(Zn,Mg)O (ZMO) thin films doped with Ga $(0\~0.03mol\%)$ in the target source were prepared by pulsed laser deposition on c-plane sapphire substrates at $500^{\circ}C$, and the effect of Ga contents on the properties of the electrical, optical and crystal properties of the deposited films was investigated. From X-ray diffraction patterns, ZMO film doped with $0.02 mol\%$ Ga showed crystal structure with c-axis preferred orientation, showing only the (0002) and (0004) diffraction peaks. In contrast, ZMO film doped with $Ga=0.03 mol\%$ showed a randomly oriented crystal structure. All the samples were highly transparent, showing the transmittance values of above $85\%$ in the visible region. For all the Ga doped ZMO films, the value of energy band gap was found to be about 3.5 eV, regardless of their Ga contents. From the Hall measurements, the resistivity and the carrier density for the ZMO film doped with $0.01 mol\%$ Ga were about $5\times10^{-4}\Omega-cm$ and $2\times10^{21}cm^{-3}$, respectively.
Proceedings of the Korean Vacuum Society Conference
/
2013.02a
/
pp.461-461
/
2013
Over the last decade, zinc oxide (ZnO) thin films have attracted considerable attention owing to large band gap of 3.37 eV and large exciton binding energy of 60 meV at room temperature [1-3]. Recent interest in ZnO related researches has been switched into the fabrication and characterization of low-dimensional nanostructures, such as nano-wires and nano-dots that can be applicable to manufacture the optoelectronic devices such as ultraviolet lasers, light-emitting-diodes and detectors. Since the optical properties of ZnO nano-structures might be distinct from those of bulk materials or thin films, the low-dimensional phenomena should be examined further. In order to utilize such advanced optoelectronic devices, one of the challenges is how to control the surface state related emissions that are drastically increased with increasing the density of the nano-structures and the surface-to-volume ratio. This paper reports the synthesis and characterization of self-assembled ZnO hexagonal nano-disks grown by radio-frequency magnetron sputtering. X-ray diffraction data and scanning electron microscopy data showed that ZnO hexagonal nano-disks were nucleated on top of the flat surfaces as the film thickness reached to 1.56 ${\mu}m$ and then the number of nano-disks increased with increasing the film thickness. The lateral size of hexagonal nano-disks was ~720 nm and height was ~74 nm. The strong photo luminescence spectra obtained at 10 K was also observed, which was assigned to a surface exciton emission at 3.3628 eV arising from the surface sites of hexagonal nano-disks.
Kim, Ji-Won;Kim, Hee-Sung;Yu, Kook-Hyun;Fujishima, Akira;Kim, Young-Soon
Bulletin of the Korean Chemical Society
/
v.31
no.10
/
pp.2849-2853
/
2010
A method to improve the photocatalytic activity of titanium dioxide by modification with a sensitizer and a metal oxide is proposed. To achieve this goal, we used metal oxides as dopants. In particular, $CaWO_4$ and $Gd_2O_2S$:Tb were used because their 2.6 eV and 2.2 eV band gap energy and optical properties have a large positive effect on photocatalysis. The improvement in the photocatalytic activity of $TiO_2$ modified with $Gd_2O_2S$:Tb under ultraviolet light irradiation is described in a previous study. The present work focuses on the sensitization of metal oxide-modified $TiO_2$. Having observed the ultraviolet-visible absorption spectra of 3,4,9,10-Perylenetetracarboxylic diimide in the wide visible-light region from 400 nm to 650 nm and the broad peaks in its photoluminescence spectra at 695 nm and 717 nm, we decided to use this perylene dye to sensitize modified $TiO_2$ to enhance its activity as a visible-light harvesting photocatalyst. We also explored the positive effects thin-film surface changes stemming from ultraviolet pre-treatment have on photocatalytic activity. Finally, we subjected several metal oxide-modified $TiO_2$ products sensitized by the perylene dye to ultraviolet pre-treatment, obtaining the most active photocatalysts.
Journal of the Microelectronics and Packaging Society
/
v.26
no.4
/
pp.113-118
/
2019
In this study, we investigated the growth of single-crystallinity α-Ga2O3 thin films on c-plane sapphire substrates using halide vapor pressure epitaxy. We also found the optimal growth conditions to suppress the phase transition of α-Ga2O3. Our results confirmed that the growth temperature and partial pressure of the reactive gas greatly influenced the crystallinity. The optimal growth temperature range was about 460~510℃, and the α-Ga2O3 thin films with the highest crystallinity were obtained at a III/VI ratio of 4. The thickness and surface morphology of the thin films was observed by scanning electron microscopy. The film thickness was 6.938 ㎛, and the full width at half maximum of the ω-2θ scan rocking curve was as small as 178 arcsec. The optical band gap energy obtained was 5.21 eV, and the films were almost completely transparent in the near-ultraviolet and visible regions. The etch pit density was found to be as low as about 6.0 × 104 cm-2.
Proceedings of the Materials Research Society of Korea Conference
/
2009.05a
/
pp.16.1-16.1
/
2009
We have fabricated solution processed oxide semiconductor active layer for thin film transistors (TFTs). The oxide semiconductor layers were prepared by ink-jet printing the sol-gel precursor solution based on doped-ZnO. Inorganic ZnO-based thin films have drawn significant attention as an active channel layer for TFTs applications alternative to conventional Si-based materials and organic semiconducting materials, due to their wide energy band gap, optical transparency, high mobility, and better stability. However, in spite of such excellent device performances, the fabrication methods of ZnO related oxide active layer involve high cost vacuum processes such as sputtering and pulsed laser deposition. Herein we introduced the ink-jet printing technology to prepare the active layers of oxide semiconductor. Stable sol-gel precursor solutions were obtained by controlling the composition of precursor as well as solvents and stabilizers, and their influences on electrical performance of the transistors were demonstrated by measuring electrical parameters such as off-current, on-current, mobility, and threshold voltage. Microstructure and thermal behavior of the doped ZnO films were investigated by SEM, XRD, and TG/DTA. Furthermore, we studied the influence of the ink-jet printing conditions such as substrate temperature and surface treatment on the microstructure of the ink-jet printed active layers and electrical performance. The mobility value of the device with optimized condition was about 0.1-1.0 $cm^2/Vs$ and the on/off current ratio was about $10^6$. Our investigations demonstrate the feasibility of the ink-jet printed oxide TFTs toward successful application to cost-effective and mass-producible displays.
Single crystalline ${ZnIn_2}{Se_4}$ layers were grown on thoroughly etched semi-insulating GaAs (100) substrate at $400^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating ${ZnIn_2}{Se_4}$ source at $630^{\circ}C$. The crystalline structure of the single crystalline thick films was investigated by the photoluminescence (PL) and Double crystalline X-ray rocking curve (DCRC). The carrier density and mobility of ${ZnIn_2}{Se_4}$ single crystalline thick films measured from Hall effect by van der Pauw method are $9.41{\times}10^{16}cm^{-3}$ and $292cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the ${ZnIn_2}{Se_4}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)$=1.8622 eV-$(5.23{\times}10^{-4}eV/K)T^2$/(T+775.5 K). After the as-grown ${ZnIn_2}{Se_4}$ single crystalline thick films was annealed in Zn-, Se-, and In-atmospheres, the origin of point defects of ${ZnIn_2}{Se_4}$ single crystalline thick films has been investigated by the photoluminescence (PL) at 10 K. The native defects of $V_{Zn}$, $V_{Se}$, $Zn_{int}$, and $Se_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Se-atmosphere converted ${ZnIn_2}{Se_4}$ single crystalline thick films to an optical p-type. Also, we confirmed that In in ${ZnIn_2}{Se_4}$/GaAs did not form the native defects because In in ${ZnIn_2}{Se_4}$ single crystalline thick films existed in the form of stable bonds.
Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
/
2007.11a
/
pp.79-80
/
2007
To obtain the single crystal thin films, $AgGaSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $630^{\circ}C\;and\;420^{\circ}C$, respectively. The temperature dependence of the energy band gap of the $AgGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g$(T) = 1.9501 eV - ($8.79{\times}10^{-4}$ eV/K)$T^2$/(T + 250 K). After the as-grown $AgGaSe_2$ single crystal thin films was annealed in Ag-, Se-, and Ga-atmospheres, the origin of point defects of $AgGaSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{Ag},\;V_{Se},\;Ag_{int},\;and\;Se_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Ag-atmosphere converted $AgGaSe_2$ single crystal thin films to an optical p-type. Also, we confirmed that Ga in $AgGaSe_2$/GaAs did not form the native defects because Ga in $AgGaSe_2$ single crystal thin films existed in the form of stable bonds.
Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
/
2007.11a
/
pp.122-123
/
2007
Single crystal $AgGaSe_2$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at $420^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $AgGaSe_2$ source at $630^{\circ}C$. The temperature dependence of the energy band gap of the $AgGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g$(T)=1.9501 eV - $(8.79{\times}10^{-4}\;eV/K)T^2$/(T+250 K). The crystal field and the spin-orbit splitting energies for the valence band of the $AgGaSe_2$ have been estimated to be 0.3132 eV and 0.3725 eV at 10 K, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $AgGaSe_2$. The three photocurrent peaks observed at 10 K are ascribed to the $A_{1^-},\;B_{1^-},\;and\;C_{1^-}$exciton peaks for n=1.
Proceedings of the Korean Vacuum Society Conference
/
2013.08a
/
pp.245.2-245.2
/
2013
Solution processed organic photovoltaic devices have relatively less attention compared to polymer photovoltaic devices even though they have high possibility to be developed because they have both advantages of polymer and organic, such as solution processable, no synthetic batch dependence of photovoltaic performance, high purity and high charge carrier mobility as well as relatively high efficiency (~7%). In addition, solution processed organic photovoltaic devices have an advantage of easiness to study the relationship between the molecular structure and photovoltaic performance due to its simple structure. In this work, five isoindigo based low band gap donor-acceptor-donor (D-A-D) small molecules with different electron donating strength were synthesized for investigating the relationship between the molecular structure and photovoltaic performance, especially, investigating the effects of different electron donating effect of donor group in isoindigo backbone to photovoltaic device performance. The variation of electron donating strength of donor group strongly affected the optical, thermal, electrochemical and photovoltaic device performances of isoindigo organic materials. The highest power conversion efficiency of ~3.2% was realized in bulk heterojuction photovoltaic device consisted of the ID3T as donor and PC70BM as acceptor. This work demonstrates the great potential of isoindigo moieties as electron deficient units as well as guideline for synthesis of donor-acceptor-donor (D-A-D) small molecules for realizing highly efficient solution processed organic photovoltaic devices.
Synthesis of RGO (reduced graphene oxide)-CdS composite material was performed through CBD (chemical bath deposition) method in which graphene oxide served as the support and Cadmium Sulfate Hydrate as the starting material. Graphene-based semiconductor photocatalysts have attracted extensive attention due to their usefulness for environmental and energy applications. The band gap (2.4 eV) of CdS corresponds well with the spectrum of sunlight because the crystalline phase, size, morphology, specic surface area and defects, etc., of CdS can affect its photocatalytic activity. The specific surface structure (morphology) of the photocatalyst can be effective for the suppression of recombination between photogenerated electrons and holes. Graphene (GN) has unique properties such as a high value of Young's modulus, large theoretical specific surface area, excellent thermal conductivity, high mobility of charge carriers, and good optical transmittance. These excellent properties make GN an ideal building block in nanocomposites. It can act as an excellent electron-acceptor/transport material. Therefore, the morphology, structural characterization and crystal structure were observed using various analytical tools, such as X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and Raman spectroscopy. From this analysis, it is shown that CdS particles were well dispersed uniformly in the RGO sheet. Furthermore, the photocatalytic property of the resulting RGO-CdS composite is also discussed in relation to environmental applications such as the photocatalytic degradation of pollutants. It was found that the prepared RGO-CdS nanocomposites exhibited enhanced photocatalytic activity as compared with that of CdS nanoparticles. Therefore, better efficiency of photodegradation was found for water purification applications using RGO-CdS composite.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.