• Korean Journal of Materials Research
• /
• v.31 no.12
• /
• pp.672-676
• /
• 2021

In this paper, the effect of Ni (0, 0.5 and 1.0 wt%) additions on the microstructure, mechanical properties and electrical conductivity of cast and extruded Al-MM-Sb alloy is studied using field emission scanning electron microscopy, and a universal tensile testing machine. Molten aluminum alloy is maintained at 750 ℃ and then poured into a mold at 200 ℃. Aluminum alloys are hot-extruded into a rod that is 12 mm in diameter with a reduction ratio of 39:1 at 550 ℃. The addition of Ni results in the formation of Al₁₁RE₃, AlSb and Al3Ni intermetallic compounds; the area fraction of these intermetallic compounds increases with increasing Ni contents. As the amount of Ni increases, the average grain sizes of the extruded Al alloy decrease to 1359, 536, and 153 ㎛, and the high-angle grain boundary fractions increase to 8, 20, and 34 %. As the Ni content increases from 0 to 1.0 wt%, the electrical conductivity is not significantly different, with values from 57.4 to 57.1 % IACS.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.466-474
• /
• 2021

A wet type scrubber for merchant vessel uses super austenitic stainless steels with pitting resistance equivalent number (PREN) of 40 or higher for operation in a harsh corrosive environment. However, it is expensive due to a high nickel content. Thus, electrochemical behavior and cavitation erosion characteristics of UNS S32750 as an alternative material were investigated. Microstructure analysis revealed fractions of ferritic and austenitic phases of 48% and 52%, respectively, confirming the existence of ferritic matrix and austenitic island. Potentiodynamic polarization test revealed damage at the interface of the two phases because of galvanic corrosion due to different chemical compositions of ferritic and austenitic phases. After a cavitation test, a compressive residual stress was formed on the material surface due to impact pressure of cavity. Surface hardness was improved by water cavitation peening effect. Hardness value was the highest at 30 ㎛ amplitude. Scanning electron microscopy revealed wave patterns due to plastic deformation caused by impact pressure of the cavity. The depth of surface damage increased with amplitude. Cavitation test revealed larger damage caused by erosion in the ferritic phase due to brittle fracture derived from different strain rate sensitivity index of FCC and BCC structures.

• Journal of the Korean Society of Industry Convergence
• /
• v.26 no.4_2
• /
• pp.585-589
• /
• 2023

Unlike general carbon steel, stainless steel's mechanical properties change depending on the content of chromium and nickel. In this study, since stainless steel for high-temperature pressure container parts is used as shafts, the fatigue strength and fatigue limit of the materials were evaluated using a rotational bending fatigue test. Meanwhile, fatigue analysis was conducted under the same conditions as the specimen for structural analysis and fatigue analysis of stainless steel for high-temperature pressure container parts. Using the fatigue analysis results, we tried to derive the life of the material and the safety factor for each part. As a result of performing a fatigue test by processing a specimen for the fatigue test of A182 F6A stainless steel, the fatigue limit was 548 MPa. The ratio between the tensile strength and fatigue limit of the material was 0.545, representing 54.5% of the tensile strength.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.877-887
• /
• 1994

Cu-Ni-Si-P alloys have been studied in order to develop connector material which has a favorable combination of strength, electrical conductivity, elastic limit, thermal softening resistence and bend formability. Three kinds of trial alloys with various nickel and silicon content were melted and cast, hot rolled at about $900^{\circ}C$ and cold rolled. Mechanical properties and electrical conductivities of these alloys annealed at $450^{\circ}C$, $500^{\circ}C$ and $550^{\circ}C$ were investigated. An alloy with the composition of Cu-2.7%Ni-0.53%Si-O.O29%P, which shows a favorable combination of high strength and high electrical conductivity, has been developed. Various characteristics of the alloy 1 connector material were evaluated and compared with phospher bronze(C521OR-H) and brass(C26OOR-EH) connector material.

• Korean Journal of Environmental Agriculture
• /
• v.23 no.1
• /
• pp.22-27
• /
• 2004

The activated paper mill sludge was treated with WF and some additives (sodium sulfide, nickel nitrate, ethyl acetate) for methane fermentation at $35^{\circ}C$. Optmum C/N ratio was 60 out of three conditions (20, 30 and 60). The Period of 40% of methane content possibly ignition, was 2 days shorter than with non-treatment during 10 days. Nevertheless, the total amount of methane production showed the 1/8 level of control far the same period. The yield and content of methane were increased by the addition of sodium Sulfur and ethyl acetate. Sulfur was an essential factor in methane fermentation of paper mill sludge.

• Journal of Soil and Groundwater Environment
• /
• v.19 no.1
• /
• pp.1-7
• /
• 2014

When processing the biomass by Hydrothermal carbonization (HTC), a slow pyrolysis process, it produces bio-gas, biooil, and biochar. Among these end products, biochar is known for isolating or storing carbon and being used as a soil amendment. In this study, the characteristics of biochar generated by HTC at $250^{\circ}C$ for 1 hour, 2 hours, 3 hours, and 20 hours with synthetic food wastes and wood wastes were analyzed for potential uses in soil contaminated with heavy metals. The yield of biochar (weight %) increased when the ratio of wood wastes increased and showed a decreasing tendency as reaction time increased. Elemental analysis of biochar based on various conditions showed a maximum of 70% carbon (C) content. The carbon content showed an increasing tendency with the increase of wood wastes. Iodine adsorption test was peformed to determine the optimum reaction condition, which was 15% wood waste for mixing ratio and 2 hours for reaction time. Using biochar generated at the optimum condition, its capability of adsorbing heavy metals (Cd, Cu, Pb, Zn, Ni) was evaluated. It was concluded that lead (Pb) was removed efficiently while zinc (Zn) and nickel (Ni) were hardly adsorbed by biochar.

• Korean Journal of Metals and Materials
• /
• v.48 no.12
• /
• pp.1090-1096
• /
• 2010

This pitting corrosion study of welded joints of austenitic stainless steels (AISI 304L and 316L) has addressed the differentiating solidification mode using three newly introduced filler wires with a flux-cored arc welding process (FCAW). The delta ferrite (${\delta}$-ferrite) content in the welded metals increased with an increasing equivalent weight ratio of chromium/nickel ($Cr_{eq}/Ni_{eq}$). Ductility dip cracking (DDC) was observed in the welded metal containing ferrite with none of AISI 304L and 0.1% of AISI 316L. The potentiodynamic anodic polarization results revealed that the $Cr_{eq}/Ni_{eq}$ ratio in a 3.5% NaCl solution didn't much affect the pitting potential ($E_{pit}$). The AISI 316L welded metals with ${\ddot{a}}$-ferrite content of over 10% had a superior $E_{pit}$ value. Though the AISI 316L welded metal with 0.1% ferrite had larger molybdenum contents than AISI 304L specimens, it showed a similar $E_{pit}$ value because the concentration of chloride ions and the corrosion product induced severe damage near the DDC.

• Journal of the Korean Magnetics Society
• /
• v.8 no.6
• /
• pp.369-373
• /
• 1998

The exchange anisotropy between NiO antiferromagnetic layer and NiFe ferromagnetic layer has been investigated in NiFe(10 nm)/NiO(60 nm) formed by magnetron sputtering. The NiO films were sputtered from nickel oxide using R. F. poser and NiFe, Ta were deposited using D. C. power under Ar atmosphere. Above all. we studied the exchange anisotropy of Ni-Fe/NiO bilayer, and focused especially on the effect of NiO depostion condition. Our experimental data showed that the dominant factor for determining the exchange anisotropy properties was the Ar pressure during NiO deposition. The better exchange anisotropy properties were found when the NiO film was deposited at low Ar pressure probably due to the flatten interface and the epitaxial tendency of NiO grains and NiFe grains. However, as Ar pressure increased, interfacial diffusion at NiFe/NiO interface and oxygen content of NiO film increase, and consequently reduced the exchange anisotropy. We concluded that the flatten interface and relatively low oxygen content of NiO layer are dominant factors for the enhancement of the exchange anisotropy in NiFe/NiO bilayer.

• Journal of Soil and Groundwater Environment
• /
• v.23 no.3
• /
• pp.27-42
• /
• 2018

It is important to identify the contaminant sources and to evaluate the fate and transport of heavy metals to crops in agricultural lands. This study was conducted to evaluate metal sources and its transfer and accumulation to crop in agricultural soils. Pollution indices were calculated and multivariate analysis was performed to identify metal sources. To evaluate transfer and accumulation of metals to crops, the contents of phytoavailable metals were evaluated by using single extraction method and the correlation between metal content and soil properties was analyzed. Also the BCF was quantitatively evaluated for investigating the metal transition to each crop grown in the research area. As a result, Cr, Ni, and Co were expected to be mainly derived from geologic factors due to weathering of certain parent rocks. The content of nickel in soils of the research area was slightly higher than that of the concern level criteria based on total concentration, but the amount transferred and accumulated in the crops was actually low. Understanding the contamination characteristics by investigating the pollution sources of heavy metals and its transfer and accumulation to crops through various evaluation techniques could provide important information for proper management of the agricultural land.

• The Korea Journal of Herbology
• /
• v.33 no.6
• /
• pp.87-92
• /
• 2018

Objectives: The aim of the study was to analyze the constituents of Pyrolusitum, which was used to eliminate static blood and inflammation, to establish the basis of clinical application. Methods: Qualitative analysis was performed by X-Ray Diffraction (XRD) using the sample as a powder, and the elemental content of granular sample was measured by X-Ray Fluorescence (XRF). 1 M hydrochloric acid and 5% sodium hydroxide aqueous solution were added to observe the changing shape, respectively. Results: Qualitative analysis by XRD revealed that the Pyrolusitum samples used in the study contained quarts and kaolinite. Quantitative analysis by XRF revealed that the manganese content in the samples used in the study was 6.16% on average, while iron was contained the highest amount of 22.99%. The minor constituents include 1.08% of titanium, 0.30% of barium, 0.18% of lead, 0.06% of zirconium, 0.05% of chromium, 0.04% of zinc, 0.03% of cadnium, 0.02% of nickel, 0.01% of arsenic, 0.01% of copper, 0.01% of rubidium, 0.01% of strontium, 0.00% of molybdenum, respectively. And cobalt, which is reported to be a constituent of Pyrolusitum, was not detected at all in the samples of the study. Pyrolusitum was dissolved in dark brown when it was put into 1 M hydrochlorid acid, and there was brown precipitate when sodium hydroxide solution was added to Pyrolusitum and stirred. Conclusions: It was found that manganese and iron were the major constituents of Pyrolusitum, and it could be identified by using concentrated hydrochloric acid and sodium hydroxide solution.