• 대한치과교정학회지
• /
• 제20권3호
• /
• pp.583-591
• /
• 1990

If the bond strength is sufficient to resist orthodontic force, orthodontic brackets can be bonded to restorations. Orthodontic brackets were bonded to composite resin and glass ionomer cement restorations with no-mix adhesive or glass ionomer cement. The shear bond strength of adhesives bonded to restorations was studied in vitro. Orthodontic brackets were bonded to 10 extracted natural teeth, 40 composite resin restorations and 40 glass ionomer restorations. The surfaces of composite resin restorations were roughened or applied with bonding agent (Scothbond) after surface roughening. The surfaces of glass ionomer cement restorations were conditioned with acid etching or applied with Scotchbond to etched surface. The adhesive was no-mix resin or glass ionomer cement. The shear bond strength was measured. The results were as follows: 1. Orthodontic brackets could be bonded to composite resin restorations effectively as they could be bonded to acid etched enamel with no-mix adhesive. The shear bond strength was sufficient to resist orthodontic force and was not affected by bonding agent greatly. 2. The shear bond strength of no-mix adhesive bonded to acid etched glass ionomer cement restorations was sufficient to resist orthodontic force. However. the fracture risk of glass ionomer cement restorations was increased during debonding. The bonding agent couldn't increase the shear bond strength greatly. 3. The shear bond strength of glass ionomer cement bonded to glass ionomer cement restorations was lower than that of no-mix adhesive. The shear bond strength was sufficient to resist orthodontic force and was greatly decreased by bonding agent. 4. The shear bond strength of glass ionomer cement bonded to composite resin restorations was too low to resist orthodontic force.

• 대한소아치과학회지
• /
• 제46권2호
• /
• pp.127-134
• /
• 2019

이 연구의 목적은 지르코니아 기성관에 대한 교정용 밴드의 접착제로서 컴포머 시멘트와 레진 시멘트를 평가하고자 하였다. 총 30개의 시편을 준비하였다. 상악 우측 제 2유구치의 스테인리스 스틸 기성관에 컴포머 시멘트로 교정용 밴드를 접착한 I군과 지르코니아 기성관에 컴포머 시멘트로 밴드를 접착한 II군, 지르코니아 기성관에 레진 시멘트로 밴드를 접착한 III군으로 나누었고 밴드의 결합력을 측정하기 위해 인장력을 가하였다. I군, II군과 III군의 결합력의 평균값은 각각 0.79 MPa, 1.09 MPa 그리고 1.56 MPa였다. II군이 I군보다 유의하게 높은 결합력을 보였고, II군과 III군 의 결합력에는 유의한 차이가 없었다. 컴포머 시멘트와 기능성 단량체를 포함한 레진 시멘트는 유구치 지르코니아 기성관에 대한 교정용 밴드의 시멘트로서 양호한 결합력을 보였다.

• 대한치과교정학회지
• /
• 제27권5호
• /
• pp.839-852
• /
• 1997

Crystal growth 용액인 황화이온을 함유한 폴리아크릴산 용액에 의한 법랑질 표면처리는 법랑질 표면에 crystal growth를 유도함으로써 통상적인 산부식법을 대체하여 교정용 브라켓을 접착하기 위한 법랑질 전처치의 방법으로 사용될 수 있음이 제안된 바 있다. 이 연구는 crystal growth후 교정용 브라켓 접착제로 브라켓을 접착하는 방법의 임상적용 가능성을 구명하기 위하여 시행되었다. 발거된 사람소구치의 법랑질 표면을 $25\%$ 폴리아크릴산과 0.3M 황산을 함유한 기본 crystal growth 용액, 각각 0.3M lithium sulfate, 0.3M magnesium sulfate, 0.3M potassium sulfate를 첨가한 crystal growth 용액, $37\%$ 인산용액, 퍼미스로 각각 처리한 후, 교정용 광중합형 글래스아이오노머 시멘트와 교정용 레진접착제로 금속브라켓을 접착하였다. $37^{\circ}C$의 증류수에 24시간 침지시킨 후, 브라켓 전단결합강도를 측정하고 접착 파절양태를 관찰하였으며 표면처리된 법랑질 표면과 브라켓 제거후의 법랑질 표면을 주사전자현미경으로 관찰하여 다음과 같은 결과를 얻었다. Crystal growth후 광중합형 글래스아이오노머 시멘트로 브라켓 접착시 0.3M magnesium sulfate를 함유한 군의 브라켓 전단결합강도가 가장 높았다(p<0.01). Crystal growth후 광중합형 글래스아이오노머 시멘트로 접착한 군의 브라켓 전단결합강도는 crystal growth 후 레진접착제로 접착한 군보다 높았다(p<0.001). Magnesium sulfate, 또는 potassium sulfate를 함유한 crystal growth 용액으로 법랑질 표면을 처리한 후 글래스아이오노머시멘트로 접착한 군의 브라켓 전단결합강도는 산부식 후 레진 접착제로 접착한 군과 유의한 차이를 보이지 않았다. 브라켓 제거시 잔류접착제의 양은 글래스아이오노머 시멘트로 접착한 것이 가장 적었다. 이상의 결과는 magnesium sulfate나 potassium sulfate를 함유한 crystal growth 용액으로 법랑질 표면처리 후 교정용 광중합형 글래스 아이오노머 시멘트로 브라켓을 접착하는 방법이 통상적으로 사용되는 산부식 후 교정용 레진접착제에 의한 브라켓 접착법을 대체할 수 있음을 시사한다.

• 구강회복응용과학지
• /
• 제37권4호
• /
• pp.209-216
• /
• 2021

목적: 본 연구의 목적은 접착제를 적용하지 않고 치열교정용 브라켓을 접착할 수 있는 레진시멘트의 법랑질에 대한 접착강도를 접착제를 적용한 경우와 비교하기 위함이다. 연구 재료 및 방법: 시편을 Transbond XT, GC Ortho Connect 및 Orthomite LC의 3개의 실험군으로 나누고, 노출된 법랑질 표면을 2분획으로 나누어 한 분획에는 37% 인산으로, 다른 한 분획에는 37% 인산 및 접착제 혹은 유니버셜 접착제로 표면 처리를 하였다. 치열교정용 브라켓에 3 종류의 시멘트를 각각 도포하고 접착을 한 뒤 전단접착강도를 측정하였다. 결과: Transbond XT와 Orthomite LC는 각각 접착제와 유니버셜 접착제를 적용한 후 치열교정용 브라켓을 접착할 경우 전단접착강도가 유의하게 증가하였다. 결론: Transbond XT와 Orthomite LC에서 산 부식 후 접착제의 적용이 치열교정용 브라켓의 전단접착강도를 향상시킬 것으로 기대한다.

• 대한치과교정학회지
• /
• 제45권6호
• /
• pp.299-307
• /
• 2015

Objective: The aims of this study were to compare the shear bond strength between orthodontic metal brackets and glazed zirconia using different types of primer before applying resin cement and to determine which primer was more effective. Methods: Zirconia blocks were milled and embedded in acrylic resin and randomly assigned to one of four groups: nonglazed zirconia with sandblasting and zirconia primer (NZ); glazed zirconia with sandblasting, etching, and zirconia primer (GZ); glazed zirconia with sandblasting, etching, and porcelain primer (GP); and glazed zirconia with sandblasting, etching, zirconia primer, and porcelain primer (GZP). A stainless steel metal bracket was bonded to each target surface with resin cement, and all specimens underwent thermal cycling. The shear bond strength of the specimens was measured by a universal testing machine. A scanning electron microscope, three-dimensional optical surface-profiler, and stereoscopic microscope were used to image the zirconia surfaces. The data were analyzed with one-way analyses of variance and the Fisher exact test. Results: Group GZ showed significantly lower shear bond strength than did the other groups. No statistically significant differences were found among groups NZ, GP, and GZP. All specimens in group GZ showed adhesive failure between the zirconia and resin cement. In groups NZ and GP, bonding failed at the interface between the resin cement and bracket base or showed complex adhesive and cohesive failure. Conclusions: Porcelain primer is the more appropriate choice for bonding a metal bracket to the surface of a full-contour glazed zirconia crown with resin cement.

• 대한치과교정학회지
• /
• 제34권4호
• /
• pp.351-362
• /
• 2004

고정식 교정 치료시 교정용 밴드가 장착된 치아의 치주조직 손상은 접착된 치아에서 보다 자주 발생한다. 일반 치과치료에 사용되는 시멘트는 세포독성을 지닌 것으로 알려져 있으므로 치주조직과 직접 접촉하거나 구강 내에서 밴드시멘트의 성분들이 용출되는 교정용 밴드 시멘트는 치주조직의 손상을 일으키는 원인이 될 수 있다 그러므로 교정용 밴드 시멘트의 생체 친화성은 재료의 물성과 함께 중요하게 고려되어야 할 사항이다. 이 연구의 목적은 교정용 밴드 시멘트의 세포독성을 평가하는 것으로 현재 임상에서 널리 사용되고 있는zinc phosphate cement (ZPC), glass ionomer (GI), resin modified glass ionomer (RMGI), compomer의 생체 친화성을 평가하기 위해 human gingiva fibroblast를 배양하고 이 세포에 대한 세포수 산정 및 세포 형태관찰, MTT(3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay, 한천중층시험 등의 세포독성 검사를 시행하여 다음과 같은 결과를 얻었다. 1. 세포수 산정 및 형태 관찰 시험에서 Gl>ZPC, RMGI, RMG124, GI24>compomer24, ZPC24, compomer 순으로 세포독성이 높게 나타났다. 2. MTT assay 에서는 GI>ZPC, RMGI>GI24>ZPC24, compomer, RMGI24, compomer24 순으로 세포독성이 높게 나타났다. 3. 한천중층시험에서 는 GI>GI24, ZPC, ZPC24, RMGI>RMG124, compomer, compomer24 순으로 세포독성 이 높게 나타났다.

• 대한치과교정학회지
• /
• 제35권6호
• /
• pp.433-442
• /
• 2005

본 연구의 목적은 브라켓 접착 시 산부식과 전처리 과정을 결합하여 접착 단계를 단순화시킨 self-etching primer (SEP)를 차용하는 경우 접착제 종류와 타액의 존재 유무에 따른 전단결합강도의 차이에 관하여 비교 연구 하는 것이다. 소의 하악 영구 전치를 포매하여 만든 시편을 접착제의 종류에 따라 레진 접착제와 레진 강화형 글래스 아이오노머 접착제를 이용한 군으로 나누었고 각각 37% 인산으로 산부식 후 기존의 본딩용 프라이머를 사용하여 접착한 군과, SEP를 사용하여 접착한 군으로 분류하고, 타액 오염 유무에 따라 다시 각 군을 분류하여 전단결합 강도를 측정하였다. 그 결과 레진 접착제로 브라켓을 부착한 경우 SEP를 사용하여 접착한 군의 전단결합강도는 인산 처리군에 비해 낮은데 비해 레진 강화형 글래스 아이오노머를 사용한 경우, 전처리법에 따른 전단결합강도는 통계적으로 유의한 차가 없었으며, 접착제의 종류에 관계없이 타액 오염이 존재 시에는 SEP를 사용한 군이 인산처리군에 비해 높은 전단결합강도를 보였다. 이상의 결과에서 SEP를 사용 시 레진 접착제와 레진 강화형 글래스 아이오노머 접착제 모두 임상적으로 사용 가능한 전단결합강도를 보였으며, 특히 타액에 오염된 치면에서도 SEP를 사용하여 브라켓을 접착하는 것은 적절한 결합강도를 얻을 수 있으므로 임상적으로 유용할 것으로 생각된다.

• 대한치과교정학회지
• /
• 제43권1호
• /
• pp.29-34
• /
• 2013

Objective: To examine the prophylactic potential of 3 orthodontic bonding adhesives: Fuji Ortho SC, Illuminate, and Resilience. Methods: Thirty-six Wistar Wag rats were randomly divided into 4 groups consisting of 9 rats each. One of the groups received no treatment and was used as a control. In the other groups, individual bands coated with one of the 3 adhesives were cemented to the lower incisors. Enamel samples were obtained after 6 and 12 weeks and analyzed using scanning electron microscopy in combination with energy dispersive spectrometry. Results: Six weeks after band cementation, no fluoride was found in the enamel of the lower incisors. After 12 weeks, there was no fluoride in the enamel of teeth coated with the Resilience composite. However, in the case of the Illuminate composite and the resin-modified glass ionomer Fuji Ortho SC cement, the depth of fluoride penetration reached $2{\mu}m$ and $4.8-5.7{\mu}m$, respectively. Conclusions: Fluoride ions from orthodontic adhesives can be incorporated into the surface layer of the enamel. Orthodontists may apply orthodontic adhesives, such as the Fuji Ortho SC, to reduce the occurrence of caries during orthodontic treatment with fixed appliances.

• 대한치과교정학회지
• /
• 제25권5호
• /
• pp.605-611
• /
• 1995

이 연구는 시간 경과에 따라 폴리아크릴산 용액으로 표면 조건화된 법랑질에 대한 광중합형 글래스아이오노머 시멘트의 브라켓 전단결합강도를 인산용액으로 부식된 법랑질에 대한 치과 교정용 레진 접착제의 그것과 비교하여 브라켓을 접착할 때 상용되어 온 치과교정용 레진 접착제를 광중합형 글래스아이오노며 시멘트로 대체할 수 있는지의 여부를 구명하기 위하여 시행되었다. 발거된 사람 소구치의 법랑질 표면을 각각 10% 폴리 아크릴산용액과 38% 인산용액으로 처리한 후, 각각 시판되고 있는 광중합형 글래스아이오노머 시멘트의 일종(Fuji II LC)과 화학중합형 치과교정용레진접착제의 일종(Mono-Lok 2)으로 법랑질 표면에 금속브라켓을 접착하고, 시편을 실온에서 5분, 15분 방치한 후, $37^{\circ}C$의 증류수 속에 1일, 35일 동안 침지시킨 후, 브라켓 전단결합강도를 측정하고, 접착파절 패턴을 관찰하였다. 브라켓 접착5분과 15분 후의 광중합형 글래스아이오노머 시멘트의 브라켓 전단결합강도는 치과교정용 레진 접착제의 그것보다 유의성 있게 높았다. 광중합형 글래스아이오노머 시멘트와 치과 교정용 레진 접착제의 브라켓 전단결합강도는 브라켓 접착 1일 까지 증가하였으나 1일군과 35일군의 그것 사이에 통계적 유의차가 없었다. 이상의 결과는 광중합형 글래스아이오노머 시멘트가 브라켓 접착제로서 임상적인 유의성이 있음을 시사한다.

• 구강회복응용과학지
• /
• 제38권4호
• /
• pp.189-195
• /
• 2022

목적: 본 연구의 목적은 치열교정용 레진시멘트의 보관 조건이 치열교정용 브라켓의 접착강도에 미치는 영향을 보고자 함이다. 연구 재료 및 방법: 소의 하악 절치 순면 법랑질에 37% 인산으로 산 부식 후 치열교정용 레진시멘트인 Ortho Connect와 Orthomite를 3개월간 4℃ 냉장 보관 후 즉시 적용, 3개월간 4℃ 냉장 보관 후 24시간 동안 실온 보관하고 적용, 3개월간 24℃ 실온 보관 후 적용하는 세 조건에 따라 각 조건별로 15개의 하악 절치용 치열교정용 금속브라켓을 접착하고 광중합 한 뒤 24시간 후에 만능재료시험기로 전단접착강도를 측정하고 접착 실패 양상을 관찰하였다. 측정한 전단접착강도를 95% 유의수준에서 레진시멘트와 보관 조건에 대해 이원배치분산분석을, 레진시멘트에 보관 조건이 미치는 영향에 대해 일원배치분산분석을 했다. 결과: Ortho Connect는 냉장 보관 후 즉시 사용했을 때 가장 높은 전단접착강도를 보였으며 다른 조건 사이에는 차이가 없었다. Orthomite는 냉장 보관 후 즉시 사용했을 때 가장 낮은 전단접착강도를, 3개월 실온 보관했을 때 가장 높은 전단접착강도를 나타냈으며 이 두 조건 사이에만 유의한 차이가 있었다. 결론: Ortho Connect는 냉장 보관 후 즉시 사용해도 적절한 접착이 가능하지만, Orthomite는 냉장 보관을 한다면 충분한 실온 보관을 하는 것이 접착에 유리할 것으로 사료된다.