• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.190.2-190.2
• /
• 2008

• 연구논문집
• /
• s.29
• /
• pp.141-149
• /
• 1999

Brazing of Fe-Cr-Al alloy was carried out at $1200^{\circ}C$ in vacuum furnace using nickel-based filler metals : BNi-5 powder(Ni-Cr-Si-Fe base alloy} and MBF-50 foil (Ni-Cr-Si-B). The effect of boron content on the stability of oxide scale on the brazed joint was investigated by means of cyclic oxidation test performed at $1050^{\circ}C$ and $1200^{\circ}C$. Apparently, the joints brazed with MBF-50 containing boron showed relatively stable oxidation rates compared to boron-free BNi-5 at both temperatures. However, it was considered that the slower weight loss of MBF-50 brazed specimen wasn’t resulted from the low oxidation rate but from the spallation of oxide layer. The oxide layer consisted of thick spinel oxide on the surface and $Al_2 O_3$ internal oxide layer along the interface between mother alloy and braze, the mother alloy was also eroded seriously by the formation of spinel oxides such as $FeCr_2 O_4$ and $NiCr_2 O_4$ on the surface, likely to be induced by the change of oxide forming mechanism due to diffusion of boron from the braze. On the contrary, the joint brazed with BNi-5 showed the good oxidation resistance during the cyclic oxidation test. It seems that the oxidation can be retarded by the formation of stable $Al_2 O_3$ layer at the surface.

• Journal of Magnetics
• /
• v.3 no.4
• /
• pp.123-126
• /
• 1998

The magneto-impedance (MI) has been measured in the annealed Co66Fe4Ni1B14Si15 amorphous ribbon for the evaluation of anisotropy field. MI at the frequency of 10 MHz is related to the transverse permeability from rotational magnetization depending on the local anisotropy field. MI varies sensitively with the annealing temperature, reflecting the change of anisotropy field distribution. The local anisotropy fields evaluated from MI Profiles are discussed in terms of the magnetic softness and microstructural change by the annealing.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.3
• /
• pp.177-182
• /
• 2017

The properties of electroless Ni-B thin film on diamond powder with different parameters (temperature, pH, surfactant etc.) were studied. The surface morphology, structure and composition distribution of the Ni-B film were observed by field effect scanning electron microscope (FE-SEM), energy-dispersive spectrometer (EDS), X-ray diffraction (XRD) and Auger electron spectroscopy (AES). The growth rate of Ni-B film was increased with increase of bath temperature. The B content in Ni-B film was reduced with increase of bath pH. As a result the structure of Ni-B film was changed from amorphous to crystalline structure. The PVP in solution plays multi-functional roles as a dispersant and a stabilizer. The Ni-B film deposited with adding 0.1 mM-PVP was strongly introduced an amorphous structure with higher B content (25 at.%). Also the crystallite size of Ni-B film was reduced from 12.7 nm to 5.4 nm.

• Nuclear Engineering and Technology
• /
• v.52 no.3
• /
• pp.589-596
• /
• 2020

Many components in the assembly section of Sodium-cooled Fast Reactor are made of good corrosionresistant 316 LN Stainless Steel material. To avoid self-welding of the components with the coolant sodium at elevated temperature, hardfacing is inevitable. Ni-based colmonoy-5 is used for hardfacing due to its lower dose rate by Plasma Transferred Arc process due to its low dilution. Since Ni-Cr-B-Si alloy becomes very fluidic while depositing, the major height of the weld overlay rests inside the groove. Hardfacing is also done over the plain surface where grooving is not possible. Therefore, grooved and ungrooved hardfaced specimens were prepared at different travel speeds. Fe content at every 100 ㎛ of the weld overlay was studied by Energy Dispersive Spectroscopy and also the micro hardness was determined at those locations. A correlation between iron dilution from the base metal and the micro hardness was established. Therefore, if the Fe content of the weld overlay is known, the hardness at that location can be obtained using the correlation and vice-versa. A new correlation between micro hardness and dilution coefficient is obtained at different locations. A comparative study between those specimens is carried out to recommend the optimum travel speed for lower dilution.

• Journal of Welding and Joining
• /
• v.18 no.6
• /
• pp.62-67
• /
• 2000

Metallurgical characteristics of bonded region and high temperature mechanical properties of heat resistant alloy, Fe-35Ni-26Cr during liquid phase diffusion bonding were investigated employing AM17 insert metal. The insert metal for bonding, AM17 was newly developed Ni-base metal using interpolation method. Bonding of specimens were carried out at 1,403~1,463K for 600s in vacuum. The microconstituents in the bonded interlayer disappeared in the bonding temperature over 1,423K. The microstructures, alloying elements and hardness distribution in the base metal. The tensile strength and elongation of the joints at elevated temperatures were the same level as one of the base metal in the bonding temperature over 1,423K. The creep rupture strength and rupture lives of joints were almost identical to those of base metal.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2009.12a
• /
• pp.71-71
• /
• 2009

• Proceedings of the Korean Magnestics Society Conference
• /
• 2000.09a
• /
• pp.506-507
• /
• 2000

• Proceedings of the Korean Magnestics Society Conference
• /
• 2016.05a
• /
• pp.85-85
• /
• 2016

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.66.1-66.1
• /
• 2008