• Fashion & Textile Research Journal
• /
• v.16 no.2
• /
• pp.326-332
• /
• 2014

To develop cool touch feeling fabrics for summer clothing material, it was manufactured several compositions of woven fabrics, having rayon multi-filament yarn (non-twisted) as warp and various kinds of yarn, such as viscose rayon multi-filament yarn (twisted), tencel$^{(R)}$ spun yarn, PET high absorbance quick dry filament yarn, and PET based rayon-like yarn, as weft. After preparing the fabrics, basic properties of the fabrics were investigated, such as air-permeability, tensile strength, absorption rate, drying rate, etc. Also, surface warm / cool sensations of the woven fabrics were assessed by Qmax Warm / Cool Touch Tester. It was observed that the fabrics composed of viscose rayon multi-filament yarn (warp) and PET high absorbance quick dry filament yarn (weft) showed excellent surface cool touch sensation-the highest Qmax value. This is because the fabric having flat shaped PET high absorbance quick dry filament shows the largest contact area with Qmax measuring plate. And, the fabric also showed superior high absorbance and quick dry property as expected. In addition, we treated phase change material (PCM) on the surface of the fabric composed of viscose rayon multi-filament yarn (warp) and PET high absorbance quick dry filament yarn(weft) to improve the cool touch feeling. However, the surface cool touch feeling was impaired by resin treated with PCM during the finishing process.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.42 no.5
• /
• pp.799-808
• /
• 2018

This study develops triacetate-containing functional fabrics with a cool-touch and cool-absorbent. For this purpose we used composite yarns made using triacetate filament and PET High absorbance quick dry filament as well as the composite fabric woven. The fineness of the yarn and structure of fabric varied the cover factor varied. The blend ratio of triacetate was differently set. When the triacetate content was the same, the cool touch of the fabric having a large cover factor and small SMD increased. The surface became smooth and the contact area became large; in addition, both the Qmax value and the cool-touch became large. In the case of similar density, the cool-touch of the fabric having a large content of triacetate increased. The cool-absorbent of the fabric containing triacetate showed a similar level of the PET High absorbance quick dry filament fabric treated with and endothermic cooling agent. It was possible to develop a functional coolness fabric with a cool-touch and a cool-absorbent when the content of triacetate and cover factor were well combined.