• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.6
• /
• pp.590-596
• /
• 2002

The resin : metal interface is at the basis of most bonding failures in resin-bonded prosthesis. Although debonding has been a problem with adhesive fixed partial dentures, various dentists classify them as long-term restorations. The advantages of resin-bonded fixed partial dentures include minimal tooth reduction and the possibility of rebonding. if resin-bonded protheses can be easily rebounded, it is of clinical importance to know if the lutingagents rebond as well the second time as they did originally. Several retentive systems for resin-to-metal bonding have recommended. Treatments such as electrolytic etching and silicone coating, despite the good result of bond strength, have proved to be time-consuming and technique-sensitive. Therefore a simple and more reliable method is desirable. This study evaluated the effect of metal surface treatments on the rebond strength of panavia 21 cement to a nickel-chromium(Ni-Cr) alloy. The samples were received the following surface treatments : Group No.1 (control or served as the control) treatment with sandblasting with 50um aluminum oxide and ultrasonically cleaned for 10minutes in double-deionized water, Group No.2 were no surface treatments. Group No.3 were treated with metal primer. Group No.4 were treated with sandblasting as previously described, and then metal priming. From the analysis of the results, the following conclusions were drawn. 1. Sandblasting and metal priming appears to be an effective method for treatment of metal after accidental debonding. 2. Group without surface treatment had significantly lower bond strengths compared with other groups. 3. The combination of sandblasting and metal priming may not develop superior bonding strengths compared with other techniques that used the Ni-Cr alloys. 4. Combination of cohesive and adhesive failures were the most common type observed. The results support the use of sandblasting as a viable procedure when rebonding accidentally lost adhesive partial denture. We concluded that sandblasting and metal priming of metal surface before bonding could provide the adequate bond strength during rebonding of resin-bonded fixed partial denture.

• Journal of the Korean Institute of Gas
• /
• v.13 no.5
• /
• pp.26-32
• /
• 2009

Ni catalysts on mesoporous silica and commercial silica were prepared for the methanation. XRD and TPR analyses indicated that Ni/mesoporous silica had smaller metal particle size and higher metal dispersion than that of Ni/commercial silica. In addition, Ni/mesoporous silica had stronger metal-support interaction. In methanation, Ni/mesoporous silica showed higher CO conversion and methane yield (65%) than Ni/commercial silica (58%). In the characterization results of catalysts after reaction, Ni/commercial silica was deactivated by the collapse of structure and metal sintering, but Ni/mesoporous silica showed stable catalytic performance.

• Current Applied Physics
• /
• v.18 no.11
• /
• pp.1240-1247
• /
• 2018

Magnetic hysteresis in Ni nanowire arrays grown by electrodeposition inside the pores of anodic alumina templates is studied as a function of temperature in the range between 5 K and 300 K. Nanowires with different diameters, aspect ratios, inter-wire distance in the array and surface condition (smooth and rough) are synthesized. These microstructure parameters are linked to the different free magnetic energy contributions determining coercivity and the controlling magnetization reversal mechanisms. Coercivity increases with temperature in arrays of nanowires with rough surfaces and small diameters -33 nm and 65 nm- when measured without removing the alumina template and/or the Al substrate. For thicker wires -200 nm in diameter and relatively smooth surfaces- measured without the Al substrate, coercivity decreases as temperature rises. These temperature dependences of magnetic hysteresis are described in terms of an effective magnetic anisotropy $K_a$, resulting from the interplay of magnetocrystalline, magnetoelastic and shape anisotropies, together with the magnetostatic interaction energy density between nanowires in the array. The experimentally determined coercive fields are compared with results of micromagnetic calculations, performed considering the magnetization reversal mode acting in each studied array and microstructure parameters. A method is proposed to roughly estimate the value of $K_a$ experimentally, from the hysteresis loops measured at different temperatures. These measured values are in agreement with theoretical calculations. The observed temperature dependence of coercivity does not arise from an intrinsic property of pure Ni but from the nanowires surface roughness and the way the array is measured, with or without the alumina template and/or the aluminum support.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.34 no.3
• /
• pp.92-97
• /
• 2024

To improve the efficiency of water splitting systems for hydrogen production, the high overvoltages of electrochemical reactions caused by catalysts in the oxygen evolution reaction (OER, Oxygen Evolution Reaction) must be reduced. Among them, LDH (Layered Double Hydroxide) compounds containing transition metal such as Ni, are attracting attention as catalyst materials that can replace precious metals such as platinum that are currently used. In this study, nickel foam, an inexpensive metallic porous material, was used as a support, and NiCo LDH (Layered Double Hydroxide) nanocrystals were synthesized through a hydrothermal synthesis process. In addition, changes in the shape, crystal structure, and water decomposition characteristics of the Mo-doped NiCo LDH nanocrystal samples synthesized by doping Mo to improve OER properties were observed.

• Applied Chemistry for Engineering
• /
• v.33 no.2
• /
• pp.202-209
• /
• 2022

Effects of the support and amount of NiCl₂ on ammonia adsorption capacity were investigated to improve the ammonia adsorption performance. NiCl₂ was impregnated onto the surface of various supports under ultrasonic irradiation. The physicochemical properties and ammonia adsorption performance of NiCl₂-impregnated adsorbents were investigated. Among the various supports, it was found that the adsorption capacity of ammonia was the best when NiCl₂ was impregnated on activated carbon (AC) with the highest specific surface area. As a result of changing the amount of NiCl₂ impregnated on AC, the NiCl₂(2.0)/AC adsorbent impregnated with 2 mmol·g^-1 of NiCl₂ showed the highest ammonia adsorption capacity of 5.977 mmol·g^-1. In addition, the adsorption capacity was found to be maintained at an almost constant level in five repeated cycle tests under the condition that low-temperature heat could be utilized. This indicates that the adsorbent has excellent regeneration ability.

• Applied Chemistry for Engineering
• /
• v.10 no.2
• /
• pp.237-241
• /
• 1999

Nickel was impregnated on the $SiO_2$ and $Al_2O_3$ supports and applied to the reduction reaction of CFC-113 ($CF_2Cl$-$CFCl_2$) with hydrogen to 3FCl ($CF_2$=CFCl, CFC-1113). The conversion was rapidly declined on the Ni/$SiO_2$(or $Al_2O_3$) and the deactivation accelerated as the increase of Ni content. However, the selectivity of 3FCl was maintained at around 80% level. The simultaneous coprecipitation of copper and lithium on Ni/$Al_2O_3$ improved both the conversion and selectivity to 3FCl, but an excessive amount of lithium reduced the conversion as well as the selectivity of 3FCl. However, in the case of Ni/$SiO_2$, the conversion was greatly reduced possibly due to a loss of silica support with high surface area by the reaction of $SiO_2$ with HF. Such a reduction in conversion also can be ascribed to the decrease in active sites, caused by the addition of alkali metal compound, LiOH.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.34 no.1
• /
• pp.30-35
• /
• 2024

In order to improve the efficiency of the water splitting system for hydrogen production, the high overvoltage in the electrochemical reaction caused by the catalyst in the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) must be reduced. Among them, transition metal-based compounds are attracting attention as catalyst materials that can replace precious metals such as platinum that are currently used. In this study, nickel foam, an inexpensive metal porous material, was used as a support, and Fe-doped β-Ni(OH)₂ microcrystals were synthesized through a hydrothermal synthesis process. In addition, in order to improve OER properties, changes in the shape, crystal structure, and water splitting characteristics of Fe-Mo co-doped β-Ni(OH)₂ microcrystals synthesized by co-doping with Mo were observed. The changes in the shape, crystal structure, and applicability as a catalyst for water splitting were examined.

• Applied Chemistry for Engineering
• /
• v.17 no.4
• /
• pp.349-356
• /
• 2006

We have investigated adsorption and desorption properties of CO adsorption on silica supported Ru/Ni alloys at various Ru/Ni mole content ratio as well as CO partial pressures using Fourier transform infrared spectrometer (FT-IR). For Ru-$SiO_{2}$ sample, four bands were observed at $2080.0cm^{-1}$, $2021.0{\sim}2030.7cm^{-1}$, $1778.9{\sim}1799.3cm^{-1}$, $1623.8cm^{-1}$ on adsorption and three bands were observed at $2138.7cm^{-1}$, $2069.3cm^{-1}$, $1988.3{\sim}2030.7cm^{-1}$ on vacumn desorption. For Ni-$SiO_{2}$ sample, four bands were observed at $2057.7cm^{-1}$, $2019.1{\sim}2040.3cm^{-1}$, $1862.9{\sim}1868.7cm^{-1}$, $1625.7cm^{-1}$ on adsorption and two bands were observed at $2009.5{\sim}2040.3cm^{-1}$, $1828.4{\sim}1868.7cm^{-1}$ on vacumn desorption. These absorption bands correspond with those of the previous reports approximately. For Ru/Ni(9/1, 8/2, 7/3, 6/4, 5/5; mole content ratio)-$SiO_{2}$ samples, three bands were observed at $2001.8{\sim}2057.7cm^{-1}$, $1812.8{\sim}1926.5cm^{-1}$, $1623.8{\sim}1625.7cm^{-1}$ on adsorption and three bands were observed at $2140.6cm^{-1}$, $2073.1cm^{-1}$, $1969.0{\sim}2057.7cm^{-1}$ on vacumn desorption. The spectrum pattern observed for Ru/Ni-$SiO_{2}$ sample at 9/1 Ru/Ni mole content ratio on CO adsorption and on vacumn desorption is almost like the spectrum pattern observed for Ru-$SiO_{2}$ sample. But the spectrum patterns observed for Ru/Ni-$SiO_{2}$ samples under 8/2 Ru/Ni mole content ratio on CO adsorption and vacumn desorption are almost like the pattern observed for $Ni-SiO_{2}$ sample. It may be suggested surfaces of alloy clusters on the Ru/Ni-$SiO_{2}$ samples contain more Ni components than the mole content ratio of the sample considering the above phenomena. With Ru/Ni-$SiO_{2}$ samples the absorption band shifts may be ascribed to variations of surface concentration, strain variation due to atomic size difference, variation of bonding energy and electronic densities, and changes of surface geometries according to surface concentration variation. Studies for CO adsorption on Ru/Ni alloy cluster surface by LEED and Auger spectroscopy, interation between Ru/Ni alloy cluster and $SiO_{2}$, and MO calculation for the system would be needed to look into the phenomena.