• 한국강구조학회 논문집
• /
• 제15권3호
• /
• pp.241-250
• /
• 2003

본 연구는 동종강재 및 이종강재 용접시 발생하는 잔류응력 특징을 파악하기 위해서 유한 요소법을 이용한 3차원 탄소성해석을 수행하였다. 결과에 의하면, 동종강재 맞대기용접시 용접부의 잔류응력은 고강도강재의 인장강도가 클수록(POSTEN60

• Journal of Welding and Joining
• /
• 제22권4호
• /
• pp.50-58
• /
• 2004

In this study, high temperature tensile properties of high strength steels(POSTEN60, POSTEN80) were investigated. The three-dimensional thermal elastic-plastic analyses were conducted to investigate the characteristics of welding residual stresses in welds of high strength steels on the basis of thermal and mechanical properites at high temperature obtained from the experiment. According to the results, high temperature tensile strength of POSTEN60 steel deteriorated slowly to 10$0^{\circ}C$. As the temperature went up, the tensile strength became better because of blue shortness, and it deteriorated radically after reaching to the maximum value around 30$0^{\circ}C$. For the POSTEN80 steel, high temperature tensile strength deteriorated slowly to 20$0^{\circ}C$. As the temperature went up the tensile strength became better and it deteriorated slowly to $600^{\circ}C$ after reached to the maximum value around 30$0^{\circ}C$. Strain of high strength steels at the elevated temperature increased radically after the mercury rose to $600^{\circ}C$. The strain hardening ratio of POSTEN60 steel was larger then that of POSTEN80 steel at the elevated temperature as in the case at the room temperature and it became smaller radically after the mercury rose to 40$0^{\circ}C$. And, in the welding of high strength steels, increasing tensile strength of the steel (POSTEN60

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.260-262
• /
• 2003

In this study, high temperature tensile properties of high tensile strength steels(POSTEN60, POSTEN80) were investigated by elevated temperature tensile test. According toe the results, high temperature tensile strength of POSTEN60 deteriorated slowly to 100$^{\circ}C$. As the temperature went up the tensile strength became better because of blue shortness and it deteriorated radically after reached to the maximum value around 300$^{\circ}C$. For the POSTEN80, high temperature tensile strength deteriorated slowly to 200$^{\circ}C$.As the temperature went up the tensile strength became better and it deteriorated slowly to 600$^{\circ}C$ after reached to the maximum value around 300$^{\circ}C$. Strain of high tensile strength steels at the elevated temperature increased radically after the mercury rose to 600$^{\circ}C$. The strain hardening ratio of POSTEN60 was larger then that of POSTEN80 at the elevated temperature as in the case at the room temperature and it became smaller radically after the mercury rose to 400$^{\circ}C$.

• 한국강구조학회 논문집
• /
• 제14권3호
• /
• pp.453-461
• /
• 2002

본 연구에서는 고강도 강재인 SM570강재와 POSTEN80강재로 제작된 하중비전달형 십자용접연결부의 피로특성을 평가하는 것으로 대상강재의 피로강도, 피로균열의 발생과 진전, 판두께효과, 정적강도와 피로강도와의 관계를 기존의 연구결과와 비교, 분석하였다. SM570강재와 POSTEN80강재의 피로강도는 설계지침에 제시된 등급보다 높은 것으로 나타났으며 판두께효과 및 일부의 경우에 있어 정적 강도 의존성을 확인하였다.

• 한국지진공학회논문집
• /
• 제8권6호통권40호
• /
• pp.45-54
• /
• 2004

최근 강구조물의 장경간화 및 고층화로 인하여 고강도강재의 사용이 점차 증가하고 있다. 고강도강재(POSTEN60, POSTEN80)가 적용된 강구조물의 정확한 내진설계를 위해서는 반복하중 작용시 발생하는 대변형 및 비선형반복거동을 구현할 수 있는 해석기법이 필요하다. 본 연구에서는 고강도강재의 단조재하실험 및 반복하중실험을 기초하여 반복소성모델을 제안하였다. 제안된 소성모델과 유한변위이론을 적용한 3차원 탄소성 유한변위해석기법을 개발하였으며 이를 실험값과 비교하여 검증하였다. 검증된 3차원 탄소성 유한변위해석을 이용하여 고강도 원형강교각의 내진해석을 수행하였다. 또한, 고강도 원형강교각의 지름-두께비에 따른 내진성능을 명확히 하였다.

• 산업기술연구
• /
• 제21권A호
• /
• pp.329-336
• /
• 2001

In this study, a series of fatigue tests are carried out in order to estimate quantitatively the characteristics of fatigue crack growth rate for high strength steels of SM570, POSTEN60, and POSTEN80 steel, that is, the influence on fatigue crack growth rate according to the welding line, the characteristics of fatigue crack growth according to the welding method and the kinds of steel, and the characteristics of fatigue crack growth for base metal, heat affected zone and weld metal. From the test results, in case that the notch if parallel to welding line, it knows that the retardations of fatigue crack growth rate in crack tip at early stage increase remarkably than in case that the notch is perpendicular to welding line due to compressive residual stress. And the characteristics of fatigue crack growth rate according to welding method are that the dispersion of fatigue crack growth rate in case of FCAW method is smaller than that of SAW method. Also, it knows that the fatigue crack growth rate converges in high stress intensity factor range.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 추계학술발표대회 개요집
• /
• pp.216-218
• /
• 2003

Most of ferrous b.c.c weld materials may experience martensitic transformation during rapid cooling after welding. And it is well known that volume expansion due to phase transformation could influence in the case of welding of high tensile strength steels on the relaxation of welding residual stress. To apply this effect practically, it is a prerequisite to establish a numerical model which is able to estimate the effect of phase transformation on residual stress relaxation quantitatively. In this study, we investigated the effect of phase transformation on the relaxation of welding residual stress through experiment. And three-dimensional thermal elastic-plastic FEM analysis is conducted to compare the effect of phase transformation on the relaxation of welding residual stress in high strength steels(POSTEN60, POSTEN80) with analytical results which is not considering the effect of phase transformation on residual stress relaxation. According to the results, the extents of welding residual stress relaxation due to phase transformation in the case of welding of POSTEN60, POSTEN80 are 0.85 $\sigma$/$\sigma$$\sub$Y0/, 0.75$\sigma$/$\sigma$$\sub$Y0/, respectively.

• 한국강구조학회 논문집
• /
• 제14권2호
• /
• pp.385-394
• /
• 2002

현재, 국내에서 사용되고 있는 고강도강은 SM570 강재만이 극히 일부분 사용되고 있으며, 그 이상의 고강도강의 사용은 국내의 강교량에는 전무한 실정이다. 본 연구에서는 국내 장대교량 및 일반교량에서의 고강도강 적용의 활성화를 위해 고강도강재인 SM570 강재와 아직 교량에는 적용된 살계가 없는 POSTEN80 강재를 대상으로 횡방향 맞대기 용접연결부의 피로특성을 분석, 평가하였다. 이를 위해 소형시험편을 제작하여 일정진폭하중하에서의 인장 피로시험을 실시하였으며, 피로균열의 발생 및 진정양상, 기존의 연구결과와 비교, 분석하였다. 또한, 모재의 정적 인장강도와 판두께가 용접연결부의 피로강도에 미치는 영향을 분석하고 피로강도를 평가하므로서 고강도강인 SM570과 POSTEN80 강재의 피로특성과 에 따른 횡방향 맞대기 용접연결부에 대한 피로설계기준 제정을 위한 기초 자료를 제시하였다.

• 한국강구조학회 논문집
• /
• 제14권5호통권60호
• /
• pp.647-656
• /
• 2002

강교량에서 사용강재의 고강도화에 의한 구조의 경량화, 합리화는 강교량의 제작 및 가설측면에서 강교량의 경제성을 부각시키고 있다. 이러한 추세에 따라서 향후 강교량 건설에 있어서 고강도강재의 적용사례는 지속적으로 증가할 전망이다. 따라서, 교량부재에 고강도강재를 적용하기 위해서는 강재의 제작작업에서 발생하는 다양한 요인, 예를 들면 용접에 의한 용접열, 부재의 절단 및 가공에 의한 변형경화 등과 같은 강재의 용접성 및 용접이음성능을 정확하게 평가하는 것이 매우 중요하다. 따라서, 본 연구에서는 현재 국내에서 생산되고 있는 SM570, POSTEN60, POSTEN80의 조질 고강도강재를 대상으로 고강도강재의 용접에 따른 용접성 및 가공성을 조사하기 위해서 용접방법별로 최고경도시험 및 경사y형용접터짐시험을 실시하였으며, 또한, 용접이음부의 인장강도, 굽힘성, 흡수에너지 및 경도를 조사하기 위해서 일련의 용접이음시험을 실시하였다.

• 한국강구조학회 논문집
• /
• 제16권5호통권72호
• /
• pp.519-528
• /
• 2004

대부분의 용접재는 용접 후 빠른 속도로 냉각하는 과정에서 재료조직의 변화, 즉 상변태(마르텐사이트변태)가 일어난다. 그리고 이러한 상변태에 의한 체적의 팽창은 특히 고강도강재의 용접시 용접부의 잔류응력완화에 기여한다. 따라서 고강도강을 적용한 강구조물 접합부의 잔류응력 특징을 파악하기 위해서는 고강도강 용접시 상변태가 잔류응력완화에 미치는 효과를 정량적으로 평가할 수 있는 수치적 모델을 확립해야 한다. 본 연구에서는 고강도강 용접시 상변태에 의한 체적의 팽창이 잔류응력 완화에 미치는 영향을 잔류응력 측정 실험을 통하여 조사하였고, 이를 바탕으로 상변태에 의한 잔류응력완화를 고려한 고강도강 및 이종강재 용접접합부의 잔류응력 특징을 3차원 열탄소성 해석기법 개발을 통하여 재현하였다.