• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.726-731
• /
• 2002

Reaction synthesis is a process to form ceramics, intermetallics and their composites from elemental powder mixture. Application of this process to a surface modification techniques has a possibilities to enable the process at a lower temperature or for a shorter time, although synthesized materials are likely to include voids and unreacted elements. This paper intend to examine the effect of Si addition to the mixture of Al and Ni on the densification of synthesized Ni-Al intermetallic compounds and to evaluate the surface properties of obtained coatings. By the Si addition, exothermic reaction temperature to form Ni-Al intermetallic was lowered to be below the melting point of Al. Si soluted $Al_3$Ni$_2$, $Al_3$Ni and $Al_{6}$Ni$_3$Si were mainly formed in the coating layer when powder mixture was heated to 973K for 300s. Besides, densification was enhanced by increasing hot press pressure, Si additions and heating rate. When the composition of eutectic Al-Si reaches 78%, void ratio of sintered compact reduced to 0.4%. It is caused by higher flowability of Al-Si liquid phase generated and its infiltration into the void. Since the hardness of NiAl(Si) compound (about 600HV) formed in the coating layer is higher than that of Ni-Al compound (about 400HV), coating layer with high density and superior wear property is obtained by hot press using reaction synthesis from Al-Ni-Si powder mixture.

• Proceedings of the Korean Society of Applied Pharmacology
• /
• 1994.11a
• /
• pp.69-80
• /
• 1994

Although ureases play important roles in microbial nitrogen metabolism and in the pathogenesis of several human diseases, little is known of the mechanism of metallocenter biosynthesis in this Ni-Containing enzyme. Klebsiella aerogenes urease apo-protein was purified from cells grown in the absence of Ni. The purified apo-enzyme showed the same native molecular weight, charge, and subunit stoichiometry as the holo-enzyme. Chemical modification studies were consistent with histidinyl ligation of Ni. Apo-enzyme could not be activated by simple addition of Ni ions suggesting a requirement for a cellular factor. Deletion analysis showed that four accessory genes (ureD, ureE, ureF, and ureG) are necessary for the functional incorporation of the urease metallocenter. Whereas the $\Delta$ureD, $\Delta$ureF, and $\Delta$ureG mutants are inactive and their ureases lack Ni, the $\Delta$ureE mutants retain partial activity and their ureases possess corresponding lower levels of Ni. UreE and UreG peptides were identified by SDS-polyacrylamide gel comparisons of mutant and wild type cells and by N-terminal sequencing. UreD and UreF peptides, which are synthesized at ve교 low levels, were identified by using in vitro transcription/translation methods. Cotransformation of E. coli cells with the complementing plasmids confirmed that ureD and ureF gene products act in trans. UreE was purified and characterized. immunogold electron microscopic studies were used to localize UreE to the cytoplasm. Equilibrium dialysis studies of purified UreE with $^{63}$ NiC1$_2$ showed that it binds ～6 Ni in a specific manner with a $K_{d}$ of 9.6 $\pm$1.3 $\mu$M. Results from spectroscopic studies demonstrated that Ni ions are ligated by 5 histidinyl residues and a sixth N or O atom, consistent with participation of the polyhistidine tail at the carboxyl termini of the dimeric UreE in Ni binding. With these results and other known features of the urease-related gene products, a model for urease metallocenter biosynthesis is proposed in which UreE binds Ni and acts as a Ni donor to the urease apo-protein while UreG binds ATP and couples its Hydrolysis to the Ni incorporation process.ouples its Hydrolysis to the Ni incorporation process.s.

• The Journal of Advanced Prosthodontics
• /
• v.4 no.1
• /
• pp.37-42
• /
• 2012

PURPOSE. The influence of the modified process in the fiber-reinforced post and resin core foundation treatment on the fracture resistance and failure pattern of premolar was tested in this study. MATERIALS AND METHODS. Thirty-six human mandibular premolars were divided into 4 groups (n = 9). In group DCT, the quartz fibre post (D.T. Light-post) was cemented with resin cement (DUO-LINK) and a core foundation was formed with composite resin (LIGHT-CORE). In group DMO and DMT, resin cement (DUO-LINK) was used for post (D.T. Lightpost) cementation and core foundation; in group DMO, these procedures were performed simultaneously in one step, while DMT group was accomplished in separated two steps. In group LCT, the glass fiber post (LuxaPost) cementation and core foundation was accomplished with composite resin (LuxaCore-Dual) in separated procedures. Tooth were prepared with 2 mm ferrule and restored with nickel-chromium crowns. A static loading test was carried out and loads were applied to the buccal surface of the buccal cusp at a 45 degree inclination to the long axis of the tooth until failure occurred. The data were analyzed with MANOVA (${\alpha}$= .05). The failure pattern was observed and classified as either favorable (allowing repair) or unfavorable (not allowing repair). RESULTS. The mean fracture strength was highest in group DCT followed in descending order by groups DMO, DMT, and LCT. However, there were no significant differences in fracture strength between the groups. A higher prevalence of favorable fractures was detected in group DMT but there were no significant differences between the groups. CONCLUSION. The change of post or core foundation method does not appear to influence the fracture strength and failure patterns.

• Journal of Preventive Medicine and Public Health
• /
• v.13 no.1
• /
• pp.3-12
• /
• 1980

Certain heavy metals which may lead peoples to poisonous status are widely used in industry and their uses have been increasing along with rapid industrialization of this country. Such an increasement of metal uses aggravates the status of environmental pollution affecting foodstuffs which are the most important life supporting factor of animal and humanbeing. Concerning the safety measures to minimize food-borne transmission of such hazardous metals, surveillance is the backbone of them and probably more so with a potential problem such as intoxication. Theoretically, this surveillance should include the determination of levels of heavy metal toxicants in foods, the determination of food consumption patterns and typical total diet, and the estimation of total load of the metal contaminant from all sources of exposure including air, water, and occupational sources. In recent year, actually, such estimates on the total daily intake of some heavy metals from foods have been made in several developed countries and a wide variation of date by season, locality, and research method was recognized. Also in this country, this kind of research data is vitally needed to make up for the serious shortage or lack of references to estimate the total amount of heavy metal intake of the people. In this study, a modification model for estimation of the total daily intake of cadmium copper, nickel, zinc, and lead through foods was applied and concentrations of the above metals in crops cultivated in this country were measured with atomic absorption spectro photometer to get the following results. 1. Level of heavy metal concentration in crops Generally, the levels of such metals in essential crops such as rice, cucumber, radish. chinese cabbage, apple, pear, grape, and orange are similar or lower than those in Japan and other developed countries. By the way, a striking result on cadmium concentration was increasement of its concentration in rice from $0{\sim}0.035ppm$ in 1970 to 0.11ppm in this study. However, the value is still far below the. Japanese Permissible Lebel of 1.0ppm. 2. Estimation of total daily intake per capita from foods A new model for estimation was devised utilizing levels of metal concentration in foods, amount of food consumed, and other food factors. Based on the above method, the daily intake of cadmium was estimated to be $70.53{\mu}g/man/day$ in average which was as high as the Limit Value of ILO/WHO(up to $71.4{\mu}g/man/day$). Also, 3.89mg of Zinc, 1.65mg of cuppor, 0.32mg of lead were given as the total daily intake per capita by this research. 3. Efficacy of washing or skinning to decrease the amount of metals in crops After washing the crops sufficiently with commercial linear alkylate sulfonate, the concentration of heavy metals could be reduced to $50{\sim}80%$ showing decreasement rate of $20{\sim}50%$. Also, after skinning the fruits, decreasement rate of the heavy metal concentration shelved $0{\sim}50%$.