• Korean Journal of Materials Research
• /
• v.23 no.1
• /
• pp.59-66
• /
• 2013

Opal glass samples having different chemical compositions were synthesized and transparent glass was obtained after melting. The effects of $TiO_2$, $BaF_2$, and $CeO_2$ content on the color of the opal glass were studied by observing images of the opal samples and analyzing the results via ultraviolet visible spectroscopy and color spectrometry. The aesthetic properties of the opal glass were determined by studying the transmittance of visible light in the 400 nm to 700 nm range. The basic chemical composition of opal glass was $SiO_2$ 52.9 wt%, $Al_2O_3$ 12.35 wt%, $Na_2CO_3$ 15.08 wt%, $K_2CO_3$ 10.35 wt%, $Ca_3(PO)_4$ 4.41 wt%, $MgCO_3$ 1.844 wt%, $LiCO_3$ 2.184 wt%, and $TiO_2$ 0.882 wt%. The glass samples were prepared by varying the weight percentage of $TiO_2$, $BaF_2$, and $CeO_2$. The transmittance of visible light was decreased from 95 % to 75 % in the glass samples in which $TiO_2$ content was increased from 0 to 3.882 wt%. In the blue spectrum region, as the content of $TiO_2$ increased, the reflectance value was observed to become higher. This implies that $TiO_2$ content induces more crystal formation and has an important effect on the optical properties of the glass. The opalescence of opal samples that contained $CeO_2$ or $BaF_2$ is stronger than that in the samples containing $TiO_2$. Opal glass samples comprising $TiO_2$ had tetragonal lattice structures; samples including $CeO_2$ as an additive had cubic lattice structures (FCC, $CeO_2$).

• Journal of the Korean Electrochemical Society
• /
• v.15 no.3
• /
• pp.149-153
• /
• 2012

The $Cu_2O/TiO_2$ inverse opal heterojunction arrays were developed by electrochemical deposition of $Cu_2O$ nanoparticles on $TiO_2$ inverse opal arrays. The $Cu_2O$ nanoparticles completely filled the inner pores of $TiO_2$ inverse opal film (prepared by liquid phase deposition with an average thickness of 400 nm) and covered the entire area; exhibiting high crystalline properties of anatase and cubic phase from $TiO_2$ and $Cu_2O$, respectively. From asymmetric current-voltage profile, it was noticeable that a heterojunction was well formed for charge transport from $Cu_2O$ to $TiO_2$ film resulting from the enhanced charge separation yield. In addition, increased photocurrent of 0.19 $mA/cm^2$ (versus 0.08 $mA/cm^2$ under dark condition) was obtained at -0.35 V from the heterojunction structure in the 0.5M $Na_2SO_4$ solution.

• The Sea:JOURNAL OF THE KOREAN SOCIETY OF OCEANOGRAPHY
• /
• v.25 no.1
• /
• pp.1-8
• /
• 2020

Biogenic opal crash at about 6.7 Ma was identified at both IODP Site U1447 and NGHP Site 17 in the Andaman Sea. The different biogenic opal content and general variation pattern between two sites may be attributed to the different concentration of analytical reagent and sedimentation rate estimated by the different chronological approaches. Nevertheless, this study suggests that the biogenic opal crash in the Andaman Sea is closely related to the restriction of Indonesian Throughflow and to the decreasing strength of Indian summer monsoon during the late Miocene, both of which resulted in the reduction of nutrient supply.

• Journal of Plant Biology
• /
• v.37 no.1
• /
• pp.53-67
• /
• 1994

The opal phytolith types in Oryza sativa L. were examined with light and scanning electron microscope, and we suggested the standard tenninoligies based on original cells of the phytoliths in situ. The distinctive fonus of opal phytoliths were observed in all plant parts such as leaf blade, leaf sheath, culm, root, glume, lemma, and palea. The phytolith fonus originated from long cell, short cell, and dennal appendages were different from part to part. The opal phytoliths derived from the long cells showed the most various form: twelve types were identified based on side wall shape. The results showed that the leaf blade did include almost all types of opal phytolith observed in the other parts of rice.f rice.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.153_154
• /
• 2009

실제 대규모 전력계통에서 발생 가능한 과도현상 모의 및 새롭게 개발된 보호 장비와 같은 전력기기들의 사전 동작검증을 위하여 실시간 시뮬레이터의 필요성이 증가하고 있다. 따라서, 본 논문에서는 여러 실시간 시뮬레이터 중 OPAL-RT eMEGAsim을 사용하여 실시간 시뮬레이션을 통한 과도안정도 분석을 수행하였다. 우선, OPAL-RT eMEGAsim의 특징 및 하드웨어 구조, 시뮬레이션 도구에 대하여 기술하였고, 간단한 1기 무한모선 계통에서 과도안정도를 분석하고 모의결과를 제시하였다.

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.75-81
• /
• 2013

We fabricated translucent opal glass to replace the polycarbonate diffuser in LED lighting systems in order to solve the durability problem. Batch materials of opal glass with a composition of calcium phosphate were created and melted at $1550^{\circ}C$, and the effect of opaqueness was identified by an addition of 1~7% calcium phosphate as an opacifier raw material. As a result, translucent opal glass was obtained by the melting of the mixed batch materials with a composition of more than 5% calcium phosphate glass at $1550^{\circ}C$ for 2 hrs, which had excellent optical properties for the diffuser of a LED lighting system with no dazzling from direct light by a high haze value exceeding 90% and a low parallel transmittance value of about 5%. For the thermal properties, the thermal expansion coefficient was found to be $5.6{\sim}5.9{\times}10^{-6}/^{\circ}C$ and the softening point was $874{\sim}884^{\circ}C$. In addition, good thermal properties such as good thermal shock resistance and feasibility for use with a general manufacturing process during the forming of glass tubes and bulbs were noted. Therefore, it is concluded that this translucent opal glass can be used as a glass diffuser material for LED lighting due to its high heat resistance and high durability as a replacement for a polycarbonate diffuser.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.650-657
• /
• 2012

For the purpose of improving the durability problem, translucent opal glass was fabricated as a substitute for the polycarbonate diffuser of LED lighting. Calcium phosphate was used as an opacifier of opal glass and melted in an electric furnace. The opaque effect was identified according to the change of the cooling procedure. As results, translucent opal glass was obtained by the melting of a batch with a composition of 3.8% calcium phosphate at $1550^{\circ}C$ for 2 hrs and then the cooling of the material in the furnace. For the cooling condition of the glass sample, HTCG (High Temperature Cooled Glass) was found to have better optical properties than LTAG (Low Temperature Annealed Glass). It had excellent optical properties for a diffuser of LED lighting, with no dazzling from direct light due to its high haze value of over 99% and low parallel transmittance value of under 1%. For the thermal properties, it had an expressed thermal expansion coefficient of $5.7{\times}10^{-6}/^{\circ}C$ and a softening point of $876^{\circ}C$; it also had good thermal properties such as good thermal shock resistance and was easy to apply to the general manufacturing process in the forming of glass tubes and bulbs. Therefore, it is concluded that this translucent opal glass can be used as a glass diffuser material for LED lighting with high heat resistance and high durability; this material is suitable as a substitute for polycarbonate diffusers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.3
• /
• pp.120-126
• /
• 2014

Translucent green colored opal glass was fabricated to substitute polycarbonate diffuser of LED lighting in order to solve the durability problem. Batch materials of green colored opal glass with the composition of calcium phosphate for opacifier and iron oxide for colorant were made and melted at $1550^{\circ}C$. As the results, translucent green colored opal glass was obtaind, which had excellent optical properties compare with nomal color glass for the diffuser of LED lighting, with no dazzling from direct light by high haze value over 90 % and low parallel transmittance value about 1 %. Therefore, it is concluded that this translucent green colored opal glass can be used for the glass diffuser materials of LED lighting with high heat resistance and high durability to substitute polycarbonate diffuser.

• Ocean and Polar Research
• /
• v.33 no.3
• /
• pp.211-221
• /
• 2011

Contents of biogenic components [opal, $CaCO_3$, TOC (total organic carbon)] were measured in Core LHB-3PC sediments collected off Lutzow-Holm Bay, in order to understand glacial-interglacial cyclic variation of the high-latitude surface-water paleoproductivity, in the Indian Sector of the Southern Ocean. An age model was established from the correlation of ARM/IRM ratios of Core LHB-3PC with LR04 stack benthic ${\delta}^{18}O$ records, in complement with radiocarbon isotope ages and biostratigraphic Last Appearance Datum (LAD). The core-bottom age was estimated to be about 700 ka. Although the $CaCO_3$ content is very low less than 1.0% throughout the core, the opal and TOC contents show clear glacial-interglacial cyclic variation such that they are high during the interglacial periods (7.2-50.3% and 0.05-1.00%, respectively) and low during the glacial periods (5.2-25.2% and 0.01-0.68%, respectively). According to the spectral analysis, the variation of opal content is controlled mainly by eccentricity forcing and subsequently by obliquity forcing during the last 700 kyrs. The opal contents of Core LHB-3PC also represent the apparent Mid-Pleistocene Transition (MPT)-related climatic variation in the glacial-interglacial cycles. In particular, the orbital variation of the opal contents shows increasing amplitudes since marine isotope stage (MIS) 11, which defines one of the important paleoclimatic events during the late Quaternary, called the "Mid-Brunhes Event". Based on the variation of the opal contents in Core LHB-3PC, we suggest that the surface-water paleoproductivity in the Indian Sector of the Southern Ocean followed the orbital (glacial-interglacial) cycles, and was controlled mainly by the extent of sea ice distribution during the last 700 kyrs.

• Ocean and Polar Research
• /
• v.45 no.3
• /
• pp.141-153
• /
• 2023

Biological pump processes generated by diatom production in the surface water of the Southern Ocean play an important role in exchanging CO₂ gas between the atmosphere and ocean. In this study, the biogenic opal content of the sediments was measured to elucidate the variation in the primary production of diatoms in the surface water of the Southern Ocean since the last glacial period. A piston core (COR-1bPC) was collected from the Conrad Rise, which is located in the Indian sector of the Southern Ocean. The sediments were mainly composed of siliceous ooze, and sediment lightness increased and magnetic susceptibility decreased in an upward direction. The biogenic opal content was low (38.9%) during the last glacial period and high (73.4%) during the Holocene, showing a similar variation to that of Antarctic ice core ΔT and CO₂ concentration. In addition, the variation of biogenic opal content in core COR-1bPC is consistent with previous results reported in the Antarctic Zone, south of the Antarctic Polar Front, in the Southern Ocean. The glacial-interglacial biogenic opal production was influenced by the extent of sea ice coverage and degree of water column stability. During the last glacial period, the diatom production was reduced due to the penetration of light being limited in the euphotic zone by the extended sea ice coverage caused by the lowered seawater temperature. In addition, the formation of a strong thermocline in more extensive areas of sea ice coverage led to stronger water column stability, resulting in reduced diatom production due to the reduction in the supply of nutrient-rich subsurface water caused by a decrease in upwelling intensity. Under such environmental circumstances, diatom productivity decreased in the Antarctic Zone during the last glacial period, but the biogenic opal content increased rapidly under warming conditions with the onset of deglaciation.