• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.10
• /
• pp.829-838
• /
• 2007

The stochiometric mix of evaporating materials for the $CdGa_2Se_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, $CdGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD).The carrier density and mobility of $CdGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.27{\times}10^{17}\;cm^{-3},\;345\;cm^2/V{\cdot}s$ at 293 K. respectively. The temperature dependence of the energy band gap of the $CdGa_2Se_4$ obtained from the absorption spectra was well described by the Varshni's relation, $Eg(T)\;=\;2.6400\;eV\;-\;(7.721{\times}10^{-4}\;eV/K)T^2/(T+399\;K)$. After the as-grown single crystal $CdGa_2Se_4$ thin films were annealed in Cd-, Se-, and Ga -atmospheres, the origin of point defects of single crystal $CdGa_2Se_4$ thin films has been investigated by PL at 10 K. The native defects of $V_{Cd}$, $V_{Se}$, $Cd_{int}$, and $Se_{int}$ obtained by PL measurements were classified as donors or accepters. We concluded that the heat-treatment in the Cd-atmosphere converted single crystal $CdGa_2Se_4$ thin films to an optical p-type. Also, we confirmed that Ga in $CdGa_2Se_4/GaAs$ did not form the native defects because Ga in single crystal $CdGa_2Se_4$ thin films existed in the form of stable bonds.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.399-399
• /
• 2008

Synthesis and characterization of ZnO structure such as nanowires, nanorods, nanotube, nanowall, etc. have been studied to multifunctional application such as optical, nanoscale electronic and chemical devices because it has a room-temperature wide band gap of 3.37eV, large exiton binding energy(60meV) and various properties. Various synthesis methods including chemical vapor deposition (CVD), physical vapor deposition, electrochemical deposition, micro-emulsion, and hydrothermal approach have been reported to fabricate various kinds of ZnO nanostructures. But some of these synthesis methods are expensive and difficult of mass production. Wet chemical method has several advantage such as simple process, mass production, low temperature process, and low cost. In the present work, ZnO nanorods are deposited on ITO/glass substrate by simple wet chemical method. The process is perfomed by two steps. One-step is deposition of ZnO seeds and two-step is growth of ZnO nanorods on substrates. In order to form ZnO seeds on substrates, mixture solution of Zn acetate and Methanol was prepared.(one-step) Seed layers were deposited for control of morpholgy of ZnO seed layers by spin coating process because ZnO seeds is deposited uniformly by centrifugal force of spin coating. The seed-deposited samples were pre-annealed for 30min at $180^{\circ}C$ to enhance adhesion and crystallinnity of ZnO seed layer on substrate. Vertically well-aligned ZnO nanorods were grown by the "dipping-and-holding" process of the substrates into the mixture solution consisting of the mixture solution of DI water, Zinc nitrate and hexamethylenetetramine for 4 hours at $90^{\circ}C$.(two-step) It was found that density and morphology of ZnO nanorods were controlled by manipulation of ZnO seeds through rpm of spin coating. The morphology, crystallinity, optical properties of the grown ZnO nanostructures were carried out by field-emission scanning electron microscopy, high-resolution electron microscopy, photoluminescence, respectively. We are convinced that this method is complementing problems of main techniques of existing reports.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.48 no.7
• /
• pp.10-16
• /
• 2011

We report on the simulation results of electrical/optical characteristics for nonpolar GaN LED having Mg-doped GaN spacer and quantum barrier, in comparison with those of the typical nonpolar GaN LED. In order to reduce the band-gap energy distortion and conduction-band discontinuity in InGaN/GaN multiple quantum wells(MQWs) of nonpolar GaN LED, and thereby to increase their current-voltage, light output power and emission peak intensity, we applied 6 nm-thick p-type($1{\times}10^{18}\;cm^{-3}$) GaN spacer and GaN QB schemes to the typical nonpolar GaN LED epitaxial structure. As a result, we found that the radiative recombination rate was increased by 23% in MQWs at 20 mA current injection. Also, the forward voltage($V_f$) and the light output power($P_{out}$) were improved by 3.7% and 7%, respectively, for the proposed nonpolar LED epitaxial structure, compared with those of the typical nonpolar GaN LED.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.44 no.5
• /
• pp.1-7
• /
• 2007

AZO thin films have been fabricated on quartz substrate with various Al doping concentrations and annealing temperatures by sol-gel method. The bset condition of (002) orientation and smooth surface (rms = 1.082 nm) is obtained for the AZO thin film doped with 1 mol % Al and annealed at 550 $^{\circ}C$. The optical transmittance of AZO thin films is higher than 80 % in the visible region. We observe that the energy band gap extends with increasing the Al doping concentration. This phenomenon is due to the Burstein-Moss effect. Through the measurement of Hall effect, it is observed that the AZO thin film has larger carrier concentration and smaller electrical resistivity than the pure ZnO thin film. However, the AZO thin film shows the decrease of carrier concentration and the increase of resistivity with the increase of Al concentration, that is due to the segregation of Al at grain boundaries. The maximum carrier concentration of $1.80{\times}10^{19}\;cm^{-3}$ and the minimum resistivity of 0.84 ${\Omega}cm$ are obtained for the AZO thin film doped with 1 mol % Al and annealed at 550 $^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.352-356
• /
• 2003

A stoichiometric mixture of evaporating materials for $CuGaSe_2$ single crystal am films was prepared from horizontal electric furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal $CuGaSe_2$, it was found tetragonal structure whose lattice constant $a_0$ and $c_0$ were $5.615\;{\AA}\;and\;11.025\;{\AA}$, respectively. To obtain the single crystal thin films, $CuGaSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $610^{\circ}C$ and $450^{\circ}C$, respectively, The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuGaSe_2$ single crystal thin films measured with Hall effect by van der Pauw method are $9.24{\times}10^{16}\;cm^{-3}$ and $295\;cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;:\;1.7998\;eV\;-\;(8.7489\;{\times}\;10^{-4}\;eV/K)T^2(T\;+\;335\;K)$. After the as-grown $CuGaSe_2$ single crystal thin films was annealed in Cu-, Se-, and Ga-atmospheres, the origin of point defects of $CuGaSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{CU}$, $V_{Se}$, $CU_{int}$, and $Se_{int}$, obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Cu-atmosphere converted $CuGaSe_2$ single crystal thin films to an optical n-type. Also, we confirmed that Ga in $CuGaSe_2/GaAs$ did not form the native defects because Ga in $CuGaSe_2$ single crystal thin films existed in the form of stable bonds.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.111-112
• /
• 2005

To obtain the single crystal thin films, $CuInSe_2$, mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wail epitaxy (HWE) system. The source and substrate temperatures were 620$^{\circ}C$ and 410$^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobilily of $CuInSe_2$ single crystal thin films measured with Hall effect by van der Pauw method are $9.62\times10^{16}$ $cm^{-3}$ and $296cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the CulnSe$_2$ obtained from the absorption spectra was well described by the Varshni's relation E$_g$(T) = 1.1851 eV - ($8.99\times10^{-4}$ ev/K)T$_2$/(T + 153K). After the as-grown $CuInSe_2$ single crystal thin films was annealed in Cu-, Se-, and In-atmospheres the origin of point defects of $CuInSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The nat ive defects of V$_{Cu}$, $V_{Se}$, Cu$_{int}$, and $Se_{int}$ obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Cu-atmosphere converted $CuInSe_2$ single crystal thin films to an optical n-type. Also, we confirmed that In in $CuInSe_2$/GaAs did not form the native defects because In in $CuInSe_2$ single crystal thin films existed in the form of stable bonds.

• Applied Chemistry for Engineering
• /
• v.28 no.5
• /
• pp.547-553
• /
• 2017

This study focused on the difference of photocatalytic performance by the incorporation of Pd into the $TiO_2$ framework and suggested five different catalysts composed of $TiO_2$ and x mol% $Pd-TiO_2$ (x = 0.25, 0.5, 0.75, and 1.0). A typical sol-gel method was used to synthesize catalysts, and the phenol photodegradation performance of each catalysts was evaluated. The physicochemical and optical properties of catalysts were confirmed by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy/energy dispersive spectrometer (SEM/EDS), ultraviolet/visible spectroscopy (UV/Vis), photoluminescence spectroscopy (PL), and photocurrent measurements. With the addition of Pd ions, the band gap of catalysts was shortened and the charge separation between photogenerated electrons and holes easily also occurred. As a result, the phenol photo-destruction performance over 0.75 mol% $Pd-TiO_2$ catalyst was 3 times higher than that of pure $TiO_2$. This is believed to be due to Pd ions acted as an electron capturing function during photocatalysis.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.47 no.2
• /
• pp.15-20
• /
• 2010

In this study, AZO (Al: 3 wt%) thin films have been prepared on PES Plastic substrates at various working pressure (5~20 mTorr), $O_2$ gas flow rate(0~3%) and the fixed substrate temperature of 200 f by using the RF magnetron sputtering and their optical and electrical properties have been studied. The XRD measurement shows that AZO thin films exhibit c-axis preferred orientation. From the results of AFM measurements, it is known that the lowest surface roughness (3.49 nm) is obtained for the AZO thin film fabricated at 5 mTorr of working pressure and 3% of $O_2$ gas flow rate. The optical transmittance of AZO thin films is measured as 80% in the visible region. We observe that the energy band gap of AZO thin films increases with decreasing the working pressure and the $O_2$ gas flow rate. This phenomenon is due to the Burstein-Moss effect. Hall measurement shows that the maximum carrier concentration ($2.63\;{\times}\;10^{20}\;cm^{-3}$) and the minimum resistivity ($4.35\;{\times}\;10^{-3}\;{\Omega}cm$) are obtained for the AZO thin film fabricated at 5mTorr of working pressure and 0% of $O_2$ gas flow rate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.493-496
• /
• 2005

비정질 실리콘 (a-Si)의 수소화를 통해 활성화 수소가 비정질 실리콘내의 댕글링본드 (dangling bond) 와 결합 하므로 에너지밴드의 국재준위(localized state)를 감소시켜 불순물 도핑이 가능하게 되므로 a-Si 이 전자소자로서 이용 가능하게 되었다. 이에 착안하여 본 연구에서는 경사($0^{\circ}$, $45^{\circ}$, $80^{\circ}$) 증착을 통해 비정질 칼코게나이드($a-As_{40}Ge_{10}Se_{15}S_{35}$) 박막을 제작하고 그 박막을 수소화처리 (15~20atm at $150\sim190^{\circ}C$)하여 처리 전 후의 surface morphology 변화 및 광학적 특성 변화를 고찰하였다. $a-As_{40}Ge_{10}Se_{15}S_{35}$ 박막의 SEM 측정을 통해 $40^{\circ}$와 $80^{\circ}$ 경사 증착된 $a-As_{40}Ge_{10}Se_{15}S_{35}$ 박막에서 각각 18.8nm 와 160nm의 transition layer와 박막의 기둥(columnar)구조가 형성됨을 관찰하였다. 특히, $80^{\circ}$ 증착박막의 경우 수소처리전 columnar구조는 약 $65\sim70^{\circ}$의 기둥 각을 가지고 형성되었고 수소화 처리를 통해 기둥구조가 붕괴 되었다. $70^{\circ}$ 경사 증착된 $a-As_{40}Ge_{10}Se_{15}S_{35}$ 박막은 $0^{\circ}$에 따른 박막 보다 흡수단 부근에서 약 20%의 투과도 증가와 광 에너지 갭 ($E_{op}$)의 증가를 관찰 할 수 있었다. $80^{\circ}$경사 증착된 수소처리 박막에서 흡수단 부근의 투과도가 약 10%증가 되었고, 광 에너지 갭은 약 0.07eV 증가 하였고, PL intensity는 흡수단 부근에서 증가한 것을 확인 할 수 있었다. 이러한 변화들은 경사 증착된 $a-As_{40}Ge_{10}Se_{15}S_{35}$ 박막 내의 상대적으로 원자 밀도가 큰 기둥(columnar)구조가 생성되고, 이 원자 밀도가 높은 기둥구조의 댕글링본드와 주입된 수소가 흡착하여 에너지대의 국재준위를 감소시키기 때문으로 판단된다.

• Journal of the Korean Applied Science and Technology
• /
• v.34 no.1
• /
• pp.50-57
• /
• 2017

Zinc oxide is, one of metal oxide semiconductor, harmless to human and environment-friendly. It has excellent chemical and thermal stability properties. Wurtzite-zinc oxide is a large band gap energy of 3.37 eV and high exciton binding energy of 60 meV. It can be applied to various fields, such as solar cells, degradation of the dye waste, the gas sensor. The photocatalytic activity of zinc oxide is varied according to the particle shape and change of crystallinity. Therefore, It is very important to specify the additives and the experimental variables. In this study, the zinc oxide were synthesized by using a microwave assisted hydrothermal synthesis. The precursor was used as the zinc nitrate, the pH value was controlled as 11 by NaOH. Surfactants are the ethanolamine, cetyltrimethylammonium bromide, sodium dodecyl sulfate, sorbitan monooleate was added by changing the concentration. The composite particles had the shape of a star-like, curcular cone, seed shape, flake-sphere. Physical and chemical properties of the obtained zinc oxide was characterized using x-ray diffractometer, field emission scanning electron microscopy, thermogravimetric analysis and optical properties was characterized using UV-visible spectroscopy, photoluminescence and raman spectroscopy.