• Journal of the Korean institute of surface engineering
• /
• v.19 no.3
• /
• pp.83-91
• /
• 1986

Codeposited of boron nitride(BN) particle dispersed into electroless nickel-phosphours (Ni-P) and nickel-boron(Ni-B) platings were studied for the purpose of developing the wear resistance and lubricity. BN can be codeposited from electroless nickel plating bath with $NaH_2PO_2$ and $NaBH_4$ as the reducing agents. Most dispersolids were distributed uniformly in the Ni-P and Ni-B matrix. Abrasion loss decreased with increasing amount of codeposits and reached a constant value 2.4 percent by volume percent of BN particle. The wear resistance and the friction coefficient of the heat treated BN composite coatings were improved about three times than that of as-coatings. The BN composite coatings were more wear resistance than hard chromium. Ni-B-BN composite coatings showed lower wear resistance and friction coefficient than Ni-P-BN. The BN content of the deposite was found to be 2.4 v/o for these optium conditions.

• Journal of Powder Materials
• /
• v.27 no.1
• /
• pp.14-24
• /
• 2020

In this work, the electrical explosion of wire in liquid and subsequent spark plasma sintering (SPS) was introduced for the fabrication of Ni-graphite nanocomposites. The fabricated composite exhibited good enhancements in mechanical properties, such as yield strength and hardness, but reduced the ductility in comparison with that of nickel. The as-synthesized Ni-graphite (5 vol.% graphite) nanocomposite exhibited a compressive yield strength of 275 MPa (about 1.6 times of SPS-processed monolithic nickel ~170 MPa) and elongation to failure ~22%. The hardness of Ni-graphite composite had a value of 135.46 HV, which is about 1.3 times higher than that of pure SPS-processed Ni (105.675 HV). In terms of processing, this work demonstrated that this processing route is a novel, simple, and low-cost method for the synthesis of nickel-graphite composites.

• Proceedings of the IEEK Conference
• /
• 2007.07a
• /
• pp.441-442
• /
• 2007

We deposited nickel oxide(NiO) thin films on silicon(Si) substrates at Room temperature and $500^{\circ}C$ using a nickel target by reactive DC and RF sputtering. In addition, we anneal to NiO thin films deposited at room temperature. Using spectroscopic eillipsometry, we obtained optical characteristics of every films. We discussed relations of the optical and structural properties of NiO thin films with the oxygen flow rate, substrate temperature and annealing temperatures. Refraction was decreased and defect was increased when NiO thin films was annealed. We also analyzed the electrical characteristics of NiO films which deposited DC and RF sputtering method.

• Korean Journal of Chemical Engineering
• /
• v.35 no.12
• /
• pp.2474-2479
• /
• 2018

Plasma-enhanced atomic layer deposition (PEALD) is well-known for fabricating conformal and uniform films with a well-controlled thickness at the atomic level over any type of supporting substrate. We prepared nickel oxide (NiO) thin films via PEALD using bis(ethylcyclopentadienyl)-nickel ($Ni(EtCp)_2$) and $O_2$ plasma. To optimize the PEALD process, the effects of parameters such as the precursor pulsing time, purging time, $O_2$ plasma exposure time, and power were examined. The optimal PEALD process has a wide deposition-temperature range of $100-325^{\circ}C$ and a growth rate of $0.037{\pm}0.002nm$ per cycle. The NiO films deposited on a silicon substrate with a high aspect ratio exhibited excellent conformality and high linearity with respect to the number of PEALD cycles, without nucleation delay.

• Korean Journal of Materials Research
• /
• v.28 no.1
• /
• pp.24-31
• /
• 2018

This study reports an environment-friendly synthetic strategy to process nickel oxide nanocrystals. A mesoporous nickel oxide nanostructure was synthesized using an environmentally benign biomimetic method. We used a natural rambutan peel waste resource as a raw material to ligate nickel ions to form nickel-ellagate complexes. The direct decomposition of the obtained complexes at $700^{\circ}C$, $900^{\circ}C$ and $1100^{\circ}C$ in a static air atmosphere resulted in mesoporous nickel oxide nanostructures. The formation of columnar mesoporous NiO with a concentric stacked doughnuts architecture was purely dependent on the suitable direct decomposition temperature at $1100^{\circ}C$ when the synthesis was carried out. The prepared NiO nanocrystals were coated on cotton fabric and their antibacterial activity was also analyzed. The NiO nanoparticle-treated cotton fabric exhibited good antibacterial and wash durability performance.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.215-216
• /
• 2013

The silicide is a compound of Si with an electropositive component. Silicides are commonly used in silicon-based microelectronics to reduce resistivity of gate and local interconnect metallization. The popular silicide candidates, CoSi2 and TiSi2, have some limitations. TiSi2 showed line width dependent sheet resistance and has difficulty in transformation of the C49 phase to the low resistive C54. CoSi2 consumes more Si than TiSi2. Nickel silicide is a promising material to substitute for those silicide materials providing several advantages; low resistivity, lower Si consumption and lower formation temperature. Nickel silicide (NiSi) nanowire (NW) has features of a geometrically tiny size in terms of diameter and significantly long directional length, with an excellent electrical conductivity. According to these advantages, NiSi NWs have been applied to various nanoscale applications, such as interconnects [1,2], field emitters [3], and functional microscopy tips [4]. Beside its tiny geometric feature, NW can provide a large surface area at a fixed volume. This makes the material viable for photovoltaic architecture, allowing it to be used to enhance the light-active region [5]. Additionally, a recent report has suggested that an effective antireflection coating-layer can be made with by NiSi NW arrays [6]. A unique growth mechanism of nickel silicide (NiSi) nanowires (NWs) was thermodynamically investigated. The reaction between Ni and Si primarily determines NiSi phases according to the deposition condition. Optimum growth conditions were found at $375^{\circ}C$ leading long and high-density NiSi NWs. The ignition of NiSi NWs is determined by the grain size due to the nucleation limited silicide reaction. A successive Ni diffusion through a silicide layer was traced from a NW grown sample. Otherwise Ni-rich or Si-rich phase induces a film type growth. This work demonstrates specific existence of NiSi NW growth [7].

• The korean journal of orthodontics
• /
• v.48 no.3
• /
• pp.153-162
• /
• 2018

Objective: The aim of this trial was to compare the alignment efficiency and intermaxillary arch dimension changes of nickel-titanium (NiTi) or copper-nickel-titanium (CuNiTi) round archwires with increasing diameters applied sequentially to the mandibular arch. Methods: The initial alignment phase of fixed orthodontic treatment with NiTi or CuNiTi round archwires was studied in a randomly allocated sample of 66 patients. The NiTi group comprised 26 women, 10 men, and the CuNiTi ($27^{\circ}C$) group comprised 20 women, 10 men. The eligibility criteria were as follows: anterior mandibular crowding of minimum 6 mm according to Little's Irregularity Index (LII), treatment requiring no extraction of premolars, 12 to 18 years of age, permanent dentition, skeletal and dental Class I malocclusion. The main outcome measure was the alignment of the mandibular anterior dentition; the secondary outcome measure was the change in mandibular dental arch dimensions during 12 weeks. Simple randomization (allocation ratio 1:1) was used in this single-blind study. LII and mandibular arch dimensions were measured on three-dimensional digital dental models at 2-week intervals. Results: No statistically significant difference was observed between NiTi and CuNiTi according to LII (p > 0.05). Intercanine and intermolar arch perimeters increased in the CuNiTi group (p < 0.001). Inter-first premolar width showed a statistically significant interaction in week ${\times}$ diameter ${\times}$ application (p < 0.05). Conclusions: The effects of NiTi and CuNiTi round archwires were similar in terms of their alignment efficiency. However, the intercanine and intermolar arch perimeters, and the inter-first premolar width changes differed between groups.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.6
• /
• pp.283-288
• /
• 2010

Nanosized NiO powder was prepared by mixing an acid nickel salt and a base nickel salt and their reduction behavior was studied. Ni formate was employed as an acid salt and nickel hydroxide and basic nickel carbonate as base salts. One equivalent acid salt was mixed with 9 equivalent base salt. The mixture of the formate and the carbonate produced ~100 run spherical NiO powder by heat treatment at $750^{\circ}C$/2 h, but the mixture of the formate and the hydroxide gave rise to ~100 nm pseudo spherical NiO powder by heat treatment at $600^{\circ}C$/2 h and grew fast to give pseudo cubic crystals of 100~600 run by heat treatment at $750^{\circ}C$/2 h. Reduction by hydrogen gas proceeded much faster for the one with the hydroxide than that with the carbonate to give porous body with well grown necks. Their behavior was studied by analysis of TG/DSC, XRD, and SEM.

• Clean Technology
• /
• v.15 no.1
• /
• pp.47-53
• /
• 2009

Mesoporous aluminas (A-C, A-A, and A-N) were prepared by a templating method using cationic(C), anionic(A), and non-ionic(N) surfactant as a structure-directing agent, respectively. Nickel catalysts supported on mesoporous alumina (Ni/A-C, Ni/A-A, and Ni/A-N) were then prepared by an impregnation method, and were applied to hydrogen production by steam reforming of liquefied natural gas (LNG). Regardless of surfactant type, nickel species were finely dispersed on the surface of mesoporous alumina in the calcined catalysts. It was revealed that interaction between nickel species and support in the reduced catalysts was strongly dependent on the identity of surfactant. LNG conversion and $H_2$ composition in dry gas increased in the order of Ni/A-C < Ni/A-A < Ni/A-N. It was found that catalytic performance increased with increasing nickel surface area in the reduced catalyst. Among the catalyst tested, Ni/A-N catalyst with the highest nickel surface area showed the best catalytic performance.

• Journal of the Korean Ceramic Society
• /
• v.46 no.6
• /
• pp.592-595
• /
• 2009

Nanosize NiO powder was prepared by mixing acidic nickel nitrate with basic nickel carbonate. The particle size and morphology of NiO were mainly governed by the mole ratio of the nitrate to the carbonate. The effects were studied by DSC, XRD, FTIR, and SEM. Heat treatment conditions influence the particle size distribution of produced NiO powder extensively for the case of 3N7C (3 moles of the nitrate and 7 moles of the carbonate) and 4N6C, but only slightly for 1N9C and 2N8C. Uniform pseudospherical NiO particles were obtained in $50{\sim}70$ nm for 1N9C and $30{\sim}60$ nm for 2N8C by calcination at $750{^{\circ}C}$ for 2 h.