• International Journal of Precision Engineering and Manufacturing
• /
• v.3 no.3
• /
• pp.69-75
• /
• 2002

Measuring dynamic fracture toughness of brittle and small ceramic specimen is very difficult in a SHPB (Split Hopkinson Pressure Bar). As a countermeasure to this difficulty, a dynamic fracture toughness measuring method by the Chevron-notch ceramic specimen was proposed. Tested chevron specimens were of Chevron notch angles of 90$^{\circ}$, 100$^{\circ}$ and 110$^{\circ}$. Through finite element analysis, shape parameters of the Chevron-notch specimens according to notch angles were calculated. And the static fracture tough1ess of the Chevron-notch alumina specimen was measured as 3.8MPa√m similar to that of CT specimen with a precrack. Dynamic fracture toughness was 4.5MPa√m slightly higher than the static one. It was shown in this study that the proposed Chevron-notch specimens are valid to measure dynamic fracture toughness of extremely brittle materials such as ceramic.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1358-1361
• /
• 2003

In this study, intrinsic static/dynamic fracture toughness of Al 7175-T74 are evaluated from the apparent static/dynamic toughness of notched specimen. The notch/crack critical average stress fracture model is suggested to establish the relationship to predict the intrinsic fracture toughness from the apparent fracture toughness of a notched specimen. The notch/crack critical average stress fracture model is established using the relation between the notch root radius and the effective distance calculated by finite element analysis. It is conclude that the true fracture toughness can be estimated from test results of apparent fracture toughness measured by using a notched specimen. Also, critical notch root radius can be predicted by notch/crack critical average stress fracture model.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.11a
• /
• pp.933-937
• /
• 1996

In this paper, the behavior of plastic zone in the notch tip was studied under Loye's Micro Vickers Hardness Measurement Method. The direction forming maximum plastic zone was estimated by finite element analysis. In the experiments, cold rolling sheet SGCD3, SK5 and hot rolling sheet SS41, S4SC was used to study the influence of carbon contents on plastic zone. The standard hardness test specimen and the notch hardness test specimen was made and loaded cyclically. The specimen was aged to stabilize the hardness. After aging treatment, the notch specimen was made and simple tension load of 50% yield strength was applied. The hardness test at the notch tip until the hardness data of standard hardness specimen was checked was performed.

• Journal of the Korean Ceramic Society
• /
• v.34 no.10
• /
• pp.1053-1059
• /
• 1997

The dynamic fatigue behavior of alumina ceramics was observed at room temperature using four point bending system. The dynamic fatigue fracture strength and the dynamic fatigue lifetime were observed as a function of crosshead speed and the notch length. The notched specimen showed the smaller deviation in dynamic fatigue fracture strength than the unnotched specimen. The crack growth exponent n and the material constant A of the notched specimen could be represented as functions of the notch length. Fracture strength of the specimen calculated from the notch length, when the notch length was regarded as the crack size, was in good agreement with the measured 4 point bending strength. Fracture surface of the specimen showed the different fracture modes according to the crosshead speed. The four point flexural strength, fracture toughness, Young's modulus and Weibull modulus of the alumina were measured as 360 MPa, 3.91 MPa.m1/2, 159GPa, 17.64, respectively.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2002.10a
• /
• pp.58-63
• /
• 2002

This study has performed rotary bending fatigue testing that smooth specimen using SM45C materials and notched specimen whose radii were R6, R4 and R2, were processed in 3% NaCl aqueous solutions or in the air. The results are as followed; 1. In the air fatigue limit at 10$^{7}$ cycles remarkably reduced as notch radius goes small. 2. In 3% NaCl aqueous solution fatigue strength at 10$^{6}$ cycles also had large range of reduction as notch radius goes small. 3. Comparing fatigue strength in the air, fatigue strength at 10$^{6}$ cycles in 3% NaCl aqueous solution reduced by 46.2% at smooth specimen, 55.3% at R6 notch radius, 45.8% at R4 and 39.7% at R2 respectively. 4. The reason that fatigue strength reduced in the reduction of notch radius sire was because the surface of notch exposed in corrosion was small and consequently it was less corroded.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.7 no.6
• /
• pp.135-143
• /
• 1999

This investigation evaluates effects of notch depth, fatigue precrack length and side groove in impact specimen for estimation of a valid K1d by instrumented Charpy impact test. Specimen material is 6005-T6. for notch depth 2.0mm and 2.5mm specimens or within about 2mm fatigue precrack length with notch depth 2.0mm and 2.5mm specimens or within about 2mm fatigue precrack length with notch depth 2.0mm , dynamic fracture toughness [$K_{1d,(1)}$] obtained by crack initiation load($P_m$) should be used. Dynamic fracture toughness of side grooved specimens are overestimated to that of standard impact specimen about 15 %-20%. It is confirmed that the formula of dynamic fracture toughness obtained by impact absorbed energy is inappropriate for ductile materials.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.1-6
• /
• 2004

In this study, the intrinsic static/dynamic fracture toughness of Al 7175=T74 is evaluated from the apparent static/ dynamic toughness of notched specimen, The critical average stress fracture model is suggested to establish the relationship to predict the intrinsic fracture toughness from the apparent fracture toughness of a notched specimen. The critical average stress fracture model is established using the relation between the notch root radius and the effective distance calculated by finite element analysis. Also, effective distance is applied to estimate the failure criterion for the combustion pipe with notch. It is conclude that the true fracture toughness can be estimated from test results of apparent fracture toughness measured by using a notched specimen. Also, the effective In this study, the intrinsic static/dynamic fracture toughness of Al 7175=T74 is evaluated from the apparent static/ dynamic toughness of notched specimen, The critical average stress fracture model is suggested to establish the relationship to predict the intrinsic fracture toughness from the apparent fracture toughness of a notched specimen. The critical average stress fracture model is established using the relation between the notch root radius and the effective distance calculated by finite element analysis. Also, effective distance is applied to estimate the failure criterion for the combustion pipe with notch. It is conclude that the true fracture toughness can be estimated from test results of apparent fracture toughness measured by using a notched specimen. Also, the effective distance can be used to evaluate the failure criterion of structure with notch.

• 연구논문집
• /
• s.32
• /
• pp.55-64
• /
• 2002

Performance demonstration with real flawed specimens has been strongly required for nondestructive evaluation of safety class components in nuclear power plant. Specimen has been designed to produce mechanical fatigue flaw with tension stress and fatigue flaw has been produced to control stress and cycle, for suitable roughness. Notch condition is considered for control of fracture mode. After seal welding for fracture surface, final welding was performed to complete flaw specimen with GTAW(Gas Tungsten Arc welding) and FCAW(Flux Cored Arc Welding). It was demonstrated flaw size of flawed specimen by radiographic. testing and ultrasonic testing.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.706-711
• /
• 2007

Numerical studies were performed to examine the effects of notch location of impact specimens on the failure behavior of HAZ (heat affected zone) when Charpy V-notch impact test were made at a low temperature ($1^{\circ}C$). Carbon steel plate (SA-516 Gr. 70) with thickness of 25mm for pressure vessel was welded by SMAW (shielded metal-arc welding) and specimens were fabricated from the welded plate. Charpy tests were then performed with specimens having different notch positions of specimens varying from the fusion line through HAZ to base metal. A series of finite element analysis which simulates the Charpy test and crack propagation initiating at the tip of V-notch was carried out as well. The finite element analysis takes into account the irregular fusion line and non-homogenous material properties due to the notch location of the specimen in HAZ. Results reveals that the energies absorbed during impact test depend significantly on the notch location and direction of specimen. Finite element analysis also demonstrates that the notch location of specimens, to a great extent, influences the reliability and consistency of the test.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2003.05a
• /
• pp.160-163
• /
• 2003

In this study, intrinsic dynamic fracture toughness of 17-4PH casting steel is evaluated from the apparent dynamic fracture toughness of notched specimen. Notch radius of notched specimen is manufactured from 0.1mm to 4mm. The results shows that dynamic fracture toughness decreases with decreasing of notch root radius above critical notch roof radius. The true dynamic fracture toughness can be predicted from test results of apparent dynamic fracture toughness measured by using notched specimen.