• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.450-459
• /
• 2009

The aim of this study was to measure the initial dynamic modulus changes of light cured composites using a custom made rheometer. The custom made rheometer consisted of 3 parts: (1) a measurement unit of parallel plates made of glass rods, (2) an oscillating shear strain generator with a DC motor and a crank mechanism, (3) a stress measurement device using an electromagnetic torque sensor. This instrument could measure a maximum torque of 2Ncm, and the switch of the light-curing unit was synchronized with the rheometer. Six commercial composite resins [Z-100 (Z1), Z-250 (Z2), Z-350 (Z3), DenFil (DF), Tetric Ceram (TC), and Clearfil AP-X (CF)] were investigated. A dynamic oscillating shear test was undertaken with the rheometer. A certain volume ($14.2\;mm^3$) of composite was loaded between the parallel plates, which were made of glass rods (3 mm in diameter). An oscillating shear strain with a frequency of 6 Hz and amplitude of 0.00579 rad was applied to the specimen and the resultant stress was measured. Data acquisition started simultaneously with light curing, and the changes in visco-elasticity of composites were recorded for 10 seconds. The measurements were repeated 5 times for each composite at $25{\pm}0.5^{\circ}C$. Complex shear modulus G*, storage shear modulus G', loss shear modulus G" were calculated from the measured strain-stress curves. Time to reach the complex modulus G* of 10 MPa was determined. The G* and time to reach the G* of 10 MPa of composites were analyzed with One-way ANOVA and Tukey's test ($\alpha$ = 0.05). The results were as follows. 1. The custom made rheometer in this study reliably measured the initial visco-elastic modulus changes of composites during 10 seconds of light curing. 2. In all composites, the development of complex shear modulus G* had a latent period for $1{\sim}2$ seconds immediately after the start of light curing, and then increased rapidly during 10 seconds. 3. In all composites, the storage shear modulus G" increased steeper than the loss shear modulus G" during 10 seconds of light curing. 4. The complex shear modulus of Z1 was the highest, followed by CF, Z2, Z3, TC and DF the lowest. 5. Z1 was the fastest and DF was the slowest in the time to reach the complex shear modulus of 10 MPa.

• Elastomers and Composites
• /
• v.31 no.1
• /
• pp.33-42
• /
• 1996

NR, NBR, and CR rubber were prepared by mixing filler in various ratios. Their vulcanization characteristics and thermal properties were studied. Vulcanization characteristics were investigated using cure curve that had been obtained from oscillating disk rheometer study. The Arrhenius law is known to describe the relationship between cure time and temperature of most elastomers. Curing could be done by the addition of sulfur, peroxides, and proper acceleratores. The optimum cure time that affects desirable values of modulus and tensile strength of the vulcanizate is taken as t90 as measured by a rheometer. Rubbers were cured in the rheometer at temperatures ranging from $130^{\circ}C\;to\;180^{\circ}C$ in order to check the validity of the curing system used. A linear relationship between ln(ts2) and ln(t90) was found for all elastomers. The term sensitivity has been used to describe the relationship between a change of ts2 to the corresponding change of t90 due to an increment of temperature. This is related to the formula of the compound.

• Elastomers and Composites
• /
• v.36 no.1
• /
• pp.14-21
• /
• 2001

To increase the properties of EVA foam such as tensile strength, rebound resilience, and compression set, ethylene-1-butene copolymer (EtBC) was blended with EVA. After that crosslink characteristics of the blends and cell structures and mechanical properties of the foam were studied. As the amount of EtBC increased in EVA/EtBC blends, torque values of oscillating disc rheometer(ODR) increased and the foaming ratio decreased because the viscosity and crosslink density of EVA/EtBC blends increased. Foaming ratio and cell size of the foam increased by increasing the amount of foaming agent. When compared the mechanical properties of the foam which have same densities, tensile strength, rebound resilience, and compression set properties of the foam were improved by increasing the amount of EtBC in the EVA/EtBC blends.

• Elastomers and Composites
• /
• v.48 no.1
• /
• pp.18-23
• /
• 2013

Nylon 12 elastomer was slightly crosslinked in molten state by the addition of small amount of dicumyl peroxide (DCP) as a crosslink agent and triallycyanuate (TAC) as a co-agent during melt compounding at $160^{\circ}C$ in an internal mixer. The effect of the peroxide crosslinking on mechanical, dynamic mechanical and rheological properties of the nylon 12 elastomer was investigated by means of tensile testing, dynamic mechanical analysis (DMA) and small amplitude oscillating rheometer, respectively. With modification, there is an improvement in tensile modulus and Young's modulus with decease in elongation at break. DMA results for peroxide modified nylon 12 elastomers demonstrated that the glass transiaiton temperature of PTMG segment shifted to higher temperature and the storage modulus remained constant above the melting temperature of nylon 12 segments. Melt rheological studies revealed that the peroxide modified nylon 12 elastomer exhibited a more solid like behavior and stronger shear thinning behavior compared to neat nylon 12 elastomer, which was more prominent at higher TAC content in the polymer matrix. The peroxide modified nylon 12 elastomer exhibited good elastic recoverability and improved mechanical properties without sacrificing melt processibilty, and especially the service temperature range increased as compared to neat nylon 12 elastomer.

• Elastomers and Composites
• /
• v.29 no.3
• /
• pp.213-225
• /
• 1994

The Purpose of this dissertation is to study the preparation technique and physical properties of expanded rubber. The respective samples of NR, NBR and the standard compounds of EPDM rubber were prepared by mixing plasticizer DOP and LCR in various ratio. And their vulcanization characteristics, physical properties and foaming states were studied. Vulcanization characteristics were investigated using cure curve that had been obtained from Oscillating Disk Rheometer study, and the microscopic photographs of foaming states were obtained using electron microscope. The vulcanization characteristics of the samples, DOP 30phr and LCR 30phr, were found to be suitable. The tests, like hardness test and resilience, tensile test on the physical properties of each sample showed that plasticizing efficiencies of DOP and LCR were almost the same. Oil resistance test exhibited DOP was better than LCR and compression set test showed LCR was excellent plasticizer. The foaming states of NR, EPDM compounds were uniform, but those of NBR compounds were not uniform. Consequently vulcanization characteristics, physical properties and foaming states of all the samples satisfied the SAE requirements.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.3
• /
• pp.269-274
• /
• 2002

statement of problem The viscoelastic property is the most important and peculiar characteristics of soft liners. But the authorized standard is not certainly established than other dental materials. purpose of study This study is aimed to compare the initial flow of gelation of the modified soft liner with 4-META with that of PMMA soft liners using dynamic method and evaluate the clinical acceptance of the trial materials. materials and method This study consists of 3 groups with the given % of 4-META powder in the Coe soft liquid; 0%, 5%, 10% Each group was tested for 10 times to record the change of G′values during 3 hours. the gelation time was recorded by the oscillating rheometer with parallel plate with 1 rad/sec. results As the results of this study, the gelation time of modified soft liner was elongated by 5 to 6 minutes. conclusion The mean gelation time of modified soft liner could be within the range of clinically acceptable.

• Elastomers and Composites
• /
• v.29 no.2
• /
• pp.113-120
• /
• 1994

The vulcanization characteristics, physical and electrical properties have been measured for magnetite-loaded CM compounds containing various concentration of magnetite. Samples of the various concentration of magnetite are characterized by oscillating disk rheometer, mooney viscometer, tensometer and resistance meter. The morphology and dispersion of magnetite are analyzed by scanning electron microscope(SEM). The results obtained are as follows : 1. The CM compound without magnetite shows plain curve, while the CM compounds containing magnetite show short curves. 2. The maximum volume of magnetite is 600 phr in the CM compounds. The magnetite of 30 to 150 phr of magnetite act as reinforcement agents and the 50 phr magnetite shows maximum tensile strength. 3. The electric conductivity is mostly influenced by the conditions of temperature, compacting pressure, and magnetite orientation. Further efforts should be made to develop a new design in various electric conductivity fillers for the most efficient and applicable rubber products.

• Elastomers and Composites
• /
• v.23 no.3
• /
• pp.223-229
• /
• 1988

The effect of triazine thiol derivative on the physical properties of silica-polychloroprene(CR) composites and glass fiber(MGF)-CR composites was investigated. Optimum cure time of the MGF composites filled with 2-dibuthylamino-4, 6-dithiol-s-triazine(DBT) was the fastest one, while maximum torque was the best in case of the silica composites filled with s-triazine-2,4,6-trithiol(TAT) on the Oscillating Disk Rheometer(ODR) test. Stress-strain curves of the composites showed that the physical properties such as 100% modulus, 300% modulus, tensile strength of the silica composites filled with DBT was very satisfactory and the silica composites filled with TAT was higher density of crosslinking than other crosslinked elastomer. In aging properties, elastomer filled DBT and TAT were progress post-curing reaction with increasing of aging time and it have been improved the tensile strength and crosslinking density.

• Elastomers and Composites
• /
• v.21 no.1
• /
• pp.13-19
• /
• 1986

The effects of several vulcanizing accelerators on the determination of kinetic parameters of natural rubber vulcanizate was studied by DSC. Kinetic parameters were determined by means of the calculation procedures of Borchardt-Daniels and Oscillating Disk Rheometer (ODR) cure curve analysis, using both DSC exothermal thermogram and ODR cure curve. In order to examine the credibility in the DSC method the same compound which was und for DSC method was used for the comparison with the results of ODR data. Upon this method, kinetic rate constant (k), and Arrehenius parameter (Ea, ko, n) have been determined for rubber compounds via a new method using DSC thermogram and ODR cure curve. In the comparison of DSC and ODR results, kinetic parameters has shown good agreements between two results. Consequently, from the present studies, it is shown that the DSC thermoanalytical method can provide an alternate new method of kinetic study of rubber vulcanization.

• Elastomers and Composites
• /
• v.46 no.1
• /
• pp.45-53
• /
• 2011

The effect of the silane coupling agent, bis(triethoxysilypropyl)tetrasulfide (TESPT), on mechanical properties of a silica-filled NBR compound for oilseal was investigated. Curing behavior and crosslinking density of the compounds were measured using ODR (oscillating disk rheometer) and swelling ratio in toluene. UTM (universal testing machine) and shore A hardness tester were used in order to study the characteristics of mechanical properties of original vulcanizates and aged ones with heated air and ASTM No. 3. oil. Recovery of elasticity which influences the performance and service life of oilseal was investigated by giving bending deformation to vulcanizates in aging condition. After bending aging test, recovery distance was measured and calculated angle of recovery from it. TR (temperature retraction) test was performed on these vulcanizates to determine the low temperature recovery behavior. Wear resistance was measured by Taber type abrasion tester. In addition, SEM was used to characterize the morphology of the worn surface of vulcanizates. The result showed that addition of TESPT into silica-filled compound improves not only compound flow-ability, interaction between NBR and silica and crosslinking density, but also hardness, 100% modulus, recovery of elasticity, wear resistance, heat resistance and ASTM No.3 oil resistance of vulcanizates.