• 한국염색가공학회지
• /
• 제4권4호
• /
• pp.81-89
• /
• 1992

Graft polymers of alginic acid-PMMA, different in composition and Mv of branched PMMA, were prepared by emulsion graft polymerization at various MMA concentrations. In aqueous dispersion solution, the adsorption of graft polymer on the montmorillonite was carried out to modify the surface property of powder, and the adsorption of PMMA in organic solvents (acetone, benzene) on the modified surface of powder were observed. The results obtained were as follows. 1. In emulsion graft polymerization of MMA on the sodium alginate in aqueous solution, SA conversion, MMA conversion and % grafting were increased with increasing MMA concentration where as graft efficiency was decreased. 2. The adsorption amount of graft polymer was increased with the elevation of temperature and the increased of dispersion concentration and with the increase of branched PMMA composition of graft polymer. 3. In organic solvent, the adsorption of PMMA on the surface modified particle was proceeded by the orientation along the stretched branched PMMA of adsorbed graft polymer which is in radial direction to the particle surface. 4. The adsorbed amount of PMMA was increased as the temperature and concentration of PMMA solution, the branching of adsorbed graft polymer and the solvency of solvent were increased.

• Macromolecular Research
• /
• 제17권10호
• /
• pp.757-762
• /
• 2009

The micro domain structures and crystallization behavior of the binary blends of poly(methyl methacrylate)-b-poly(pentafluorostyrene)-b-poly(methyl methacrylate) (PMMA-PPFS-PMMA) triblock copolymer with a low molecular weight poly(vinylidene fluoride) (PVDF) were investigated by small-angle X-ray scattering (SAXS), small-angle light scattering (SALS), transmission electron microscopy (TEM), optical microscopy, and differential scanning calorimetry (DSC). A symmetric, PMMA-PPFS-PMMA triblock copolymer with a PPFS weight fraction of 33% was blended with PVDF in N,N-dimethylacetamide (DMAc). In the wide range of PVDF concentration between 10.0 and 30.0 wt%, PVDF was completely incorporated within the PMMA micro domains of PMMA-PPFS-PMMA without further phase separation on a micrometer scale. The addition of PVDF altered the phase morphology of PMMA-PPFS-PMMA from well-defined lamellar to disordered. The crystallization of PVDF significantly disturbed the domain structure of PMMA-PPFS-PMMA in the blends, resulting in a poorly-ordered morphology. PVDF displayed unique crystallization behavior as a result of the space constraints imposed by the domain structure of PMMA-PPFS-PMMA. The pre-existing microdomain structures restricted the lamellar orientation and favored a random arrangement of lamellar crystallites.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.347-350
• /
• 2000

The purpose of this study is to research and develop solid polymer electrolyte(SPE) for Li polymer battery. The temperature dependence of conductivity, impedance spectroscopy and electrochemical properties of PMMA/PVDF electrolytes as a function of a mixed ratio were reported for PMMA/PVDF based polymer electrolyte films, which were prepared by thermal gellification method of preweighed PMMA/PVDF, plasticizer and Li salt. The ion conductivity of PMMA/PVDF electrolytes was 10$\^$-3/S/cm, which may be applicable to a constituent of lithium secondary battery. 5PMMA20PVDFLiC1O$_4$PC$\sub$8/EC$\sub$8/ electrolyte remains stable up to 5V vs. Li/Li$\^$+/. Steady state current method and AC impedance were used for the determination of transference numbers in PMMA/PVDF electrolyte film. The transference number of 5PMMA20PVDFLiC1O$_4$PC$\sub$8/EC$\sub$8/ electrolyte is 0.55.

• Korean Chemical Engineering Research
• /
• 제47권4호
• /
• pp.476-480
• /
• 2009

본 연구는 리튬 이차전지용 고분자 전해질 복합재료에 관한 것으로, 고분자는 poly(ethylene oxide)(PEO)와 poly(methyl methacrylate) (PMMA) 블렌드를 사용하고, 용매로는 Ethylene carbonate(EC), 그리고 $LiClO_4$를 리튬염으로 하는 전해질 복합체 필름을 제조하였으며, PMMA의 함유량에 따른 고분자 전해질의 전기화학적 특성을 관찰하였다. 제조된 고분자 전해질의 결정화도와 이온전도도는 시차주사열량계(DSC)와 주파수반응분석기(FRA)로 분석하였다. 그 결과 PMMA의 함량을 증가시킴에 따라서, PEO의 결정 영역이 감소하고 이온전도도가 증가하였다. 또한, PMMA의 함량이 20 wt.% 이상인 경우, 고분자 블렌드필름에서 상분리되는 현상을 관찰하였다. 즉, SEM 분석결과에 의해서, PMMA 주성분 영역과 PEO 주성분 영역의 구분이 가능하였다. 고분자 전해질의 이온전도도는 20 wt.% 첨가한 경우 가장 큰 이온전도도를 가지며, 함유량이 20 wt.% 이상에서는 PMMA 상의 증가로 인해 다소 감소된 이온전도도 변화를 나타내었다.

• Korea-Australia Rheology Journal
• /
• 제16권3호
• /
• pp.135-140
• /
• 2004

Morphological and rheological properties of the poly(methyl methacrylate) (PMMA) and polystyrene (PS) blends were studied by scanning electron microscopy (SEM) and advanced rheometric expansion system (ARES). From the SEM results, the PMMA-PS blends showed dispersed morphology and the particle size of the dispersed phase was quite small (0.1~0.6 $\mu\textrm{m}$ compared with other immiscible polymer blends. Values of the interfacial tension of the PMMA-PS blend were obtained from the Choi-Schowalter and the Palierne emulsion models using the storage modulus of the PMMA and PS, and found to be 1.0 and 2.0 mN/m, respectively. The interfacial tension between the PMMA and PS was also calculated from the Flory-Huggins polymer-polymer interaction parameter ($\chi$) and found to be from 0.98 to 1.86 mN/m depending on the molecular weight and composition. Comparing the values of the interfacial tension from the Flory-Huggins polymer-polymer interaction parameter and the values measured by oscillatory rheometer, it is suggested that the interfacial tension of the PMMA-PS blend obtained from the polymer-polymer interaction parameter are in good agreement with the values obtained by rheological measurements.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 춘계학술대회 논문집
• /
• pp.29-32
• /
• 2005

Poly (methyl methacrylate) (PMMA) is one of the promising representive of polymer gate dielectric for its high resistivity and sutible dielectric constant. PMMA (Mw=96700) films were prepared on p-Si by spin coating method. PMMA were coated compactively and flatly as observeed by AFM. MIS(Al/PMMA/p-Si) structure was made and capacitance-voltage (C-V) and current-voltage (I-V) measurements were done with PMMA films for different thermal treatment temperature. PMMA films were showed proper dielectric constant and breakdown voltage. Above the glass transition temperature PMMA films degraded. C-V measured at various frequencies, dielectric constant increased a little. The absence of hysteresis in the C-V characteristics, which eliminate the possibility of mobile charges in the PMMA films. The observed thermal stability, smooth surfaces, dielectric constant, I-V behavior implies PMMA formed by spin coating can be used as an efficient gate dielectric layer in OTFTs.

• 접착 및 계면
• /
• 제2권1호
• /
• pp.18-22
• /
• 2001

Poly(vinylidene fluoride)(PVDF)를 포함하는 고분자 블렌드 필름의 표면층의 모폴로지를 원자력간 현미경과 시차주사열량계 측정을 토대로 연구하였다. ${\alpha}$ 및 ${\gamma}$형 결정상을 가진 PVDF는 Poly(methyl methacrylate)(PMMA) 및 가수분해된 PMMA(carboxyl content:14wt%)와의 블렌딩에서 표면층은 PVDF의 결정상만으로 이루어져 있음을 확인하였다. 그러나 PMMA의 결정상이 가수분해율이 증가함에 따라 표면 자유에너지의 차이도 증가함에도 불구하고 가수분해된 PMMA의 존재를 확인하였다. 이러한 결과는 표면층에서의 낮은 표면 자유에너지 성분인 PVDF의 농축 정도는 자유에너지 차보다 상호작용력의 크기에 밀접히 관련되어 있음을 알 수 있었다. 한편, carboxyl group의 도입은 PVDF와 PMMA의 상용성을 저해하는 것으로 밝혀졌다.

• 폴리머
• /
• 제26권3호
• /
• pp.410-414
• /
• 2002

중심 금속을 안정화시킬 수 있는 ferrocene-based diimine 리간드를 가지고 낮은 산소 친화성을 가진 후전이금속인 Pd 촉매를 합성하여, 극성 단량체인 메틸메타크릴레이트 (MMA)의 중합에 사용하였다. 중합계 내의 impurity scavenger로 triisobutylaluminium (TIBA)를 사용하였을 때에, 중합온도와 [TIBA]/[Pd] 몰비가 생성 중합체(PMMA)의 수율 및 유리전이온도 ($T_g$)에 미치는 영향을 조사하였다. PMMA의 수율은 40~$50^{\circ}C$의 중합온도 및 2000~3000의 [TIBA]/[Pd] 몰비에서 가장 높았다. PMMA의 $T_g$는 중합온도에는 크게 영향을 받지 않으나, [TIBA]/[Pd] 몰비에 의존한다는 것을 관찰할 수 있었다. PMMA의 $T_g$의 변화를 PMMA의 미세구조와 연관시켜 조사한 결과, PMMA의 $T_g$ 이소탁틱도와 직선적 관계를 가짐을 알았다.

• 폴리머
• /
• 제33권5호
• /
• pp.429-434
• /
• 2009

본 연구에서는 PMMA의 전기 방사 조건을 자세히 조사하였다. 즉, DMF 및 THF를 용매로 하여 최적의 혼합비 및 농도를 조사하였다. 또한, 은을 첨가했을 때 용액의 전도성 및 섬유 직경에 대해 검토하였고, 얻어진 나노섬유 부직포의 항균성을 조사하였다. 그 결과 DMF와 THF가 7:3이며 18 wt%일 때 섬유형성능이 우수하였고, 은을 1000ppm 넣어 전기방사하였을 때 섬유 직경은 100-400 nm 이었다. 투과형 전자현미경으로 관찰한 결과 은 나노입자는 섬유의 테두리에 분포되어 있었으며, 이들은 그램 양성균 및 그램 음성균에 대해 높은 항균성을 나타내었다.

• 접착 및 계면
• /
• 제11권3호
• /
• pp.112-119
• /
• 2010

PMMA와 PBA core 제조 시 개시제는 APS를, 유화제 SDBS의 농도를 0.01에서 0.03 wt% 일 때 전환율이 95.8과 92.3%로 가장 우수하였으며, core-shell 복합입자의 제조 시에는 SDBS의 농도 0.02 wt% 일 때 PMMA/PBA core-shell 복합입자는 전환율이 90.0%, PBA/PMMA core-shell 복합입자는 89.0%가 되었다. FT-IR 분석과 GPC에 의한 평균분자량 측정을 통해 core와 shell 단량체들이 중합되어 있음을 확인하고, 복합입자의 형태는 상온에서의 필름형성정도와 TEM 분석으로 확인하였다. DSC에 의해 유리전이온도를 측정함으로써 일반 공중합체와는 달리 2개의 유리전이온도가 존재하여 core-shell 복합입자가 형성되었음을 알 수 있고, 각각의 core-shell 복합입자의 인장강도와 신율의 측정을 통해 고기능성 접착바인더로서의 사용가능성을 확인하였다.