin films onto polished Cu foils, where they act as an active layer to convert mechanical energy to electrical energy. A triboelectric nanogenerator consisting of a PTFE layer and Al metal foil pair shows typical output characteristics, exhibiting positive and negative peaks during applied strain and relief cycles due to charging and discharging of electrical charge carriers. Further, the voltage and current outputs increase with increasing strain cycle owing to accumulation of electrical charge carriers during charge-discharge.

• Transactions of the Korean hydrogen and new energy society
• /
• v.10 no.2
• /
• pp.81-89
• /
• 1999

Various characteristics - mechanical propertis, thermal cyclic hydriding characteristics and resistance to degradation by $H_2O$, CO in hydrogen - of hydrogen storage alloy powder compacts using PTFE and silicon sealant as a polymer binder were studied. Diametral tensile strength of 10wt% PTFE and 5wt% silicon sealant added compacts showed relatively high value of $4kg/cm^2$ and $10kg/cm^2$, respectively. Compacts show a good resistance to degradation by $H_2O$ in hydrogen. But hydrogen absorption rate and capacity of compacts were decreased by CO in hydrogen with the number of cycles. Cu coated and PTFE bonded compacts showed very small decrease of capacity and a good strength even after 1000 cycles of thermal hydriding and dehydriding.