• Journal of Welding and Joining
• /
• 제12권4호
• /
• pp.102-109
• /
• 1994

The thick and hard alloyed layer was formed on the surface of Aluminum Cast Alloy(AC2B) by PTA overlaying process with Cr, Cu and Ni metal powders under the condition of overlaying current 150A, overlaying speed 150mm/min and different powder feeding rate 5-20g/min. The characteristics of hardening and were resistance of alloyed layer have been investigated in relation to microstructure of alloyed layer. As a result, it was made clear that Cu powder was the most superier one in three metal powders used due to an uniform hardness distribution of Hv 250-350, good wear resistance and freedom from cracking in alloyed layer of which microstructure consisted of hypereutectic. On the contrary, irregular hardness distribution was usually obtained in Cr or Ni alloyed layers of which hardness was increased as Cr or Ni contents and reached to maximum hardness of about Hv 400-850 at about 60wt% Cr or 40wt% Ni in alloyed layer. However the cracking occurred in these alloyed layers with higher hardness than Hv 250-300 at more than 20-25wt% of Cr or Ni contents in alloyed layer. Wear rate of alloyed layer was decreased to 1/10 in Cu alloyed layer and 1/5 or 1/3 in Cr or Ni alloyed layer with same hardness of about Hv 300 in comparison with that of base metal at higher sliding speed.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2010년도 춘계학술발표대회 초록집
• /
• pp.72-72
• /
• 2010

최근 오일샌드, 극지유전, 심해저자원 등 극한지 자원개발이 활발해짐에 따라 수요가 증대되고 있는 극한지용 내마식 소재는 내마식성과 함께 저온 인성이 요구된다. 철계 합금에서 관찰되는 변형유기 마르텐사이트 상변태는 입자의 충돌에 의한 충격을 흡수하고 소재의 표면을 가공경화시켜 내마식성 향상 및 저온 인성에 기여할 수 있을 것으로 기대되고 있지만 합금조성의 정교한 제어가 필요하기 때문에 오버레이 용접에 적용하기 위해서는 모재와의 희석률을 제어하는 방안이 필요하다. 용접플럭스 설계기술은 용접시 금속이행모드, 용융지 유동거동 등과 같은 용접현상 제어를 통해 오버레이 용접재료의 용접성과 용접부 희석률을 최적화할 수 있는 기술이다. 본 연구에서는 내마식 고인성 오버레이 용접재료의 개발을 위해 Fe-12Cr-1.2C 합금조성을 갖는 메탈코어드 와이어에 대하여 아크안정제로 사용되는 Ca 함유 용접플럭스 첨가가 용착부 형상 및 희석률 변화에 미치는 영향을 조사하였다.

• 한국결정성장학회지
• /
• 제22권5호
• /
• pp.227-232
• /
• 2012

차세대 원자력발전용 고온 열교환기 소재로 이용될 가능성이 높은 Ni-Cr계 고온합금인 Inconel 617과 Hastelloy X의 표면처리에 따른 FLiNaK(LiF-NaF-KF) 용융염 하에서의 고온물성에 대한 연구를 수행하였다. Inconel 617과 Hastelloy X기판 상에 각각 PVD인 arc discharge 및 sputtering법에 의해 TiAlN 및 $Al_2O_3$ 박막을 코팅 하였다. 이러한 표면처리가 이들 합금의 FLiNaK 용융염 하 고온 안정성에 미치는 영향에 대해 연구하였다. 용융염 하 Ni-Cr계 고온합금의 부식 원리를 이해하기 위해, 용융염 수송 loop에 사용 중 파단된 Inconel 파이프에 대한 미세구조 분석을 수행하였다. 표면처리 된 합금들을 $600^{\circ}C$ 용융염 내에서 열처리 하였으며, 열처리 전후 시편들에 대해 상형성, 미세구조 등 고온 물성 변화를 측정하였다. 연구결과 코팅되지 않은 경우 보다 TiAlN 및 $Al_2O_3$ 박막이 코팅된 소재에서 보다 우수한 고온 안정성을 보여주었다.

• Journal of Welding and Joining
• /
• 제6권2호
• /
• pp.40-46
• /
• 1988

The effect of heat input on the content of residual .delta.-ferrite and the hot cracking susceptibility in the austenitic stainless steel overlaid on the carbon steel was studied in the range of heat input from 7.5 to 15.1 KJ/cm. Present study shows that residual .delta.-ferrite content in the overlay is mainly determined by the dilution of the base metal (carbon steel) which is in turn affected by heat input, i.e. the amount of dilution decreases as heat input increase. Accordingly, higher heat input results in a substantial increase in Cr equivalent but a little increase in Ni equivalent due to the less dilution of carbon from base metal. This fact can explain the result obtained in this study, i, e, the higher content of .delta.-ferrite in the weld deposit made with higher heat input. This in turn causes more resistant overlaying weld metal to hot cracking.

• 한국정보통신학회논문지
• /
• 제18권12호
• /
• pp.3029-3034
• /
• 2014

이 논문은 사람 눈의 공막컬러코드와 공막혈관징후패턴코드 생성에 의한 공막진단시스템 구현에 관한 연구이다. 시스템은 고성능 DSP 영상처리 프로세서를 기반으로 PGC 프로그램어불 게인제어 선처리 및 RISC SD프레임저장 메모리 등으로 구성된다. PGC는 RGB신호를 최적화하고 그래리 영상에서 에지가 검출된다. 판별 및 매칭 처리알고리듬은 공막컬러코드화 및 혈관징후패턴코드 생성을 실행된다. 공막컬러코드는 메모리 맵의 위치에서 YCbCr값을 구하고 허용오차 범위를 적용하여 생성된다. 혈관징후패턴코드는 24시간등분과 13환형등분 구역에 의해 디지털화 되고 중첩매칭과 허용오차 적용에 의해 코드화된다. 실험결과 성능에서 시스템은 40ms로 동작하고 진단오차는 컬러판별이 평균 약20%, 혈관징후패턴 매칭이 약 24%이다. 이 시스템 및 기술은 세분화와 환자데이터베이스화 하면 공막진단 의용시스템으로 사용 할 수 있다.

• KSII Transactions on Internet and Information Systems (TIIS)
• /
• 제14권3호
• /
• pp.1313-1336
• /
• 2020

Cognitive radio (CR) is regarded as an effective approach to avoid the inefficient use of spectrum. However, CRNs have more special security problems compared with the traditional wireless communication systems due to its open and dynamic characteristics. Primary user emulation attack (PUEA) is a common method which can hinder secondary users (SUs) from accessing the spectrum by transmitting signals who has the similar characteristics of the primary users' (PUs) signals, and then the SUs' quality of service (QoS) cannot be guaranteed. To handle this issue, we first design a multiple-phase energy detection scheme based on the cooperation of multiple SUs to detect the PUEA more precisely. Second, a joint SUs scheduling and power allocation scheme is proposed to maximize the weighted effective capacity of multiple SUs with a constraint of the average interference to the PU. The simulation results show that the proposed method can effectively improve the effective capacity of the secondary users compared with the traditional overlay scheme which cannot be aware of the existence of PUEA. Also the good delay QoS guarantee for the secondary users is provided.