• Korean Journal of Crystallography
• /
• v.14 no.1
• /
• pp.1-6
• /
• 2003

NiZn-ferrites were synthesized from the waste catalysts. which were by product of styrene monomer process and buried underground as an industrial wastes, and their magnetic properties were investigated. Nickel oxide and zinc oxide powders were mixed with finely ground waste catalysts, and spinel type ferrite was obtained by calcination at 900℃ and sintering at 1325℃ for 5 hours. The initial permeabilities were measured and reflection losses were calculated from S-parameters for the composition of Ni/sub x/Zn/sub 1-x/Fe₂O₄(x=0.36, 0.50, 0.66) and (Ni/sub 0.5/Zn/sub 0.5)/sub 1-y/Fe/sub 2+y/O₄(y=-0.02, 0, 0.02).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.331-334
• /
• 2001

In this study, the magnetic properties for Ni-Zn ferrite were investigated as the function of $Co_3$ $O_4$ additive contents which was predicted to improve the resonance frequency. Toroid specimens with the composition of N $i_{0.8-x}$Z $n_{0.2+x}$F $e_2$ $O_4$(x = 0, 0.05, 0.1, 0.15) ferrites were preparation by conventional ceramic processing technique. The maximum resonance frequency of 19.905 MHz and the permeability of 90.88 in 10 MHz were attained to the N $i_{0.8}$Z $n_{0.2}$F $e_2$ $O_4$with $Co_3$ $O_4$0.3 wt%. Both of the permeability in 10 MHz and the resonance increased to 107.11 and 19.005 MHz respectively for the N $i_{0.8}$Z $n_{0.2}$F $e_2$ $O_4$with $Co_3$ $O_4$wt% than the N $i_{0.8}$Z $n_{0.2}$F $e_2$ $O_4$/ with the free $Co_3$ $O_4$composition.composition.

• Resources Recycling
• /
• v.9 no.5
• /
• pp.16-21
• /
• 2000

Generation of abnormally large grains in the microstructure of small grains has been investigated on some ferrites. Some fractions of large grains were observed in the microstructue of sintered ZnFe$_2$O$_4$, Mn-ZnFe$_2$O$_4$, Fe$_3$O$_4$(in $N_2$) and MnFe$_2$O$_4$(in air). On the other hand, the large grains were not observed in $NiFe_2$$O_4$ and $CoFe_2$$O_4$, independent of calcining and sintering conditions. The large grains seem to be generated in such ferrites that are easy to very their compositions or valencies at high temperatures. as the sintering proceeded, the number of large grains was increasing to from a continuous structure consisting of large grains, while the size of large grains did not increase remarkably. In addition, the growth of small grains was also very slow during the generation of the large grains. The large grains appeared be suddenly generated after some induction periods. Avrami equation could be applied to the relation between net volume of large grains and sintering time. Thus, the grain boundaries may be strongly stabilized when the large grains are generated. The large grain is generated y the local activation of the stabilized rain boundaries, which is caused by the variation of composition or valencies during sintering. It is concluded that the essence of the abnormal gain growth is not the generation of abnormally large grains, but the abnormal stabilization and the local activation of he grain boundaries.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.28A no.11
• /
• pp.880-886
• /
• 1991

Multi-layered chip inductors were prepared with good magnetic properties by sintering Ni-Zn-Cu ferrites at a lower temperature. A slurry with 49.5mol%Fe$_{2}O_{3}$, 20.5mol% ZnO, 20mol% NiO and 10nol% CuO was cast into tapes with 60-100\ulcorner of thickness with a doctor blade techniques. The tapes were screen-pronted with 100% silver electrodes, layered and pressed at 250kg/cm$^{2}$ and then sintered ant 900$^{\circ}C$ for 2h. Inductance with internal electrodes printed 5, 10, and 15 turns showed 4.9, 15 and 24$\mu$, respectively, at 1MHz.

• Advances in nano research
• /
• v.12 no.4
• /
• pp.415-426
• /
• 2022

Nickel substituted cobalt-zinc ferrite nanoparticles with composition Co_0.5Zn_0.5Ni_xFe_2-xO₄ (x = 0.25, 0.5, 0.75, 1.0) were synthesized using a wet chemical method named citrate precursor method. Various characterizations of the prepared nanoferrites were done using X-ray powder diffractometry (XRD), Scanning electron microscopy (SEM), UV visible spectroscopy and Fourier transform spectroscopy technique (FT-IR). XRD confirmed the formation of cubic spinel structure of the samples with single phase having one characteristic peak at (311). The value of optical band gap (E_g) was found to decrease with Ni substitution and have values in the range 2.30eV to 1.69eV. A Fenton-type system was created by photocatalytic activity using source of visible light for removal of methylene blue dye. Observations revealed increase in the degradation of methylene blue dye with increasing nickel content in the samples. The degradation percentage was increased from 77.32% for x = 0.25 to 90.16% for x = 1.0 in one hour under the irradiation of visible light. Also, the degradation process was found to have pseudo first order kinetics model. Hence, it can be observed that synthesized nickel doped cobalt-zinc ferrites have good capability for water purification and its degradation efficiency enhanced with increase in nickel concentration.

• Journal of Powder Materials
• /
• v.15 no.4
• /
• pp.292-296
• /
• 2008

The electromagnetic (EM) wave absorption properties of the $Fe_{73}Si_{16}B_7Nb_3Cu_1$ nanocrystalline powder mixed with 5 to 20 vol% of Ni-Zn ferrites has been investigated in a frequency range from 100MHz to 10GHz. Amorphous ribbons prepared by a planar flow casting process were pulverized and milled after annealing at 425 for 1 hour. The powder was mixed with a ferrite powder at various volume ratios to tape-cast into a 1.0mm thick sheet. Results showed that the EM wave absorption sheet with Ni-Zn ferrite powder reduced complex permittivity due to low dielectric constant of ferrite compared with nanocrystalline powder, while that with 5 vol% of ferrite showed relatively higher imaginary part of permeability. The sheet mixed with 5 vol% ferrite powder showed the best electromagnetic wave absorption properties at high frequency ranges, which resulted from the increased imaginary part of permeability due to reduced eddy current.

• Journal of Magnetics
• /
• v.8 no.4
• /
• pp.138-141
• /
• 2003

$Ni_{0.65}Zn_{0.35}Fe_2O_4$thin films were prepared by using a sol-gel method. Their crystallographic, dielectric and magnetic properties were investigated as a function of Cu contents by means of an X-ray diffractometer (XRD), X-ray reflectivity, LCZ meter (NF2232), a vibrating sample magnetometer (VSM), and an atomic force microscope (AFM). From typical C-V measurements for $Ni_{0.65}Zn_{0.35}Fe_2O_4$ thin films on p-type silicon substrate, the surface charge density was calculated as 1.4 ${\mu}$C/$m^2$. The dielectric constant evaluated from the capacitance at the accumulation state was 28. The high $H_{c}$ and low $M_{sat}$ at x=0.0 and 0.1 were due to the growth of the ${\alpha}$-$Fe_2O_3$ phase having antiferromagnetic properties. The rapidly decreased $H_{c}$ and increased $M_{sat}$ at x=0.2 and 0.3 can be explained that the ${\alpha}$-$Fe_2O_3$ phases have completely disappeared at x=0.3 and so, non-magnetic defects are minimized. The $M_{sat}$ was slightly decreased and the $H_{c}$ was increased above at x=0.3 because the increase of grain boundary due to smaller grain size acts as defects during magnetization process.

• Journal of the Korean Ceramic Society
• /
• v.50 no.3
• /
• pp.231-237
• /
• 2013

Thermodynamic modeling of the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ complex ferrite system has been adopted as a rational approach to establish routes to better synthesis conditions for pure phase $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ complex ferrite. Quantitative analysis of the different reaction equilibria involved in the precipitation of $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ from aqueous solutions has been used to determine the optimum synthesis conditions. The spinel ferrites, such as magnetite and substitutes for magnetite, with the general formula $MFe_2O_4$, where M= $Fe^{2+}$, $Co^{2+}$, and $Ni^{2+}$ are prepared by coprecipitation of $Fe^{3+}$ and $M^{2+}$ ions with a stoichiometry of $M^{2+}/Fe^{3+}$= 0.5. The average particle size of the as synthesized $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$, measured by transmission electron microscopy (TEM), is 14.2 nm, with a standard deviation of 3.5 nm the size when calculated using X-ray diffraction (XRD) is 16 nm. When $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ ferrite is annealed at elevated temperature, larger grains are formed by the necking and mass transport between the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ ferrite nanoparticles. Thus, the grain sizes of the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ gradually increase as heat treatment temperature increases. Based on the results of Thermogravimetric Analysis (TGA) and Differential Scanning Calorimeter (DSC) analysis, it is found that the hydroxyl groups on the surface of the as synthesized ferrite nanoparticles finally decompose to $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ crystal with heat treatment. The results of XRD and TEM confirmed the nanoscale dimensions and spinel structure of the samples.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 1999.09a
• /
• pp.1-63
• /
• 1999

Generation of abnormally large grains in the microstructure of small grains has been investigated on some ferrites. Some fractions of large grains were observed in the microstructure of sintered ZnFe$_2$O$_4$, Mn-ZnFe$_2$O$_4$, Fe$_3$O$_4$(in N$_2$) and MnFe$_2$O$_4$(in air). On the other hand, the large grains were not observed in NiFe$_2$O$_4$ and CoFe$_2$O$_4$, independent of calcining and sintering conditions. The large grains seem to be generated in such ferrites that are easy to vary their compositions or valencies at high temperatures. As the sintering proceeded, the number of large grains was increasing to form a continuous structure consisting of large grains, while the size of large grains did not increase remarkably. In addition, the growth of small grains was also very slow during the generation of the large grains. The large grains appeared to be suddenly generated after some induction periods. Avrami equation could be applied to the relation between net volume of large grains and sintering time. Thus, the grain boundaries may be strongly stabilized when the large grains are generated. The large grain in generated by the local activation of the stabilized grain boundaries, which is caused by the variation of compositions or valencies during sintering. It is concluded that the essence of the abnormal grain growth is not the generation of abnormally large grains, but the abnormal stabilization and the local activation of the grain boundaries.