• 열처리공학회지
• /
• 제8권3호
• /
• pp.169-181
• /
• 1995

This study has been performed to investigate some effects of the power density and traverse speed of laser beam on the optical microstructure, hardness and fatigue resistance of gray cast iron treated by laser surface hardening technique. Optical micrograph has shown that the dissolution of graphite flakes and the coarsening of lath martensite tend to increase with a small amount of retained austenite as the power density increases under the condition of a given traverse speed. Hardness measurements have revealed that as the power density increases, hardness values of outermost surface layer increases from Hv=620 to Hv=647 in case of traverse speed of 2.0m/min at gray cast iron. Fatigue test has exhibited that the fatigue strength of laser surface hardened specimen is superier compared to that of untreated specimen, showing that values for the fatigue strength at $N_f=10^7$ of gray cast iron laser-surface-hardened at a low power density of $4076w/cm^2$ and a high power density of $8153w/cm^2$ under the condition of a given traverse speed of 2.0m/min are $15kg_f/mm^2$ and $20kg_f/mm^2$, respectively, whereas the fatigue strength of untreated specimen is $11kg_f/mm^2$. Under high stress-low cycle condition a noraml brittleness fracture appears, whereas a ductile fracture with beach mark is observed in the specimen tested under low stress-high cycle condition.

• 열처리공학회지
• /
• 제5권2호
• /
• pp.122-132
• /
• 1992

This study has been performed to investigate into some effects of the power density and traverse speed of laser beam on the optical microstructure, hardness and wear characteristics of medium carbon low alloy steel treated by laser surface hardening technique. The results obtained from the experiment are summarized as follows : (1) Optical micrograph has shown that finer lath martensite is formed and the amount of undissolved complex carbides increases as the traverse speed increases under the condition of a given power density, whereas the coarsening of lath martensite and the reduction of undissolved complex carbides occur with increasing the power density at a given traverse speed. (2) Hardness measurements have revealed that as the traverse speed increases, hardness values of outermost surface layer more of less decrease under low power densities, but are uniformly distributed under high power densities, also showing that they are uniformly distributed at low traverse speeds and more or less decrease at high traverse speeds with increasing the power density. (3) The effective case depth has been found to decrease from 0.26 mm to 0.17 mm with increasing the traverse speed from 1.5 m/min to 3.0 m/min at a given power density of $25.48{\times}10^3w/cm^2$ and to increase from 0.20 mm to 0.36 mm with increasing the power density from $19.11{\times}10^3w/cm^2$ to $38.22{\times}10^3w/cm^2$ at a given traverse speed of 2.0 m/min. (4) Wear test has exhibited that the amount of weight loss of laser surface hardened specimen with respect to sliding distance at a given load increases with increasing traverse speed at a given power density and decreses with increasing power density at a given traverse speed.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.55-55
• /
• 2003

Ferroelectric 물질은 고유전성, 자발분극과 전기장에 따른 유전상수의 변화 등의 특성을 가지고 있으므로 많은 연구가 진행중이다. 이러한 ferroelectric 물질의 유전 특성에 미치는 요소로는 물질의 조성비, 박막의 스트레스, 결정성 등이 있다. 특히 스트레스에 대한 연구가 활발히 진행중이다. 본 연구에서 산화물 인공격자를 이용하여 단일박막에서 얻을 수 없는 격자변형도를 얻어 격자 변형이 박막의 유전특성에 미치는 영향을 연구하였다. BaTiO$_3$ (BTO)/SrTiO$_3$ (STO) 산화물 인공격자를 Pulsed laser deposition (PLD)법으로 (La,Sr)CoO$_3$ 전극이 코팅된 MGO (100) 단결정 기판위에 증착시켰다. 적층 주기에 변화를 주어 BTO와 STO 각각 1.01~1.095와 0.925 ~ 1.003의 단일 막에서는 얻을 수 없는 격자 변형도를 얻었다. 이 실험적 데이터를 기초로 하여 density functional theory (DFT)라고 불리는 범함수밀도론를 기초한 제일원리적 계산 방법을 통하여 격자 변형된 SrTiO$_3$의 구조적, 전기적 특성을 계산하였다. SrTiO$_3$와 BaTiO$_3$ 격자의 안정성을 분석하기 위하여 Vienna Ab-intio Simulation Package (VASP) code가 사용되었다. SrTiO$_3$와 BaTiO$_3$ 산화물 격자의 안정성 분석 후, frozen-phonon 계산 방법을 사용하여 zone-centered optical phonon mode가 계산되었으며, mode effective charge는 Berry-phase polarization 으로부터 얻어졌다. SrTiO$_3$ 격자가 격자변형이 일어나지 않은 상태로부터 c/a= 0.985로 격자 변형 이 일어남에 따라 optical phonon mode는 점차 hardening되었다. BaTiO$_3$ 격자의 경우 SrTiO$_3$ 격자와는 달리 격자 변형이 1.01~1.023으로 진행됨에 따라 optical phonon mode의 증가를 가져왔으나 Born effective charge의 증가하였으며, 더 이상 격자 변형이 진행됨에 따라 optical phonon mode의 감소를 가져왔으나 Born effective charge의 증가 유전상수는 증가했다. 격자 변형이 SrTiO$_3$ 와 BaTiO$_3$ 산화물 격자의 optical phonon mode와 Born effective charge에 크게 영향을 미쳤다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제36권1호
• /
• pp.78-84
• /
• 2012

금형의 공정 과정에서 금형과 성형품 사이에서 발생하는 마찰로 인해 발생하는 금형의 마모가공차로 작용하여 성형 품질을 저하시킬 수 있다. 따라서 금형의 내마모성을 향상시키기 위해 질화나 침탄처리, 화염 및 고주파 표면처리 등의 방법들이 적용되어 왔다. 하지만 형상의 제한이나 제품의 변형 등과 같은 문제점을 수반하고 있기 때문에, 이러한 문제점을 해결할 수 있는 표면처리 방법으로써 레이저 표면처리 기술이 검토되고 있다. 따라서 본 연구에서는 고출력 다이오드 레이저를 이용, 금형재료용 주철의 표면처리를 시도하였다. 앞서 제1보와 제2보의 논문에서는 금형의 재료 및 형상의 차이에 따른 열처리 특성을 비교하였다면, 본 논문에서는 열처리 후 생성되는 경화부, 경계부위 및 모재의 조직적 차이를 분석하기 위해 광학 현미경 및 전자 현미경을 이용하여 미세조직을 관찰하고, EDS를 통해 조직의 상태를 파악하였다. 미세조직 관찰 결과, 경화부는 침상의 마르텐사이트 조직이 형성되어 있었다.

• 열처리공학회지
• /
• 제13권4호
• /
• pp.224-230
• /
• 2000

Garbon steel(SM35C) was gas nitrocarburized at $580^{\circ}C$ in $55%N_2-40%NH_3-5%CO_2$ mixed gas atmosphere, and then the steel was induction hardened at $850^{\circ}C$. The microstructure of gas nitrocarburized surface layer was observed by optical microscope and SEM. The phase analysis was carried out by X-ray diffraction method. The mechanical properties of gas nitrocarburized SM35C steel was evaluated by hardness, wear and fatigue test. The thickness of compound and diffusion layer were increased with increasing the gas nitrocarburizing time and the densest compound layer was obtained at 3 hours gas nitrocarburizing time. In case of 15sec induction hardening after gas nitrocarburizing, the surface hardness was decreased from 800Hv to 630Hv owing to the decomposition of compound layer, but wear resistance was increased because of increased hardness of diffusion layer. The fatigue strength of induction hardened steel after gas nitrocarburizing, $58kgf/mm^2$, was higher than $41.5kg/mm^2$ of gas nitrocarburized steel and $45kg/mm^2$ of induction hardened steel, respectively.

• 한국표면공학회지
• /
• 제51권4호
• /
• pp.249-255
• /
• 2018

High temperature and low temperature gaseous nitriding was performed in order to study of the surface hardening and wear properties of the nitrided AISI 410 Martensitic stainless steels. High temperature gaseous nitiridng (HTGN) was carried out using partial pressure $N_2$ gas at $1,100^{\circ}C$ for 10 hour, and Low temperature gaseous nitiridng (LTGN) was conducted in a gas mixture of NH3 and N2 at $470^{\circ}C$ for 10 hour. The nitrided samples were characterized by microhardness measurements, optical microscopy and scanning electron microscopy. The phases were identified by X-ray diffraction and nitrogen concentration was analyzed by GD-OES. The HTGN specimen had a surface hardness of about $700HV_{0.1}$, $350{\mu}m$ of case depth. A ${\sim}50{\mu}m$ thick, $1,250HV_{0.1}$ hard nitrided case formed at the surface of the AISI 410 steel by LTGN, composed nitrogen supersaturated expanded martensite and ${\varepsilon}-Fe_{24}N_{10}$ iron nitrides. Additionally, the results of the wear tests, carried out LTGN specimen was low friction coefficient and high worn mass loss of ball. The increase in wear resistance can be mainly attributed to the increase in hardness and to the lattice distortion caused by higher nitrogen concentration.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 2005년도 ICCAS
• /
• pp.2160-2163
• /
• 2005

Solid freeform fabrication (SFF) technology plays a major role in industry and represents a reasonable percentage of industrial rapid prototyping/tooling/manufacturing (RP/RT/RM) development applications. However, SFF technology still has long way to progress to achieve satisfactory process speed, surface finish and overall quality improvement of its application. Today, three dimensional printing (3DP) technique that is one of SFF technology is receiving many interests, and is applied by various fields. It can fabricate three dimensional objects of solid freeform with high speed and low cost using ink jet printing technology. However, need long curing time after manufacture completion. And it must do post-processing process necessarily to heighten strength of objects because strength of fabricated objects is very weak. Therefore, in this study, we proposed an improved 3DP process that can solve problems of conventional 3DP process. The general 3DP process is method to spout binder simply through printer head on powder, but proposed process is method to cure jetted UV resin by UV lamp after jet UV resin using printhead on powder. The hardening of resin is achieved strongly at early time by UV lamp in proposed method. So, the proposed process can fabricate three dimensional objects with high speed without any post-processing.

• 한국주조공학회지
• /
• 제32권1호
• /
• pp.32-37
• /
• 2012

In this study, microstructural evaluation was carried out on secondary hardening type ultrahigh strength steel, Fe-Co-Ni composition. This paper as a first part of whole research presented the microstructural behavior by cyclic heat treatment. The cyclic heat treatment method includes normalizing, stress relieving, solution treatment and aging. Especially, solution treatments performed triple times to get maximized solution hardening. Phase transformation and microstructure were observed by using optical microscope (OM), Electron back-scattered diffraction (EBSD) and X-ray stress analyzer. During the triple solution treatment, size of grain boundary was dramatically decreased by generating a packet from the martensite transformation of residual austenite in the inner part of grain, whereas the hardness increase was not significant.

• Advances in materials Research
• /
• 제4권1호
• /
• pp.1-12
• /
• 2015

Low carbon steel of composition 0.05C - 0.18 Mn - 0.012 Si is intercritically annealed at temperatures $750^{\circ}C$, $775^{\circ}C$ and $800^{\circ}C$. The equilibrated alloys of different amounts of austenite with varying carbon contents are quenched in iced water. The same alloys are subcritically annealed at $675^{\circ}C$ and $700^{\circ}C$ for varying periods of times; the subcritically annealed alloy samples are quenched in iced water. Optical, scanning electron and transmission electron microscopy are carried out for all the samples. The dislocation structure, its distribution and density present in the above prepared duplex ferrite martensite steels are studied. The martensites are found to be highly dislocated due to lattice invariant deformation. At the same time ferrite adjoining the martensite areas also exhibits quite a high dislocation density. The high dislocation density is favorable for strain ageing and hence bakes hardenability. EDS analyses were carried out for both martensite and ferrite phases; it is found that the degree of supersaturation in ferrite together with carbon content in martensite varies with the process parameters. The microhardness test results show that the hardness values of different phases differ appreciably with process parameters. The microstructures and the corresponding microanalyses reveal that differently processed steels contain phases of varying compositions and different distribution.

• 한국정밀공학회지
• /
• 제21권2호
• /
• pp.186-194
• /
• 2004

Micro-stereolithography is a newly proposed technology as a means that can fabricate a 3D micro-structure of free form. It makes a 3D micro-structure by dividing the shape into many slices of relevant thickness along horizontal surfaces, hardening each layer of slice with a focused laser beam, and stacking them up to a desired shape. In this technology, differently from the conventional stereolithography, scale effect is dominant. To realize micro-stereolithography technology, we developed the micro-stereolithography apparatus which is composed of an Ar+ laser, x-y-z stages. controllers. optical devices and scan path generation software. Related processes were developed, too. Using the system, a number of micro-structures were successfully fabricated. Some of these samples are shown for prove this system. Laser scan path generation algorithm and software considering photopolymer solidification phenomena as well as given 3D model were developed. Sample fabrication of developed software shows relatively high dimensional accuracy compared to the uncompensated result.