• Fibers and Polymers
• /
• 제6권4호
• /
• pp.277-283
• /
• 2005

In order to prepare high molecular weight poly(methyl methacrylate) (PMMA)/silver nanocomposite microspheres, methyl methacrylate was suspension-polymerized in the presence of silver nanoparticles at low temperature with 2,2'-azobis(2,4-dimethylvaleronitrile) as an initiator. The rate of conversion was increased by increasing the initiator concentration. When silver nanoparticles were added, the rate of polymerization decreased slightly. High monomer conversion (about $85\%$) was obtained in spite of low polymerization temperature of $30^{\circ}C$. Under controlled conditions, PMMA/silver microspheres with various number-average degrees of polymerization (6,000-37,000) were prepared. Morphology studies revealed that except for normal suspension microspheres with a smooth surface, a golf ball-like appearance of the microspheres was observed, due to the migration and aggregation of the hydrophilic silver nanoparticles at the sublayer beneath the microsphere's surface.

• 폴리머
• /
• 제34권4호
• /
• pp.341-345
• /
• 2010

현탁중합에 의한 폴리(메틸 메타크릴레이트)((poly(methyl methacrylate)(PMMA))/은 미세입자 제조시 사용된 은 나노입자가 중합속도 및 PMMA 미세입자의 형태에 미치는 영향을 고찰하였다. 은 나노입자의 친수성 정도 는 중합속도 및 PMMA/은 미세입자의 형태에 큰 영향을 주었다. 개질된 은 나노입자를 이용하여 중합한 경우에 중합 속도가 약간 증가하였다. 중합온도가 낮음에도 불구하고 85% 이상의 전환율을 가지는 PMMA/은 미세입자를 제조할 수 있었다. 사용된 은 나노입자 표면의 친수성 정도에 따라 중합 후 미세입자의 표면은 볼록한 모양과 오목한 모양의 입자가 제조되었다. 친수성 정도가 감소된 은 나노입자를 이용하여 현탁중합된 미세입자가 안정적인 나노복합체를 형성하였다.