• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2000.05a
• /
• pp.874-877
• /
• 2000

Pre-coated sheet materials are a cost-effective and environmentally attractive alternative to conventional sheet materials coated after forming. At present but the high scratch sensitivity of coating used for pre-coated metal sheet is a major limitation to use of these materials. Because of high scratch sensitivity, products made by pre-coated metal sheet are not formed by conventional design method. This study has been performed to investigate scratch characteristic of non-vinyl pre-coated metal (PCM) sheet. Using the simple U-bending test equipment, three non-vinyls PCM's were tested. This paper provides the results of bending tests showing the influence of sheet surface texture, tool material and process conditions. It was found that the influence of punch, die clearance and tool material had an effect upon the scratch characteristic.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.4
• /
• pp.121-128
• /
• 2001

This study has been performed to investigate formability of non-vinyl PCM(pre-coated metal)sheet. First, physical test of PCM sheets were tested to evaluate finish coating characteristic of PCM. And then, test equipment was made for friction test and three non-vinyl PCM sheets were tested by straight pulling method. This paper provides the results of the friction tests showing the influence of sheet surface texture and process conditions. It was found that the influence of contact pressure and speed had an effect upon the level of friction. Also using tests, the scratch resistance of a series of polyester coating has been investigated. This investigation aims to clarify the process conditions that prevent the scratch of PCM to form the good electrical appliances such as microwave oven, air conditioner and refrigerator etc.

• Transactions of Materials Processing
• /
• v.9 no.5
• /
• pp.463-468
• /
• 2000

An experimental study has been performed to investigate the forming characteristics of pre-coated metals(PCMs) widely used in domestic appliances through Erichsen tests and deep drawing tests. Erichsen tests are performed to find out the forming limits of seven pre-coated metals in normal conditions. Rectangular deep-drawing tests are carried out to know the effects of die materials and blank metals on forming loads and surface defects of final PCM products. In the deep-drawing test, four die materials ［STD11(TiCN), STD11, STD11(TD), AMPCO] are used. In the Erichsen test, the forming limits of PCMs are obtained from flaking or crack of pre-coated films and lower than those of base metals. In respect of surface roughness and forming load, STD11(TD) and AMPCO materials are superior to my other die-materials used in the deep-drawing test.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.159-162
• /
• 1999

This study has been performed to investigate forming limit of PCM(Pre-Coated Metal) widely using appliances. Die set was made for deep drawing test and some PCMs were inrectangular deep drawing test in no-lubricant 20% clearance some die materials(STD11(TiCN) STD11(HrC60) STD11(TD) AMOCO and 6mm/sec punch speed. and Ericshen test was performed in regular conditions In this experiment forming limit forming characteistics superior die materials and fracture of PCMs been investigated. In results tested PCMs have lower forming limit than base material because lower elongation ultimate strength than base material And two-fracture types - occurring band and flaking - of PCMs have been investiqated.

• Journal of Adhesion and Interface
• /
• v.12 no.4
• /
• pp.105-110
• /
• 2011

Polyester/melamine cured coatings had been used for pre-primed coatings and pre-coated metal coatings, because it has good mechanical,chemical properties, and mar resistance. But it has weak points such as stiffness and low formability for making automotive components. Polyester had been synthesized using polycarbonate diol of long alkyl chain which can improve flexibility and formability which is one of the important factors for pre-coated steel sheets (PCM). In this study, strain and tensile strength were examined by the tensile test and formability was examined by the drawing test. Also, Those polyester resins were also measured by DMA to verify flexibility of cured coatings.

• Elastomers and Composites
• /
• v.48 no.2
• /
• pp.167-171
• /
• 2013

Weatherability was examined according to aluminum particle size and its orientation used in PCM(Paint Coated Metal). Substrate delamination was checked by different UV transmission rate with QUV$^{(R)}$ (Q-LAB) equipment that can make accelerated UV irradiation. Film was prepared using three different types of conflake aluminum pastes under a PCM coating process and clearcoat was sprayed. UV transmission test results showed low transmission rate when EKART #790 having the smallest particle size and horizontal orientation was used. From the gloss retention results, gloss retention was highest in EKART #790 and followed by #770, #750.