• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.556-560
• /
• 1991

The behavior of Ni-Zn ferrite/Mn-Zn ferrite composite electromagnetic absorber was investigated. The imaginary part of complex permeability of the composite was higher than that of either ferrite alone at all frequency range (50∼1400MHz) studied. The difference, which was pronounced in low frequency range, was reached the maximum value when the composite consisted of constituent ferrites with equal amount. Since the thickness in inversely proportional to the imaginary part of complex permeability for the ferrite absorber, it was possible to reduce the thickness of electromagnetic absorber by employing a composite of two different ferrites.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.539-542
• /
• 2004

전자기기의 발달과 더불어 정보통신분야의 발달로 고주파 대역에서 우수하고 안정적인 Ni-Zn 페라이트를 제조하기 위해, Ni(니켈)의 일부를 코발트(Co)로 치환하여 결정자기이방성 상수 값을 증가시켜, 공명 주파수를 고주파 대역으로 높이고자 하였다. Co 함량이 증가함에 따라 투자율은 감소하는데, 이는 결정자기 이방성 상수를 크게 하여 공명 주파수를 높이는 결과를 보였으며, x=0.05에서 투자율 75, 공명 주파수 20MHz의 특성을 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.39 no.7
• /
• pp.669-674
• /
• 2002

Ni-Zn ferrite was sintered by microwave hybrid sintering method using microwave energy of 2.45 GHz, 700 W in the temperature range of 900$^{\circ}C$ ∼ 1070$^{\circ}C$. A high density (98%TD) Ni-Zn ferrite, added Bi$_2$O$_3$ and CuO, with a single phase was obtained by microwave sintering at 970$^{\circ}C$ for 15 min. All the sintered samples showed sintered density over 90% of TD. These results indicate that the processing time and energy consumption can be reduced significantly by microwave hybrid sintering method.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.109-113
• /
• 2002

본 연구에서는 공침법에 의한 초미세분말을 이용하여 제조된 (NiCuZn)-ferrite와 건식법을 이용하여 제조된 (NiCuZn)-ferrite의 저온소결 특성 및 전자기적 특성을 상호 비교 분석하였다. 조성은 (N $i_{0.4-x}$C $u_{x}$Z $n_{0.6}$)$_{1+w}$(F $e_2$ $O_4$/)$_{1-w}$에서 x의 값을 0.2, w의 값은 0.03으로 고정하였고, 소결은 공침법으로 합성된 분말의 경우 초기열처리과정을 거쳐 최종적으로 90$0^{\circ}C$에서, 건식법의 경우 11$50^{\circ}C$의 온도에서 진행하였다. 그 결과, 공침법으로 제조된 (NiCuZn)-ferrite는 건식법으로 제조된 (NiCuZn)-ferrite보다 20$0^{\circ}C$이상 낮은 소결온도에서 높은 소결밀도 값을 가졌으며, 품질계수 등 칩 인덕터에서 중요한 요소인 전자기적 특성이 우수하게 나타났다. 또한, 공침법으로 합성된 페라이트는 분말의 초기열처리온도에 따라 최종소결 특성이 크게 변하였다. 그밖에 공침법과 건식법으로 합성한 (NiCuZn)-ferrite의 결정성, 미세구조들을 XRD, SEM, TEM을 이용하여 비교 고찰하였다.하였다.다.

• Journal of the Korean Magnetics Society
• /
• v.9 no.5
• /
• pp.234-238
• /
• 1999

Lithium ferrites are prominent in the element of microwave frequency communication core and high frequency memory core because of their low coercivity and the high squareness ratio. This paper reports primarily the development of lithium ferrites with the low coercivity and high squareness ratio. The materials with $Li_{0.48-0.5x}Bi_{0.02}Ni_{0.04}Zn_xFe_{2.46-0.5x}O_4$ (x = 0,0.01, 0.02, 0.03) have been prepared to investigate the physical properties. The addition of ZnO gave raised maximum induction $(B_m)$ and decreased coercive force $(H_c)$, but the squareness ratio $(R\;=\;B_m/B_r)$ was decreased. The specimen of squareness ratio R=0.82, coercive force $H_c=\;1.80\;Oe$ was obtained for $Li_{0.48-0.5x}Bi_{0.02}Ni_{0.04}Zn_xFe_{2.46-0.5x}O_4$ (X=0) sintered at 105$0^{\circ}C$. Also the sample of squareness ratio R = 0.75, coercive force $H_c=\;1.70\;Oe$ for $Li_{0.48-0.5x}Bi_{0.02}Ni_{0.04}Zn_xFe_{2.46-0.5x}O_4$ (X = 0) sintered at 110$0^{\circ}C$ was measured. The Tc was obtained 463$^{\circ}C$ and the Br of environmental temperature variation was stable.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.48.1-48
• /
• 2002

• Journal of the Korean Ceramic Society
• /
• v.17 no.2
• /
• pp.89-95
• /
• 1980

The effect of non-stoichimetry and sintering temperature on the magnetic properties of materials in the system $Ni_{0.39}Zn_{0.61}Fe_{2.0+x}O_4$ have been investigated. The value of x used in initial weighing of oxides were varied from -0.04 to -0.12. The value of x, however, appears to be from +0.04 to -0.04 after ferrite powder preparation due to iron pick up during ball mill mixing and grinding. The densities of specimens which were deficientinrion were higher than those with excess ion. Specimens with near stoichiometric composition showed maximum initial permeability an dminimum coercivity whereas high values of quality factor (Q) were observed in iron deficient specimens. The quality factor decreased monotonically with increasing sintering temperature, but the permeability showed maxima with increasing sintering temperature. Thus highest value of figure of merit $\mu$Q was obtained in composition $Ni_{0.39}Zn_{0.61}Fe_{1.98O4}$ sintered at 100$0^{\circ}C$ for 3 hrs. in an air atmosphere.

• Applied Chemistry for Engineering
• /
• v.20 no.5
• /
• pp.500-504
• /
• 2009

NiCuZn Ferrites, known as preventing EMI/EMC, were prepared and their properties were investigated based on the chemical composition ratio, sintering temperature, and mean particle size. The NiCuZn ferrite made of $Fe_2O_3$ 49.0 mol%, NiO 9.0 mol%, CuO 8.0 mol%, ZnO 34.0 mol% could be applied at the largest range of electromagnetic wave. The optimal calcination and sintering temperature were $900^{\circ}C$ and $1080^{\circ}C$, respectively. The electromagnetic wave loss capacity of its mean particle size $1.12{\mu}m$ was superior to others examined.

• Korean Journal of Crystallography
• /
• v.14 no.1
• /
• pp.1-6
• /
• 2003

NiZn-ferrites were synthesized from the waste catalysts. which were by product of styrene monomer process and buried underground as an industrial wastes, and their magnetic properties were investigated. Nickel oxide and zinc oxide powders were mixed with finely ground waste catalysts, and spinel type ferrite was obtained by calcination at 900℃ and sintering at 1325℃ for 5 hours. The initial permeabilities were measured and reflection losses were calculated from S-parameters for the composition of Ni/sub x/Zn/sub 1-x/Fe₂O₄(x=0.36, 0.50, 0.66) and (Ni/sub 0.5/Zn/sub 0.5)/sub 1-y/Fe/sub 2+y/O₄(y=-0.02, 0, 0.02).

• Journal of the Korean institute of surface engineering
• /
• v.50 no.3
• /
• pp.212-218
• /
• 2017

$Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrite powders were prepared by self-propagating high temperature synthesis followed by classifying with an ultrasonic wet-magnetic separation unit to get high pure nano-sized particles. The $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrites were well formed by using several powders like iron, nickel oxide, zinc oxide and magnesium oxide at 0.1 MPa of oxygen pressure. The ultrasonic wet-magnetic separation of pre-mechanical milled ferrite powders resulted in producing the powders with average size of 800 nm. The addition of a surfactant during the wet-magnetic separation process improved productivity more than twice. The coercive force, maximum magnetization and residual magnetization of the $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ nano-powders with 800 nm size were 3651 A/m, $53.92Am^2/kg$ and $4.0Am^2/kg$, respectively.