• Journal of Sensor Science and Technology
• /
• v.12 no.1
• /
• pp.10-15
• /
• 2003

$PbTiO_3$/P(VDF/TrFE) thin film for pyroelectric infrared sensor's sensing materials have been fabricated by spin coating technique. 65 wt% VDF and 35 wt% TrFE were for P(VDF/TrFE) powder. $PbTiO_3$ powder was used for a ceramic - polymer composites materials. Surface of composite thin film by ceramic fraction factor was observed by SEM. The $PbTiO_3$/P(VDF/TrFE) thin film capacitancy, dielectric constant and dielectric loss measured by impedence analyzer(HP4192A) and pyroelectric coefficient was measured by semiconductor parameter analyzer(HP4145B).

• Journal of environmental and Sanitary engineering
• /
• v.10 no.3
• /
• pp.16-28
• /
• 1995

Influences of capsaicin on the activities of cytochrome P45O of liver cell were studied in rats. Rats were provided food and water ad libitum and capsaicin and methylcellulose were gavaged for 6 days. Body weight gain and liver weight/body weight ratio, microsomal protein content and serum HDL- cholesterol content, the activity of cytochrome P450 and erythromycin demethylase, the activities of ethoxyresorufin and pentoxyresorufin O- dealkylase were determined. Capsaicin increased body weight gain but showed no significant changes on liver weight as compared with control group. Capsaicin increased the microsomal protein significantly but decreased the serum HDL- cholesterol. Capsaicin decreased the microsomal cytochrome P4SO significantly and did not show any influences on erythromycin demethylase ( cytochrome P45O III A ). Capsaicin increased the activity of pentoxyresorufin O- dealkylase ( cytochrome P45O II B) and decreased the activity of ethoxyresorufin O-dealkylase ( cytochrome P45O I A). It might be concluded that capsaicin reduced the microsomal cytochrome P45O and induced the CYP III and inhibited the CYP I A. It also might be concluded that capsaicin had no influence on CYP III A and decreased serum HDL- cholesterol. In these results capsaicin can not be used as an anti- atherosclerotic agent by increasing the CYP III A and HDL- cholesterol but it is considered that the more precise study on these theme is necessary.

• Proceedings of the KIEE Conference
• /
• 2003.10a
• /
• pp.72-74
• /
• 2003

Rf magnetron sputtering을 이용하여 InP, GaAs 기판위에 ZnO 박막을 증착시켰다. 진공 ampul 및 $Zn_3P_2$ 분위기 하에서 열처리 과정을 통해 P와 As을 ZnO 박막내에 도핑하였으며, 박막의 전기적 특성 측정 결과 정공의 농도가 $10^{16}cm^{-3}-10^{19}cm^{-3}$ 으로서 p-형 전기전도도를 나타내었다. XRD 측정을 통하여 ZnO 박막의 내부에 이상이 존재하지 않는다는 것을 확인하였다. 또한 FESEM을 이용하여 p-형 ZnO 박막의 표면을 관찰하였으며 그 위에 n-형 ZnO 박막을 sputtering을 이용하여 증착시켜 I-V 특성을 관찰하였다. 본 실험을 통해 P 및 As의 확산을 통한 p-형 ZnO 박막의 성장이 가능하였으며, I-V 특성으로부터 ZnO의 발광소자 및 자외선 검출기로의 응용이 가능함을 확인하였다.

• 제어로봇시스템학회:학술대회논문집
• /
• 1994.10a
• /
• pp.49-53
• /
• 1994

Advanced Real-Time Satellite Simulator(ARTSS) has been developed to support the telemetry, tracking and command operations of the ETRI satellite control system and to provide satellite engineers a more powerful and informative satellite simulations tool on the desktop. To provide extensive simulation functions for a communication satellite system in the pre-operational and operational missions, ARTSS uses a geosynchronous orbit(GEO) satellite model consisting of the attitude and orbit control subsystem, the power subsystem, the thermal subsystem, the telemetry, command and ranging subsystem, and the communications payload subsystem. In this paper, the system features and functions are presented and the satellite subsystem models are explained in detail.

• Applied Biological Chemistry
• /
• v.37 no.2
• /
• pp.124-129
• /
• 1994

The rate of hydrolysis of insecticidal $O,O-diethyl-{\alpha}-cyanobenzylideneamino-oxyphosphorothioate\;(Volaton^{\circledR})$ has been studied in 25% (v/v) aqueous dioxane. On the basis of solvent effect (pH 6.0; m=0.21, n=1.55, pH 12.0; m=0.42, n=3.14 & $|m|{\ll}|l|$), general base catalysis, hydrolysis product analysis, calculation of molecular orbital (MO) and rate equation, it may be concluded that the hydrolysis of Volaton proceeds through the $A_{AC}2$ mechanism via trigonal bipyramidal $(sp^3d^2)$ intermediate below pH 7.0, while above pH 9.0 the hydrolysis proceeds through the $B_{AC}2$ mechanism. Hydrolysis reactivity of Volaton depends on positive charge strength $(p{\gg}{\alpha}C_2)$ rather than steric hindrance. In the range between pH 7.0 and pH 9.0, these two reactions occur competitively.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.505-512
• /
• 1994

It has been reported that a biocement obtained by mixing CaO-SiO2-P2O5 glass powder and ammonium phosphate solution has biocompatibility as well as high strength. However, the compositional dependence on its hardening and hydroxyapatite formation phenomena has not been studied. Therefore, the main objective of this work is to study the effects of P2O5, MgO in CaO-SiO2 system glass on the hardening and hydroxyapatite formation. When more than 50 mole% of CaO containing CaO-SiO2 glasses was reacted with ammonium phosphate solution, CaNH4PO4.H2O crystal was formed, but the glass with less than 50 mol% of CaO formed (NH4)2HPO4 and NH4H2PO4 crystals which are derived from ammonium phosphate solution without reacting with the glasses. As the amount of P2O5 in CaO-SiO2-P2O5 glass system was increased, the formation of CaNH4PO4.H2O crystal was enhanced. When those hardened samples were reacted with tris-buffer solution, hydroxyapatite was obtained only for the sample with CaNH4PO4.H2O. While the substitution of MgO for CaO decreased the formation of CaNH4PO4.H2O crystal. MgNH4PO4.H2O crystla was formed in high MgO containing glass, which did not react with tris-buffer solution.

• Journal of Environmental Science International
• /
• v.28 no.11
• /
• pp.971-981
• /
• 2019

This study evaluated the photocatalytic oxidation efficiency of volatile organic compounds by $Cu_2O-TiO_2$ under visible-light irradiation. $Cu_2O-TiO_2$ was synthesized by an ultrasonic-assisted method. The XRD result indicated successful p-n type photocatalysts. However, no diffraction peaks belonging to $TiO_2$ were observed for the $Cu_2O-TiO_2$. The Uv-vis spectra result revealed that the synthesized $Cu_2O-TiO_2$ can be activated under visible-light irradiation. The FE-TEM/EDS result showed the formation of synthesized nanocomposites in the commercial P25 $TiO_2$, the undoped $TiO_2$, and $Cu_2O-TiO_2$ and componential analysis in the undoped $TiO_2$ and $Cu_2O-TiO_2$. The photocatalytic oxidation efficiencies of benzene, toluene, ethylbenzene, and o-xylene with $Cu_2O-TiO_2$ were higher than those of P25 $TiO_2$ and undoped $TiO_2$. These results indicate that the prepared $Cu_2O-TiO_2$ photocatalyst can be applied effectively to control gaseous BTEX.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.5
• /
• pp.210-213
• /
• 2011

Glass-ceramics composed of $5Na_2O-36CaO-10TiO_2-xP_2O_5$ could be obtained with $P_2O_5$ content as following procedure: 1) leaching out $Ca_3(PO_4)_2$ crystals between $Ca_3(PO_4)_2$ and $NaTi_2(PO_4)_3$ selectively in 1 N HCl solution for 2 days, and 2) exchanging $Na^+$ ion to $Ag^+$ ion in Ag($NO_3$) solution for 1 day. Scanning electron microscope (SEM) and X-rat diffractometer (XRD) were measured to verify the proper synthesis of glass-ceramics. And anti-bacteria test was accomplished using Staphylococus aureus bacteria. In the results of anti-bacteria test, the bacteria were died perfectly after 3 hours.

• Journal of the Korean Ceramic Society
• /
• v.23 no.3
• /
• pp.67-77
• /
• 1986

various properties and manufacturing conditions were investigated in order to synthesize the glass-ceramics of $CaO-P_2O_5$ system for bioceramics. Compositions of easy unidirectional crystallization were between 47.5 and 50, 0mol% CaO For the glass rods prepared by pulling them to about 3 times the original rod length unidirectional crystallization was easier than original glass rods. These samples were crystallized in the axial direction at 15${\mu}{\textrm}{m}$/min in an electric furnace with a temperature gradient of about 3$0^{\circ}C$/cm at 57$0^{\circ}C$. Bending strengths of surface and unidirectionally crystallized samples were investigated with various CaO/$P_2O_5$ molar ratios. The bending strengths of unidirectionally crystallized samples were larger than those of surface -crystallized samples and the value of 47.5CaO.52.5 $P_2O_5$ was 1650kg/$cm^2$. XRD patterns showed that major phase is $\beta$-Ca(PO3) with minor phase 2CaO.$P_2O_5$ Relative crystal-linity of surface-crystallized sample was inversely propertional to the bending strenth. SEM of fracture surface of unidirectionally crystallized samples revealed an unidirectionally aligned structures.

• Polymer(Korea)
• /
• v.35 no.5
• /
• pp.375-377
• /
• 2011

$PbTiO_3$/P(VDF/TrFE) 0~3 composites thin films with 0.10 and 0.13 of ceramic volume fraction factor have been fabricated by two-step spin coating technique and analyzed. 0~3 connectivity of $PbTiO_3$/P(VDF/TrFE) composites film was observed successfully by SEM micrography. The SEM picture confirmed 0~3 connectivity. And, in all the properties, 0~3 $PbTiO_3$/P(VDF/TrFE) composites film was superior to P(VDF/TrFE) copolymer. Therefore, with a good low-dielectric constant and a high pyroelectric coefficient, the composite thin films can be used for a new pyroelectric infrared sensor of higher performance.