• Journal of Korean Society for Atmospheric Environment
• /
• v.8 no.1
• /
• pp.58-67
• /
• 1992

For removing $NO_x$ and $SO_x$ from the flue gases emitted from stationary sources, $V_2O_5-MoO_3/TiO_2$ catalysts were prepared by the conventional impregnation method (aqueous solution) and a sort of surface fixation method(nonaqueous solution) as reported excellent reproducibility catalysts. And these catalysts observed their catalytic activities as well as their surface properties. V-Mo-O oxide, prepared from nonaqueous solution of $VOCl_3$ and $Mo(CO)_6$ and aqeous solution method, was supported as amorphous state by XRD and SEM measurements. The infrared spectra of fresh and used catalysts showed that in used catalysts, V=O bands decreased and new bands of vanadium oxysulfate bands were very sensitive. So the catalysts prepared from nonaqueous solution may bring about the high activity. Results from catalytic activity measurements at 350$^\circ$C, in the presence of $SO_2, NO$ conversion was more increased than in absence of $SO_2$. As the $MoO_3$ was added to $V_2O_5/TiO_2 system, SO_2$ conversion increased. It found that from the results, $V_2O-5-MoO_3/TiO_2$ catalysts prepared from an nonaqueous solution may bring about the high activity for both the reaction of NO and $SO_2$ removal.

• Journal of the Korean Chemical Society
• /
• v.9 no.4
• /
• pp.185-189
• /
• 1965

Korean acid clays and silica gel were put into action on benzene solution of dye, such as aniline yellow, o-nitro aniline and oil orange, and then the adsorptivity of dye in nonaqueous solution was measured, with the result that adsorptivity was greater with silica than acid clays and it had no relation to acidity. And when chemical compounds, such as amine, alcohol, halogen derivative, were added to each dye solution by 10%(in volume), the change of the adsorptivity of dye by solid acid(that is, the interfered adsorption rate) decreased in order of amine > alcohol > halogen derivative, and in homologue the smaller the molecular weight, the larger was the effect. So adsorption in nonaqueous solution was a selective adsorption of chemical compounds which contained negative groups such as amine and hydroxyl radicals, and it had no relation to surface tension and showed inverted phenomenon of Traube series. It is guessed that the inverted phenomenon (the interfered adsorption phenomenon) was due to the polar chemical adsorption between active $SiO_2$ which was an origin of solid acid and the adsorbed substances, considering that the order of inversion was nearly in accord with dipole moment of added solvents. The results of this study led to find adsorption mechanism and inverted phenomenon of Traube series in nonaqueous solution.

• Journal of the Korean Chemical Society
• /
• v.24 no.3
• /
• pp.209-217
• /
• 1980

The relative viscosities and osmotic coefficients of solutions of urea, 1,3-dimethyl-urea(DMU), acetamide(AA), and propionamide (PA) in dimethylsulfoxide(DMSO), water, methanol, and in ethanol have been measured at 25 and $45^{\circ}$C by viscometry and osmometry. Viscosity increment in nonaqueous solutions decreased with increasing of the partial molal volumes of the solutes, but in aqueous solution the result was inversed. Viscosity increment of aqueous solution was smaller than that of aqueous DMU solution, but that of nonaqueous urea solution was larger than that of DMU. Amides, however, showed similar viscosity increment in any solvent.Osmotic coefficients of aqueous solution of urea were larger than those of DMU. In the nonaqueous solutions urea exhibited larger deviation from Raoult's law than DMU. The results indicated that urea molecules break water-structure in water, self-associate in DMSO, and showed larger solute-solvent interaction in alcohols than DMU. It can be also confirmed that amides break alcohol structure to a greater extent than any other solutes.

• Bulletin of the Korean Chemical Society
• /
• v.19 no.2
• /
• pp.212-217
• /
• 1998

The electrochemistry and valence tautomerism of CoⅢ(N-N)(SQ)(Cat), [N-N=N,N,N',N'-tetramethylethylenediamine (TMEDA); SQ=3,5- or 3,6-di-tert-butyl-semiquinone, Cat=3,5- or 3,6-di-tert-butyl-catechol], have been investigated by spectroscopic, electrochemical, spectroelectrochemical methods in nonaqueous solvents under anaerobic condition. The transition temperature between tautomers is dependent upon the donation effect of substituted quinone ligand and solvent. It increases with the increase of donation effect of solvent and quinone ligand. CoⅢ(TMEDA)(SQ)(Cat) is reduced to [CoⅡ(TMEDA)(SQ)(Cat)]-, and then reduces to [CoⅡ(TMEDA)(Cat)2]2-. CoⅢ(TMEDA)(SQ)(Cat) is oxidized to [CoⅢ(TMEDA)(SQ)2]+, but the stability of the oxidized form in DMF is dependent upon the solution temperature. With the increase of solution temperatrue the oxidized form may be converted to [CoⅡ(TMEDA)(SQ)(BQ)]+ by intramolecular electron transfer from SQ ligand to CoⅢ.

• Analytical Science and Technology
• /
• v.7 no.3
• /
• pp.361-369
• /
• 1994

Voltammetric behavior of some light lanthanide ions($La^{3+}$, $Pr^{3+}$, $Nd^{3+}$, $Sm^{3+}$ and $Eu^{3+}$) in acetonitrile(AN) and dimethylformamide(DMF) has been investigated by direct current, differential pulse polarography and cyclic voltammetry. The reduction of $La^{3+}$, $Pr^{3+}$ and $Nd^{3+}$ in 0.1M TEAP proceeded directly to the metallic state through three-electron charge transfer of irreversible process where as $Sm^{3+}$ and $Eu^{3+}$ proceeded by charge transfer of two steps. As the results of the cyclic voltammetric investigation, the first step reduction of $Sm^{3+}$ and $Eu^{3+}$ were a quasireversible reaction, the second step reductions were an irreversible reaction. The cathodic peak currents of the differential pulse polarogram showed adsorptive properties at lower sweep rates and high concentrations of these metal ions. The peak potenital was shifted to a negative petential and the peak current decreased with the increase of percentage of water in AN. On the other hand, the peak potential was shifted to a positive potential and the peak current decreased with an increased percentage of water in DMF.

• Korean Journal of Crystallography
• /
• v.14 no.2
• /
• pp.67-72
• /
• 2003

Graphite powders were coated with ZrO₂ by the controlled hydrolysis of a DI water, ethanol and DI water+ethanol solutions. The hydrolysis process was carried out with temperature control because of the low wettability of Zr ions to the surface of the graphite. PVA was added to the solution for the enhancement of metal ion adsorption. The surface of the graphite powders coated with ZrO₂ was observed by SEM and TEM. There are two types of ZrO₂ particles with the condition of ZrOCl₂°§8H₂O aqueous solutions were used; (a) primary particles a few nm in size and (b) secondary particles with ∼0.1 ㎛ size were obtained. The graphite powders coated in 50% ethanol-50% DI water solution of Zr(SO₄)₂ㆍ4H₂O have the relatively uniform coating layer and the starting temperature of oxidation was 100℃ higher than the raw graphite.

• Bulletin of the Korean Chemical Society
• /
• v.20 no.9
• /
• pp.1049-1055
• /
• 1999

Electrochemical oxidation of silicon (p-type Si(100)) at room temperature in ethylene glycol and in aqueous solutions has been performed by applying constant low current densities for the preparation of thin SiO2 layers. In-situ ac impedance spectroscopic methods have been employed to characterize the interfaces of electrolyte/oxide/semiconductor and to estimate the thickness of the oxide layer. The thicknesses of SiO2 layers calculated from the capacitive impedance were in the range of 25-100Å depending on the experimental conditions. The anodic polarization resistance parallel with the oxide layer capacitance increased continuously to a very large value in ethylene glycol solution. However, it decreased above 4 V in aqueous solutions, where oxygen evolved through the oxidation of water. Interstitially dissolved oxygen molecules in SiO2 layer at above the oxygen evolution potential were expected to facilitate the formation of SiO2 at the interfaces. Thin SiO2 films grew efficiently at a controlled rate during the application of low anodization currents in aqueous solutions.

• Bulletin of the Korean Chemical Society
• /
• v.18 no.5
• /
• pp.496-500
• /
• 1997

Electrochemical behavior of mer-tris(2-pyridinethiolato)cobalt(Ⅲ) in dimethylformamide was studied on a platinum electrode by means of cyclic voltammetry, chronoamperometry, and chronocoulometry. It was found that the neutral complex molecule was electroactive between the potential region of 1.0 and - 1.2 V vs. a nonaqueous Ag/Ag+ electrode. The Co(Ⅲ) complex was reversibly reduced to Co(Ⅱ) species by one-electron transfer at about - 1.1 V, followed by an irreversible dissociation reaction. However, the oxidation process at around 0.8 V, was responsible for an irreversible two-electron transfer that occurred at a ligand site.

• Proceedings of the KIEE Conference
• /
• 1996.07c
• /
• pp.1498-1501
• /
• 1996

To evaluate insulating properties of polyimide thin film on high temperature over $100\;^{\circ}C$, polyimide film were prepared by electrophoretic deposition onto metal surface from nonaqueous emulsion. The emulsion is made by adding a solution of the resin to a precipitant, which is an organic liquid compeltely miscible with the solvent of the organic resin solution, but which does not dissolve the resin. The polyimide film obtained by annealing shows good insulation properties of 5.8 MV/cm at elevated temperature and breakdown strength of the film reveals thickness dependence.

• Journal of the Korean Chemical Society
• /
• v.65 no.2
• /
• pp.125-132
• /
• 2021

An electrochromic nickel oxide thin film was fabricated on a flexible PET/ITO substrate using a nanocrystallite- dispersed coating sol and bar coater. Nanocrystalline NiOx of 3-4 nm crystallite size was first synthesized by base precipitation and thermal conversion. This NiOx nanocrystallite powder was mechanically dispersed in an alcoholic solvent mixed with a silane binder to prepare a coating sol for thin film. This sol method is different from the normal sol-gel method in that it does not require the conversion of precursor by heat treatment. Therefore, this method provides a very facile method to prepare NiOx thin films on any kind of substrate and it can be easily applied to mass production. The electrochromic performance of this NiOx thin film on PET/ITO electrode with a thickness of about 400 nm was investigated in a nonaqueous LiClO4 electrolyte solution by cyclic voltammetric and repeated chronoamperometric measurements in conjunction with spectrophotometry. The visible light modulation of 44% and the colorization efficiency of 41 ㎠/C at 550 nm were obtained at the step potentials of -0.8/+1.2 V vs Ag and a duration of 30 s.