• Polymer(Korea)
• /
• v.35 no.6
• /
• pp.580-585
• /
• 2011

This article aims to enhance the biodegradability and environment-friendliness of petroleum based biodegradable poly(butylene adipate-co-succinate-co-terephthalate)(PBAST) by blending chemically modified thermoplastic starch(CMPS). CMPS is a kind of bio-based biodegradable resin which is manufactured by reacting starch with maleic anhydride(MA) in the presence of a plasticizer and a free radical initiator. The characteristic properties of PBAST/CMPS blends were investigated by observing their morphology, thermal, mechanical properties, and biodegradability. The good interfacial adhesion between the phases examined by SEM revealed that PBAST/CMPS blends were compatible blends. The tensile strength and elongation decreased with increasing CMPS content, while modulus increased. The biodegradability of the blends was much higher than that of pristine PBAST and increased with increasing CMPS contents.

• Clean Technology
• /
• v.14 no.4
• /
• pp.256-264
• /
• 2008

In this study, using PBAST (poly(butylene adipate-co-succinate-co-terephthalate)) which was eco-friendly biodegradable aliphatic polyester, PBAST/PVA (poly(vinyl alcohol)) double-layered hollow microspheres were prepared with the water/oil/water multiple emulsion ($W_1/O/W_2$) method. The double-layered hollow microspheres were manufactured with the yield of 30.92% when the concentration of polymer PBAST in organic phase was 5 wt%, the concentration of PVA in inner aqueous phase was 5 wt%, the volume ratio of $W_1/O$ emulsion to outer aqueous phase was 1:4.5, and when co-surfactants that had large gap in HLB (hydrophile-lipophile balance) value were used. The bulk density of prepared hollow microsphere was 0.180 g/ml and particle size was $1.5{\sim}3\;{\mu}m$.

• Applied Chemistry for Engineering
• /
• v.16 no.6
• /
• pp.800-808
• /
• 2005

The compounding resin for biodegradable wrap was developed, and its manufacturing process and physical properties were studied. For these purposes, following factors were optimized: the types and amounts of raw resin material, anti-oxidants, and lubricants used. In this work, the stable compounding resin used to make biodegradable wrap was based on poly(butylene adipate-co-butylenesuccinate) (PBAS) and poly(butyleneadipate-co-butylene succinate-co-butyleneterephthalate) (PBAST). The improved properties of resin with an additive were investigated by melting flow index (MFI). From these results, the physical properties of compounding resin, based on PBAST, were more than those of PBAS. For PBAS, the Irganox 1010, 1076 and Irgafos TNPP as the first and second anti-oxidants, respectively, were good. For PBAST, the good first and second anti-oxidants, respectively, were Irganox 1076 and Mark PEP 36. The good lubricants for feeding PBAS and PBAST were glycerol monostearate and palmityl alcohol, respectively. The stability and tensile strength experiment of wrap were also investigated by the elution of heavy metals and universal testing machine (UTM), respectively. The decomposition ratio of developed wrap was increased proportional to the reclaiming time. The degradation ratio of compounding resin sample was about 60% after 40 days.