OPACITY AND MASHING EFFECT OF THE OPAQUE SHADE COMPOSITE RESINS (Opaque shade 복합레진의 opacity와 배경 색상 차단 능력의 평가)

  • Park, Su-Jung;Hwang, Yun-Chan;Oh, Won-Mann;Hwang, In-Nam
    • Restorative Dentistry and Endodontics
    • /
    • v.32 no.4
    • /
    • pp.356-364
    • /
    • 2007
  • The purpose of this study was to assess the background color-interceptive ability ana opacity of opaque shade composites (Universal composite, Filtek Z350, Charisma, Clearfil ST, Palpaque Estelite, Esthet-X, and Metafil Flo). Twenty four background specimens (diameter 5.5 mm, thickness 3.0 mm) with Root dentin Mustard (Bisco, Schaumburg, IL, USA) were made. The CIE $L^*a^*b^*$ value of background specimens was measured by a spectrophotometer (Spectrolino, GretagMacbeth, Regensdorf, Switzerland). Three specimens in every group were filled on the background specimens. The surface color of samples was measured by a spectrophotometer in 3.0 mm and every thickness to 0.5 mm while grinding. The color difference in the background color along with 3.0 mm specimen gauged the masking effect in each thickness while grinding and polishing. The opacity was calculated in 1 mm thick specimens. The opacity was in the decreasing order of Clearfil ST, Metafil Flo, Filtek Z350, Palpaque Estelite, Universal composite, Charisma, and Esthet-X (p < 0.05). As the thickness get reduced, $L^*$ value showed decreasing, $a^*$ increasing tendency. The surface color difference between pair of the 3.0 mm thick specimen and after grinding in same opaque resin was above 3.3 except Clearfil ST and Metafil Flo. The color difference (${\Delta}E^*$) between pair of background specimen and opaque resin built-up specimen showed more than 10.0 regardless kinds and thickness. The variance in opacity characteristics and color of the opaque composites is dependent upon manufacturer. When using the opaque resin, the optical properties of each material must be considered as well as cavity.

Optical characteristics of resin composite before and after polymerization (광중합 전후 복합레진의 광학적 특성)

  • Eom, Ah-Hyang;Kim, Duck-Su;Lee, Soo-Hee;Byun, Chang-Won;Park, Noh-Hoon;Choi, Kyoung-Kyu
    • Restorative Dentistry and Endodontics
    • /
    • v.36 no.3
    • /
    • pp.219-230
    • /
    • 2011
  • Objectives: The aim of this study was to evaluate the optical characteristics such as color and translucency changes before and after light curing, to quantify the CQ and to measure refractive indices of body and opaque shade of resin composites materials. Materials and Methods: Resin composites used in this study were A2 body and A2 opaque shade of Esthet-X, Filtek supreme, Gradia Direct, Clearfil Majesty and Beautifil II. Color and translucency changes before and after light curing were evaluated by colorimeter, the CQ was quantified by GC-MS and refractive index changes were measured by spectroscopic ellipsometer. Results: Translucency parameter (TP) was significantly increased after curing. The CQ content of body shades are higher than that of opaque shades in all resin composites. Refractive index increased after polymerization in all materials and significant difference in ${\Delta}$refractive index was found between body and opaque shade (significance level 0.05). Conclusions: For an accurate shade match, direct shade matching of resin composite should be performed by using the cured material.

Thickness and translucency of opaque shade composite resin for masking effect (배경 색조 차단 목적의 불투명 복합 레진의 두께와 반투명도)

  • Baek, Kyung-Won;Kim, Sung-Joon
    • The Journal of the Korean dental association
    • /
    • v.49 no.4
    • /
    • pp.203-210
    • /
    • 2011
  • The aims of this study were to evaluate the adequate thickness of opaque resins for situations such as an oral black cavity and discolored tooth structure, as well as the translucency of each opaque material at various thicknesses. Six opaque-shade composite resins (Z-350 OA3, Amelogen Universal A2O, Esthet-X A2O, Esthet-X A4O, Charmfil UO and Aelite Universal OA3) were prepared in metal molds with a hole of 8 mm in diameter and various thicknesses (0.5mm, 1.0mm, 1.5mm, 2.0mm, 2.5mm, 3.0 mm and 4.0mm). Four backgrounds (white tile, black tile, C4 shade porcelain and opaque resin itself) were used to determine the translucency parameter (between black and white backgrounds). and to mimic a black oral cavity (between black and opaque resin backgrounds) and a discolored tooth structure (between C4 and opaque resin backgrounds). Color measurements were made by a colorimeter to determine the CIELAB values of each specimen with each background and to calculate the translucency parameter and ${\Delta}E^*$ value difference among the specimens on the backgrounds. The translucency parameter and ${\Delta}E^*$ obtained between black and opaque resin backgrounds decreased in similar pattern as thickness increased. A C4 background was masked by resin thicknesses of 0.5-1.0mm, while a black background required thicknesses of 1.0-2.0mm. Adequate knowledge about differences in the optical character like translucency of the materials used is essential, together with the accumulated experience of the individual clinician.