• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.3 s.32
• /
• pp.17-22
• /
• 2004

The microwave dielectric properties of $CaZrO_3$ ceramics with addition of $CaTiO_3$ were studied. The effect of glass addition on the low-temperature sintering and microwave dielectric properties of $CaZrO_3-CaTiO_3$ ceramics were also evaluated to develop the materials for functional substrates of low-temperature co-fired ceramics. When $10-20 wt\%$ of lithium borosilicate glass was added, the sintering temperature of the $CaZrO_3-CaTiO_3$ ceramics decreased from $1450^{\circ}C$ to below $900^{\circ}C$. As the $T_f$ of glass frits and $CaZrO_3$ are slightly negative and that of $CaTiO_3$ is significantly positive, zero $T_f$ could be realized by mixing an appropriate amount of $CaTiO_3$ with $CaZrO_3$. The $CaZrO_3-CaTiO_3$ ceramics sintered at $875^{\circ}C$ with $15wt\%$ glass frits showed the relative density of $98\%$, permittivity of 23, quality factor of 2500 GHz, and temperature coefficient of resonant frequency of $ -3 ppm/^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.28 no.3
• /
• pp.215-224
• /
• 1991

The synthesis of SrTiO3 powders having high purity and homogeneous submicron particle size was attempted by the oxalate method. The microstructure and dielectric properties of SrTiO3 based boundary layer capacitor (BLC) were investigated. Strontium titanyl oxalate[SrTiO(C2O4)2.4H2O] was prepared from the mixing solution of (Sr, Ti) using oxalic acid(H2C2O4) as a precipitating agent at 8$0^{\circ}C$. The crystalline SrTiO3 powder was obtained by thermal decomposition of the precipitate above $600^{\circ}C$. The crystalline SrTiO3 powder containing Nb2O5 as a dopant, TiO2 and SiO2 as additives was sintered at 1360~144$0^{\circ}C$ in the reducing atmosphere to get semiconductive SrTiO3. Insulating material containing PbO-Bi2O3-B2O3 frit was printed on the sintered semiconductive SrTiO3 and fired at 120$0^{\circ}C$ for 2h to get the grain boundary diffusion.

• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.629-635
• /
• 1997

The effects of the annealing atmospheres(O2, N2) and sintering additives that Bi2O3 is a major composition on the microwave dielectric and sintering propertie of (1-x)CaTiO3-xLaAlO3 system were investigated. The annealing atmospheres and the increase of annealing time after sintering did not affect the relative dielectric constant($\varepsilon$r) and temperature coefficient of resonant frequency($\tau$f) of (1-x)CaTiO3-xLaAlO3 system. However, the Q.f0 values of (1-x)CaTiO3-xLaAlO3 were very sensitive to annealing atmospheres. As the annealing time increased under O2 atmosphere the Q.f0 values of (1-x)CaTiO3-xLaAlO3 enhanced untill 10 hrs in 0.3$\leq$x$\leq$0.6 region, but degraded over that time. The increasing rate of Q.f0 value increased wth increasing x. On the other hand, as the annealing time increased under N2 atmosphere the Q.f0 values were constant in x$\leq$0.6 region, increased gradually in x$\geq$0.7 region. When 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% as sintering additives were added to (Ca0.5La0.5) (Ti0.5Al0.5)O3 (x=0.5) the sintering temperature of 1$600^{\circ}C$ was lowered to 140$0^{\circ}C$, and the relative dielectric constant($\varepsilon$r) and temperature coefficient of resonant frequency($\tau$f) were not nearly changed. The addition of 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% to (Ca0.5La0.5)(Ti0.5Al0.5)O3 made the Q.f0 values to be lower about 15% and 34%, respectively.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.81-86
• /
• 2003

Microwave dielectric properties have been investigated in the$(1-x)CaTiO_3-xYAlO_3$ (x=0.1~1.0) solid solution system. The mixtures of $CaTiO_3$ and $YalO_3$using solid state method were sintered at various temperatures. Their dielectric constants and related temperature coefficients were strongly depend on the composition of the solid solution. The optimum properties were recorded as for ${\varepsilon}_r=47,$ $Q{\times}f_0$=35000 and ${\tau}_f=+11ppm/^{\circ}C$ without sintering agent. Even at $1200^{\circ}C$ full densification has been achieved with addition of $CaB_2O_4$ in the $0.75CaTiO_3-0.25YalO_3$ composition. The sample of $0.3 wt%-CaB_2O_4$ added $ 0.75CaTiO_3-0.25YalO_3$ sintered at $1300^{\circ}C$ for 3 h showed optimum microwave dielectric properties of ${\varepsilon}_r=47$, $Q{\time}f_0=37000$ and ${\tau}_f=+17ppm/^{\circ}C$, which demonstrates the promising candidates for microwave dielectric materials covering 5~7 GHz range.

• Journal of the Korean earth science society
• /
• v.42 no.2
• /
• pp.149-163
• /
• 2021

In this study, the changes in ozone (O3) concentrations due to the removal of power plant emissions were analyzed using a community multi-scale air quality (CMAQ) model. Two different CMAQ model simulations, one considering the emissions from the Hadong power plant and one without considering the emissions, were conducted to investigate the effect of the emissions on the changes in the O3 concentrations in the surrounding areas. Subsequently, the CMAQ simulations exhibited an increase in the O3 concentration (25.24%) despite a decrease in the NOx (-18.87%) and volatile organic carbon (VOC, -11.27%) concentrations, which are major O3 precursors. The changes in the NO and O3 concentrations due to the removal of power plant emissions presented a strong negative correlation (r= -0.72). This indicated that the increase in the O3 concentration was mainly attributed to the significantly decreased NO concentration, thus, mitigating the O3 titration reaction (NO+O3→NO2+O2). Additionally, due to the VOC-limited (i.e., NOx-saturated) conditions in the study region, NO affected the O3 concentration, indicating that the O3 concentrations in a particular region are not only proportional to the increase or decrease in emissions. Therefore, an in-depth understanding of the chemical O3 production and loss in a particular region is necessary to accurately evaluate the effect of emission control on the changes in the O3 concentration.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1261-1262
• /
• 2007

At first the $Ba_{0.5}Sr_{0.5}TiO_{3}$-MgO powder with $B_{2}O_{3}-Li_{2}CO_{3}$ were made by the Sol-Gel method. And then the thick films of BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ were fabricated on the $Al_{2}O_{3}$ substrates coated with Pt by the screen printing method. The structural and dielectric properties of the BST-MgO thick film with $B_{2}O_{3}-Li_{2}CO_{3}$ addition were investigated. The structure of the BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ thick films were dense and homogeneous with no pores. The dielectric constant and dielectric loss were increased with decreasing the $B_{2}O_{3}-Li_{2}CO_{3}$ addition ratio.

• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.173-183
• /
• 1988

Effects of oxide additives such as MoO3, MnO2 ZrO2 and Fe2O3 on the phase separation and the chemical durability of sodium borosilicate glasses which are the host of waste glasses have been investigated as the basic study on the nuclear-waste immobilization through vitrification. MoO3 and MnO2 were found to be phase separation promotors which increased the temperature as well as catalyzed nucleation and growth for the phase separation of the 10Na2-O-3OB2O3-6OSiO2 (wt%) parent glass within the immiscibility region. The glasses had the interconnected phase-separated structure as the amount of addition increased. On the other hand, ZrO2 and Fe2O3 were inhibitors which showed the reverse effects to the above promotors. It was also found that addition of MoO3 could cause the phase separaton of the 20Na2O-10B2O3-70SiO2(wt%) glass even within the miscibility region. Addition of ZrO2 and Fe2O3 increased the chemical durability of the parent glass within the immiscibility region. Within the miscibility region, however, the addition of 1.96 wt % of MoO3 increased the chemical durability considerably, while MnO2 had little effects.

• Journal of the Korean Ceramic Society
• /
• v.38 no.7
• /
• pp.615-620
• /
• 2001

E $r_2$ $O_3$-MgO 복합 첨가가 BaTi $O_3$계 내환원성 X7R 재질의 유전특성에 미치는 영향에 대하여 환원성 분위기에서 연구하였다. (B $a_{1-x}$ E $r_{x}$)( $Ti_{1-y}$M $g_{y}$ ) $O_3$첨가계에서 1.0 mol% 이상 MgO의 복합첨가로 E $r_{Ba}$ 도너 불순물과 $Mg_{Ti}$ 억셉터 불순물이 전기적으로 보상되어, 환원성분위기 소결 후에도 $10^{10}$Ωcm 이상의 높은 절연저항을 나타내었다. E $r_2$ $O_3$가 첨가된 시편에서 MgO가 2.0 mol% 이상 첨가될 경우, 유전율의 온도안정성이 향상되어 X7R 규격을 만족시켰으며 1.0$mu extrm{m}$ 이하의 작고 균일한 입자가 관찰되었다. 한편, E $r_2$ $O_3$의 첨가량이 3.0 mol%로 증가함에 따라 유전율의 온도안정성이 향상되었으나 상대적으로 상온 유전상수값이 현저히 감소하였다.였다.다.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.543-544
• /
• 2006

The effect of the additives, $Y_2O_3$ and MgO, on the sintering and properties of $Al_2O_3-TiC$ composites was investigated. It is known that MgO is used as additive for improving densification and $Y_2O_3$ is applied as sintering aid. In this study, the amounts of TiC were varied in the range of 30-47 wt%. The 0.5 wt% MgO and also varied amounts of $Y_2O_3$ from 0.3 to 1 wt% were added into the composites. The sintering of $Al_2O_3-TiC$ composites was performed in a graphite-heating element furnace at different sintering temperature, 1700 and $1900\;^{\circ}C$, for 2 hr under an argon atmosphere. The results demonstrated that the properties of the composites sintered at $1700\;^{\circ}C$ were much better than those sintered at $1900\;^{\circ}C$. The comparisons on physical properties, mechanical properties and microstructure of composites with and without additives were reported. Comparing with other samples, $Al_2O_3-30wt%TiC$ composites with 0.5wt% MgO and $1\;wt%Y_2O_3$ exhibited the highest density of approximately 98% of theoretical and flexural strength of 302 MPa.

• Journal of the Korean Ceramic Society
• /
• v.30 no.9
• /
• pp.731-739
• /
• 1993

R-curve measurements were performed on Al2O3(matrix)-ZrO2-SiC whisker composite and Al2O3-ZrO2, Al2O3-SiC whisker composites in the favor of comparing the effect of ZrO2 and SiC whisker, as a second phase, to Al2O3 matrix. Al2O3-SiC whisker and Al2O3-ZrO2-SiC whisker were fabricated by hot pressing at 1$700^{\circ}C$, 15MPa and Al2O3-ZrO2 by pressureless sintering at 1$600^{\circ}C$. A controlled flaw/strength technique was utilized to determine fracture resistance as a function of crack extension and R-curve behaviour was determined from the relationship which is KR=K0(Δa)m. R-curveresults were KR=6.173$\times$Δa0.031 for Al2O3-ZrO2, KR=18.796$\times$Δa0.172 for Al2O3-SiC whisker and KR=11.96$\times$Δa0.110 for Al2O3-ZrO2-SiC whisker composite. From the analysis of R-curve and expeirmental data above three composites, it is found that R-curve behaviour of Al2O3-ZrO2-SiC whisker composite was dominated initially by the strengthening effect of ZrO2 and after, some extended crack were influenced by the effect of SiC whisker. Analysis of SEM and X-ray data revealed that whisker bridging in the crack wake and whisker pull-out mechanisms were the main mechanism for the R-curve behaviour.