• 한국세라믹학회지
• /
• 제28권9호
• /
• pp.661-666
• /
• 1991

Microstructure, room temperature resistivity and temperature coefficient of resistance of BaTiO3 ceramics were studied by varying cooling rates and additives such as TiO2, SiO2 and Al2O3. The basic composition of the BaTiO3 ceramics was formed by adding 0.25 mol% Dy2O3 and 0.07 mol% MnO2 to the BaTiO3 composition. Unlike the additives of SiO2 and Al2O3, an addition of 2 mol% TiO2 to the basic composition was effective to control the grain size of the fired specimens. The room temperature resistivity and the temperature coefficient of resistance for the specimen of this particular compostion were measured as about 102 ohm.cm and 16.5%/$^{\circ}C$, respectively. The observed grain boundary phase of the sample with Al2O3 additive was BaTi3O7, while that of the samples with SiO2 additive was confirmed as BaTiSiO5.

• 한국세라믹학회지
• /
• 제20권1호
• /
• pp.25-30
• /
• 1983

This experiment was studied in the system of (1-x) CaO MgO $2SiO-Al_2O_3$ to investigate forming of solid solution. The technique empolyed was the well known water-quenching method. Differential thermal analysis of the each glass water quenched indicated that under 30 mole% $Al_2O_3$ was lowered with increasing of the amount of $Al_2O_3$ It was supposed by X-ray diffraction patterns of each specimen sintered at various temperature that only solid solution was formed under the 30mole % $Al_2O_3$ compositions solid solution and anorthite were formed at the 20mole% $Al_2O_3$ composition anorthite solid solution and spinel$(MgAl_2O_4)$ were formed over the 40mole% $Al_2O_3$ compositions. The maximum density and thermal expanison coefficient was 2.89g/cm 7.74x106./C$^{\circ}$ respectively in the composi-tion of 10 mole% $Al_2O_3$ . All the specimens showed linear thermal expansion behavior. Microhardness was as high as 850kg/nm2 in the composition of 5, 10, 20 mole % $Al_2O_3$ and dielectric constant was 7.3-6.9.

• 한국세라믹학회지
• /
• 제33권11호
• /
• pp.1267-1275
• /
• 1996

Green sheet was prepared by tape casting in the composition of (1-x)Pb(Mg1/3Nb2/3)O3-PbTiO3 system using Pb(Mg1/3Nb2/3)O3 and PbTiO3 synthesized with PbO, Nb2O5 MgO and TiO2 The densest green sheet was obtained in the weight ratio 70:30 of powder to binder. Green sheet wasmultilayered in metal mould and formed into lamination at 7$0^{\circ}C$, 300kg/cm2 The lamination was sintered at 110$0^{\circ}C$ 2hr, Dielectric constant and Curie temperature of disc type sintered body was highered with increasing the amount of PbTiO3 and was in the range of 19000-21000, -7~45$^{\circ}C$ respectively. Green and sintered relative density of lamination was 61% and 95% respectively.

• 한국안광학회지
• /
• 제8권1호
• /
• pp.7-10
• /
• 2003

4성분 $SrO-B_2O_3-Al_2O_3-SiO_2$ 유리들을 $R({\equiv}SrO\;mole%/B_2O_3\;mole%)$과 $K({\equiv}(Al_2O_3+SiO_2)\;mole%/B_2O_3\;mole%)$에 의하여 제작하여 적외선 흡수(Infrared absorption)을 이용하여 유리들의 구조를 조사하였다. R의 증가에 따라 $1,200{\sim}1,600cm^{-1}$ 영역에서 대칭적 3배위 구조인 $BO_3$ 단위구조에 의한 B-O 결합의 신축떨기(stretching vibration)에 의한 흡수 띠의 세기가 감소되어지며, 사면체 구조인 $BO_4$ 단위구조에 의한 B-O 결합의 신축떨기에 의한 흡수 띠의 세기는 $800{\sim}1,200cm^{-1}$ 영역에서 변화되어졌다. 그라고 K의 증가에 따라 대칭적 3배위 구조인 $BO_3$ 단위구조에 의한 B-O 결합의 신축떨기에 의한 흡수 띠의 세기는 증가되어지며, 사면체 구조인 $BO_4$ 단위구조에 의한 B-O 결합의 신축떨기에 의한 흡수 띠의 세기가 감소되어졌다.

• Korean Chemical Engineering Research
• /
• 제45권3호
• /
• pp.298-303
• /
• 2007

오존을 중심으로 한 다양한 조합의 고급산화 공정(advanced oxidation process: AOP)을 이용하여 2,4,6-trinitrotoluene (TNT) 제조 공정에서 발생되는 난분해성 폐수인 red water(RW)의 유기물 및 색도 제거 연구를 수행하였다. 적용된 고급산화 공정은 $O_3$, $UV/O_3$, $UV/O_3/H_2O_2$, $UV/O_3/H_2O_2/Fe^{2+}$ 공정이었으며, 유기물 및 색도 제거 효과는 $O_3 < $UV/O_3/H_2O_2/Fe^{2+}$ 공정의 순서로 나타났다. $UV/O_3/H_2O_2/Fe^{2+}$ 공정에서 최적 분해조건은 오존 유량 0.053 g/min, $H_2O_2$ 주입농도 10 mM, $FeSO_4$ 주입농도 0.1 mM로 나타났으며, 90 min 동안 유기물 및 색도 제거율은 각각 96, 100%로 나타났다. tert-butyl alcohol(t-buOH)을 이용한 수산화 라디칼(hydroxyl radical : ${\cdot}OH$)의 scavenging 실험을 통해 오존에 UV, $H_2O_2$, $FeSO_4$를 산화제로 조합함으로써 수산화 라디칼의 발생량을 더욱 증가시키고 유기물 제거율을 효과적으로 향상시킬 수 있음을 확인하였다.

• ETRI Journal
• /
• 제18권1호
• /
• pp.15-27
• /
• 1996

The effects of $Nd_2O_3$ and $TiO_2$ addition on the microstructures and microwave dielectic properties of $BaO-Nd_2O_3-TiO_2$ system were investigated. $BaNd_2Ti_4O_{12}$ or $BaNd_2Ti_{5}O_{14}$ phases were observed for compositions based on BaO/$Nd_2O_3$ = 1 ratio. The compositions deviated from $BaO/Nd_2O_3=1$ ratio were composed of major phases of $BaNd_2Ti_4O_{12}$ or $BaNd_2Ti_5O_{14}$, and the compound of $Nd_2O_3$ and $TiO_2(Nd_2Ti_2O_7)$ or that of BaO and $TiO_2(BaTi_4O_9)$. The microstructure of ceramic with $BaO{\cdot}Nd_2O_3{\cdot}4TiO_2$ composition varied from spherical grains to needlelike grains with increasing sintering temperature. With increasing $Nd_2O_3$, the optimum sintering temperature with maximum density increased, and the dielectric constant(${\varepsilon}_r$) and quality factor(Q) decreased due to the formation of secondary phases. With increasing $TiO_2$, the optimum sintering temperature and the dielectric constant decreased with increased Q value. And the temperature coefficient of resonant frequency, ${\tau}_f$ shifted toward positive direction. The dielectric ceramics with $BaO/Nd_2O_3=1$ showed Q values of above 2000 and dielectric constants of above 80 at 3GHz.

• 한국세라믹학회지
• /
• 제25권3호
• /
• pp.251-260
• /
• 1988

$10Li_2O$.$(90-x)B_2O_3$.$xSiO_2$ 기초유리에 $Al_2O_3$ 또는 $MoO_3$를 첨가한 유리를 열처리한 후 열수 또는 산처리하여 이온교환성 다공질 유리를 제조하였다. 그리고 $Al_2O_3$ 또는 $MoO_3$ 첨가가 분상과 양이온교환능(CEC)에 미치는 영향을 조사하였다. 이들 유리의 분상최적조건은 48$0^{\circ}C$, 10시간 열처리하였다. 분상은 $Al_2O_3$ 10mol%까지는 급격히 억제되고 그 이후에는 분상억제 효과가 완화되었다. 양이온교환능의 최대값은 $1OLi_2O$.$45B_2O_3$.$45SiO_2＋7.5Al_2O_3$ 조성유리를 열수처리한 다공질유리에서 약 252meq/100g을 나타냈으며 이 유리의 세공평균반경은 약 16.3A이었다. $MoO_3$ 첨가는 분상과 용출속도를 증가시켰다. $MoO_3$첨가에 의해 다공질유리의 세공반경과 세공용적이 크게 증가하는 것으로 보아 $MoO_3$는 유리의 붕산염상중의 실리카 농도를 낮추고 용출처리중 실리카를 수용성 착체로 형성시키는 효과가 있다고 생각된다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2001년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.118-120
• /
• 2001

The $0.96MgTiO_3-0.04SrTiO_3+xLa(0{\sim}1.0wt%)$ ceramics were prepared by conventional mixed oxide method. The structural properties of $0.96MgTiO_3-0.04SrTiO_3+xLa(0{\sim}1.0wt%)$ ceramics with sintering temperature were investigated by the XRD and SEM. From the X-ray diffraction patterns, it was found that the perovskite $SrTiO_3$ and ilmenite $MgTiO_3$ structures were coexisted in the $0.96MgTiO_3-0.04SrTiO_3$ ceramics. The second phase of $Sr_{0.5}LaTi_2O_6$ was shown with addition of the $La_2O_3$. The dielectric constant(${\varepsilon}_r$), $Q{\times}f$ value and the temperature coefficient of the $0.96MgTiO_3-0.04SrTiO_3+0.2La$ ceramics were 21. 41, 39991, $-3.3ppm/^{\circ}C$, respectively.

• The Korean Journal of Ceramics
• /
• 제5권3호
• /
• pp.260-264
• /
• 1999

Effect of the particle size of $MgTiO_3$ and $CaTiO_3$ on the microstructural evolution during sintering of $0.93MgTiO_3-0.07CaTiO_3$ system was investigated. Microwave dielectric characteristics of the sintered ceramics were also measured. The microstructural evolutions were explained with an emphasis on the entrapping behavior of $CaTiO_3$ grain into the $MgTiO_3$ grain and were correlated with microwave dielectric characteristics. With an increasing particle size ratio between $CaTiO_3$and $MgTiO_3$, the fraction of entraped $CaTiO_3$ grains increased, which grain growth of $MgTiO_3$were concurrently accelerated due to decreasing drag force of its boundary migration. Besides, $CaTiO_3$-grain entrapment into the $MgTiO_3$grain interior led to decreaseing quality factor values.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.323-323
• /
• 2007

Influence of $La_2O_3$ addition to $CaO-B_2O_3$-based glass on the water leaching resistance of the glass was first investigated. The optimized $La_2O_3-CaO-B_2O_3$(LCB) glass was ball milled for varying time, followed by mixing with $Al_2O_3$ crystalline phase to form $Al_2O_3$-LCB glass composites at $875^{\circ}C$ for 1h. Microwave dielectric properties of the composites were investigated as a function of the ball milling time of the LCB glass. Dielectric constant and quality factor of the composites were 6.31 and 13856 GHz, respectively, when the LCB glass was ball milled for 2h prior to mixing with $Al_2O_3$.