• The Journal of the Petrological Society of Korea
• /
• v.27 no.1
• /
• pp.37-47
• /
• 2018

Volcanic ash samples of historical eruptions from Mt. Baekdu were analyzed for major oxides, trace and rare earth elements by a variety of analytical techniques. The results indicate that the ashes consist of approximately 58.8~71.1 wt.% $SiO_2$, 9.6~16.8 wt.% $Al_2O_3$, 4.5~6.9 wt.% $Fe_2O_{3t}$, 0.1~1.7 wt.% MgO, 0.3~1.6 wt.% CaO, 5.2~6.3 wt.% $Na_2O$, 4.3~5.9 wt.% $K_2O$ and less than 1.2 wt.% $TiO_2$. Thirty two trace metals including Ba, Cu, Cr. Co, Ni, Sr, V, Zn, and Zr were analyzed. The ashes can be divided two groups: group A(1 ka Millennium pumice, 1668 and $190{\underline{3}}$ pumice) and group B(1702 pumice) according to the relative enrichment of HREEs. The abundances of heavy metals such as Cu, Co, Mn, and Zn were relatively low. As compared to the Sakurajima volcanic ash, Baekdusan volcanic ash has low concentrations of Y, Nb, Pb, U, Sc, V, Ni and Cu and high concentrations of Zr, Ba, Hf, Cr, Co, Zn and rare-earth (except Eu).

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.124.1-124.1
• /
• 2008

• Journal of the Korean Chemical Society
• /
• v.35 no.5
• /
• pp.512-519
• /
• 1991

The axial ligations of nitrogenous bases (pyridine, imidazole, 1-methylimidazole and 2,6-lutidine) to Zn(II)-, Cu(II)-, and Ni(II)-tetrakis(o-chlorophenyl)porphyrin(o-ClTPP), and -tetraphenylporphyrin (TPP) were investigated in organic solvents $(CH_2Cl_2,\;C_6H_6,\;CH_3NO_2,\;(CH_3)_2CO,\;CHCl_3,\;DMF\;and\;DMSO)$ and at 0.01M of ionic strength. The equilibrium constants for the ligation reactions of methalloporphyrins were determined using spectrophotometric method at 15∼35${\circ}C$. In case of M(II)-TPP the equilibrium constants K were considerably larger than those of M(II)-(o-Cl)TPP, depending on steric effect of the porphyrin. The linear relationships between logK of the axial ligation and $pK_a$ of nitrogenous base were shown in M(II)-TPP, but not in M(II)-(o-Cl)TPP. The stabilities of MTPP(L) were controlled by the reation enthalpy and entropy, while those of M(o-Cl)TPP almost by the reaction entropy. The coordinating power of solvent to the methalloporphyrin were also studied in $CHCl_3,\;(CH_3)_2CO$, DMF and DMSO. From those results the solvent effects on the equilibrium constants were discussed.

• Journal of the Korean Magnetics Society
• /
• v.5 no.2
• /
• pp.109-111
• /
• 1995

We suggest the phenominological model to determine the mangetoelastic coupling coefficient in Cu/Ni/Cu thin films by considering effective anisotropy energy with magnetic film thicknesses. This indirect determination can be applied other single crystalline systems.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2004.12a
• /
• pp.200-201
• /
• 2004

The $H_{EB}$ was investigated for exchange coupling $20\;{\AA}\;Fe/x\;{\AA}\;NiO\;(type-I samples)$, $20\;{\AA}\;Fe/x\;{\AA}$ nonmagnetic layer $(MgO, Ag, Cu)/(500-x{\AA})$ NiO (type-II smaples). In type-I samples, the $H_{EB}$ is long-range coupling when looking from the point of view of the AFM. The $H_{EB}$ consistent with a generalized Meiklejohn-Bean approach. The critical thickness, which $H_{EB}$ is observed, is $130\;{\AA}$. In type-II samples, MgO layer more decouples the thin interfacial NiO from bottom NiO than other nonmagnetic layer. Nd the decoupling of Ag smallest. This means that the Ag layer has strong coupling the thin interfacial NiO with bottom NiO.

• Korean Journal of Metals and Materials
• /
• v.49 no.4
• /
• pp.298-303
• /
• 2011

Mg-23.5 wt%Ni-xwt%Cu (x = 2.5, 5 and 7.5) samples for hydrogen storage were prepared by melt spinning and crystallization heat treatment from a Mg-23.5 wt%Ni-5 wt%Cu alloy synthesized by the gravity casting method. They were then ground under $H_2$ to obtain a fine powder. Among these samples the Mg-23.5Ni-2.5Cu sample had the highest hydriding and dehydriding rates after activation. The Mg-23.5Ni-2.5Cu sample absorbed 3.59 and 4.01 wt%H for 10 and 60 min, respectively, at 573K under 12 bar $H_{2}$. The activated 88(87.5Mg-10Ni-2.5Cu)-$5Nb_{2}O_{5}-7NbF_{5}$ sample absorbed 2.93 wt%H for 10 min, and 3.14 wt%H for 60 min at 573K under 12 bar $H_{2}$.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.430-436
• /
• 2000

In this paper, we have studied the effect of constituent ratio NiO, CuO and doped with B-Bi-Zn on proper-ties(microstructure, density, shrinkage, permeability as a function of frequency, etc.) of hexagonal-ferrite for high fre- quency chip-inductor material about several GHz. The permeability were analyzed by impedance analyzer(100 kHz∼ 40 MHz) and network analyzed(30 MHz∼3 GHz). As a result of the characteristics. the B-Bi-Zn glass ceramic was used to lower the sintering temperature for additive as function of frequency from 100kHz to 1.8 GHz showed con-stant tends. The maximum imaginary value of complex permeability was observed near the resonance frequency of 2 GHz.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.4
• /
• pp.47-53
• /
• 2002

In this study, two different (NiCuZn)-ferrite which were fabricated by using ultra-fine powders synthesized by the wet processing and conventionally commercialized powder, were investigated and compared each other in terms of the low temperature sintering and electromagnetic properties. Composition of x and w in $(Ni_{0.4-x}Cu_xZn_{0.6})_{1+w}(Fe_2O_4)_{1-w}$ were controlled as 0.2 and 0.03, respectively. The sintering temperature were $900^{\circ}C$ for ultra-fine powders by way of initial heat treatment and $1150^{\circ}C$ for commercialized powders. The (NiCuZn)-ferrite by ultra-fine powders showed love. sintering temperature than that of commercialized powders by over $200^{\circ}C$, and excellent electromagnetic properties such as the quality factor which is a important factor in the multi-layered chip inductor. In addition, characteristics of B-H hysteresis, crystallinity, microstructure and powder morphology were analyzed by a vibrating sample method(VSM), x-ray diffractometer(XRD), transmission electron microscope (TEM) and scanning electron microscope(SEM).

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.5
• /
• pp.261-264
• /
• 2017

$Ni_{0.79}Co_{0.15-x}Cu_xMn_{2.06}O_4$ ($0{\leq}x{\leq}0.09$) thick films were fabricated using the conventional solid-state reaction method and screen-printing method. Structural and electrical properties of specimens based on the amount of Cu were observed in order to investigate their applicability in the infrared detector. All specimens showed a single spinel phase with a homogeneous cubic structure. As the amount of Cu increased, the average grain size increased and was found to be approximately $5.01{\mu}m$ for the $Ni_{0.79}Co_{0.06}Cu_{0.09}Mn_{2.06}O_4$ specimen. The thickness of all specimens was approximately $55{\sim}56{\mu}m$. As Cu content increased, the resistivity and TCR properties at room temperature decreased, and these values for the $Ni_{0.79}Co_{0.06}Cu_{0.09}Mn_{2.06}O_4$ specimen were $502{\Omega}-cm$ and $-3.32%/^{\circ}C$, respectively. The responsivity and noise properties decreased with an increase in Cu content, with the specimen with a Cu content of x=0.09 showing 0.0183 V/W and $5.21{\times}10^{-5}V$, respectively.

• Korean Journal of Materials Research
• /
• v.15 no.8
• /
• pp.503-507
• /
• 2005

Microstructure and wear behavior of A1203-based nanocomposites with Cu and Ni-Co dispersions were investigated. $Al_2O_3/Cu$ and $Al_2O_3/Ni-Co$ nanocomposites were fabricated by hydrogen reduction and sintering method using metal oxide and metal nitrates. The nanocomposites showed increased mechanical properties compared with monolithic $Al_2O_3$. In particular, high toughness and hardness were measured for the $Al_2O_3/Ni-Co$ nanocomposite consolidated by spark plasma sintering. A minimum value of wear coefficient comparable to the monolithic $Al_2O_3$ was obtained for $Al_2O_3/Ni-Co$ nanocomposite. Wear behavior is discussed in terms of microstructure and mechanical properties of nanocomposites