• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.265-268
• /
• 2002

In this work, the blend system of epoxy and PMR-15 polyimide is investigated in terms of the cure behaviors and thermal stabilities. The cure behaviors are studied in DSC measurements and thermal stabilities are also carried out by TGA analysis. DDM (4, 4'-diamino diphenyl methane) is used as curing agent for EP and the content of PMR-15 is varied within 0, 5, 10, 35, and 20 phr to neat EP. As a result, the cure activation energy ($E_a$) is increased at 10 phr of PMR-15, compared with that of neat EP. From the TGA results of EP/PMR-15 blend system, the thermal stabilities based in the initial decomposed temperature (IDT) and integral procedural decomposition temperature (IPDT) are increased with increasing the PMR-15 content. The fracture toughness, measured in the context of critical stress intensity factor ($K_{IC}$) and critical strain energy release rate ($G_{IC}$), shows a similar behavior with $E_a$. This result is probably due to the crosslinking developed by the interactions between intermolecules in the polymer chains.

• 접착 및 계면
• /
• 제4권1호
• /
• pp.1-8
• /
• 2003

본 연구에서는 이관능성 에폭시와 PMR-15 블렌드계의 접촉각 측정과 파괴인성 측정을 통하여 PMR-15 조성비에 따른 표면자유에너지가 기계적 계면특성에 미치는 영향에 대하여 고찰하였다. 블렌드계의 FT-IR 분석 결과, PMR-15의 이미드화에 따른 특성 밴드가 1,722, $1,778cm^{-1}$ (C=O)와 $1,372cm^{-1}$ (C-N)에서 나타났고, 에폭시의 개환 반응에 따른 -OH peak는 PMR-15 phr의 함량에서 가장 크게 나타나는 것을 확인할 수 있었다. 증류수와 diiodomethane을 젖음액으로 사용하여 sessile drop 방법으로 접촉각을 측정한 결과, 표면자유에너지는 극성 요소의 증가에 의해서 PMR-15의 함량이 10 phr일 때 최고값을 나타내었다. 또한, 기계적 계면특성을 파괴인성 측정을 통하여 알아본 결과 $K_{IC}$와 $G_{IC}$ 또한 표면자유에너지와 유사한 경향을 나타내는 것을 알 수 있었는데, 이는 PMR-15 10 phr의 조성에서 수소결합의 증가에 의한 블렌드계의 극성요소가 증가함에 따라 분자들간의 계면결합력이 증가했기 때문인 것으로 관찰된다.