• Carbon letters
• /
• v.1 no.3_4
• /
• pp.133-137
• /
• 2001

Mesoporous activated carbon fiber (ACF) was prepared from phenolic resin containing a small amount (0.1 wt %) of organic nickel complex through carbonization and steam activation. Microporous ACF as reference sample was also prepared from phenolic resin without agent. In both cases of the mesoporous ACFs and the microporous ACFs, the electric double layer capacitance of the nonaqueous electrolyte (0.5 M $TEABF_4$/PC or 1.0 M $LiClO_4$/PC) was not proportional to the BET specific surface area. This is owing to the low permeability of nonaqueous electrolyte or the low mobility of ion in narrow micropores. However, the mesoporous ACF showed higher double layer capacitance than the microporous (normal) ACF. This result suggests that the presence of many mesopores promotes the formation of effective double layer or the transfer of ion in the micropore.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.4
• /
• pp.192-196
• /
• 2002

Ionic liquids based on l-ethyl-3-methylimidazolium cation $(EMI^+)$ and inorganic or organic anions containing fluorine atoms were applied to electrolyte materials for double-layer capacitors. The double-layer capacitors composed of a pair of activated carbon electrodes and an ionic liquid selected from $EMIBF_4,\; EMINbF_6,\;EMITaF_6,\;EMICF_3SO_3,\;EMI(CF_3SO_2)_2N,\;and\;EMI(C_2F_5SO_2)_2N$ showed inferior low-temperature characteristics to those of a conventional nonaqueous electrolyte based on propylene carbonate (PC) solvent. On the other hand, the capacitor using $EMIF{\cdot}2.3HF$ showed excellent low-temperature characteristics due to its high conductivity at low temperatures, however, it had a lower working voltage $(\~2V)$ than the conventional nonaqueous counterpart $(\~3V)$.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.3
• /
• pp.329-334
• /
• 2011

The electrochemical performances of an asymmetric hybrid capacitor were investigated using $LiFePO_4$ as the positive electrode and active carbon fibers(ACF) as the negative electrode. The electrochemical behaviors of a nonaqueous hybrid capacitor were characterized by constant current charge/discharge test. The specific capacitance using $LiFePO_4$/ACF electrode turned out to be $0.87F/cm^2$ and the unit cell showed excellent cycling performance. This hybrid capacitor was able to deliver a specific energy as high as 178 Wh/kg at a specific power of 1,068 W/kg.

• Journal of the Korean Chemical Society
• /
• v.15 no.4
• /
• pp.211-217
• /
• 1971

The theory of solubility proposed by Jhon and Kihara has been tested and applied to various systems. In the present paper, the systems are the solubilities of gases such as $Ar,\;H_2,\;N_2,\;O_2,\;CO_2,\;CH_4,\;and\;C_2H_6$ in liquid benzene and carbon disulfide, those of solids iodine and naphthalene in the nonaqueous solvents, and those of gases $H_2,\;N_2,\;O_2,\;Ar,\;CH_4,\;and\;C_2H_4$ in the electrolyte solutions. The theoretical values of solubilities are in good agreement with the experimental data in the literature.

• Bulletin of the Korean Chemical Society
• /
• v.20 no.9
• /
• pp.1049-1055
• /
• 1999

Electrochemical oxidation of silicon (p-type Si(100)) at room temperature in ethylene glycol and in aqueous solutions has been performed by applying constant low current densities for the preparation of thin SiO2 layers. In-situ ac impedance spectroscopic methods have been employed to characterize the interfaces of electrolyte/oxide/semiconductor and to estimate the thickness of the oxide layer. The thicknesses of SiO2 layers calculated from the capacitive impedance were in the range of 25-100Å depending on the experimental conditions. The anodic polarization resistance parallel with the oxide layer capacitance increased continuously to a very large value in ethylene glycol solution. However, it decreased above 4 V in aqueous solutions, where oxygen evolved through the oxidation of water. Interstitially dissolved oxygen molecules in SiO2 layer at above the oxygen evolution potential were expected to facilitate the formation of SiO2 at the interfaces. Thin SiO2 films grew efficiently at a controlled rate during the application of low anodization currents in aqueous solutions.

• Journal of the Korean Chemical Society
• /
• v.36 no.5
• /
• pp.709-719
• /
• 1992

We synthesized the binuclear tetradentate Schiff base cobalt(II), nickel(II) and copper(II) complexes such as [Co(II)_2(TSBP)(L)_4], [Ni(II)_2(TSBP)(II)_4] and [Cu(II)_2(TSBP)] (TSBP: 3,3',4,4'-tetra(salicylideneimino)-1,1'-biphenyl, L: Py, DMSO and DMF). We identified the binucleated structure of these complexes by elemental analysis, IR-spectrum, UV-visible spectrum, T.G.A. and D.S.C. According to the results for cyclic voltammogram and differential pulse polarogram of 1 mM complexes in nonaqueous solvents included 0.1M TEAP-L (L; Py, DMSO and DMF) as supporting electrolyte, it was found that diffusionally controlled redox processes of four steps through with one electron for binucleated Schiff base Cobalt(II) complex was Co(III)_2 {^\longrightarrow \\_\longleftarrow^e^-}Co(III)Co(II)_2{^\longrightarrow \\_\longleftarrow^e^-}Co(II){^\longrightarrow \\_\longleftarrow^e^-}Co(I){^\longrightarrow \\_\longleftarrow^e^-}Co(I)_2 and two steps with one electron for Nickel(II) and Copper(II) complexes were M(II)_2 {^\longrightarrow \\_\longleftarrow^e^-}M(I)M(I){^\longrightarrow \\_\longleftarrow^e^-}M(I)_2 (M; Ni and Cu) in nonaqueous solvents.

• Journal of the Korean Electrochemical Society
• /
• v.22 no.3
• /
• pp.87-103
• /
• 2019

Nonaqueous organic electrolyte solution in commercially available lithium-ion batteries, due to its flammability, corrosiveness, high volatility, and thermal instability, is demanding to be substituted by safer solid electrolyte with higher cycle stability, which will be utilized effectively in large-scale power sources such as electric vehicles and energy storage system. Of various types of solid electrolytes, composite solid electrolytes with polymer matrix and active inorganic fillers are now most promising in achieving higher ionic conductivity and excellent interface contact. In this review, some kinds and brief history of solid electrolyte are at first introduced and consequent explanations of polymer solid electrolytes and inorganic solid electrolytes (including active and inactive fillers) are comprehensively carried out. Composite solid electrolytes including these polymer and inorganic materials are also described with their electrochemical properties in terms of filler shapes, such as particle (0D), fiber (1D), plane (2D), and solid body (3D). In particular, in all-solid-state lithium batteries using lithium metal anode, the interface characteristics are discussed in terms of cathode-electrolyte interface, anode-electrolyte interface, and interparticle interface. Finally, current requisites and future perspectives for the composite solid electrolytes are suggested by help of some decent reviews recently reported.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.3
• /
• pp.159-168
• /
• 2007

An electrochemical study related to the redox characteristics of Ethyl-3-acetyl-6-methyl-1, 4-diphenyl-4, 3a-dihydro-1, 3, 4-triazolino[3, 4-a] pyrimidine-5-carboxylate ester and its derivatives (1a-f) and (2a-e) in nonaqueous solvents such as 1, 2-dichloroethane (DCE), dichloromethane (DCM), acetonitrile (AN), dimethylsulphoxide (DMSO) and tetrahydrofurane (THF) using $0.1\;mol\;dm^{-3}$ tetrabutylammonium perchlorate (TBAP) as a supporting electrolyte at platinum, glassy carbon and gold electrodes, has been performed using cyclic voltammetry (CV). Controlled potential electrolysis (CPE) is also carried out to elucidate the course of different electrochemical reactions through the separation and identification of the intermediates and final electrolysis products. The redox mechanism is suggested and proved. It was found that all the investigated compounds in all solvents are oxidized in a single irreversible one electron donating process following the well known pattern of the EC-mechanism to give a dimer. On the other hand, these compounds are reduced in a single irreversible one electron step to form the anion radical, which is basic enough to proton from the media forming the radical which undergoes tautomerization and then dimerization processes to give also another bis-compound through N-N linkage formation.

• Journal of Electrochemical Science and Technology
• /
• v.5 no.2
• /
• pp.58-64
• /
• 2014

The surface of an ordered mesoporous silica (OMS) was functionalized using 1H,1H,2H,2H-perfluorooctyltrimethoxysilane at $20^{\circ}C$ and $60^{\circ}C$. It was shown that only elevated temperature allows lyophobic properties on the walls of OMS, eventually preventing pore flooding with nonaqueous electrolytes. The functionalized OMSs (OMS-F) were characterized with various techniques: wettability test, $N_2$ sorption measurement, high-resolution transmission electron microscopy (HR-TEM). Cathodes of $10mg/cm^2$ loading were prepared with a commercial Pt/C catalyst and polyvinylidene fluoride (PVDF, 2.5 wt.%) binder using a typical doctor blade method on a commercial gas diffusion layer (GDL) in the presence or in the absence of OMS-F additives. Subsequent discharge-charge curves were taken in a 1M LiTFSI-TEGDME electrolyte at 60oC in pure oxygen atmosphere. It was found that the discharge capacity was significantly affected by OMS-F: 5 wt.% of additive extended discharge capacity by a factor 1.5. On the other hand, a similar OMS material but synthesized at $20^{\circ}C$ did not show lyophobic properties and deteriorated cathode capacity.

• Journal of the Korean Chemical Society
• /
• v.65 no.2
• /
• pp.125-132
• /
• 2021

An electrochromic nickel oxide thin film was fabricated on a flexible PET/ITO substrate using a nanocrystallite- dispersed coating sol and bar coater. Nanocrystalline NiOx of 3-4 nm crystallite size was first synthesized by base precipitation and thermal conversion. This NiOx nanocrystallite powder was mechanically dispersed in an alcoholic solvent mixed with a silane binder to prepare a coating sol for thin film. This sol method is different from the normal sol-gel method in that it does not require the conversion of precursor by heat treatment. Therefore, this method provides a very facile method to prepare NiOx thin films on any kind of substrate and it can be easily applied to mass production. The electrochromic performance of this NiOx thin film on PET/ITO electrode with a thickness of about 400 nm was investigated in a nonaqueous LiClO4 electrolyte solution by cyclic voltammetric and repeated chronoamperometric measurements in conjunction with spectrophotometry. The visible light modulation of 44% and the colorization efficiency of 41 ㎠/C at 550 nm were obtained at the step potentials of -0.8/+1.2 V vs Ag and a duration of 30 s.