• Clean Technology
• /
• v.29 no.2
• /
• pp.95-101
• /
• 2023

An experiment was conducted to produce vaterite-type precipitated calcium carbonate from waste oyster shells in order to use them as recyclable resources. Calcined oyster shells containing calcium oxide as their main component were prepared at a temperature of 800℃ for 24 h. The oyster shells were dissolved in nitric acid or hydrochloric acid solution to make 0.1 M calcium nitrate or calcium chloride aqueous solution, and a carbonation reaction was performed using a 0.1 M sodium carbonate aqueous solution under various experimental conditions, which included varying the amount of aspatic acid additive, the amount of NH₄OH added, the reaction time, the reaction temperature, the stirring speed, and the type of dissolved acid. The XRD, SEM, and size distributions were analyzed and the vaterite content was calculated. Spherical precipitated calcium carbonate with a vaterite content of 95.9% was synthesized by adding 0.1 mol aspatic acid/1 mol CaO and 2 cm³ of NH₄OH, and reacting for 1 h at 25℃ while stirring at 600 rpm. The average particle diameter was found to be 12.11 ㎛. Calcium carbonate contatining high vaterite is used as high value added calcium carbonate for medical, food, inke additiver, etc.

• Korean Journal of Materials Research
• /
• v.3 no.1
• /
• pp.33-42
• /
• 1993

Abstract The increasing application of $Al_2$,$O_3$ and related ceramics as engineering materials is because of their attractive properties of fine ceramics. One solution to the wide variety of ceramic to metal combination lies in the effective joining. Active metal brazing of $Al_2$,$O_3$, to STS304 was investigated using Cu -Ti alloys. Titanium additive is chosen since it is good oxide former~. Brazing is performed under vacuum($10^{-3}$-$10^{-4}$ torr), a temperature between 1100 and 120$0^{\circ}C$ and time of 0.5-1.5hr. The microstructure of the brazed joints of $Al_2$,$O_3$ to STS304 with Cu-Ti insert metals were examined by using optical microscope and SEM and reaction products were analyzed by using EDX, WDX and XRD. Also interfacial reactions occuring during the brazing of $Al_2$,$O_3$/Cu-Ti/STS304 system are discussed. Experimental results showed formation of Titanium oxide T$i_2$$O_3$ which is attributable to the joining $Al_2$,$O_3$ to STS304 with Cu-Ti insert metal.

• Korean Journal of Food Science and Technology
• /
• v.45 no.5
• /
• pp.619-627
• /
• 2013

We investigated the characteristics and biological activity of makgeolli supplemented with different levels (0%, 1%, 3%, 5%, and 7%) of Akebia quinata fruit during fermentation. Our results showed that supplementation with Akebia quinata fruit led to an increase in the acidity level, amino acid concentration, alcohol content, and total sugar level. Makgeolli supplemented with 7% Akebia quinata fruit showed the highest total sensory score. Supplementation with Akebia quinata fruit resulted in a significant increase in the antioxidant activity and nitric oxide inhibitory activity. Further, makgeolli supplemented with Akebia quinata fruit showed anticancer activity against DU145, HeLa, MCF-7, and U87cells, and significantly enhanced antibacterial activity against Shigella flexneri. Our results indicate that Akebia quinata fruit represents an effective natural additive for enhancing the biological activities of makgeolli.

• Korean Journal of Food Science and Technology
• /
• v.45 no.5
• /
• pp.545-549
• /
• 2013

Liquid paraffin is a mixture of heavier alkanes derived from petroleum. It can be used as a lubricant in processing machinery, as a coating agent, or as a releasing agent. The purpose of this study was to analyze liquid paraffins in foods by using a gas chromatography-flame ionized detector (GC-FID). Liquid paraffin was extracted from the food samples using n-hexane. Non-polar aromatic or olefinic co-extractives were removed by alkaline permanganate oxidation followed by clean up on an aluminium oxide SPE cartridge before the GC-FID analysis. The results of recovery tests were 91.5-103.2%. Based on this optimized method, we investigated the amount of liquid paraffin in various food samples purchased from domestic markets. The levels of liquid paraffin in bread were $95.5{\pm}156.0$ mg/kg (0.008%), those in capsules were $40.2{\pm}54.5$ mg/kg (0.001%), and those in dried fruits and vegetables were $3.0{\pm}18.1$ mg/kg (0.0001%). No liquid paraffin was detected in fresh fruits and vegetables. We propose that our method can be used to monitor and detect liquid paraffin in foods for food safety management.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.9
• /
• pp.473-479
• /
• 2017

Due to environmental pollution, hazards of the human body, and global warning, changes in the power train of automobiles are intensifying, and the market forelectronic vehicles is rising. Also, in order to meet the stricter emission regulations forautomobiles with internal combustion engines based on fossil fuel, the proportion of after-treatments for vehicles and vessels is increasing gradually. The objective of this study is to investigate the effectsfrom additive ceric oxide ($CeO_2$) loading amounts to improve the methane ($CH_4$) and nitric oxide (NOx) abatement ability of the natural gas oxidation catalysts(NGOC) reducing toxic gases emitted from compressed natural gas (CNG) buses. Three kinds of NGOC were prepared under the following conditions: fresh and $700^{\circ}C$ for 12hr thermal aging, and the reduction performance of toxic gases was evaluated. Fresh $1Pt-3Pd-1Rh-3MgO-6CeO_2/(Al+Z)$ NGOC containing 6wt% $CeO_2$ had the highest dispersivity of palladium (Pd) with high selectivity to $CH_4$ and improved harmful gas reduction performance. The NGOC with 6wt% $CeO_2$ loaded the least decreased in the dispersivity of the noble metal, and showed the highest reduction of harmful gases due to the thermal durability of $CeO_2$.

• Journal of Powder Materials
• /
• v.16 no.6
• /
• pp.442-448
• /
• 2009

$ZrB_2$-based composites are candidate materials for ultra-high temperature materials (UHTMs). $ZrB_2$ has become an indispensable ingredient in UHTMs, due to its high melting temperature, relatively low density, and excellent resistance to thermal shock or oxidation. $ZrB_2$ powders are usually synthesized by solid state reactions such as carbothermal, borothermal, or combined carbothermal reaction. SiC is added to this system in order to enhance the oxidation resistance of $ZrB_2$. In this study, $ZrB_2$?based composites were successfully synthesized and densified through two different processing paths. $ZrB_2$ or $ZrB_2$ 25 vol.%SiC was fully synthesized from oxide starting materials with reducing agents after heat treatment at 1400$^{\circ}C$. Besides, $ZrB_2$?20 vol.%SiC was fully densified with $B_4C$ as a sintering additive after hot pressing at 1900$^{\circ}C$. The synthesis mechanism and the effect of sintering additives on densification of $ZrB_2$ ?SiC composites were also discussed.

• Applied Chemistry for Engineering
• /
• v.2 no.1
• /
• pp.30-37
• /
• 1991

The production of hydrogen from steam by reduced iron with additives such as CuO, $In_2O_3$, $MoO_3$ and $WO_3$ has been kinetically investigated. It was shown that all additives have a promoting effect on reaction activity in the order of $$MoO_3{\gg}In_2O_3{\sim_=}WO_3{\sim_=}CuO$$. The shrinking core model was applied to predict the complete conversion time and the results were quite comparable with experimental values. The reaction was carried out in a fixed flow reactor packed with reduced iron with 1 wt % of additives under the conditions, $600-750^{\circ}C$, Ar flow rate of 1 L/min and steam partial pressure of 0.085 atm. The apparent activation energies were 14.2, 20.9, 21.3, 22.4 and 27.9 kJ/mol with $MoO_3$, $In_2O_3$, $WO_3$, CuO and without additive, respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.4
• /
• pp.364-370
• /
• 1998

Boron-phoshor-silicate glass was fabricated on Si substrates by FHD(Flame Hydrolysis Deposition) The microstructrue of silica soot deposited at various conditon such as composition and substrate temperature was analysed by SEM. After consolidation the refractive index and composition of the silica layer were in-vestigated. For refractive index control B, P and Ge were used as additive elements while B and Ge oxides are easily mixed into $SiO_2$, P oxide($B_2O_3$) doping is difficult because of the volatile property due to low melt-ing point. Boron-phosphorous-silicate glass (BPSG) layer were fabricated using bertical torch and optimized flame temperature substrate temperature and distance of torch and substrate. P concentration of BPSG lay-er measured 3.3 Wt% and the consolidation temperature was lower than $1180^{\circ}C$. The measured refractive index of BPSG silica layer in $1.55\;\mu\textrm{m}$ wavelength was $1.4480{\pm}1{\times}10^{-1}$ and the thickness was $22{\pm}1\;\mu\textrm{m}$.

• Journal of the Korean Vacuum Society
• /
• v.20 no.5
• /
• pp.374-380
• /
• 2011

Carbon coils could be synthesized on nickel catalyst layer-deposited silicon oxide substrate using $C_2H_2$ and $H_2$ as source gases and $SF_6$ as an additive gas under thermal chemical vapor deposition system. The characteristics (formation density and morphology) of as-grown carbon coils according to the injection stage of $SF_6$ gas incorporation were investigated. A continuous injecting of $SF_6$ gas flow could give rise to many types of carbon coils-related geometries, namely linear tub, micro-sized coil, nano-sized coil, and wave-like nano-sized coil. However, the limitation of the geometry as the nano-sized geometries of carbon coils could be achieved by the incorporation of $SF_6$ in a short time (1 min) during the initial deposition stage. A delayed injection of a short time $SF_6$ gas flow can deteriorate the limitation of the geometries. It confirms that the injection time and its starting point of $SF_6$ gas flow would be very important to determine the geometries of carbon coils.

• The Korean Journal of Malacology
• /
• v.32 no.2
• /
• pp.119-125
• /
• 2016

The present study aimed to understand the effects of a ${\beta}$-glucan-added abalone feed (Immuneglu$^{TM}$) on the immune parameters, survival rate, and anti-bacterial activity of the abalone Nordotis discus hannai. During the study, spat and adult abalones were fed 0, 0.1, and 1% of Immuneglu$^{TM}$ mixed with artificial feed for 2 weeks, and their immune parameters, survival rate, and anti-bacterial activity were measured. The results showed that abalones fed on Immuneglu$^{TM}$-added feed showed a higher phagocytic rate, survival rate, and anti-bacterial activity against Vibrio alginolyticus, than those with the control treatment. In addition, the nitric oxide concentration, which indicates an inflammatory response, increased in the treatment group. Our study suggests that Immuneglu$^{TM}$ might be a useful additive for increasing the immunity and survival rates of abalones during mass culture.