• 한국입자에어로졸학회지
• /
• 제10권4호
• /
• pp.177-182
• /
• 2014

In this study, nickel-coated aluminum (Ni/Al) powders were synthesized for the utilization of energetic applications. Oxide materials present at the surface of Al powders of $45{\mu}m$ in averaged size were removed by using sodium hydroxide(NaOH) solution which is used for controlling pH. Nickel material is coated into the surface of oxide-removed Al powders by electroless-plating process. The microstructure of fabricated Ni/Al powders shows that nickel layers with a few hundreds nm were very homogeneously formed onto the surface of Al powders. The oxidation behavior of Ni/Al exihibit somewhat faster oxidation rate than that of pure Al with surface oxidation. Also, the higher exothermic reaction was observed from the Ni/Al powders. From the result of this, nickel coating is very promising method to obtain highly reactive and safe Al powders for energetic applications.

• 한국추진공학회지
• /
• 제18권4호
• /
• pp.9-17
• /
• 2014

본 연구에서는 고에너지 알루미늄 분말의 점화성 향상을 위해 자연상태 알루미나 산화막을 화학적으로 제거하고 니켈 코팅을 수행하였다. 니켈 코팅은 무전해 방법을 사용하였으며 SEM/EDS에 의한 표면 분석을 통해 시간에 따른 니켈 코팅 정도를 정성 정량적으로 확인하였다. 또한 XRD에 의한 화학종 분석과 TGA/DSC를 이용한 공기 환경 내에서의 열물성 분석을 수행하였고 이를 통해 공기 산화제 분위기에서의 니켈 코팅 된 알루미늄 분말의 점화촉진 메커니즘을 설명하였다. 이러한 결과를 통해 니켈 코팅 된 알루미늄이 코팅 되지 않은 알루미늄보다 좋은 점화성을 갖는 것을 정성적으로 확인하였다.