• 한국세라믹학회지
• /
• 제44권9호
• /
• pp.524-528
• /
• 2007

The results of evaluating steel corrosion in concrete containing chloride content of various levels indicated that the more chloride content in concrete leads to the lower potential and higher corrosion current density. However, the open circuit potential of steel varied with time and exposure condition, and the corelation between the open circuit potential and corrosion current density was not obvious. In order to determine the critical threshold content of chloride of steel corrosion in concrete, the concept of average corrosion current density was employed. The range of critical chloride content in portland cement concretes was about $1.56{\sim}1.77%$($Cl^-$, %, wt of cement content) along with water-cement ratio, and higher water-cement ratio resulted in reduction in critical threshold chloride content.

• 공업화학
• /
• 제9권4호
• /
• pp.523-528
• /
• 1998

본 연구에서는 고체전해질셀 내에서 작업전극으로 사용된 $V_2O_5$의 전기화학적 특성을 알아보기 위해 YSZ를 고체전해질로 사용하여 전기화학셀(1-Butene+$O_2$, $V_2O_5{\mid}YSZ{\mid}Ag$, $O_2$)을 구성하였다. 상대전극인 Ag는 소성에 따라 sintering이 일어나고 $3{\mu}m$ 이상의 기공을 갖는 구조를 얻었다. 작업전극은 소성조건에 따라 부분산화반응에 영향을 주는 (010)면이 발생되었다. $V_2O_5$의 1-부텐에 대한 주요생성물은 부타디엔이었고 SEP (solid electrolyte potentiometry) 기술을 이용하여 작업전극상에 흡착된 화학종의 화학포텐셜을 측정하였다. 가스조성에 따른 개로전위 (OCV; open circuit voltage)를 측정하여 표면 산소종에 혼합전위의 발생을 확인하였다.

• 한국건설순환자원학회논문집
• /
• 제10권1호
• /
• pp.124-132
• /
• 2022

콘크리트 내의 부식전위는 노출환경 및 배합에 따라 크게 변화한다. 본 연구에서는 피복 두께, 염화물 농도, 물-시멘트 비를 변수로 하여 RC 시편을 제조하였으며, 철근과 표면과의 전위차를 평가하는 HCP 측정을 수행하였다. 또한 매립된 철근과 상대전극을 이용하여 OCP의 측정하였다. 한천과 NaOH 수용액을 이온교환물질로, Hg/HgO를 기준전극으로 사용하여 OCP를 측정하였는데, HCP에 비하여 온도에 더욱 민감하게 작용하였다. 영향 인자 중 존치 기간 및 염화물 농도는 피복 두께 및 물-시멘트 비보다 상대적으로 큰 영향을 가지고 있었다. 또한 전체 측정된 HCP 및 OCP는 피복 두께 및 물-시멘트와 뚜렷한 선형관계를 나타내었다. 다중회귀분석을 통하여 HCP와 OCP의 관계를 정량화하였으며 온도를 고려하여 개선된 상관성을 도출하였다.

• 대한전기학회논문지:시스템및제어부문D
• /
• 제50권11호
• /
• pp.550-556
• /
• 2001

The computerized cardiac analysis system, which acquires and analyzes the electrical activation signal propagating along the surface of the heart, is indispensible equipment for the open heart surgery and electrical cardiac study. In this paper, the design requirement and the electrical circuit analysis are performed to construct the multi-channel cardiac activation pre-amplifier necessary for a signal conditioning circuit. The general 64 channel configuration is expanded into 128 channels to enhance the spatial resolution on the mapped surface of the heart. The 128 channels pre-amplifier consists of input circuit, differential amplifier, right leg driven circuit and isolation part. It has distinct features; high voltage protection, leakage current limitation, isolation and the maximization of common mode rejection ratio with respect to the half-cell potential difference due to different electrode materials. The final pre-amplifier circuit is assembled with 8 boards, each of which composing of 16 channels.

• 대한안전경영과학회지
• /
• 제2권4호
• /
• pp.187-195
• /
• 2000

Electrochemical promotion of the reaction rate was investigated for CO oxidation in a solid electrolyte catalytic reactor where a thin film of Pt was deposited on the yttria stabilized zirconia as an electrode as well as a catalyst. It was shown under open circuit condition that potential was a mixed potential of $O_2$exchange reaction and electrochemical reaction induced by CO. The effect of electrochemical modification on the CO oxidation rate was studied at various overpotentials and $P_{CO}$$P_{O2}$.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2002년도 춘계학술대회논문집
• /
• pp.135-139
• /
• 2002

Most of all the mechanical devices are becoming more high-speed and high-power as well as their used condition being more polluted. So, it is necessary for these devices to equip cooling system to overcome that kind of severe using condition. In this study, corrosion test was carried out in distilled and tap water for the investigation on the corrosion characteristics of Al-alloy that is using as material for radiator.

• 수산해양교육연구
• /
• 제12권2호
• /
• pp.164-175
• /
• 2000

Port facilities and marine structures used in marine environment were encountered to corrosion damages because of the influence of Cl-. Generally, to protect these accidents, anti-corrosion paint and epoxy coating have been used. But they were still remained erosion-corrosion damage like impingement erosion, cavitation erosion and deposit attack. It is necessary to develope the new composite lining material in order to protective those corrosion damages. In this paper, polyester glass flake, vinylester glass flake lining and epoxy coating for SS400 were investigated by the electrochemical polarization test and the impingement-cavitation erosion test for corrosion behaviour under the sea water. The main results obtained are as follows ; 1) Epoxy coating appear potentiodynamic polarization behaviour, but polyester glass flake and vinylester glass flake lining do not appear potentiodynamic polarization behaviour. 2) Open circuit potential of polyester glass flake lining is more noble than that of epoxy coating and corrosion current density of polyester glass flake lining is less drained than that of epoxy coating in sea water. 3) Open circuit potential of vinylester glass flake lining is more noble than that of polyester glass flake lining and corrosion current density of vinylester glass flake lining is less drained than that of polyester glass flake lining in the sea water.

• Journal of Advanced Marine Engineering and Technology
• /
• 제25권6호
• /
• pp.1336-1340
• /
• 2001

Due to increase of air pollution substance, such as $SO_2$,$SO_3$, H2S ,CO, HCI, $Cl_2$ and so on, the operating environment of mechanical equipment and facilities like generating plants, ships, metal structure etc., are acidified and corroded. In these environments, the crevice corrosion of marine facilities frequently occurs at crevice like jointed bolt, gasket or sealant, riveted plates, contact of metal with non-metallic solids etc. Therefore, this paper was studied on the crevice corrosion behavior of mild steel(SS 400) in marine environment. In a variety of NaCl solutions, the aspect of he .crevice corrosion and polarization behavior under the crevice corrosion was investigated. The main results obtained are as follows: 1) Under crevice corrosion, the open circuit potential become less treble as the concentration of NaCl solution increased. 2) The corrosion current density of mild steel was high drained as the concentration of NaCl solution increased by 3.5%, but in the concentration increased over 3.5%, the corrosion current density was low drained. 3) The crevice corrosion is more sensitive to the synergy effect of dissolved oxygen and NaCl.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2006년도 전기학술대회논문집
• /
• pp.271-272
• /
• 2006

Zinc confers high corrosion resistance by acting as a sacrificial anode, and a zinc coating improves the appearance of steel. Chromate conversion coating (CCC) films are still one of the most efficient surface treatments for steel. Although such films can self-repair via the dissolution of Cr(VI), dissolved Cr(VI) have adverse effects on humans, and the environment. Therefore, we examined the corrosion protection property and morphology of colloidal silica conversion films as an alternative to CCC films. The corrosion behavior was investigated in 3% NaCl solution using electrochemical techniques, including electrochemical impedance spectroscopy, open circuit potential, and the salt spray test(SST). Corrosion was implied by the appearance of red rust on the specimen surface. In corrosion resistance at 3% NaCl solution, red rust appeared at 15-20, 55-70, and 83-98 days on Zn-electroplated steel, colloidal silica conversion-coated specimens, and CCC-coated specimens, respectively. In the salt spray test, the colloidal silica film provided better corrosion protection than CCC films, i.e., red rust appeared at 96 hours on the Zn-electroplated steel sheet, at 432 hours with the CCC films, and at 888 hours with silica conversion coating.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2001년도 추계학술대회 논문집(Proceeding of the KOSME 2001 Autumn Annual Meeting)
• /
• pp.92-97
• /
• 2001

This paper was studied on the effect of temperature on corrosion of absorption refrigeration systems using LiBr-$H_2O$ working fluids. In the fresh water and 62 %lithium bromide solution at $70^{\circ}C$, polarization test of SS 400, Cu(Cl220T-OL) and Ni-Al bronze was carried out. And Polarization behavior, polarization resistance characteristics, corrosion rate(mmpy) and corrosion sensitivity of materials forming absorption refrigeration systems was considered. The main results are as following: As the experimental temperature increase, the change of corrosion rate of Ni-Al bronze become duller than SS 400 and Cu in 62 % lithium bromide solution. Open circuit potential of SS 400 is less noble than that of Cu and Ni-Al bronze in fresh water, but that becomes noble than Cu and Ni-Al bronze in 62 % lithium bromide solution. The corrosion sensitivity of Ni-Al bronze was controlled than that of Cu and SS 400 in 62% LiBr solution.