• 한국자기학회지
• /
• 제17권6호
• /
• pp.238-241
• /
• 2007

복합 전파흡수체로 사용할 Ni-Cu-Zn ferrite는 공침법을 사용하여 제조 하였고,제조 시편의 물리적 특성 및 전파흡수특성은 소결온도 변화에 따라 고찰하였다. Ni-Cu-Zn ferrite의 스피넬 구조는 XRD pattern을 통하며 확인하였다. 소결온도가 $1100^{\circ}C$에서 흡수 능력도 좋아짐을 알 수 있었으며, 소결된 페라이트의 초투자율은 평균 50 정도로 나타났다. $Ni_{0.7}Cu_{0.2}Zn_{0.1}Fe_2O_4$ 조성에서 소결 온도가 $1100^{\circ}C$ 일 때가 복합 전파흡수체로 사용할 조성임을 확인할 수 있었으며, 그 결과 복합 전파흡수체에서 사용할 수 있다고 사료된다.

• 한국분말재료학회지
• /
• 제11권3호
• /
• pp.202-209
• /
• 2004

In this study, nano-sized powder of Ni-ferrite was fabricated by spray pyrolysis process using the Fe-Ni complex waste acid solution generated during the shadow mask processing. The average particle size of the produced powder was below 100 nm. The effects of the reaction temperature, the inlet speed of solution and the air pressure on the properties of powder were studied. As the reaction temperature increased from 80$0^{\circ}C$ to 110$0^{\circ}C$, the average particle size of the powder increased from 40 nm to 100 nm, the fraction of the Ni-ferrite phase was also on the rise, and the surface area of the powder was greatly reduced. As the inlet speed of solution increased from 2 cc/min. to 10 cc/min., the average particle size of the powder greatly increased, and the fraction of the Ni-ferrite phase was on the rise. As the inlet speed of solution increased to 100 cc/min., the average particle size of the powder decreased slightly and the distribution of the particle size appeared more irregular. Along with the increase of the inlet speed of solution more than 10 cc/min., the fraction of the Ni-ferrite phase was decreased. As the air pressure increased up to 1 $kg/cm^2, the average particle size of the powder and the fraction of the Ni-ferrite phase was almost constant. In case of 3 $kg/cm^2 air pressure, the average particle size of the powder and the fraction of the Ni-ferrite phase remarkably decreased.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1993년도 추계학술대회 논문집
• /
• pp.124-127
• /
• 1993

In this paper, the magnetic properties of Ni-Zn ferrite powders dependent on pH have been studied. Ni-Zn ferrite powders were synthesized by coprecipitation method(pH were 7. 9. 11 and 13. respetively) using FeCl$_3$$.$ 6H$_2$O, NiCl$_2$$.$6H$_2$O and ZnCl$_2$as starting materials and its powders were calcined at 1,000($^{\circ}C$). The saturated magnetizations of the Ni-Zn ferrite powders dependent on various pH. such as 7, 9, 11 and 13 were 11.44, 29.77, 69.62 and 66.75(emu/g), respetively.

• 신재생에너지
• /
• 제2권2호
• /
• pp.69-74
• /
• 2006

본 연구는 페라이트의 Fe 양이온 일부를 Ni, Mn, Co등으로 치환하여 M-ferrite를 제조하여 열화학적 2단계 물 분해 반응의 특성을 비교 평가하였고, XRD, SEM, GC등의 분석으로 각 금속산화물의 특성을 확인하였다. M-ferrites 는 고상법으로 제조하였다. 각각의 M-ferrite에 대한 열적환원은 1573K 에서 진행하였고 물 분해 반응은 1273K 에서 실시하였다. 이 반응에서 생성된 가스는 전량 포집하여 GC를 통해 분석하였다. 반응 전후의 시료에 대하여 SEM, XRD를 분석하여 GC결과와 함께 금속산화물의 산화환원반응 특성을 고찰하였다. 그 결과로서 물 분해 반응 후 M-ferrite (M=Co, Ni, Mn)의 생성을 XRD를 통하여 확인할 수 있었고, 물 분해 반응과의 비교결과 격자상수의 증대가 M-ferrite내의 산소의 환원에 영향을 미치는 것을 알 수 있었다. SEM결과에서는 4cycle의 물 분해 반응 후 Mn-ferrite의 심한 sintering 현상을 확인 할 수 있었다.

• 한국세라믹학회지
• /
• 제39권12호
• /
• pp.1119-1123
• /
• 2002

Nanostructured spinel NiZn ferrites were prepared by the sol-gel method from metal nitrate raw materials. Analyses by X-ray diffraction and scanning electron microscopy showed the average particle size of NiZn ferrite was under 50 nm. The single phase of NiZn ferrites was obtained by firing at 250${\circ}C$, resulting in nanoparticles exhibiting normal ferrimagnetic behavior. The nanostructured $Ni_{1-X}Zn_XFe_2O_4$ (x=0.0∼1.0) were found to have the cubic spinel structure of which the lattice constants ${\alpha}_2$ increases linearly from 8.339 to 8.427 ${\AA}$ with increasing Zn content x, following Vegard's law, approximately. The saturation magnetization $M_s$ was 48 emu/g for x=0.4 and decreased to 8.0 emu/g for higher Zn contents suggesting the typical ferrimagnetism in mixed spinel ferrites. Pure NiZn ferrite phase substituted by Cu was observed before using the additive but hematite phase was partially appeared at $Ni_{0.2}Zn_{0.2}Cu_{0.6}Fe_2O_4$. On the other hand, the hematite phase in this NiZn Cu ferrite was disappeared after using the additive of acethyl aceton with small amount. The saturation magnetization Ms of $Ni_{0.2}Zn_{0.8-y}Cu_yFe_2O_4$(y=0.2∼0.6) as measured was about 51 emu/g at 77K and 19 emu/g at room temperature, respectively.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2002년도 동계연구발표회 논문개요집
• /
• pp.104-105
• /
• 2002

Ni$_{1-x}$-Zn$_{x}$ ferrite는 매우 큰 저항과 적은 eddy current loss를 가지고 있어 transfomer core나 radio frequency coil같은 high power device등의 전자 재료로 이용된다[1]. Ni$_{1-x}$-Zn$_{x}$ ferrite의 합성에는 여러 가지 방법이 이용되고 있으나 oxide/carbonate를 이용하여 120$0^{\circ}C$ 이상의 고온의 열을 가해 하소하는 solid-state reation과 diethylamine을 이용하여 metal nitrate를 공침 하는 coprecipition방법, sol-gel 방법 등의 wet chemical method가 가장 일반적이다[2-3]. (중략)

• 한국수소및신에너지학회논문집
• /
• 제14권3호
• /
• pp.268-275
• /
• 2003

The water-splitting process by the metal oxides using solar heat is one of the hydrogen production method. The hydrogen production process using the metal oxides (NiFe2O4/NiAl2O4,CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite) was carried out by two steps. The first step was carried out by the CH4-reduction to increase activation of metal oxides at operation temperature. And then, it was carried out the water-splitting reaction using the water at operation temperature for the second step. Hydrogen was produced in this step. The production rates of H2 were 110, 160, 72, 29, 17, $21m{\ell}/hr{\cdot}g-_{Metal\;Oxide}$ for NiFe2O4/NiAl2O4, CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite respectively in the second step. CoFe2O4/CoAl2O4 had higher H2 production rate than the other metal oxides.

• 한국자기학회지
• /
• 제18권2호
• /
• pp.58-62
• /
• 2008

칩인덕터용 $Ni_{0.4}Zn_{0.4}Cu_{0.2}Fe_2O_4$ ferrite(NiZnCu ferrite)를 고상반응법 및 졸겔법으로 제조하였다. 고상반응법에 의해 제조된 마이크론크기의 NiZnCu ferrite 분말과 졸겔법에 의해 제조된 나노크기의 분말을 혼합하여 소결성 및 자기적 특성을 증가 시켰다. 나노크기의 분말을 20wt%첨가한 토로이달 코아 시편의 초투자율은 1 MHz에서 $880^{\circ}C$ 소결시 78.1에서 $920^{\circ}C$ 소결시 178.2의 값을 가졌으며 소결온도가 증가할수록 초투자율값이 증가하였다. 소결 밀도, 수축율 및 포화자화값도 소결온도가 증가함에 따라 증가하였으며 이것은 grain사이즈 효과 및 소결성이 증가 되었기 때문이다. 고상반응법에 의해 제조한 ferrite에 졸겔법에 의해 제조한 나노크기의 ferrite 분말을 혼합하여 소결성을 향상시키고 자기적 특성을 향상시킬 수 있었다.

• 한국자기학회지
• /
• 제24권3호
• /
• pp.81-85
• /
• 2014

$BaFe_{12}O_{19}/Ni_{0.5}Zn_{0.5}Fe_2O_4$ 나노복합체 페라이트는 솔-젤 연소법으로 합성하였고, 합성된 나노복합체 페라이트를 $600{\sim}900^{\circ}C$ 범위에서 1시간 동안 하소하였다. XRD 분석 결과, 경자성/연자성 나노복합체에서 경자성과 연자성이 공존하고 있음을 확인하였다. 나노복합체의 입자크기는 90 nm보다 작게 나타났다. 나노복합체는 단일 페라이트의 hysteresis 곡선과 같은 모양을 나타내었으며, 이로서 경자성과 연자성 사이에 exchange coupling이 잘 되었음을 확인할 수 있었다. 경자성/연자성 나노복합체 페라이트의 포화자화 값은 연자성보다 낮고 경자성보다 높았다. 잔류자화 값은 경자성과 연자성보다 크게 나타났고, 전체적으로 $(BH)_{max}$이 향상되었음을 확인할 수 있었다.

• 한국자기학회지
• /
• 제5권1호
• /
• pp.27-33
• /
• 1995

$Ni_{2-x}Zn_{x}Y$ - 고무 복합체의 ferrite 조성과 입자 크기 변화에 따른 복소투자율과 전파흡수 특성을 조사하였다. Ferrite 입자가 $1\mu\textrm{m}$ 이하인 경우에는 ferrite-고무 복합체가 단자구 거동을 하여 자연공명 현상만이 관찰되었다. $Ni_{2-x}Zn_{x}Y$ - 고무 복합체의 제 1정합주파수는 Zn 함량이 증가함에 따라서 저주파 대역으로 이동하였으며, 자연공명 주파수와 비례함을 알 수 있었다. 반면에 제 2정합주파수는 자연공명 주파수에 비례하지 않음을 확인하였다. 또한 복합 ferrite 전파흡 수체의 전파흡수 현상은 자벽공명보다는 자연공명에 크게 영향을 받음을 확인하였다.