Objective: To study and compare the effects of different demineralization-inhibition methods on the shear bond strength (SBS) and fracture mode of an adhesive used to bond orthodontic brackets to demineralized enamel surfaces. Methods: Eighty freshly extracted, human maxillary premolars were divided into 4 equal groups and demineralized over the course of 21 days. Brackets were bonded to the demineralized enamel of teeth in Group 1. In Group 2, bonding was performed following resin infiltration ($ICON^{(R)}$, DMG, Hamburg, Germany). Before bonding, pre-treatment with acidulated phosphate fluoride (APF) or solutions containing casein phosphopeptide-amorphous calcium phosphate with 2% neutral sodium fluoride (CPP-ACP/wF) was performed in Groups 3 and 4, respectively. The SBS values of the brackets were measured and recorded following mechanical shearing of the bracket from the tooth surface. The adhesive remnant index (ARI) scores were determined aft er the brackets failed. Statistical comparisons were performed using one-way ANOVA, Tukey's post-tests, and G-tests. Results: Significant differences were found in some of the intergroup comparisons of the SBS values (F = 39.287, p < 0.001). No significant differences were found between the values for the APF-gel and control groups, whereas significantly higher SBS values were recorded for the resin-infiltrated and CPP-ACP/wF-treated groups. The ARI scores were also significantly different among the 4 groups (p < 0.001). Conclusions: Tooth surfaces exposed to resin infiltration and CPP-ACP/wF application showed higher debonding forces than the untreated, demineralized surfaces.
Nascimento, Glaucia Cristina Rodrigues;Miranda, Cyndi Albuquerque De;Machado, Sissy Maria Mendes;Brandao, Gustavo Antonio Martins;Almeida, Haroldo Amorim De;Silva, Cecy Martins
The korean journal of orthodontics
/
v.43
no.5
/
pp.242-247
/
2013
Objective: To test the null hypothesis that no difference exists between the effects of at-home bleaching and in-office bleaching on shear bond strength (SBS) with bracket bonding at 4 different time intervals after dental bleaching. Methods: Ninety extracted human premolars were randomly divided into 9 groups (n = 10) according to the bleaching methods used (at-home bleaching and in-office bleaching) and the storage time in artificial saliva (30 min, 1 day, 2 weeks, and 3 weeks before bonding). The control group was stored in artificial saliva for 7 days. Brackets were bonded with the Transbond XT adhesive system, and SBS testing was performed. The adhesive remnant index (ARI) was used to assess the amount of resin remaining on the enamel surfaces after debonding. The SBS data were analyzed by analysis of variance (ANOVA) and the Tukey test. For the ARI, the Kruskal-Wallis test was performed. Significance for all statistical tests was predetermined to be p < 0.05. Results: The SBS of the unbleached group was significantly higher (p < 0.05) than that of the bleached groups (except for the group bonded 30 min after at-home bleaching). Conclusions: The null hypothesis was not totally rejected. All bleaching groups tested had decreased SBS of the brackets to the enamel, except for the group bonded 30 min after at-home bleaching. The SBS returned to values close to those of the unbleached enamel within 3 weeks following bleaching.
PURPOSE. The purpose of this study was to investigate the bonding properties of denture bases to silicone-based soft denture liners immersed in isobutyl methacrylate (iBMA) and 2-hydroxyethyl methacrylate (HEMA) for various lengths of time. MATERIALS AND METHODS. Polymethyl methacrylate (PMMA) test specimens were fabricated (75 mm in length, 12 mm in diameter at the thickest section, and 7 mm at the thinnest section) and then randomly assigned to five groups (n=15); untreated (Group 1), resilient liner immersed in iBMA for 1 minute (Group 2), resilient liner immersed in iBMA for 3 minutes (Group 3), resilient liner immersed in HEMA for 1 minute (Group 4), and resilient liner immersed in HEMA for 3 minutes (Group 5). The resilient liner specimens were processed between 2 PMMA blocks. Bonding strength of the liners to PMMA was compared by tensile test with a universal testing machine at a crosshead speed of 5 mm/min. Data were evaluated by 1-way ANOVA and post hoc Tukey-Kramer multiple comparisons tests (${\alpha}$=0.05). RESULTS. The highest mean value of force was observed in Group 3 specimens. The differences between groups were statistically significant (P<.05), except between Group 1 and Group 4 (P=.063). CONCLUSION. Immersion of silicone-based soft denture liners in iBMA for 3 minutes doubled the tensile bond strength between the silicone soft liner and PMMA denture base materials compared to the control group.
It has been studied that relations between electronic structure and anti-tumor activity by variation of amine group in cis-diamminedichloroplatinum (Ⅱ) complexes. We were also interested in these Pt (Ⅱ) complexes interaction with 1-methylcytosine of DNA base and the electronic structure of these complexes in order to understand the mechanism of the metal-nucleobases interaction. The results showed that net charge of center metal in Pt complexes effect anti-tumor activity. The mechanisgm of the bonding between metal and ligands largely based on charge transfer from ligand to metal atom. Furthermore, the established molecular orbitals showed that metal 6p-orbitals played an important role in the bonding scheme for the interactions between platinum (Ⅱ) complexes and 1-methylcytosine. We also found that the stronger Pt-N3 bonding strength became, the better anti-tumor agents were.
This study aimed to evaluate the marginal microleakage of Class V cavities of All-bond 2 (Wet - bonding system), Gluma (Adhesion of resin to exposed collagen fibers), and Scotchbond Multi-purpose(Mild Etching System). Hundred extracted human teeth divided into a control and three experimental groups consisting of eight teeth. The experimental group was further subdivided into All- bond2, Gluma and Scotchbond MP groups, Vitrebond served as the control. The positive control group consisted of specimens filled with resin and with no etching, primer and bonding procesure. Polished specimens underwent temperature changed from $5^{\circ}C$ to $55^{\circ}C$ a thousand times. After thermocycling, speciemens were placed in 2 % methylene blue dye solution for 24 hours in an incubator set at $37^{\circ}C$. The teeth were sectioned buccolingually and the degree of dye penetration was observed with a stereomicroscoped(*20). The following results were obtained. 1. Both the control and the experimental group showed a lower degree of dye penetration on enamel than on dentin margins(p<0.05) 2. Gluma exhibited a statistically significant lower degree of dye penetration than All-bond 2 on enamel margins(p<0.05) Scotchbond MP also exhibited a lower degree of dye penetration than All-bone 2 but was no statistically significant. Gluma and Scotchbond MP exhibited a similar degree of dye penetration. 3. The degree of dye penetration of All-bond 2, Gluma and Scotch bond MP showed no statistically singnificance on enamel margins but was significantly lower than in the control using Vitrebond. 4. All-bond 2 exhibited a statistically significant lower degree of dye penetration than Gluma on dentin margins. All- bond 2 and Scotchbond MP showed a similar degree of dye penetration. 5. The degree of dye penetration of All-bond 2, Gluma and Scotchbond MP showed no statistically significance on dentin margins. There was neither a statistical significance with the control.
Purpose: We compare the bond strength of heat-cured PMMA of Lucitone 199 and QC-20 and Tokuyama Rebase Resin of self-cured resin, which are widely used and well accepted in clinical practice. In order to test the mechanical bonding and chemical bonding, we will compare the bond strength between EstheShot Bright, Smiletone, Repair and Rebase resins. Methods: The denture base resin used in this study was PMMA heat-cured QC-20 and Lucitone 199, polyamide resin EstheShot Bright, Smiletone. And Two types of self-curing Rapid Repair and Tokuyama Rebase were used as resection resins. To measure the bond strength, the denture specimens were fabricated in the size of $10{\times}64{\times}3.5mm$ as instructed by the manufacturer. A surface treatment agent was applied to the cut surfaces of each denture specimen, and the specimens were placed in a preformed silicone mold, and autoclaved excimer resins were prepared. The bending strength of the fabricated specimens was measured using a universal testing machine (STM-5, United Calibration Co., U.S.A.) to measure the three-point bending strength. Results: In both polycarbonate and polyacetal resin, a special resin surface treatment agent showed higher bonding strength than the resin surface treatment agent(p<0.05). Regardless of the type of surface treatment, polycarbonate showed higher bond strength than polyacetal resin(p<0.05). Conclusion: It is considered desirable to use a special surface treating agent for the thermoplastic denture base resin such as polycarbonate and polyacetal resin.
Mi-Kyung Yu;Eun-Jin Oh;Myung-Jin Lim;Kwang-Won Lee
Restorative Dentistry and Endodontics
/
v.46
no.4
/
pp.54.1-54.10
/
2021
Objectives: The purpose of this study was to quantify phase transformation after hydrofluoric acid (HF) etching at various concentrations on the surface of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP), and to evaluate changes in bonding strength before and after thermal cycling. Materials and Methods: A group whose Y-TZP surface was treated with tribochemical silica abrasion (TS) was used as the control. Y-TZP specimens from each experimental group were etched with 5%, 10%, 20%, and 40% HF solutions at room temperature for 10 minutes. First, to quantify the phase transformation, Y-TZP specimens (n = 5) treated with TS, 5%, 10%, 20% and 40% HF solutions were subjected to X-ray diffraction. Second, to evaluate the change in bond strength before and after thermal cycling, zirconia primer and MDP-containing resin cement were sequentially applied to the Y-TZP specimen. After 5,000 thermal cycles for half of the Y-TZP specimens, shear bond strength was measured for all experimental groups (n = 10). Results: The monoclinic phase content in the 40% HF-treated group was higher than that of the 5%, 10%, and 20% HF-treated groups, but lower than that of TS-treated group (p < 0.05). The 40% HF-treated group showed significantly higher bonding strength than the TS, 5%, and 10% HF-treated groups, even after thermal cycling (p < 0.05). Conclusions: Through this experiment, the group treated with SiO2 containing air-borne abrasion on the Y-TZP surface showed higher phase transformation and higher reduction in bonding strength after thermal cycling compared to the group treated with high concentration HF.
The purpose of this study was to observe the tensile and bonding strength of the joined amalgam restoration. Amalgam alloys of fine-cut (F-type), spherical (S-type), and dispersed type (D-type) were selected in this study, and all specimens were divided into three groups according to the condensation methods as follows. Group I : the control group which condense the same kinds of mixed amalgam into the whole part of the mold respectively. Group II : the group which condense a mix of amalgam into one half of the mold, and then condense a new mix of amalgam into the rest half of the mold 15 minutes later. Group III : the group which condense a mixed amalgam into one half of the mold, and then condense a new mix of amalgam into the rest half of the mold 7 days later. All specimens were stored in incubator at $37{\pm}1^{\circ}C$ for seven days with immersing in saline solution before testing. The tensile and bonding strength of them were measured with Instron Universal Testing machine. The results were as follows: 1. In Group I, the order of tensile strength was F-type, S-type, and D-type. 2. In case of bonding of S-type + S-type, the difference of the bonding strength between Group II and III was not significant. (P> 0.05) 3. The bonding strength of F-type + S-type of Group II was marked the highest in value, and the lowest bonding strength was showed in bonded D-type + D-type of Group III. 4. In case of bonding with the different kinds of amalgam alloy in Group II, the specimen bonded to F-type was marked the highest bonding strength, and the specimen bonded with F-type was marked the lowest one. In Group II, the bonding strength of the specimens bonded with the same kinds of amalgam alloy was presented as the same order as that of Group I. 5. In Group III, the specimen connected with D-type marked the lowest bonding strength of all specimens. In Group III, the bonding strength of the specimens connected with the same kinds of amalgam alloy was the order of S-type + S-type, F-type + F-type, and D-type + D-type.
Now composite resin restoration is clinically accepted in the repair of fractured PFM case, many mechanical surface treatment methods are performed to increase retentive force. The main purpose of this study was to compare the retentive force among the possible surface treatments and to insure the best method for the clinical application to the fractures porecelain and the exposed metal surface. To compare and to analyze the retentive force of repair resin, porcelain specimen were divided into 2 groups, etching group and non-etching group, and etching group were treated with 37% $H_3PO_4$, 1.23% APF, 10% HF and non-etching groups were treated with diamond bur, micro-sandblasasting. Also, metal specimens were divided by 2 groups : one was non-precious metal group which was treated with diamond bur, micro-sandblasting and tin plating and electrolytic etching, the other was precious metal group which was composed of micro-sandblasting treatment only and tin plating treatment with micro-sandblasting. Each specimen had been restored for 48 hours and the bond strength of each specimen was calculated with Universal testing machine. The results were as follows : 1. Porcelain specimen had higher bonding strength than metal specimen for the repair resin(P<0.01). 2. In porcelain specimen, 10% HF etching group had the highest bonding strength among etching and non-etching group. 3. Metal specimen treated with micro-sandblasting had highest bonding strength among the non-sandblasting had hightest bonding strength among the non-precious group, tin plating group had higher bonding strength than micro-sandblasting group between the precious metal groups. 4. Bonding strength of tin plating was increased in precious metal group only.
Park, Hee-Geun;Park, Won-UK;Zhao, Jinming;Hwang, Kyu-Hong
Journal of Technologic Dentistry
/
v.38
no.3
/
pp.175-183
/
2016
Purpose: Observation of Oxide Film Formation and Bonding Strength according to surface treatment of Co-Cr Alloy for porcelain fused to Metal. Methods: metal specimens $0.5mm{\times}25mm{\times}4mm$ in size were made using Co-Cr alloys for porcelain fused to metal crown (Heraenium P, Tae jung Medis). Dental porcelain $0.5mm{\times}25mm{\times}4mm$ in size was sintered on the metal specimens after changing the etching time, sandblasting condition, and heat treatment temperature. Subsequently, the bonding strength was compared by the three-point flexural strength test using a universal testing machine (UTM) to observe the fracture surface and oxidized layers. Results: With regard to the experimental group treated with acid-etching, Specimen 1 treated for 25 minutes (B-3) showed the highest bonding strength, and Specimen 2 treated only with sandblasting showed the most excellent bonding force at 3.5 bar (C-3). With regard to the experimental group treated with sandblasting at 3.5 bar after acid-etching for 25 minutes, Specimen 3 with heat treatment at $980^{\circ}C$ (D-3) showed the highest bonding strength. Conclusion: The specimen which went through both sandblasting and etching, showed an excellent ceramicmetal bond strength.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.