Titanium nitride(TiN) has been synthesized by nitrogen ion irradiation onto the Ti thin film deposited on STD11 and SKH9 tool materials. The effect of irradiation flux and substrate temperature on the formation behavior and mechanical properaties of TiN were investigated through X-ray diffraction analysis, hardness and pin-on-disc wear testings. Nitrogen ion irradiation onto arc evaporated Ti thin film produced TiN of < 200> orientation at elevated temperature and thereby enhancing surface microhardness by 50% at maximum. Wear resistance was also improved by nitrogen irradiation at most process conditions. The enhancement of wear resistance appeared to be more effective for the nitrogen irradiated conditions at room temperature than at elevated temperature.

• 설비공학논문집
• /
• 제29권12호
• /
• pp.621-627
• /
• 2017

Nitrogen ion with various levels of dose and irradiation energy was irradiated on aluminum surfaces. Contact angle of surface was increased and surface color was changed by nitrogen ion implantation. During steam condensation experiment using nitrogen ion implanted specimen, dropwise condensation initially occurred on specimens. However, condensation mode eventually changed into filmwise condensation. The color of the surface was also changed from yellow-brown to silver-white. This change of surface color and condensation mode were results of hydrolysis reaction between condensate and nitrogen ion implanted on aluminum surfaces.

• 한국재료학회지
• /
• 제16권6호
• /
• pp.367-372
• /
• 2006

Polytetrafluoroethylene (PTFE) surface was modified for improving hydrophilicity by ion irradiation in environmental gas of $N_2$ and $NH_3$, respectively. The water contact angle onto the PTFE surface increased from $104{\circ}$ to over $140{\circ}$ by Ar ion irradiation in $N_2$ gas. In the case of $NH_3$ as environmental gas, there were a slight increase of contact angle from ion dose of $1{\times}10^{15}\;to\;5{\times}10^{15}\;ions/cm^2$, and its dramatic decrease to the value of 35o at the conditions of ion dose higher than $1{\times}10^{16}\;ions/cm^2$. It was found from SEM results that the surface morphology of PTFE was changed into one with filament structure after Ar ion irradiation in $N_2$ gas environments. On the contrary, Ar ion irradiation in $NH_3$ gas condition induced the PTFE surface with network structure. Hydrogen ion irradiation resulted in a little change of PTFE surface morphology, comparing with the case of Ar ion irradiation. The water contact angle of hydrogen ion irradiated PTFE surface in reactive gas decreased with increment of ion dose. Hydrogen ion irradiation could improve hydrophilicity with little change of surface morphology. It might be considered from FT-IR results that the improvement in wettability of PTFE surface by ion irradiation in $N_2$ and $NH_3$ gases could be due to the hydrophilic groups of NHx bonds.

• 방사선산업학회지
• /
• 제2권1호
• /
• pp.9-14
• /
• 2008

Livestock wastewater containing high concentrations of organic matters and ammonia-nitrogen has been known as one of the recalcitrant wastewater. It is difficult to treat by conventional wastewater treatment techniques. This study was carried out to evaluate the feasibility of zeolite ion exchange and gamma-ray irradiation treatment of livestock wastewater. The removal efficiencies of $SCOD_{Cr}$ and $NH_3-N$ were significantly enhanced by gamma-ray irradiation after zeolite ion exchange as a pre-treatment. However, the effects of zeolite particle size on the $SCOD_{Cr}$ and $NH_3-N$ removal efficiencies were insignificant. These results indicate that the combined process of zeolite ion exchange and gamma-ray irradiation has potential for the treatment of livestock wastewater.

• 한국인쇄학회지
• /
• 제12권1호
• /
• pp.81.1-91
• /
• 1994

Irradiation of aromatic diazonium salts resulted in an effcient elimination of nitrogen, yielding substitution products. This paper was not only studies about photolysis of aromatic diazonium with double salts but also coexistence of ion and radical when they was photolysis. Photolysis of aromatic diazonium was depend on excite wave length therefore photolysis products out put different absorption intensity such other. We also confirmed coexistence of ion and radical when they was accomplished photolysis. In case of BD, there are ion decomposition process about 90 percentage, decreased ion decomposition process the other side radical`s it was becomeing increased according to excite of short-wave length.

• Macromolecular Research
• /
• 제10권2호
• /
• pp.80-84
• /
• 2002

Silver species other than the silver ion were formed by UV irradiation on polymer electrolyte membranes containing silver salts and their effect on complexation behavior between the silver and olefin was investigated through the separation performance of olefin/paraffin mixtures. The ideal propylene/propane separation factor reached 350 and the separation coefficient was ca.15 due to the high loading amount of silver ions into poly(2-ethyl-2-oxazoline) (POZ) without UV irradiation. On UV irradiation either in air or under nitrogen, the silver-POZ membranes became yellow-brown initially due to the formation of colloidal silver particles, and finally black and metal-like luster. Even when Ag$^{+}$ was converted, to some extent, to Ag$^{\circ}$ by UV irradiation in air at the early stage, the separation coefficient of olefin/paraffin mixtures was maintained. This suggests that silver species other than the silver ion is active for olefin carrier for facilitated transport. Meanwhile the steady decrease of the separation coefficient was observed in the silver/POZ membranes irradiated under $N_2$. It is suggested that the reduction of silver ions in POZ goes through a different photoreduction mechanism with UV irradiation depending on the environment.t.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.1
• /
• pp.413-416
• /
• 2004

In this study, zinc oxide(ZnO) having large misfit(18.2%) with sapphire was tried to be grown on very thin nitride buffer layers. For the creation of various kinds of nitride buffer layer, sapphire surface was modified by an irradiation of nitrogen ion beam with low energy generated from stationary plasma thruster(SPT) at room temperature. After the irradiation of ion beam, Al-N and Al-O-N bonding was identified to be formed as nitride buffet layers. Surface morphology was measured by AFM and then ZnO growth was followed by pulsed laser deposition(PLD). Their properties are analyzed by XRD, AFM, TEM, and PL. We observed that surface morphology was improved and deep level emission related to defects was almost vanished in PL spectra from the ZnO grown on nitride buffer layer.

• 한국진공학회지
• /
• 제18권5호
• /
• pp.384-389
• /
• 2009

ZnO는 육방정계결정구조의 물질로서 3.37 eV의 넓은 띠 간격과 60 meV의 큰 exciton 결합에너지에 따른 높은 효율의 자외선발광으로 짧은 파장의 빛 (녹, 청, 자외선)을 내는 LED (Light Emitting Diode) 분야에서 관심을 기울이고 있는 물질이다. LED제작을 위해서는 n형의 ZnO와 p형의 ZnO가 필요하지만 기본적으로 ZnO은 n형이므로 신뢰성 있는 p형 ZnO박막을 제작하기 위한 노력이 기울여지고 있다. 본 연구에서는 ALD (Atomic Layer Deposition)로 제작된 ZnO박막에 20 keV의 에너지를 갖는 질소이온을 $10^{13}{\sim}10^{15}ions/cm^2$로 조사한 후 Hall 효과 측정장치를 이용하여 질소이온 조사에 따른 전기적 특성변화를 조사하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2010년도 제39회 하계학술대회 초록집
• /
• pp.90-90
• /
• 2010

We investigated the modification of optical response properties of titanium dioxide (TiO2) coatings on the ceramic water-purification filters by using ultraviolet-visible absorption spectroscopy and X-ray diffraction. The TiO2 coatings were prepared on ceramic substrate by e-beam evaporation method. These amorphous TiO2 were turned into anatase phase by heat treatment at $700^{\circ}C$ for 2 hours. The doping of N atoms into the TiO2 coatings was done by using 70KeV of N＋ ion implantation with the dose of $1.0{\times}1017$ ions/cm2, followed by post-irradiation heat treatment at $550^{\circ}C$ for 2 hours. Methylene blue test of TiO2 coatings to solar irradiation showed that the post-evaporation heated TiO2 was photocatalytic and N-doped TiO2 reacted to the visible part of solar irradiation.

• 열처리공학회지
• /
• 제24권2호
• /
• pp.77-81
• /
• 2011

Aluminum nitride (AlN) thin films were prepared by using nitrogen ion beam assisted reactive radio frequency (RF) magnetron sputtering on the glass substrates without intentional substrate heating. After deposition, the effect of nitrogen ion beam energy on the structural and optical properties of AlN films were investigated by x-ray diffraction (XRD), atomic force microscope (AFM) and UV-Vis. spectrophotometer, respectively. AlN films deposited with $N^+$ ion irradiation at 100 eV show the higher (002) peak intensity in XRD pattern than other films. It means that $N^+$ ion energy of 100 eV is the favorable condition for low temperature crystallization. AFM images also show that surface average roughness is increased from 1.5 to 9.6 nm with $N^+$ ion energy in this study. In an optical observation, AlN films which deposited by $N^+$ ion beam energy of 100 eV show the higher transmittance than that of the films prepared with the other $N^+$ ion beam conditions.