• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.506-508
• /
• 2001

The ferrite plating with applying power ultrasound waves of 19.5 kHz and 600W enabled us to encapsulate entirely MnZn ferrite cores for transformers with Ni$\sub$x/Zn$\sub$y/Fe$\sub$3-x-y/O$_4$coating. Supplying a NH$_4$OH solution during the plating broke the limit of the solubility of Ni ions to ferrite-plated films. The electrical resistivity of the NiZn ferrite coating increased with increasing the Ni and Zn content, reaching 2.3${\times}$10$\^$5/Ωcm at the composition of Ni$\sub$0.24/Zn$\sub$0.30/Fe$\sub$2.46/O$_4$. The saturation magnetization was 540 emu/㎤. As a result, the MnZn ferrite cores were successfully encapsulated with the NiZn ferrite coatings for an insulation layer.

• Journal of the Korean Magnetics Society
• /
• v.5 no.6
• /
• pp.937-946
• /
• 1995

In this research, the processing control of NiCuZn Ferrite has been developed. The relationship between initial permeability and bulk density of NiCuZn Ferrite with processing factors was studied. NiCuZn Ferrite, which calcinated at $700^{\circ}C$ for 3 hours, was ball milled for about 60 hours to make a size of $0.5\mu\textrm{m}$ followed by granulation using spray dryer. The physical properties and the magnetic properties of NiCuZn Ferrite were investigated with the processing factor, such as (i) granule size and forming pressure, and (ii) sintering temperature. The green density of NiCuZn Ferrite was largely depended on the forming pressure rather than its granule size. The green density of NiCuZn Ferrite was increased from $2.484\;g/cm^{3}$ to $3.002\;g/cm^{3}$ with increase in forming pressure. The bulk density of NiCuZn Ferrite was increased from $3.470\;g/cm^{3}$ to $4.754\;g/cm^{3}$ linearly with increase in sintering temperature. The relationship between initial permeability and bulk density of NiCuZn Ferrite was expressed with the empirical equation,$\mu_{i}=a+b_{\rho}+c_{\rho}^2$ at forming pressure and sintering temperature.

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.18 no.6
• /
• pp.848-853
• /
• 1993

The properties of ferrite bead, a low-pass filter, are determined by the frequency dispersion of the complex permeability. In this study, frequency dispersion of complex permeability of the Ni-Zn ferrites with different Ni/Zn ratio were investigated. Relationship between the behavior of filter and dispersion of complex permeability of a ferrite was studied. As a result, it was concluded that the compositions for Ni/Zn ratio of $0.41{\sim}0.47$, having high initial permeability and good sensitivity, were favorable as a ferrite bead filter.

• Journal of the Korean Magnetics Society
• /
• v.5 no.3
• /
• pp.191-196
• /
• 1995

NiCuZn ferrites were prepared by a solid-state reaction and sintered at $900^{\circ}C$ for 5 hours. Its properties were investigated by controlling the ferrite composition and processing. NiCuZn ferrite with a composition of ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1.02}{(Fe_{2}O_{3})}_{0.98}$ was found to have the maximum initial permeability as a result of the variation of Cu content and the (Ni+Cu)/Zn ratio. Curie temperature($T_{c}$) of NiCuZn ferrite was decreased with the larger Cu content and increased with the larger Ni content. NiCuZn ferrites of ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$ composition milled for 20~80 hours had the maximum initial permeability at w=-0.015 and Curie temperature ($T_{c}$) was decreased with the increasing of $Fe_{2}O_{3}$ deficiency(w).

• Journal of the Korean institute of surface engineering
• /
• v.45 no.5
• /
• pp.188-192
• /
• 2012

The hetero junction on dielectrics and ferrite for LTCC was prepared by using NiCuZn ferrite. The shrinkage behaviour of ferrite tapes in combination with a dielectric tape was investigated. The characteristics of NiCuZn ferrite were investigated using XRD (X-ray diffractometer), Dilatometer, FE-SEM (Field emission scanning electron microscope), EDS (Energy dispersive spectrometer). NiCuZn ferrite calcined at $700^{\circ}C$ had a good apparent density and initial permeability of magnetic properties. The shrinkage rate of the NCZF700 ferrite and dielectric material was similar. The multilayer revealed dense, uniform morphologies with excellent interface quality. Diffusion of hetero junction such as dielectric and ferrite was not occuring at $900^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.28 no.3
• /
• pp.225-233
• /
• 1991

In this study, we tried to find out the appropriate synthetic condition and magnetic properties of Ni-Zn ferrite {(NixZn1-x)Fe2O4} powders (where X=0, 0.1, 0.2, 0.3, ……0.9, 1). Ferrite powders were prepared by wet-direct method at 86℃ for 6hrs from FeCl36H2O, NiCl26H2O, and ZnCl2. The powders of (NixZn1-x)Fe2O4 (where X=0.4, 0.5, 0.6) have a good crystallinity, but the other ferrite powders consist of crystal and precursor ferrite. The ferrite powder's lattice constant is increased when ratio of ZnO contant is increased in the ferrite composition. And initial permeability was measured after sintering, result indicated regular pattern except (Ni0.4Zn0.6)Fe2O4 when the frequency were changed 10KHz to 10MHz.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.3
• /
• pp.45-50
• /
• 2015

The goal of this research is the create novel magnets with no rare-earth contents, with larger energy product by comparison with currently used ferrites. For this purpose we developed nano-sized hard-type/soft-type composite ferrite in which high remanent magnetization (Mr) and high coercivity (Hc). Nano-sized Ba-ferrite, Ni-Zn ferrite and $BaFe_{12}O_{19}/Ni_{0.5}Zn_{0.5}Fe_2O_4$ composite ferrites were prepared by sol-gel combustion method by use of glicine-nitrate and citric acid. Nanocomposite ferrites were calcined at temperature range $700-900^{\circ}C$ for 1h. According to the X-ray diffraction patterns and FT-IR spectra, single phase of NiZn-ferrite and Ba-ferrite were detected and hard/soft nanocomposite ferrite was indicated to the coexistence of the magnetoplumbite-structural $BaFe_{12}O_{19}$ and spinel-structural $Ni_{0.5}Zn_{0.5}Fe_2O_4$ that agreed with the standard JCPDS 10-0325 data. The particle size of nanocomposite turn out to be less than 120 nm. The nanocomposite ferrite shows a single-phase magnetization behavior, implying that the hard magnetic phase and soft magnetic phase were well exchange-coupled. The specific saturation magnetization ($M_s$) of the nanocomposite ferrite is located between hard ($BaFe_{12}O_{19}$) and soft ferrite($Ni_{0.5}Zn_{0.5}Fe_2O_4$). The remanence (Mr) of nanocomposite ferrite is much higher than that of the individual $BaFe_{12}O_{19}$ and $Ni_{0.5}Zn_{0.5}Fe_2O_4$ ferrite, and $(BH)_{max}$ is increased slightly.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.4
• /
• pp.47-53
• /
• 2002

In this study, two different (NiCuZn)-ferrite which were fabricated by using ultra-fine powders synthesized by the wet processing and conventionally commercialized powder, were investigated and compared each other in terms of the low temperature sintering and electromagnetic properties. Composition of x and w in $(Ni_{0.4-x}Cu_xZn_{0.6})_{1+w}(Fe_2O_4)_{1-w}$ were controlled as 0.2 and 0.03, respectively. The sintering temperature were $900^{\circ}C$ for ultra-fine powders by way of initial heat treatment and $1150^{\circ}C$ for commercialized powders. The (NiCuZn)-ferrite by ultra-fine powders showed love. sintering temperature than that of commercialized powders by over $200^{\circ}C$, and excellent electromagnetic properties such as the quality factor which is a important factor in the multi-layered chip inductor. In addition, characteristics of B-H hysteresis, crystallinity, microstructure and powder morphology were analyzed by a vibrating sample method(VSM), x-ray diffractometer(XRD), transmission electron microscope (TEM) and scanning electron microscope(SEM).

• Journal of the Korean Magnetics Society
• /
• v.18 no.3
• /
• pp.120-125
• /
• 2008

In this study, NiCoZn ferrites with the variation of sintering temperature and chemical composition were prepared by the coprecipitation. Microstructures Crystal structure of NiCoZn ferrites were analyzed by XRD and their electric magnetic characteristics were analyzed by LCR meter and their morphology observed by SEM. We identified that these powders have a typical NiCoZn spinel structure and nanoparticles average size of 40 nm. The impurity, the initial permeability and the Q factor value are the lowest of sintered NiCoZn ferrite at $1250^{\circ}C$. Also, we measured S-parameter for $(Ni_{0.4}Co_{0.1}Zn_{0.5})Fe_2O_4$ which showed a maximum reflection loss of -3.1 dB at 6 GHz for the 2 mm thick sample. From this result, we found that the NiCoZn ferrite can be used in ferrite microwave-absorbing application at a higher frequency region (> 6 GHz).

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.1
• /
• pp.11-17
• /
• 2007

The spherical NiZn ferrite particles were prepared by ultrasonic spray pyrolysis with mixed solution of aqueous metal nitrates. The NiZn ferrite particle was observed with nano-sized primary particles of about 10 nm or less before annealing which represented as paramagnetic behavior measured at 77 K and room temperature. The typical abnormal growth of primary particles like polyhedral primary particles was observed by annealing at 1273 K with Zn-concentration dependency. The XRD patterns showed good crystallinity of NiZn ferrite powder after annealing. In annealing process, the intra-particle sintering phenomenon was observed and the spherical particle morphology was collapsed at 1673 K. The saturation magnetization of NiZn ferrite powder for each annealing temperature was decreased with measuring temperature of $77{\sim}$300K.