• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1992년도 하계학술대회 논문집 B
• /
• pp.724-726
• /
• 1992

In this paper, the permeability ($\mu_{\tau}'$, $\mu_{\tau}''$), dielectric constants($\varepsilon_{\tau}'$, $\varepsilon_{\tau}''$) and absorbption characteristics of Ferrite/Rubber 0-3 composites were investigated. The composite specimens were prepared by molding and curing the mixtures of matrix rubber and Ni-Zn ferrite powders which were synthesized by wet-direct method. The permeability ($u_{\tau}'$) of specimen was decreased from 2.58 to 0.7 in the range of 1$\sim$7(GHz) and kept constant 0.7$\sim$0.8 at higher than 7(GHz), the higher the frequency was, the less the valves of $u_{\tau}"$ was from 1.57 to 0.03. The optimum thickness of microwave absorber, utilizing the Smith chart, was 5(mm). The reflection loss shows over than 20(dB) from 5.5(GHz) to 7.5(GHz) at 5(mm) thickness and relative band width(B/fm) was about 30%.

• 한국정보통신학회논문지
• /
• 제3권1호
• /
• pp.43-50
• /
• 1999

Electromagnetic wave absorbers for anechoic chamber are needed to broaden the useful frequency bandwidth, reduce the thickness, and decrease the weight. There are various absorbers proposed for the above conditions, but they could not decisively solve the above requirements. The Electromagnetic wave absorber made by a conventional ferrite tile has, for example, broadened the useful frequency bandwidth by the way of forming air layer. Therefore, an air layer is formed absorber between a reflection plate and a sintered Ni-Zn ferrite tile of 7 mm in thickness, which has reflectivity less than -20 dB from 30 MHz to 450 MHz in frequency band, far narrower than the aimed bandwidth. The purpose of this paper is on the development of a universal anechoic chamber for measuring radiated electromagnetic wave or immunity of electronic equipments, GTEM-cell, wall material for prevention of TV ghost, etc. Accordingly, in this paper, a broadened electromagnetic wave absorber is designed, which has the reflection characteristics less than -20 dB from 30 MHz to 5,430 or 8,000 MHz in the bandwidth. Then we will design a super broadband electromagnetic wave absorber by inserting square Ferrite Cylinders Type with the thickness less than 23.5 m in three-layed type and with the frequency band from 30 MHz to 5,430-8,000 MHz under the above tolerance limits.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2007년도 The 1st International Symposium on Advanced Magnetic Materials
• /
• pp.281.1-281.1
• /
• 2007

• 한국세라믹학회지
• /
• 제36권3호
• /
• pp.284-292
• /
• 1999

고체함량을 변화시킨 NiCuZn 페라이트 페이스트를 사용하여 스크린 인쇄법으로 7.7$\times$4.5$\times$1.0 nm 크기의 칩인덕터를 제조한 후, 페라이트 페이스트의 고체함량에 따른 수축률, 소결밀도, 미세구조, 계면반응 등의 물리적 특성 및 자기적 특성 변화를 분석하였다. 조온소결을 위하여 attrition milling 공정을 통하여 미세분말을 준비하였으며, 소결온도는 880~94$0^{\circ}C$로 변화시켰다. 90$0^{\circ}C$에서 2시간 열처리된 페라이트 후막의 소결밀도는 고체함량이 50,55,60%로 증가할수록 5.12,5.14,5.18g/㎤로 증가하였으며, 이에 따라 칩 인덕터 시편들의 주파수 10 MHz에서 L값이 2.1,2.3,2.5 $\mu$H로 커졌다.Q값은 소결밀도 증가에 의한 Q값 증가효과와 아울러 입자가 커짐에 따른 반대효과로 인하여 고체함량에 따라 87,90,94로 큰 변화가 없었다. 페라이트 페이\ulcorner의 고체함량 및 소결온도와 무관하게 Ag 성분의 페라이트 쪽으로의 확산현상은 나타나지 않았다.

• 한국세라믹학회지
• /
• 제29권8호
• /
• pp.639-645
• /
• 1992

Effects of additives on electromagnetic properties of a Ni-Cu-Zn ferrite for a noise filter in high frequency regions were studied. Both resistivity and permeability were increased with the amount of Mn2O3 up to 1wt%, then decreased with further addition. Addition of Co2O3 decreased the permeability of the ferrite and shifted the resonance frequency to a higher frequency region, which was thought due to the stabilization of domain walls. Therefore it was possible to improve both the permeability and the loss and to control the cut-off frequency by the concurrent addition of Mn2O3 and Co2O3.

• Journal of Magnetics
• /
• 제19권4호
• /
• pp.399-403
• /
• 2014

We designed an ultra-high frequency (UHF: 300MHz to 3 GHz) ferrite circulator to investigate magnetic parameters, which are suitable for a self-biased GHz circulator design. The size of the ferrite disk was 1.58 mm in thickness and 13.5 mm in diameter. The saturation magnetization ($4{\pi}M_s$) of 3900 Gauss, internal magnetic field ($H_{in}$) of 1 kOe, and ferromagnetic linewidth (${\Delta}H$) of 354 Oe were used in circulator performance simulation. The simulation results show the isolation of 36.4 dB and insertion loss of 2.76 dB at 2.6 GHz and were compared to measured results. A Ni-Zn ferrite circulator was fabricated based on the above design parameters. An out-of-plane DC magnetic field ($H_0$) of 4.8 kOe was applied to the fabricated circulator to measure isolation, insertion loss, and bandwidth. Experimental magnetic parameters for the ferrite were $H_{in}$ of about 1.33 kOe and $4{\pi}M_s$ of 3935 Gauss. The isolation 43.9 dB and insertion loss of 5.6 dB measured at 2.5 GHz are in close agreement with the simulated results of the designed ferrite circulator. Based on the simulated and experimental results, we demonstrate that the following magnetic parameters are suitable for 2 GHz self-biased circulator design: $4{\pi}M_r$ of 3900 Gauss, $H_a$ of 4.5 kOe, $H_c$ greater than 3.4 kOe, and ${\Delta}H$ of 50 Oe.

• Journal of Magnetics
• /
• 제20권3호
• /
• pp.229-240
• /
• 2015

In this study, nanocrystalline ferrite powders with the composition $Ni_{0.5}Zn_{0.5}Fe_2O_4$ were prepared by the autocombustion method. The obtained powders were sintered at $800^{\circ}C$, $900^{\circ}C$ and $1,000^{\circ}C$ for 4 h in air atmosphere. The as-prepared and the sintered powders were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, and magnetization studies. An increase in the crystallite size and a slight decrease in the lattice constant with sintering temperature were observed, whereas microstrain was observed to be negative for all the samples. Two significant absorption bands in the wave number range of the $400cm^{-1}$ to $600cm^{-1}$ have been observed in the FT-IR spectra for all samples which is the distinctive feature of the spinel ferrites. The force constants were found to vary with sintering temperature, suggesting a cation redistribution and modification in the unit cell of the spinel. The M-H loops indicate smaller coercivity, which is the typical nature of the soft ferrites. The observed variation in the saturation magnetization and coercivity with sintering temperature has been attributed to the role of surface, inhomogeneous cation distribution, and increase in the crystallite size.

• 한국항해항만학회지
• /
• 제34권1호
• /
• pp.33-37
• /
• 2010

본 논문에서는 선박 탑재 전자기기들이 외부의 전자파에 의한 장해와 과도 전압에 의해 전자파 간섭 또는 오동작을 방지하기 위한 목적으로 EMC 필터를 설계 및 제작하였다. 먼저 필터를 구성하는 인덕터의 경우 높은 투자율을 가진 Ni-Zn계열 페라이트 비드와 컨덴서의 경우 공진현상을 최대한 억제하기 위해 공진점이 없는 관통형 컨덴서를 이용하여 EMC 필터를 설계 제작하고, 그 특성을 평가하였다. 그 결과 0 kHz~1.5 GHz 광대역에서 25~70 dB의 우수한 감쇠특성을 얻을 수 있었으며, 과도진압의 경우, IEC 61000-4-4에서 규정하는 level 4에서 4 kV를 인가 시 600 V로 과도전압이 감쇠되는 특성을 얻음으로써, 선박 탑재 전자기기들 간의 전자파 간섭을 억제할 수 있음을 확인하였다.

• 한국항해항만학회:학술대회논문집
• /
• 한국항해항만학회 2009년도 공동학술대회
• /
• pp.183-184
• /
• 2009

본 논문에서는 선박 탑재 전자기기들이 외부의 전원장해와 과도 전압에 의해 전자파 간섭과 오동작 하는 것을 방지하기 위해 EMC 필터를 설계 및 제작하였다. 먼저 인덕터의 경우 높은 투자율을 가진 Ni-Zn계열 페라이트 비드와 컨덴서의 경우 공진현상을 최대한 억제하기 위해 공진점이 없는 관통형 컨덴서를 이용하여 EMC 필터를 설계 제작하고, 그 특성을 평가하였다. 그 결과 0 kHz$\sim$1.5 GHz 광대역에서 $25{\sim}70$ dB의 우수한 감쇠특성을 얻을 수 있었으며, 과도전압의 경우, IEC 61000-4-4에서 규정하는 level 4에서 4 kV를 인가시 600 V로 과도전압이 감쇠되는 특성을 얻음으로써, 선박 탑재 전자기기들 간의 전자파 간섭을 억제할 수 있음을 확인하였다.

• 한국세라믹학회지
• /
• 제16권1호
• /
• pp.3-12
• /
• 1979

The effects of sintering temperature and sintering atmosphere on magnetic properties and microstructuresof Mn-Zn ferrites have been studied. Mixture of 52.8mole% $Fe_2O_3$, 26.4mole% MnO, 15.1mole0% ZnO and 5.7mole% NiO was prepared, and 0.1mole% CaO, 0.02mole% $SiO_2$ were added as minor additives. After calcining and ball milling the powder was granulated for compacting. The specimens were sintered at $1, 250^{\circ}$, $1, 300^{\circ}$and 1, 35$0^{\circ}C$ in the various atmosphere of $N_2$, $N^_2\DIV0.6% O_2$, $N_2＋2.7% O_2$, $N_2＋4.1% O_2$, $N^2＋8.2% O_2$ and air for 3 hours and cooled in $N_2$ atmosphere. The grian growth rate and densities increase as sintering temperature and oxygen content of atmosphere increase. At the sintering temperature of $1, 250^{\circ}C$ the initial permeabilities increase as oxygen content of atmosphere increase. At the sintering temperature of$ 1, 300^{\circ}$and $1, 350^{\circ}$ the initial permeabilities show maximum values at $N_2＋4.1% O_2$ atmosphere. The secondary peaks of initial permeabilities are observed between 100$^{\circ}$and 20$0^{\circ}C$, and the positions of secondary peaks move to higher temperature as oxygen content of atmosphere increases. Q-factors decrease as sintering temperature increases and oxygen content of atmosphere decreases.