• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.583-590
• /
• 1997

The effects of Mn2O3 and Y2O3 additives on the microstructure and dielectric properties of Sr(Zr, Ti)O3 have been investigated. Powders with Sr(Zr1-xTix)O3(0$\leq$x$\leq$0.1) composition were prepared by the conventional solid state processing from commercial TiO2 and precipitation-processed ZrO2. The powders containing sintering additives of Mn2O3 and Y2O3 were compacted and then sintered at 1,55$0^{\circ}C$ for 4 h to get>97% relative density. Mn2O3 suppressed the grain growth and Y2O3 enhanced the density of sintered body. The oxidation state of Mn ions were determined by a chemical wet method and EPR spectroscopy. Mn ions were present as Mn2+ and Mn4+ in SrZrO3, while as Mn3+ and Mn4+ in Ti-substituted Sr(Zr, Ti)O3. With the substitution of Ti, the lattice parameters of SrZrO3 decreased and its dielectric constant increased with remarkable decrease in Q value. The dielectric constant of Sr(Zr, Ti)O3 was in the range of 30 to 40, Q values 1,200~5,400 at 6 GHz and temperature coefficient of resonant frequency -67~100 ppm/K.

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1108-1114
• /
• 1999

Microstructure and electrical properties of ZnO-doped (0-5 mol%) 0.05 Pb(Mn1/3Sb2/3)O3-0.95 PZT ceramics were investigated. Sintering temperature was decreased to 100$0^{\circ}C$ due to eutetic reaction between PbO and ZnO. Grain-size increased up to adding 1mol% ZnO and then decreased. Compositions of grain and grain-boundary were investigated by WDS. Lattice parameter was decreased with ZnO addition. Density increased with ZnO addition and reached to the maximum of 7.84(g/cm2) at 2 mol% ZnO. The effect of ZnO on electrical properties of PMS-PZT was investigated. At 3mol% ZnO addition electromechanical coupling factor(kp) was about 50% and relative dielectric constant($\varepsilon$33/$\varepsilon$0) was 997 Mechanical quality factor(Qm) decreased with ZnO addition. Lattice parameters and tetragonality(c/a) were measured to investigate relationship between the electric properties and substitution of Zn2+. At 3 mol% ZnO tetragonality was maximiged at c/a=1.0035 Curie temperature (Tc) decreased slightly with ZnO addition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.272-273
• /
• 2006

LTCC(low temperature co-fired ceramics)용 glass/ceramic 복합체를 제조하기 위해 4 종류의 borosilicate계 glass를 선정하고 filler로 $Al_2O_3$ ceramics를 filler 사용하여 30~50 vol% glass frit에 따른 소결 및 유전 특성에 대하여 조사하였다. Glass frit은 $SiO_2$와 $B_2O_3$ 함량비를 고정한 후 R(CaO, BaO, ZnO, $Bi_2O_3$)에 따라 유리 연화온도(Ts)와 함량이 소결에 미치는 영향 및 유전 특성 변화를 고찰한 결과, CaO-$B_2O_3-SiO_2$ glass의 경우 다량의 2 차상이 형성되었고, 이에 $900^{\circ}C$ 이하에서 완전 소결이 이루어지지 않았으며, BaO-$B_2O_3-SiO_2$ glass는 celsian($BaAl_2Si_2O_8$) 결정이 형성되면서 소결성의 저하를 갖고 왔으며, ZnO-$B_2O_3-SiO_2$ glass는 소결이 진행됨에 따라 주상이 $Al_2O_3$에서 gahnite($ZnAl_2O_4$) 결정이 형성되면서 품질계수가 크게 증가하였으며, $Bi_2O_3-B_2O_3-SiO_2$ glass는 45 vol%일 때 $900^{\circ}C$에서부터 일정한 선수축율 특성을 나타내었지만, 다량의 액상으로 인하여 유전 특성의 저하를 나타내었다.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc1
• /
• pp.37-41
• /
• 2012

A lithium ion conducting borosilicate glass was fabricated by a conventional melt quenching technique from a mixture of Li2CO3, B2O3 and SiO2 powders. The Li ion conductivity of the lithium borosilicate glasses was evaluated in terms of the SiO2/B2O3 ratio. In the Li2O-B2O3-SiO2 ternary glass, the glass forming region decreases with an increasing Li2O content. At the same Li2O, the crystallization tendency of the glass samples increases with the SiO2/B2O3 ratio, resulting in a reduced glass forming region in the Li2O-B2O3-SiO2 ternary glass. The electrical conductivity moderately depends on the SiO2/B2O3 ratio in the Li2O-B2O3-SiO2 ternary glass. The conductivity of the glasses slightly increases with the SiO2/B2O3 ratio. The observed phenomenon can be explained by the modification of the glass structure as a function of the SiO2 content.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1097-1104
• /
• 2000

MOD(Metal-Organic-Decomposition)법에 의해 $Y_2$O$_3$버퍼층에 Pt/TiO$_2$/SiO$_2$/Si 기판 위에 제조한 후, 그 표면 위에 졸-겔 방법으로 YMnO$_3$박막을 형성하였다. 기판의 종류와 수화조건 변화가 YMnO$_3$박막의 결정화 거동에 미치는 영향을 고찰하였으며, 또한 $Y_2$O$_3$버퍼층 유.무에 따른 Mn의 산화상태를 확인하고 이에 따른 유전특성 변화를 연구하였다. $Y_2$O$_3$버퍼층을 삽입하지 않고 직접 기판 위에 형성한 YMnO$_3$박막의 결정상은 기판의 종류 및 Rw 변화에 관계없이 orthorhombic 구조임이 확인되었다. 반면, $Y_2$O$_3$버퍼층 위에 형성된 YMnO$_3$박막의 경우에는 Rw($H_2O$/alkoxide mole ratio)가 0~6 범위 내에서 낮아질술고 hexagonal 결정상 성장에 유리하였으며, 또한 Pt(111)/TiO$_2$/SiO$_2$/Si 기판이 Ptd(200)/TiO$_2$/SiO$_2$/Si에 비하여 결정상 형성에 용이하였다. $Y_2$O$_3$버퍼층은 YMnO$_3$결정상 내에서 $Mn^{4+}$ 이온형성을 억제함으로써 누설전류밀도가 크게 감소되는 효과를 주었으며, 동시에 강유전 특성을 지닌 hexagonal 결정상 형성에 유리하게 작용하였다. 결론적으로, $Y_2$O$_3$는 Pt가 코팅된 Si 기판 위에 YMnO$_3$박막 제조시 그 강유전 특성을 향상시켜주는 우수한 버퍼층 재료임을 확인하였다.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1080-1085
• /
• 2001

Dielectric properties and leakage current characteristics of 100 nm-thick $Ta_2O_5/Al_2O_3$multilayer thin films, which were fabricated by reactive sputtering of$Al_2O_3$and$Ta_2O_5$ successively on top of each other for total 9 layers, have been investigated with variation of the$Al_2O_3$content$(i.e,\;Ta_2O_5/Al_2O_3 \;thickness\;ratio)$.$Ta_2O_5/Al_2O_3$films were amorphous regardless of the$Al_2O_3$content. With increasing the$Al_2O_3$content from 0% to 100%, refractive index of the $Ta_2O_5/Al_2O_3$films decreased linearly from 2.03 to 1.56 and dielectric constant was lowered from 23.9 to 7.7 Variation of the dielectric constant with the$Al_2O_3$content was in good agreement with the behavior that was obtained by assuming parallel capacitors of$Al_2O_3$and Ta_2O_5$. Leakage current characteristics of $Ta_2O_5/Al_2O_3$ multilayer films were superior to those of $Ta_2O_5$ and$Al_2O_3$films. $Ta_2O_5/Al_2O_3$ films of 5% and 10%$Al_2O_3$content exhibited excellent leakage current densities which were lower than $10^{-7} A/cm^2$ at 1MV/cm.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.2 no.2
• /
• pp.71-76
• /
• 1992

Piezoceramic filters were fabricated by adding $MnO_2 and FeZ0_3$ to the $0.05Pb(Al_{2/3}W_{1/3})O_3-0.95Pb(Zr_{0.52}Ti0.48)O_3$ system using photolithography method. As the amounts of $MnO_2$ increased, the electro-mechanical coupling factor(Kp) decresed. On the other hand, for $Fe_2O_3$ added samples, Kp was 57%, but mechanical quality factor(Qm) showed relatively low value. The passband widths were 155kHz for 0.3wt % $MnO_2$ addition and 260kHz for 0.1 wt % $Fe_2O_3$ addition, and were inversely propotional to Qm values. Group delay time characteristics showed Gausian for $MnO_2$ additions and Butterworth for$Fe_2O_3$ additions.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.102-108
• /
• 1997

ZrO2 powders stabilized with Y2O3 and CeO2 of various compositions were prepared by the coprecipitation of water-soluble ZrOCl2.8H2O, YCl3.6H2O and Ce(NO3)3.6H2O, and their compacts were pressurelessly sintered at 1400 and 150$0^{\circ}C$ for 2hrs in air. 2mol% Y2O3-ZrO3 showed the most superior strength (1003MPa) and microhardness (12.6GPa), while 10 mol%CeO2-ZrO2 had the hightest toughness (13.3 MPa.m1/2) after sintering at 140$0^{\circ}C$. The addition of Y2O3 into Y2O3-ZrO3 decreased mean grain size and increased strength and hardness but decrease toughness. On the other hand, the addition of CeO2 into Y2O3-ZrO2 enhanced the stability of tetragonal phase during low-temperature aging for a long time under hydrothermal atmosphere.

• Journal of the Korean Ceramic Society
• /
• v.22 no.6
• /
• pp.42-52
• /
• 1985

Several $Al_2O_3$-based polycrystalline which had different dopant ratio in the range of 0.5mol% were prepared by doping pure $Cr_2O_3$ $HfO_2$. Single crystalline which had same composition with above polycrystalline were made by means of floating zone method. This study examined the role of each dopant for enhancing the mechanical properties of $Al_2O_3$-based Ceramics. Optical micrographs $({ imes}200)$ of $Al_2O_3-Cr_2O_3$ single crystal showing not only radial crack (rc) on the specimen surface but median crack(mc) and lateral crack(lc) under surface at the edge of indentation mark. Fracture toughness of Al2O3-based Ceramics was increased with $ZrO_2$ content. Alloying effect of $Cr_2O_3$ contributed to the hardness of $Al_2O_3$ based ceramics.

• Journal of the Korean Ceramic Society
• /
• v.29 no.9
• /
• pp.719-728
• /
• 1992

ZrO2/Al2O3-Mullite composites were prepared by infiltration of the silica sol to the porous ZrO2/Al2O3 bodies. The porous ZrO2/Al2O3 bodies for infiltration were fabricated using ZrO2 (20wt%)/Al2O3 composite powders synthesized by the emulsion-hot kerosene drying method. The preparation of silica sols was conducted by the hydrolysis-peptization of an alcoholic TEOS solution. When ZrO2/Al2O3-Mullite and ZrO2/Al2O3 composites were sintered at 1$650^{\circ}C$ for 4 hrs, both of them showed an excellent sinterability. As the amount of mullite added in the composites increased, the ratio of the tetragonal phase of zirconia to the monoclinic phase at the room temperature became higher. It was known that values of the fracture toughness of the ZrO2/Al2O3-Mullite composites were about 5.48 MPa.m1/2 much larger than that of the ZrO2/Al2O3 system.